CN104878373A - Antioxidant for ultrafine electrician braided copper wire - Google Patents
Antioxidant for ultrafine electrician braided copper wire Download PDFInfo
- Publication number
- CN104878373A CN104878373A CN201510206668.6A CN201510206668A CN104878373A CN 104878373 A CN104878373 A CN 104878373A CN 201510206668 A CN201510206668 A CN 201510206668A CN 104878373 A CN104878373 A CN 104878373A
- Authority
- CN
- China
- Prior art keywords
- electrician
- antioxidant
- fine
- ultra
- copper wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an antioxidant for an ultrafine electrician braided copper wire. The antioxidant comprises the following chemical components in percentage by weight: 15%-30% of a scale and corrosion inhibitor, 15%-30% of ethanol, 12%-20% of benzotriazole, 20%-25% of rare-earth salt, 1%-5% of sodium molybdate, 2%-6% of zinc salt, 0.5%-3% of citric acid, 4%-8% of propylene glycol methyl ether acetate and the balance of water; the antioxidant is nontoxic and environmentally friendly; after a copper wire is annealed and cooled, a layer of uniform, compact and difficult-to-fall protective film can be generated on the surface of the copper wire, so that the copper wire has good anti-tarishing capacity and antioxidant capacity; the storage life and service life of the copper wire are effectively prolonged; and the production cost is reduced.
Description
Technical field
The invention belongs to electric installation, field protected by electronic component connection line, particularly, relate to a kind of ultra-fine electrician's copper litz wire antioxidant.
Background technology
In the industry of copper wire processing now, the share of the market share of copper material processing is increasing, and particularly in plating, spraying, cable, wiring board, CNC, mould, punching press five metals, the industries such as powder metallurgy, the proportion occupied is year by year in the trend risen.
Going from strength to strength of industry, the quality requirements of product is also constantly improved, but in the process of Copper fabrication, copper and copper alloy are after processing cleaning, occur that the problem be oxidized is a disadvantage in the industry always, especially for copper wire, copper litz wire and electrician's copper soft whipping wire that electric installation, electronic component connect, after making copper wire, surface is very easily oxidized, occur that the situation of oxidation is very general, often within after cleaning, drying several hours, occur oxidation stain, can verdigris be generated under normal temperature oxidation, both ventilation breather is green; Maybe may be oxidized to Red copper oxide, for brick-red, after a few days, play oxidation sludge.The copper wire that copper material is originally more valuable, adds now expensive tooling cost and labour cost, and the product allowing many producers look at a pile oxidation is worried, and the product how processing oxidation has been delivered goods into the anxious problem that must solve of many producers.
Summary of the invention
For solving above-mentioned Problems existing; the object of the present invention is to provide a kind of ultra-fine electrician's copper litz wire antioxidant; nontoxic, environmental protection; after copper wire annealing cooling; can produce on copper wire surface one deck evenly, fine and close and be difficult to the protective membrane that comes off; make copper wire have good Anti-tarnishing ability, resistance of oxidation, effectively promote storage life and the work-ing life of copper wire, reduce production cost.
For achieving the above object, technical scheme of the present invention is:
A kind of ultra-fine electrician's copper litz wire antioxidant, described antioxidant comprises the chemical composition of following weight percent: anti-incrustation corrosion inhibitor: 15 ~ 30%, ethanol: 15 ~ 30%, benzotriazole: 12 ~ 20%, rare-earth salts: 20 ~ 25%, Sodium orthomolybdate: 1 ~ 5%, zinc salt: 2 ~ 6%, citric acid: 0.5 ~ 3%, 1-Methoxy-2-propyl acetate: 4 ~ 8%, all the other are water.
Preferably, described antioxidant comprises the chemical composition of following weight percent: anti-incrustation corrosion inhibitor: 15 ~ 20%, ethanol: 15 ~ 20%, benzotriazole: 14 ~ 16%, rare-earth salts: 20 ~ 24%, Sodium orthomolybdate: 2 ~ 3%, zinc salt: 4 ~ 5%, citric acid: 1 ~ 2%, 1-Methoxy-2-propyl acetate: 5 ~ 7%, all the other are water.
Further, described antioxidant comprises the chemical composition of following weight percent: anti-incrustation corrosion inhibitor: 15%, ethanol: 15%, benzotriazole: 14%, rare-earth salts: 24%, Sodium orthomolybdate: 2.5%, zinc salt: 5%, citric acid: 2%, 1-Methoxy-2-propyl acetate: 6%, all the other are water.
And, described anti-incrustation corrosion inhibitor be selected from 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid, poly-epoxy succinic acid, poly aspartic acid, ethylene diamine tetra methylene phosphonic acid sodium one or more.
Separately, described rare-earth salts is selected from Nd (NO
3)
3, LaCl
3, La (NO
3)
3, CeCl
3, Ce (NO
3)
3, PrCl
3in one or more.
Again, described zinc salt is ZnSO
4or ZnCl
2.
