CN104869954B - 胶粘制品 - Google Patents
胶粘制品 Download PDFInfo
- Publication number
- CN104869954B CN104869954B CN201380064958.0A CN201380064958A CN104869954B CN 104869954 B CN104869954 B CN 104869954B CN 201380064958 A CN201380064958 A CN 201380064958A CN 104869954 B CN104869954 B CN 104869954B
- Authority
- CN
- China
- Prior art keywords
- adhesive layer
- adhesive
- reversible
- irreversible
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本公开总体上涉及胶粘制品且特别涉及包括可逆胶粘层和不可逆胶粘层的胶粘制品。所述胶粘制品还可包括背衬材料。所述胶粘制品还可包括敷裹材料。所述胶粘制品可特别适合治疗损伤的敏感组织,例如在脆弱皮肤上形成的伤口。
Description
相关申请的交叉引用
本申请基于2012年12月14日提交的代理人案号064693-0270、题为“胶粘制品”的美国临时申请61/737,297并且要求保护其优先权,其全部内容通过引用结合到本文中。
技术领域
本公开总体上涉及胶粘制品。本公开还涉及包括可逆胶粘层和不可逆胶粘层的胶粘制品。
背景技术
结合压敏胶粘剂的胶粘制品是众所周知并且市售的。胶粘制品的实例有例如胶粘绷带、经皮药物贴片和外科贴片的医学敷料。
尽管这类胶粘剂在施加压力时立刻粘附到表面上,但随后它们从表面的去除变成困难。例如,通过使用压敏胶粘剂制造的绷带可以以高粘附性容易地施用到在皮肤上形成的伤口。然而,当该绷带将要从皮肤上除去以用另一绷带代替或者在伤口的治疗完成之后,必须施加力以抵消该绷带的高粘附性,这可引起患者疼痛和/或对伤口或伤口周围的健康组织造成损伤。这类困难在由医疗机构的专门人员以及家中的个人干预伤口期间非常频繁地遇到。
此外,施用到脆弱皮肤如新生儿和老人的那些的市售胶粘制品可能具有不足的胶粘力,可能易于移位或被无意中除去。或者,在施用这类胶粘制品之后,它们的去除可能是困难的,这有时可损伤下层组织。它们在潮湿环境中也可能无法良好地起作用。
已经例如在以下文献中公开了包含热可逆胶粘剂的胶粘制品:Zhang等,“可逆胶粘剂(Reversible Adhesives),”美国专利公开号2012/0109035;Chen等,“通过辐射接枝制备易剥掉的临时伤口敷料物质(Preparation of Easily Stripped off Temporary WoundDressing Materials by Radiation Grafting);Kubota“伤口敷料(Wound Dressing)”,美国专利公开号2002/0028232。这些公开文本的全部内容通过引用结合到本文中。
发明内容
本公开总体上涉及胶粘制品。本公开还涉及包含可逆胶粘剂的胶粘制品。
