CN104876529A - 一种寒冷地区用抗冻混凝土 - Google Patents
一种寒冷地区用抗冻混凝土 Download PDFInfo
- Publication number
- CN104876529A CN104876529A CN201510273935.1A CN201510273935A CN104876529A CN 104876529 A CN104876529 A CN 104876529A CN 201510273935 A CN201510273935 A CN 201510273935A CN 104876529 A CN104876529 A CN 104876529A
- Authority
- CN
- China
- Prior art keywords
- parts
- concrete
- water
- stirring
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种寒冷地区用抗冻混凝土,它是由下述重量份的原料组成的:聚乳酸纤维1-2、普通硅酸盐水泥300-400、石灰岩碎石900-1000、粉煤灰60-70、新型减水剂4-5、赤泥50-60、河砂300-400、黑沙30-40、炉尘40-60、丙酸钙3-5、二水石膏粉30-40、二硬脂酸乙二酯0.8-1、碱式硫酸镁晶须3-5、水170-200、羧甲基纤维素钠1-2、矿粉40-50、引气剂1-1.5;本发明的混凝土,具有均匀、稳定、封闭,避免混凝土中形成毛细管道,缓和自由水受冻结所产生的膨胀压力,有效提高混凝土的抗冻性能,加入的碱式硫酸镁晶须、聚乳酸纤维,可以协助混凝土承担拉应力,从而提高混凝土的韧性和抗裂性。
Description
技术领域
本发明主要涉及混凝土领域,尤其涉及一种寒冷地区用抗冻混凝土。
背景技术
普通混凝土由胶凝材料、粗、细骨材和水按适当比例配置,再经硬化而成的人工石材。具有易成型,能耗低,耐久性好价格便宜以及与钢材结合可制成各种承重机构的优点,是当代应用最广泛的建筑材料对人类社会的发展起着十分重要的作用。目前混凝土还存在抗冲击韧性差、脆性大、干燥收缩大,易发生开裂等不足。
发明内容
本发明目的就是提供一种寒冷地区用抗冻混凝土。
本发明是通过以下技术方案实现的:
一种寒冷地区用抗冻混凝土,其特征在于它是由下述重量份的原料组成的:
聚乳酸纤维1-2、普通硅酸盐水泥300-400、石灰岩碎石900-1000、粉煤灰60-70、新型减水剂4-5、赤泥50-60、河砂300-400、黑沙30-40、炉尘40-60、丙酸钙3-5、二水石膏粉30-40、二硬脂酸乙二酯0.8-1、碱式硫酸镁晶须3-5、水170-200、羧甲基纤维素钠1-2、矿粉40-50、引气剂1-1.5;
所述的新型减水剂是由下述重量份的原料组成的:
聚羧酸减水剂20-30、氟硅酸钠3-4、乙二醇0.8-1、氨水1-2、硅烷偶联剂KH560 0.1-0.2;
将乙二醇与氨水混合,搅拌均匀后得到醇氨溶液,加入氟硅酸钠,在30-35℃下保温搅拌10-20分钟,加入硅烷偶联剂KH560,100-120转/分搅拌分散4-6分钟,加入聚羧酸减水剂,搅拌均匀,即得;
所述的引气剂为松香皂类引气剂。
一种寒冷地区用抗冻混凝土的制备方法,其特征在于包括以下步骤:
(1)将羧甲基纤维素钠加入到10-15倍水中,搅拌均匀后加入丙酸钙,升高温度为60-70℃,搅拌混合4-6分钟,加入二硬脂酸乙二酯、碱式硫酸镁晶须、聚乳酸纤维,200-300转/分搅拌分散6-10分钟,得分散液;
(2)将引气剂加入到剩余的水中,搅拌均匀,得引气液;