Form further, the stranded copper wire that described ultra-fine electrician's copper litz wire is 0.03 ~ 0.05mm by diameter weaves.
Beneficial effect of the present invention is:
Anti-incrustation corrosion inhibitor can form stable complex compound with cupric ion, can dissolve the oxide compound on copper wire surface.Copper wire and described antioxidant generate the insoluble and sull of densification, thus prevent the anode dissolution of copper wire or promote the passivation of copper wire, thus suppressing the corrosion of copper wire.Copper wire and antioxidant can generate the salt of indissoluble, thus copper wire and corrosive medium are isolated, and avoid corrosion.Benzotriazole and copper wire can generate inner complex Cu (C
6h
4n
3)
2, the surface of protection copper wire is not oxidized.
Embodiment
Following examples for illustration of the present invention, but can not be used for limiting the scope of the invention.The implementation condition adopted in embodiment can be for further adjustments according to the condition of producer, and unaccounted implementation condition is generally conventional laboratory conditions.
One provided by the present invention ultra-fine electrician's copper litz wire antioxidant, described antioxidant comprises the chemical composition of following weight percent: anti-incrustation corrosion inhibitor: 15 ~ 30%, ethanol: 15 ~ 30%, benzotriazole: 12 ~ 20%, rare-earth salts: 20 ~ 25%, Sodium orthomolybdate: 1 ~ 5%, zinc salt: 2 ~ 6%, citric acid: 0.5 ~ 3%, 1-Methoxy-2-propyl acetate: 4 ~ 8%, all the other are water.
Preferably, described antioxidant comprises the chemical composition of following weight percent: anti-incrustation corrosion inhibitor: 15 ~ 20%, ethanol: 15 ~ 20%, benzotriazole: 14 ~ 16%, rare-earth salts: 20 ~ 24%, Sodium orthomolybdate: 2 ~ 3%, zinc salt: 4 ~ 5%, citric acid: 1 ~ 2%, 1-Methoxy-2-propyl acetate: 5 ~ 7%, all the other are water.
Further, described antioxidant comprises the chemical composition of following weight percent: anti-incrustation corrosion inhibitor: 15%, ethanol: 15%, benzotriazole: 14%, rare-earth salts: 24%, Sodium orthomolybdate: 2.5%, zinc salt: 5%, citric acid: 2%, 1-Methoxy-2-propyl acetate: 6%, all the other are water.
And, described anti-incrustation corrosion inhibitor be selected from 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid, poly-epoxy succinic acid, poly aspartic acid, ethylene diamine tetra methylene phosphonic acid sodium one or more.
Separately, described rare-earth salts is selected from Nd (NO
3)
3, LaCl
3, La (NO
3)
3, CeCl
3, Ce (NO
3)
3, PrCl
3in one or more.
Again, described zinc salt is ZnSO
4or ZnCl
2.
Form further, the stranded copper wire that described ultra-fine electrician's copper litz wire is 0.03 ~ 0.05mm by diameter weaves.
Embodiment 1
Get 15wt% 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid, 15wt% ethanol, 20wt% benzotriazole, 25wt% Nd (NO
3)
3, 5wt% Sodium orthomolybdate, 6wt% ZnSO
4, 0.5wt% citric acid, 4wt% 1-Methoxy-2-propyl acetate, all the other are water.
Embodiment 2
Get 15wt% poly-epoxy succinic acid, 20wt% ethanol, 14wt% benzotriazole, 24wt% LaCl
3, 1wt% Sodium orthomolybdate, 2wt%ZnCl
2, 0.5wt% citric acid, 5wt% 1-Methoxy-2-propyl acetate, all the other are water.
Embodiment 3
Get 30wt% ethylene diamine tetra methylene phosphonic acid sodium, 20wt% ethanol, 13wt% benzotriazole, 20wt%LaCl
3, 1wt% Sodium orthomolybdate, 2wt%ZnCl
2, 0.5wt% citric acid, 5wt% 1-Methoxy-2-propyl acetate, all the other are water.
Embodiment 4
Get 15wt% ethylene diamine tetra methylene phosphonic acid sodium, 15wt% ethanol, 14wt% benzotriazole, 20wt% LaCl
3, 2.5wt% Sodium orthomolybdate, 5wt% ZnCl
2, 2wt% citric acid, 6wt% 1-Methoxy-2-propyl acetate, all the other are water.
Embodiment 5
Get the mixture of 17wt% 1-hydroxy ethylene-1,1-diphosphonic and poly-epoxy succinic acid, 16wt% ethanol, 15wt% benzotriazole, 21wt%CeCl
3, 3wt% Sodium orthomolybdate, 5wt%ZnSO
4, 1wt% citric acid, 7wt% 1-Methoxy-2-propyl acetate, all the other are water.
