CN104877624A - 一种浴室防霉专用密封胶及其制备方法 - Google Patents
一种浴室防霉专用密封胶及其制备方法 Download PDFInfo
- Publication number
- CN104877624A CN104877624A CN201510255904.3A CN201510255904A CN104877624A CN 104877624 A CN104877624 A CN 104877624A CN 201510255904 A CN201510255904 A CN 201510255904A CN 104877624 A CN104877624 A CN 104877624A
- Authority
- CN
- China
- Prior art keywords
- parts
- titanium dioxide
- bathroom
- raw material
- sealing adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种浴室防霉专用密封胶,涉及密封胶技术领域,由以下重量份的原料制成:聚二甲基硅烷25-27份、二氧化钛10-20份、硅溶胶15-25份、碳酸钙8-10份、炭黑8-10份、钛白粉8-10份、铁粉2-4份、硬脂酸10-20份、石蜡7-9份、硫磺3-5份、促进剂1-3份。本发明的有益效果是:本发明工艺流程简洁,原料配比合理,采用的均为无毒无害的化学产品制作,制备的密封胶,具有防霉防潮,使用寿命长久的优势,使用效果好,粘接性强,密封性能佳,强度高,市场价值高,便于推广及使用。
Description
技术领域
本发明涉及密封胶技术领域,具体涉及一种浴室防霉专用密封胶及其制备方法。
背景技术
密封胶是指引随密封面形状而变形,不易流淌,有一定粘结性的密封材料,是用来填充构形间隙、以起到密封作用的胶粘剂,具有防泄漏、防水、防振动及隔音、隔热等作用,通常以沥青物、天然树脂或合成树脂、天然橡胶或合成橡胶等干性或非干性的粘稠物为基料,配合滑石粉、白土、炭黑、钛白粉和石棉等惰性填料,再加入增塑剂、溶剂、固化剂、促进剂等制成,密封胶的功能有很多,更具不同的功能会有这不同配方及制备的方法,目前建筑行业内使用的密封胶频率比较高,然而大多数使用的密封胶其功能及配方都是相同的,这样就会导致,在实际的使用中,不同环境应用会存在很大的差异,浴室是家庭中遇水最为频繁的功能室,其在使用普通密封胶的时候,时间长久后,会出现霉变等原因的存在。
发明内容:
本发明所要解决的技术问题在于提供一种配方合理,密封性好,防潮防霉的浴室防霉专用密封胶及其制备方法。
本发明所要解决的技术问题采用以下技术方案来实现:
一种浴室防霉专用密封胶,其特征在于:由以下组分的原料制成:
聚二甲基硅烷25-27份、二氧化钛10-20份、硅溶胶15-25份、碳酸钙8-10份、炭黑8-10份、钛白粉8-10份、铁粉2-4份、硬脂酸10-20份、石蜡7-9份、硫磺3-5份、促进剂1-3份。
各原料的优选组分为:聚二甲基硅烷26份、二氧化钛15份、硅溶胶20份、碳酸钙9份、炭黑9份、钛白粉9份、铁粉3份、硬脂酸15份、石蜡8份、硫磺4份、促进剂2份。
所述的促进剂为二正丁基二硫代氨基甲酸锌。
本发明的另一个目的是提供一种制备本发明浴室防霉专用密封胶的方法,其特征在于包括以下步骤:
a、选用反应釜,将原料中的聚二甲基硅烷、硅溶胶和硬脂酸加入其中,然后升温至80-90℃,搅拌反应2-3h,得到物料A取出备用;