所述胶粘制品可包括至少一个可逆胶粘层和至少一个不可逆胶粘层。
所述可逆胶粘层可包含可逆胶粘剂。所述可逆胶粘层可包含可逆聚合物。所述可逆聚合物可通过使包含可逆聚合物的单体的制剂反应形成。所述可逆胶粘层的实例可为热可逆的胶粘层。
所述不可逆胶粘层可能没有所述可逆胶粘层的可逆性。所述不可逆胶粘层可包含不可逆胶粘剂。所述不可逆胶粘层不含任何可逆胶粘剂。也就是说,所述不可逆胶粘层不含可逆胶粘剂。
所述胶粘制品还可包括至少一个正面。所述至少一个可逆胶粘层可在所述至少一个正面上。所述至少一个不可逆胶粘层可在所述至少一个正面上。所述至少一个可逆胶粘层可沉积在所述至少一个正面上。所述至少一个不可逆胶粘层可沉积在所述至少一个正面上。
所述至少一个可逆胶粘层可覆盖所述至少一个正面的至少0.1%的表面积。所述至少一个不可逆胶粘层可覆盖所述至少一个正面的至少0.1%的表面积。
所述至少一个可逆胶粘层可不与所述至少一个不可逆胶粘层接触。所述至少一个可逆胶粘层可与所述至少一个不可逆胶粘层接触。所述至少一个可逆胶粘层和所述至少一个不可逆层可重叠。所述至少一个可逆胶粘层可覆盖所述至少一个不可逆胶粘层的一部分。所述至少一个不可逆胶粘层可覆盖所述至少一个可逆胶粘层的一部分。
所述至少一个可逆胶粘层可在所述至少一个不可逆胶粘层沉积在所述至少一个正面上之后沉积在所述至少一个正面上。所述至少一个可逆胶粘层可在所述至少一个不可逆胶粘层沉积在所述至少一个正面上之前沉积在所述至少一个正面上。
所述至少一个可逆胶粘层可具有高于所述至少一个不可逆胶粘层的胶粘强度。所述至少一个可逆胶粘层可具有低于所述至少一个不可逆胶粘层的胶粘强度。所述至少一个可逆胶粘层在20℃以上的温度可具有高于0.1N/cm2的胶粘强度。所述至少一个可逆胶粘层在20℃以上的温度可具有低于0.1N/cm2的胶粘强度。所述至少一个不可逆胶粘层在20℃以上的温度可具有高于0.1N/cm2的胶粘强度。
所述胶粘制品还可包括至少一种背衬材料。所述至少一种背衬材料可具有至少一个正面。所述至少一个可逆胶粘层可在所述背衬材料的至少一个正面上。所述至少一个可逆胶粘层可沉积在所述背衬材料的至少一个正面上。所述至少一个可逆胶粘层可覆盖所述背衬材料的至少一个正面的至少0.1%的表面积。所述至少一个不可逆胶粘层可在所述背衬材料的至少一个正面上。所述至少一个不可逆胶粘层可沉积在所述背衬材料的至少一个正面上。所述至少一个不可逆胶粘层可覆盖所述背衬材料的至少一个正面的至少0.1%的表面积。
所述胶粘制品可为粘附到人类组织的胶粘制品。所述组织可为皮肤。所述皮肤可为脆弱皮肤。所述脆弱皮肤可为属于儿科群体的人类的脆弱皮肤。所述脆弱皮肤可为属于老年群体的人类的脆弱皮肤。
所述至少一个可逆胶粘层可为热可逆的胶粘层。
所述至少一个可逆胶粘层可包含可逆聚合物。所述可逆聚合物可通过使包含可逆聚合物的单体的制剂反应形成。所述至少一个可逆胶粘层可包含聚N-异丙基丙烯酰胺。所述至少一个不可逆胶粘层可不含聚N-异丙基丙烯酰胺。
所述胶粘制品可为伤口敷料。该胶粘制品还可包括伤口敷裹材料。该胶粘制品可为粘附到人类组织的胶粘制品。该组织可为皮肤。该皮肤可为脆弱皮肤。该脆弱皮肤可为属于儿科群体的人类的脆弱皮肤。该脆弱皮肤可为属于老年群体的人类的脆弱皮肤。
