CN104893333A - Novel wood-plastic composite floor board - Google Patents
Novel wood-plastic composite floor board Download PDFInfo
- Publication number
- CN104893333A CN104893333A CN201510285874.0A CN201510285874A CN104893333A CN 104893333 A CN104893333 A CN 104893333A CN 201510285874 A CN201510285874 A CN 201510285874A CN 104893333 A CN104893333 A CN 104893333A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood
- plastic
- powder
- floor board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel wood-plastic composite floor board which is prepared from the following raw materials in parts by weight: 10-30 parts of recycled plastic, 5-20 parts of chlorinated polyethylene, 5-20 parts of polyethylene, 50-70 parts of wood meal, 5-15 parts of complex fiber, 0.5-4 parts of a stabilizer, 1-4 parts of fire retardant, 3-12 parts of hollow glass beads, 2-10 parts of a plasticizer, 0.1-1.7 parts of zinc stearate, 1-2.5 parts of light calcium carbonate, 0.05-0.5 part of a UV absorber, 0.1-1 part of antioxidant, 0.5-1.5 parts of color masterbatch and 0-3 parts of an antimicrobial additive. In the novel wood-plastic composite floor board, recycled plastic is used for partially replacing polyvinyl chloride, and the complex fiber made of various crops is used as a base material; therefore, wastes can be recycled and reused, and the production cost of the wood-plastic composite floor board is saved. In addition, due to addition of the fire retardant, the UV absorber and the antimicrobial additive, the novel wood-plastic composite floor board has inflaming retarding, uvioresistant and antimicrobial properties. Paint applied to the surface of the floor board can be made into various colors, is capable of effectively protecting the floor board, also has faint scent, good gloss, good flexibility and levelling property, and is high in concentration, non-poisonous, pollution-free and harmless to a human body.
Description
Technical field
The invention belongs to field, floor, specifically a kind of plastic wood floor.
Background technology
Floor is more and more used in indoor decoration, and floor comprises solid wooden floor board, reinforced composite wooden floor, solid wooden compound floor, bamboo-wood floor, cork flooring.Wherein wood-plastic floor board is a kind of primarily of material based on timber (wood cellulose, plant cellulose) and thermoplastic macromolecule material (PE, PVC plastics) and processing aid etc., the high-tech green material made through die apparatus heating extrusion moulding again after mixing, have performance and the feature of timber and plastics concurrently, can timber be substituted.But current plastic-wood floor cost is high, be difficult to comprehensive multiple premium properties, as flame retardant resistance, anti-uv-ray and anti-microbe ability, and color is single.
Summary of the invention
The object of the present invention is to provide a kind of plastic wood floor, to solve the problem proposed in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme:
A kind of plastic wood floor, is characterized in that, be made up of the raw material of following weight parts:
Recycled plastic 10-30 part, chlorinatedpolyethylene 5-20 part, polyethylene 5-20 part, wood powder 50-70 part, conjugated fibre 5-15 part, stablizer 0.5-4 part, fire retardant 1-4 part, hollow glass microbead 3-12 part, softening agent 2-10, Zinic stearas 0.1-1.7 part, light calcium carbonate 1-2.5 part, UV absorption agent 0.05-0.5 part, oxidation inhibitor 0.1-1 part, look female 0.5-1.5 part, microbicidal additives 0-3 part;
Described wood-plastic floor board surface scribbles hard floor paint, and described hard floor paint is made up of the raw material of following weight parts: water-base resin 10,2 parts, defoamer 1 part, titanium dioxide 1.5, silica powder 3 parts, flow agent 0.5 part, pigment 1 part, hydrophober 0.8 part, 1.5 parts, solidifying agent, mill base 3 parts, 1 part, barium sulfate, silicone oil 4 parts, 8 parts, water.