Embodiment 6
Get 20wt% poly aspartic acid, 15wt% ethanol, 16wt% benzotriazole, 21wt% Ce (NO
3)
3and La (NO
3)
3, 2wt% Sodium orthomolybdate, 4wt%ZnSO
4, 1.5wt% citric acid, 6wt% 1-Methoxy-2-propyl acetate, all the other are water.
Embodiment 7
Get the mixture of 15wt% poly aspartic acid and ethylene diamine tetra methylene phosphonic acid sodium, 17wt% ethanol, 14wt% benzotriazole, 23wt% PrCl
3and CeCl
3, 3wt% Sodium orthomolybdate, 4wt%ZnCl
2, 1.5wt% citric acid, 6wt% 1-Methoxy-2-propyl acetate, all the other are water.
Embodiment 8
Get 18wt% 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid thing, 18wt% ethanol, 16wt% benzotriazole, 23wt% Nd (NO
3)
3and La (NO
3)
3, 2wt% Sodium orthomolybdate, 5wt%ZnCl
2, 2wt% citric acid, 7wt% 1-Methoxy-2-propyl acetate, all the other are water.
The preparation method of described ultra-fine electrician's copper litz wire antioxidant is as follows:
Carry out according to weight percent described in embodiment 1 ~ 8 mixing of weighing respectively, put into reactor, stir 10 ~ 30 minutes, described ultra-fine electrician's copper litz wire antioxidant can be obtained.
The using method of ultra-fine electrician's copper litz wire antioxidant provided by the present invention in copper wire annealing process is as follows:
By diameter be 0.03 ~ 0.05mm copper wire through constant speed wheel constant speed after send in baking oven, the vapor baking copper wire of 400 DEG C-500 DEG C is adopted in baking oven, copper wire after roasting enters in water tank, described ultra-fine electrician's copper litz wire antioxidant (usage ratio: 1:800 is doubly watered use) is added in water tank, the antioxidation treatment to described copper wire can be realized, treatment time 5 ~ 60s, temperature 25 ~ 50 DEG C, the copper wire after process can obtain described ultra-fine electrician's copper litz wire through braiding.
Use the copper litz wire that the proof copper-wire braided after antioxidant process provided by the present invention becomes, preservation time average can reach 3 years.
It should be noted that, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted.Although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to the technical scheme of invention or equivalent replacement, and not depart from the scope of technical solution of the present invention, it all should be encompassed in right of the present invention.
Claims (7)
1. ultra-fine electrician's copper litz wire antioxidant, it is characterized in that, described antioxidant comprises the chemical composition of following weight percent: anti-incrustation corrosion inhibitor: 15 ~ 30%, ethanol: 15 ~ 30%, benzotriazole: 12 ~ 20%, rare-earth salts: 20 ~ 25%, Sodium orthomolybdate: 1 ~ 5%, zinc salt: 2 ~ 6%, citric acid: 0.5 ~ 3%, 1-Methoxy-2-propyl acetate: 4 ~ 8%, all the other are water.
2. ultra-fine electrician's copper litz wire antioxidant according to claim 1, it is characterized in that, described antioxidant comprises the chemical composition of following weight percent: anti-incrustation corrosion inhibitor: 15 ~ 20%, ethanol: 15 ~ 20%, benzotriazole: 14 ~ 16%, rare-earth salts: 20 ~ 24%, Sodium orthomolybdate: 2 ~ 3%, zinc salt: 4 ~ 5%, citric acid: 1 ~ 2%, 1-Methoxy-2-propyl acetate: 5 ~ 7%, all the other are water.
3. ultra-fine electrician's copper litz wire antioxidant according to claim 1, it is characterized in that, described antioxidant comprises the chemical composition of following weight percent: anti-incrustation corrosion inhibitor: 15%, ethanol: 15%, benzotriazole: 14%, rare-earth salts: 24%, Sodium orthomolybdate: 2.5%, zinc salt: 5%, citric acid: 2%, 1-Methoxy-2-propyl acetate: 6%, all the other are water.
4. the ultra-fine electrician's copper litz wire antioxidant according to claim 1 or 2 or 3, it is characterized in that, described anti-incrustation corrosion inhibitor be selected from 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid, poly-epoxy succinic acid, poly aspartic acid, ethylene diamine tetra methylene phosphonic acid sodium one or more.
5. the ultra-fine electrician's copper litz wire antioxidant according to claim 1 or 2 or 3, it is characterized in that, described rare-earth salts is selected from Nd (NO
3)
3, LaCl
3, La (NO
3)
3, CeCl
3, Ce (NO
3)
3, PrCl
3in one or more.
6. the ultra-fine electrician's copper litz wire antioxidant according to claim 1 or 2 or 3, it is characterized in that, described zinc salt is ZnSO
4or ZnCl
2.
7. the ultra-fine electrician's copper litz wire antioxidant according to claim 1 or 2 or 3, is characterized in that, the stranded copper wire that described ultra-fine electrician's copper litz wire is 0.03 ~ 0.05mm by diameter weaves and forms.