方法可包括施用所述胶粘制品到伤口或皮肤病变。所述伤口可为人类皮肤的伤口。该人类皮肤可为脆弱皮肤。该脆弱皮肤可为属于儿科群体或老年群体的人类的脆弱皮肤。
包括可逆胶粘剂和不可逆胶粘剂的上文公开的实施方式或实施例的任何组合可适合形成本公开的胶粘制品。
这些以及其它组件、步骤、特征、目的、益处和优势现在将从说明性实施方式的以下详细详述、附图和权利要求书的综述而明朗化。
附图说明
在附图中,胶粘制品的各方面通过实例而不是限制来说明。因此附图公开了说明性实施方式。它们并不给出所有实施方式。另外或作为替代,可使用其它实施方式。可忽略可显而易见或不必要的细节以节约空间或更有效地说明。相反地,一些实施方式可在没有所公开的所有细节的情况下实施。当在不同图中出现相同的数字时,其是指相同或相似的组件或步骤。
图1为例示性胶粘制品的正面图;
图2为例示性胶粘制品的正面图;
图3为例示性胶粘制品的正面图;
图4为例示性胶粘制品的正面图;
图5为例示性胶粘制品的正面图;
图6为例示性胶粘制品的正面图;
图7为例示性胶粘制品的正面图。
具体实施方式
现在描述说明性实施方式。另外或作为替代,可使用其它实施方式。可忽略可显而易见或不必要的细节以节约空间或更有效地展示。相反地,一些实施方式可在没有所公开的所有细节的情况下实施。
本公开总体上涉及包含胶粘剂的制品且特别涉及包含可逆胶粘剂的制品。本公开还涉及包含至少一种可逆胶粘剂和至少一个不可逆胶粘剂的胶粘制品。
所述胶粘制品可包括包含可逆胶粘剂的至少一层和包含不可逆胶粘剂的至少一层。
所述胶粘制品可包括可粘附到组织的至少一个表面。该表面在下文中被称作“正面”。当将胶粘制品施用到组织时,可使正面与组织接触。可逆胶粘层可在正面上。不可逆胶粘层可在正面上。可逆胶粘剂和不可逆胶粘剂可至少沉积在正面上且各自在其上形成一层。在将胶粘制品施用到组织时,可使该至少一个可逆胶粘层和/或该至少一个不可逆胶粘层与该组织接触。
可逆胶粘层可具有在使胶粘制品与组织接触时粘附到组织的表面。类似地,不可逆胶粘层可具有在使胶粘制品与组织接触时粘附到组织的表面。
可逆胶粘层可覆盖正面的至少0.1%、1%、10%或基本上全部。不可逆胶粘层可覆盖正面的至少0.1%、1%、10%或基本上全部。
可逆胶粘剂可具有任何厚度。例如,可逆胶粘层可具有相当于形成该可逆胶粘层的化合物的特征性分子长度的厚度。或者,可逆胶粘层可为至少10nm、至少100nm、至少1000nm、至少1微米、至少10微米或至少100微米厚。或者,可逆胶粘层的厚度可在1nm~1,000微米、10nm~100微米或100nm~10微米的范围内变化。可逆胶粘剂的该厚度可形成可逆胶粘剂的至少一个侧表面。
类似地,不可逆胶粘剂可具有任何厚度。例如,不可逆胶粘层可具有形成该可逆胶粘层的化合物的厚度。或者,不可逆胶粘层可为10nm、100nm、1000nm、1微米、10微米或100微米厚。或者,不可逆胶粘层的厚度可在1nm~1,000微米、10nm~100微米或100nm~10微米的范围内变化。不可逆胶粘剂的该厚度可形成不可逆胶粘层的至少一个侧表面。
可逆胶粘层可以与不可逆胶粘层接触(即,可触及)。例如,可逆胶粘层的侧表面可与不可逆胶粘层部分地或基本上接触。或者,可逆胶粘层和不可逆胶粘层可重叠。例如,可逆胶粘层可部分地或基本上覆盖不可逆胶粘层。或者,不可逆胶粘层可部分地或基本上覆盖可逆胶粘层。重叠区域可在可逆胶粘层的正面区域的1%~99%、10%~90%、20%~80%或30%~70%范围内。