(3)将炉尘、黑沙混合送入浓度为4-6%的氢氧化钠溶液中浸泡1-2小时,取出后与二水石膏粉、粉煤灰混合搅拌均匀,加入上述除了分散液和引气液以外的各原料,干混均匀,加入剩余各原料,搅拌均匀,即得所述寒冷地区用抗冻混凝土。
本发明的优点是:
本发明的混凝土,具有均匀、稳定、封闭,避免混凝土中形成毛细管道,缓和自由水受冻结所产生的膨胀压力,有效提高混凝土的抗冻性能,加入的碱式硫酸镁晶须、聚乳酸纤维,可以协助混凝土承担拉应力,从而提高混凝土的韧性和抗裂性。
具体实施方式
实施例1
一种寒冷地区用抗冻混凝土,其特征在于它是由下述重量份的原料组成的:
聚乳酸纤维2、普通硅酸盐水泥400、石灰岩碎石1000、粉煤灰70、新型减水剂5、赤泥60、河砂400、黑沙40、炉尘60、丙酸钙5、二水石膏粉40、二硬脂酸乙二酯0.8、碱式硫酸镁晶须3、水200、羧甲基纤维素钠1-2、矿粉50、引气剂1.5;
所述的新型减水剂是由下述重量份的原料组成的:
聚羧酸减水剂30、氟硅酸钠3、乙二醇0.8、氨水1、硅烷偶联剂KH560 0.2;
将乙二醇与氨水混合,搅拌均匀后得到醇氨溶液,加入氟硅酸钠,在35℃下保温搅拌20分钟,加入硅烷偶联剂KH560,120转/分搅拌分散6分钟,加入聚羧酸减水剂,搅拌均匀,即得;
所述的引气剂为松香皂类引气剂。
一种寒冷地区用抗冻混凝土的制备方法,其特征在于包括以下步骤:
(1)将羧甲基纤维素钠加入到15倍水中,搅拌均匀后加入丙酸钙,升高温度为60℃,搅拌混合6分钟,加入二硬脂酸乙二酯、碱式硫酸镁晶须、聚乳酸纤维,300转/分搅拌分散10分钟,得分散液;
(2)将引气剂加入到剩余的水中,搅拌均匀,得引气液;
(3)将炉尘、黑沙混合送入浓度为4%的氢氧化钠溶液中浸泡2小时,取出后与二水石膏粉、粉煤灰混合搅拌均匀,加入上述除了分散液和引气液以外的各原料,干混均匀,加入剩余各原料,搅拌均匀,即得所述寒冷地区用抗冻混凝土。
性能测试:
抗折强度:8.4MPa。
Claims (2)
1.一种寒冷地区用抗冻混凝土,其特征在于它是由下述重量份的原料组成的:
聚乳酸纤维1-2、普通硅酸盐水泥300-400、石灰岩碎石900-1000、粉煤灰60-70、新型减水剂4-5、赤泥50-60、河砂300-400、黑沙30-40、炉尘40-60、丙酸钙3-5、二水石膏粉30-40、二硬脂酸乙二酯0.8-1、碱式硫酸镁晶须3-5、水170-200、羧甲基纤维素钠1-2、矿粉40-50、引气剂1-1.5;
所述的新型减水剂是由下述重量份的原料组成的:
聚羧酸减水剂20-30、氟硅酸钠3-4、乙二醇0.8-1、氨水1-2、硅烷偶联剂KH560 0.1-0.2;
将乙二醇与氨水混合,搅拌均匀后得到醇氨溶液,加入氟硅酸钠,在30-35℃下保温搅拌10-20分钟,加入硅烷偶联剂KH560,100-120转/分搅拌分散4-6分钟,加入聚羧酸减水剂,搅拌均匀,即得;
所述的引气剂为松香皂类引气剂。
2.一种如权利要求1所述的寒冷地区用抗冻混凝土的制备方法,其特征在于包括以下步骤:
(1)将羧甲基纤维素钠加入到10-15倍水中,搅拌均匀后加入丙酸钙,升高温度为60-70℃,搅拌混合4-6分钟,加入二硬脂酸乙二酯、碱式硫酸镁晶须、聚乳酸纤维,200-300转/分搅拌分散6-10分钟,得分散液;
(2)将引气剂加入到剩余的水中,搅拌均匀,得引气液;
(3)将炉尘、黑沙混合送入浓度为4-6%的氢氧化钠溶液中浸泡1-2小时,取出后与二水石膏粉、粉煤灰混合搅拌均匀,加入上述除了分散液和引气液以外的各原料,干混均匀,加入剩余各原料,搅拌均匀,即得所述寒冷地区用抗冻混凝土。