b、选用一塑炼机,将步骤a中的物料A加入其中,然后加入原料中的二氧化钛、碳酸钙、炭黑、钛白粉、铁粉、石蜡和硫磺,然后进行混炼,控制混炼温度为30-40℃,混炼4-5h;
c、待步骤b混炼结束后,将原料中的石蜡和促进剂加入其中,搅拌混合均匀后即可、冷却后,出料,计量包装。
本发明的有益效果是:本发明工艺流程简洁,原料配比合理,采用的均为无毒无害的化学产品制作,制备的密封胶,具有防霉防潮,使用寿命长久的优势,使用效果好,粘接性强,密封性能佳,强度高,市场价值高,便于推广及使用。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1
一种浴室防霉专用密封胶,由以下组分的原料制成:
聚二甲基硅烷25-27kg、二氧化钛10-20kg、硅溶胶15-25kg、碳酸钙8-10kg、炭黑8-10kg、钛白粉8-10kg、铁粉2-4kg、硬脂酸10-20kg、石蜡7-9份、硫磺3-5kg、正丁基二硫代氨基甲酸锌1-3kg。
制备方法如下:
a、选用反应釜,将原料中的聚二甲基硅烷、硅溶胶和硬脂酸加入其中,然后升温至80-90℃,搅拌反应2-3h,得到物料A取出备用;
b、选用一塑炼机,将步骤a中的物料A加入其中,然后加入原料中的二氧化钛、碳酸钙、炭黑、钛白粉、铁粉、石蜡和硫磺,然后进行混炼,控制混炼温度为30-40℃,混炼4-5h;
c、待步骤b混炼结束后,将原料中的石蜡和正丁基二硫代氨基甲酸锌加入其中,搅拌混合均匀后即可、冷却后,出料,计量包装。
实施例2
一种浴室防霉专用密封胶,由以下组分的原料制成:
聚二甲基硅烷26kg、二氧化钛15kg、硅溶胶20kg、碳酸钙9kg、炭黑9kg、钛白粉9kg、铁粉3kg、硬脂酸15kg、石蜡8kg、硫磺4kg、正丁基二硫代氨基甲酸锌2kg。
制备方法如下:
a、选用反应釜,将原料中的聚二甲基硅烷、硅溶胶和硬脂酸加入其中,然后升温至80-90℃,搅拌反应2-3h,得到物料A取出备用;
b、选用一塑炼机,将步骤a中的物料A加入其中,然后加入原料中的二氧化钛、碳酸钙、炭黑、钛白粉、铁粉、石蜡和硫磺,然后进行混炼,控制混炼温度为30-40℃,混炼4-5h;
c、待步骤b混炼结束后,将原料中的石蜡和正丁基二硫代氨基甲酸锌加入其中,搅拌混合均匀后即可、冷却后,出料,计量包装。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种浴室防霉专用密封胶,其特征在于:由以下组分的原料制成:
聚二甲基硅烷25-27份、二氧化钛10-20份、硅溶胶15-25份、碳酸钙8-10份、炭黑8-10份、钛白粉8-10份、铁粉2-4份、硬脂酸10-20份、石蜡7-9份、硫磺3-5份、促进剂1-3份。
2.根据权利要求1所述的一种浴室防霉专用密封胶,其特征在于:各原料的优选组分为:聚二甲基硅烷26份、二氧化钛15份、硅溶胶20份、碳酸钙9份、炭黑9份、钛白粉9份、铁粉3份、硬脂酸15份、石蜡8份、硫磺4份、促进剂2份。
3.根据权利要求1所述的一种浴室防霉专用密封胶,其特征在于:所述的促进剂为二正丁基二硫代氨基甲酸锌。
4.一种制备权利要求1和2中任意一种浴室防霉专用密封胶的方法,其特征在于,包括以下步骤:
a、选用反应釜,将原料中的聚二甲基硅烷、硅溶胶和硬脂酸加入其中,然后升温至80-90℃,搅拌反应2-3h,得到物料A取出备用;
b、选用一塑炼机,将步骤a中的物料A加入其中,然后加入原料中的二氧化钛、碳酸钙、炭黑、钛白粉、铁粉、石蜡和硫磺,然后进行混炼,控制混炼温度为30-40℃,混炼4-5h;
c、待步骤b混炼结束后,将原料中的石蜡和促进剂加入其中,搅拌混合均匀后即可、冷却后,出料,计量包装。