并且,可逆胶粘层可以不与不可逆胶粘层接触。此外,正面可具有不含可逆胶粘层和不可逆胶粘层两者的表面。
可逆胶粘层可在沉积不可逆胶粘层之后沉积在正面上。在这样沉积时,可逆胶粘层可部分地覆盖不可逆胶粘层的表面。该部分覆盖率可为不可逆胶粘层的表面的至少0.1%、至少1%、至少10%或基本上全部。
不可逆胶粘层可在沉积可逆胶粘层之后沉积在正面上。在这样沉积时,不可逆胶粘层可部分地覆盖可逆胶粘层的表面。该部分覆盖率可为可逆胶粘层的表面的至少0.1%、至少1%、至少10%或基本上全部。
可逆胶粘层可在胶粘制品的任何表面上。不可逆胶粘层可在胶粘制品的任何表面上。例如,双侧胶带可通过在双侧胶带的一侧上沉积可逆胶粘层并在该双侧胶带的另一侧上沉积不可逆胶粘层来形成。在另一实施例中,双侧胶带的两侧可包括可逆胶粘层和不可逆胶粘层。
可逆胶粘层可具有高于不可逆胶粘层的胶粘强度。可逆胶粘层可具有低于不可逆胶粘层的胶粘强度。可逆胶粘剂的胶粘强度在20℃以上的温度可高于0.01N/cm2、0.1N/cm2、1N/cm2或5N/cm2。可逆胶粘剂的胶粘强度在20℃以上的温度可低于0.01N/cm2、0.1N/cm2或1N/cm2。
不可逆胶粘剂的胶粘强度在20℃以上的温度可高于0.01N/cm2、0.1N/cm2、1N/cm2或5N/cm2。
所述胶粘制品还可包括至少一种背衬材料。该至少一种背衬材料可包括至少一个正面。可逆胶粘层和/或非胶粘层可在由背衬材料形成的正面上。可逆胶粘层可覆盖背衬材料的正面的至少0.1%、1%、10%或基本上全部。不可逆胶粘层可覆盖背衬材料的正面的至少0.1%、1%、10%或基本上全部。可逆胶粘层可与不可逆胶粘层接触。可逆胶粘层和不可逆胶粘层可重叠。或者,可逆胶粘层可以不与不可逆胶粘层接触。此外,背衬材料的正面可具有不含可逆胶粘层和不可逆胶粘层两者的表面。可逆胶粘层可在沉积不可逆胶粘层之后沉积在背衬材料的正面上。在这样沉积时,可逆胶粘层可部分地覆盖不可逆胶粘层的表面。该部分覆盖率可为不可逆胶粘层的表面的至少0.1%、至少1%、至少10%或基本上全部。不可逆胶粘层可在沉积可逆胶粘层之后沉积在背衬材料的正面上。在这样沉积时,不可逆胶粘层可部分地覆盖可逆胶粘层的表面。该部分覆盖率可为可逆胶粘层的表面的至少0.1%、至少1%、至少10%或基本上全部。
该胶粘制品也可不含任何背衬材料。例如,该胶粘制品可由可逆胶粘层和不可逆胶粘层组成。在另一实施例中,该胶粘制品可由可逆胶粘层、不可逆胶粘层和由可逆胶粘层和不可逆胶粘层形成的无胶粘剂体积组成。
该胶粘制品还可包括至少一种敷裹材料。该敷裹材料可至少在正面上。在施用该胶粘制品时,可使该敷裹材料与组织接触。
该组织可为包含细胞的聚集体的任何有机组织。例如,该组织可为动物的任何组织。该组织还可为哺乳动物的任何组织。该哺乳动物可为人类。该组织可包括可为健康或处于正常状态下的组织。该组织还可包括可为不健康的或并非处于正常状态下的组织。
这类不健康组织的实例可为伤口。这类不健康组织的另一实例可为皮肤病变。皮肤病变的实例可包括皮肤疾病、病状、损伤、缺陷、异常或其组合。这类皮肤病变的实例可为常见疣、癌前病变(例如,光化性角化病)、免疫相关病状(例如,牛皮癣)或其组合。