Preferably, described a kind of plastic wood floor, is made up of the raw material of following weight parts: recycled plastic 17 parts, chlorinatedpolyethylene 7 parts, polyethylene 13 parts, wood powder 53 parts, conjugated fibre 7.5 parts, stablizer 2 parts, fire retardant 3 parts, hollow glass microbead 8 parts, softening agent 7, Zinic stearas 1 part, light calcium carbonate 1.5 parts, 0.2 part, UV absorption agent, 0.4 part, oxidation inhibitor, look female 1 part, microbicidal additives 1.5 parts.
Preferably, after described wood powder processes offal first drying process, skimming treatment by waste wood, be ground into fine powder raw material, fineness reaches 80 to 100 orders.
Preferably, described conjugated fibre is made up of 50% degreasing straw powder, 10% tea dregs of rice powder, 17% Folium Artemisiae Argyi powder, 20% bamboo wood powder, 3% activated carbon nano particle.
Preferably, its component of described anti-biologic additives B is Ag
xna
yh
zzr
2(PO
4)
3, wherein X+Y+Z=1.
Preferably, described softening agent be epoxy Toenol 1140, epoxyoleic acid butyl ester, octyl epoxy stearate, epoxidation tri-glyceride, epoxy tetrahydro-2-ethylhexyl phthalate one or more.
Preferably, described stablizer is calcium zinc stabilizer.
Compared with prior art, the invention has the beneficial effects as follows: in the present invention, replace polyvinyl chloride by recycled plastic part, use the conjugated fibre made of multiple kinds of crops as base material in addition, recycling is carried out to refuse, realize environmental protection, energy-conservation, resource recovery, save the production cost of wood-plastic floor board, add fire retardant, UV absorption agent and microbicidal additives simultaneously, make the present invention have fire-retardant, uvioresistant and antimicrobial properties.
The paint that wood-plastic floor board surface of the present invention scribbles, make shades of colour according to market demand, component is simple; with low cost, can not only available protecting floor, also there is quiet and beautiful fragrance; good luster; printing lines is clear, printing adaptability, excellent transferability, and soft levelling is good; concentration is high; nontoxic, pollution-free, harmless.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
A kind of plastic wood floor of the present invention, be made up of the raw material of following weight parts:
Recycled plastic 17 parts, chlorinatedpolyethylene 7 parts, polyethylene 13 parts, wood powder 53 parts, conjugated fibre 7.5 parts, stablizer 2 parts, fire retardant 3 parts, hollow glass microbead 8 parts, softening agent 7, Zinic stearas 1 part, light calcium carbonate 1.5 parts, 0.2 part, UV absorption agent, 0.4 part, oxidation inhibitor, look female 1 part, microbicidal additives 1.5 parts.
Described wood-plastic floor board surface scribbles hard floor paint, and described hard floor paint is made up of the raw material of following weight parts: water-base resin 10,2 parts, defoamer 1 part, titanium dioxide 1.5, silica powder 3 parts, flow agent 0.5 part, pigment 1 part, hydrophober 0.8 part, 1.5 parts, solidifying agent, mill base 3 parts, 1 part, barium sulfate, silicone oil 4 parts, 8 parts, water.
After described wood powder processes offal first drying process, skimming treatment by waste wood, be ground into fine powder raw material, fineness reaches 80 to 100 orders.
Described conjugated fibre is made up of 50% degreasing straw powder, 10% tea dregs of rice powder, 17% Folium Artemisiae Argyi powder, 20% bamboo wood powder, 3% activated carbon nano particle.
Its component of described anti-biologic additives B is AgxNayHzZr2 (PO4) 3, wherein X+Y+Z=1.
Described softening agent be epoxy Toenol 1140, epoxyoleic acid butyl ester, octyl epoxy stearate, epoxidation tri-glyceride, epoxy tetrahydro-2-ethylhexyl phthalate one or more.
Described stablizer is calcium zinc stabilizer.