该组织的另一实例可为脆弱皮肤。脆弱皮肤的一个实例为属于儿科群体的人类的敏感性皮肤。这一人类的一个实例为新生婴儿。脆弱皮肤的另一实例为属于老年群体的人类的敏感性皮肤。
在老年人中皮肤形态的年龄相关改变导致脆弱皮肤的发展。外皮层(表皮)随着年龄变薄,例如胶原蛋白和弹性蛋白的胞外组分减少,这导致皮肤的拉伸强度和伸长弹性减小。其它年龄相关的皮肤改变包括皮下脂肪层变薄、血管脆性增加和在真皮和下层疏松***之间的粘着性减小,这导致对皮肤撕裂和破裂的易患性增加。脆弱皮肤还可通过癌症化学疗法和放射疗法而诱发。具有脆弱皮肤的人类易于具有由在这类皮肤上遭受的处于对正常人类皮肤而言可忽略水平的菌株所造成的伤口。例如,物体软冲击脆弱皮肤可在脆弱皮肤上容易地诱发伤口。如果这一伤口被用于保护性或治疗目的的市售典型伤口敷料(例如,胶粘绷带)覆盖,则由于该伤口敷料对脆弱皮肤的显著粘附性而使得该伤口敷料的随后去除变成一个重要的问题。该典型伤口敷料的去除可易于导致对脆弱皮肤或对在这一皮肤上形成的伤口的进一步损伤。
包括可逆胶粘层和不可逆胶粘层的胶粘制品可提供该重要问题的解决方法。利用可逆胶粘层,可以在施用胶粘制品之后较容易地从组织除去该胶粘制品。例如,胶粘制品的可逆胶粘层表面可在皮肤温度下粘附到脆弱皮肤并且在该胶粘制品例如通过使用冷空气、冷敷或冰冷却到皮肤温度以下时,可以以最小的力和对脆弱皮肤具有可忽略损伤或没有进一步损伤的情况下容易地除去。因此,该可逆胶粘层的存在可减小在较低温度下胶粘制品的胶粘性并且由此帮助其在对脆弱皮肤具有最小损伤或疼痛下除去。不可逆层可提供给胶粘制品另外的胶粘强度并且防止胶粘制品从脆弱组织的偶然位移或非故意去除。
该组织也可为例如另一哺乳动物、脊椎动物或微生物的非人类有机体的组织。该组织甚至可为活或死的细胞培养物。该组织可处于任何条件下,例如其可为湿或干的。
并且,该胶粘制品可适合任何非组织表面。例如,该胶粘制品可适合将木材表面粘结到玻璃表面。在另一实施例中,该胶粘制品可适合将医疗器材粘结到例如织物或塑料的任何无机表面。
该胶粘制品也可适合将任何两个表面粘结在一起,例如将伤口敷料粘结到受伤皮肤上。
方法可包括施用该胶粘制品到伤口或皮肤病变处。该伤口可为人类皮肤的伤口。该人类皮肤可为脆弱皮肤。该脆弱皮肤可为属于儿科群体或老年群体的人类的脆弱皮肤。
本发明通过以下另外的实施例进一步说明,这些实施例不被看作是限制本发明的范围到在其中描述的具体程序或产物。
胶粘制品的实施例
如在图1中所示,例示性胶粘制品100可包括至少一种背衬材料105、至少一个不可逆胶粘层110和至少一个可逆胶粘层115。在该实施例中,该至少一个不可逆胶粘层110和该至少一个可逆胶粘层115彼此接触。
在另一实施例中,例示性胶粘制品还可包括至少一种敷裹材料120,如在图2中所示。
可逆胶粘层115和不可逆胶粘层110可彼此接触,如在图1~2和图7中所示。这些层也可彼此重叠(未在图中示出)。这些层也可彼此不接触,如在图3~6中所示。不可逆胶粘层110可包围可逆胶粘层115,如在图1~3中所示。可逆胶粘层115也可包围不可逆胶粘层110,如在图7中所示。
可逆胶粘层115和不可逆胶粘层110可各自以片段形式沉积在胶粘制品的正面上,如在图4~6中所示。
胶粘制品的正面可具有不含可逆胶粘层115和不可逆胶粘层110的区域,如在图1~6中所示。(该区域在图中没有编号)。
可逆胶粘层的实施例
可逆胶粘层可包含可逆胶粘剂。例如,可逆胶粘层可通过沉积包含可逆胶粘剂的制剂在胶粘制品的正面上而形成。
可逆胶粘层可为在第一预定条件下比在第二预定条件下可具有更好胶粘性质或更高胶粘性的胶粘剂。例如,可逆胶粘层可在皮肤温度下或皮肤温度以上提供足够的胶粘性,使得结合这一可逆胶粘层的胶粘制品例如在约37℃(即,第一预定条件)下适当地粘附到组织。当该胶粘制品例如通过使用冰冷却到37℃以下(即,第二预定条件)时,该可逆胶粘层的胶粘性因此可基本上降低到该胶粘制品可在减小或可忽略的力和对组织的最小损伤下从组织除去的水平。也就是说,该热可逆胶粘层在约37℃下的胶粘性可明显高于其在37℃以下的胶粘性。在该实施例中,可逆胶粘层可在约37℃下热可逆。然而,根据其应用的类型,可逆胶粘层可在任何其它温度下热可逆。
这种热可逆性是希望的:其可随意开启或闭合使其适合期望或甚至需要胶粘性的可逆性的多种应用。
该热可逆性不是可制造该可逆胶粘层的唯一机制。这类层的可逆性也可通过使用其它机制控制。例如,这类层可在正常超明条件(例如,太阳或人造光源)下对表面提供足够的粘附性。但是,当它们被紫外(UV)光照射时,它们的胶粘性可降到可忽略的水平。在另一实施例中,它们可在正常湿度条件(例如,皮肤湿度和天气湿度)下对组织提供足够的胶粘性。然而,当施用足够量的溶剂(例如,水、醇等)时,它们可丧失它们的胶粘性。可使用所有的这类可逆胶粘层。这类胶粘层在本公开中被称作“可逆胶粘层”。
可逆胶粘层可适合将任何两个表面粘结在一起,例如将胶粘制品粘结到组织上。该组织可为人类组织或例如另一哺乳动物、脊椎动物或微生物的非人类有机体的组织。该组织甚至可为活或死的细胞培养物。该组织可处于任何条件下,例如其可为湿或干的。
可逆胶粘层可适合将任何两个非组织表面粘结在一起。例如,可逆胶粘层可适合将木材表面粘结到玻璃表面。
可逆胶粘层可包含可逆胶粘剂。可逆胶粘剂可包含可逆聚合物。例如,可逆胶粘剂可通过使包含可逆聚合物的单体的制剂反应形成。在另一实施例中,使热可逆聚合物的单体反应可形成可逆胶粘剂。
用以制备可逆胶粘剂的热可逆聚合物在水性介质中具有新的热性能:它们随着温度增加具有可逆的溶解性。它们的分子结构通过加热从亲水结构过渡到疏水结构,使得它们在较高的温度下沉淀,而在较低的温度下完全可溶。该结构改变可在已知为下限临界溶解温度(LCST)的温度下相当突然地发生。例如,虽然聚N-异丙基丙烯酰胺在低于LCST的温度下为亲水的且完全可溶的,但在高于LCST下其变得疏水并且从水性介质中沉淀出来。对于该热可逆的聚合物,LCST在30℃~35℃的范围内。该聚合物在高于LCST下对组织有胶粘性并且在低于LCST下具有明显降低或甚至可以忽略的胶粘性。
存在可用以制备可逆胶粘剂的许多可逆聚合物。它们的LCST可与它们的分子结构一起改变。也可制备热可逆聚合物与其它热可逆聚合物或任何其它聚合物的共聚物以获得具有不同LCST的聚合物。由此,可通过具有多种均聚物和共聚物而将LCST控制在期望水平下,并且可获得用于多种医学或非医学应用的许多可逆胶粘剂。所有这样的均聚物和共聚物都在本发明的范围内。