The difference of following examples and embodiment 1 is,
Embodiment 2
A kind of plastic wood floor of the present invention, be made up of the raw material of following weight parts:
Recycled plastic 10 parts, chlorinatedpolyethylene 15 parts, polyethylene 7 parts, wood powder 65 parts, conjugated fibre 12 parts, stablizer 4 parts, fire retardant 4 parts, hollow glass microbead 11 parts, softening agent 10, Zinic stearas 1.1 parts, light calcium carbonate 2 parts, 0.1 part, UV absorption agent, 0.6 part, oxidation inhibitor, look female 0.5 part, microbicidal additives 3 parts.
Embodiment 3
A kind of plastic wood floor of the present invention, be made up of the raw material of following weight parts:
Recycled plastic 25 parts, chlorinatedpolyethylene 5 parts, polyethylene 6 parts, wood powder 50 parts, conjugated fibre 5 parts, stablizer 3.6 parts, fire retardant 1.4 parts, hollow glass microbead 5 parts, softening agent 3, Zinic stearas 0.7 part, light calcium carbonate 2.2 parts, 0.3 part, UV absorption agent, 0.8 part, oxidation inhibitor, look female 0.7 part, microbicidal additives 1 part.
Claims (7)
1. a plastic wood floor, is characterized in that, is made up of the raw material of following weight parts:
Recycled plastic 10-30 part, chlorinatedpolyethylene 5-20 part, polyethylene 5-20 part, wood powder 50-70 part, conjugated fibre 5-15 part, stablizer 0.5-4 part, fire retardant 1-4 part, hollow glass microbead 3-12 part, softening agent 2-10, Zinic stearas 0.1-1.7 part, light calcium carbonate 1-2.5 part, UV absorption agent 0.05-0.5 part, oxidation inhibitor 0.1-1 part, look female 0.5-1.5 part, microbicidal additives 0-3 part;
Described wood-plastic floor board surface scribbles hard floor paint, and described hard floor paint is made up of the raw material of following weight parts: water-base resin 10,2 parts, defoamer 1 part, titanium dioxide 1.5, silica powder 3 parts, flow agent 0.5 part, pigment 1 part, hydrophober 0.8 part, 1.5 parts, solidifying agent, mill base 3 parts, 1 part, barium sulfate, silicone oil 4 parts, 8 parts, water.
2. a kind of plastic wood floor according to claim 1, is characterized in that, is made up of the raw material of following weight parts: recycled plastic 17 parts, chlorinatedpolyethylene 7 parts, polyethylene 13 parts, wood powder 53 parts, conjugated fibre 7.5 parts, stablizer 2 parts, fire retardant 3 parts, hollow glass microbead 8 parts, softening agent 7, Zinic stearas 1 part, light calcium carbonate 1.5 parts, 0.2 part, UV absorption agent, 0.4 part, oxidation inhibitor, look female 1 part, microbicidal additives 1.5 parts.
3. a kind of plastic wood floor according to claim 1, is characterized in that, after described wood powder processes offal first drying process, skimming treatment by waste wood, be ground into fine powder raw material, fineness reaches 80 to 100 orders.
4. a kind of plastic wood floor according to claim 1, is characterized in that, described conjugated fibre is made up of 50% degreasing straw powder, 10% tea dregs of rice powder, 17% Folium Artemisiae Argyi powder, 20% bamboo wood powder, 3% activated carbon nano particle.
5. a kind of plastic wood floor according to claim 1, is characterized in that, its component of described anti-biologic additives B is Ag
xna
yh
zzr
2(PO
4)
3, wherein X+Y+Z=1.
6. a kind of plastic wood floor according to claim 1, it is characterized in that, described softening agent be epoxy Toenol 1140, epoxyoleic acid butyl ester, octyl epoxy stearate, epoxidation tri-glyceride, epoxy tetrahydro-2-ethylhexyl phthalate one or more.
7. a kind of plastic wood floor according to claim 1, is characterized in that, described stablizer is calcium zinc stabilizer.