在一个实施方式中,热可逆聚合物在0℃~100℃范围内的温度下热可逆。在另一实施方式中,热可逆聚合物在0℃~50℃范围内的温度下热可逆。
热可逆聚合物及其典型的LCST的实例为聚(N-甲基-N-正丙基丙烯酰胺),约19.8℃;聚(N-正丙基丙烯酰胺),约21.5℃;聚(N-甲基-N-异丙基丙烯酰胺),约22.3℃;聚(N-正丙基甲基丙烯酰胺),约28.0℃;聚N-异丙基丙烯酰胺,约30.9℃;聚(N,N-二乙基丙烯酰胺),约32.0℃;聚(N-异丙基甲基丙烯酰胺),约44.0℃;聚(N-环丙基丙烯酰胺),约45.5℃;聚(N-乙基甲基丙烯酰胺),约50.0℃;聚(N-甲基-N-乙基丙烯酰胺),约56.0℃;聚(N-环丙基甲基丙烯酰胺),约59.0℃;和聚(N-乙基丙烯酰胺),约72.0℃,及它们与其它聚合物的共聚合物及其混合物。热可逆聚合物的另一实例为聚环氧乙烷(PEO)-共-聚(对苯醚)(PPO)-共-聚乙二醇(PEO)的丙烯酸酯改性的三嵌段共聚物。在最后的实例中,可改变各聚合物的分子比以改变聚合物的LCST。可用于本发明的目的的热可逆单体的实例为在这类热可逆聚合物的制备中使用的单体。
这些热可逆聚合物可通过N-烷基丙烯酰胺、N-烷基甲基丙烯酰胺的单体或其混合物的聚合来制备的聚合物。这一单体的一个实例为N-异丙基丙烯酰胺。并且,这一聚合物的一个实例为聚N-异丙基丙烯酰胺。
可逆胶粘剂还可包括常规胶粘剂,例如压敏胶粘剂,或在制造这类常规胶粘剂中使用的化合物。常规胶粘剂或在制造常规胶粘剂中使用的化合物可改进可逆胶粘剂的胶粘强度。然而,该可逆胶粘剂的胶粘性通过将在制造这类可逆胶粘剂中使用的可逆胶粘剂或化合物结合到常规胶粘剂的化学结构或制剂中来控制或开启或关闭。
常规胶粘剂的实例为压敏胶粘剂的聚合物,例如通过丙烯酸酯单体的聚合而形成的丙烯酸酯和/或甲基丙烯酸酯聚合物。这类丙烯酸酯单体的实例为丙烯酸、丙烯酸甲酯、甲基丙烯酸甲酯、丙烯酸乙酯、甲基丙烯酸乙酯、丙烯酸丙酯、甲基丙烯酸丙酯、丙烯酸正丁酯、甲基丙烯酸正丁酯、丙烯酸正戊酯、丙烯酸正己酯、甲基丙烯酸正己酯、丙烯酸正庚酯、丙烯酸正辛酯、丙烯酸正壬酯、丙烯酸月桂酯、丙烯酸硬脂酰酯、甲基丙烯酸硬脂酰酯、丙烯酸山嵛酯、丙烯酸十八烷基酯、丙烯酸2-乙基己基酯及其混合物。
该可逆胶粘层可具有任何厚度,但该厚度至少等于或大于形成该层的化合物的厚度。例如,如果该层包含N-异丙基丙烯酰胺单体,则其厚度等于或大于该单体的厚度。这类单体的不同分子量的二聚物、三聚物、低聚物或聚合物的尺寸也可形成各单独层的厚度。
如果该层比预定厚度薄,则该可逆胶粘层可能不具有期望的性质。例如,如果通过使用热可逆单体沉积的层的厚度太薄,则该可逆胶粘层不可能具有足够的胶粘性。预定厚度范围可取决于形成该可逆胶粘层的化合物的化学或物理性质并且其值可相应地变化。该厚度可在实验上对于该可逆胶粘层测定。
可逆胶粘剂的一个实例公开在Zhang等“可逆胶粘剂(Reversible Adhesives)”,美国专利公开号2012/0109035中。该公开文本的全部内容通过引用结合到本文中。
该可逆胶粘层可具有高于该不可逆胶粘层的胶粘强度。该可逆胶粘层可具有低于该不可逆胶粘层的胶粘强度。该可逆胶粘层可具有基本相当于该不可逆胶粘层的胶粘强度。
该可逆胶粘层和该不可逆胶粘层的胶粘强度可通过使用题为“拉伸中组织胶粘剂的强度特性的标准试验方法(Standard Test Method for Strength Properties ofTissue Adhesives in Tension).”的ASTM国际标准试验方法编号ASTM F2258-05(2010)测定。
不可逆胶粘层的实施例
不可逆胶粘层可包含不可逆胶粘剂。不可逆胶粘层不含可逆胶粘剂。例如,不可逆胶粘层可通过沉积包含不可逆胶粘剂的制剂在胶粘制品的正面上而形成。
不可逆胶粘剂可包括常规胶粘剂,例如压敏胶粘剂,或在制造这类常规胶粘剂中使用的化合物。
常规胶粘剂的实例为压敏胶粘剂的聚合物,例如通过丙烯酸酯单体的聚合而形成的丙烯酸酯和/或甲基丙烯酸酯聚合物。这类丙烯酸酯单体的实例为丙烯酸、丙烯酸甲酯、甲基丙烯酸甲酯、丙烯酸乙酯、甲基丙烯酸乙酯、丙烯酸丙酯、甲基丙烯酸丙酯、丙烯酸正丁酯、甲基丙烯酸正丁酯、丙烯酸正戊酯、丙烯酸正己酯、甲基丙烯酸正己酯、丙烯酸正庚酯、丙烯酸正辛酯、丙烯酸正壬酯、丙烯酸月桂酯、丙烯酸硬脂酰酯、甲基丙烯酸硬脂酰酯、丙烯酸山嵛酯、丙烯酸十八烷基酯、丙烯酸2-乙基己基酯及其混合物。
不可逆胶粘层不具有上文公开的可逆胶粘层的可逆性。因此,不可逆胶粘层可不包含可逆胶粘剂、可逆聚合物或可逆单体。例如,不可逆胶粘层可能不是热可逆的。例如,当胶粘制品的温度冷却到37℃以下时,不可逆胶粘层可具有比可逆胶粘层明显更高的胶粘强度。
不可逆胶粘层可具有任何厚度,但该厚度至少等于或大于形成该层的化合物的厚度。例如,如果该层包含丙烯酸2-乙基己基酯单体,则其厚度可等于或大于该单体的厚度。这类单体的不同分子量的二聚物、三聚物、低聚物或聚合物的尺寸也可形成该不可逆胶粘层的厚度。
如果该不可逆胶粘层比预定厚度薄,则该不可逆胶粘层可能不具有期望的性质。例如,如果通过使用不可逆单体沉积的层的厚度太薄,则该不可逆胶粘层不可能具有足够的胶粘性。在另一实施例中,如果通过使用压敏单体沉积的层的厚度太薄,则该不可逆胶粘层可能不具有足够的胶粘强度。
预定厚度范围可取决于形成该不可逆胶粘层的化合物的化学或物理性质并且其值可相应地变化。该厚度可在实验上对于该不可逆胶粘层测定。
背衬材料的实施例
该胶粘制品还可包括背衬材料。这些背衬材料可具有多种形状和结构。例如,该背衬材料可为基本平坦的,具有相对光滑的表面,如聚合物薄膜;其可具有海绵样结构;并且其还可具有包含纤维状结构的表面。
背衬材料的实例可为布料、网、薄膜及其混合物。布料的实例可为纺布如纱网、无纺布、编织物、海绵及其复合材料。薄膜的实例可包括通过使用例如聚氨酯、聚硅氧烷、聚酰亚胺、聚(单氯-对亚二甲苯)(例如,聚氯代对二甲苯)、聚(二甲基硅氧烷)(例如,PDMS)的聚合物制造的薄膜或通过使用例如弹性蛋白、海藻酸盐、壳多糖、胶原蛋白和纤维蛋白的生物源材料制造的薄膜。可使用半透膜。还可使用例如弹性蛋白的源自生物材料的多肽。也可使用所有这类材料的复合材料来制造背衬材料。
纱网、无纺布、编织物等可通过使用例如天然纤维、合成纤维及其复合材料的纤维来制造。这些纤维可包括例如棉、亚麻、黄麻、***、棉、羊毛、木浆、再生纤维素纤维如粘胶人造丝和铜铵法人造丝、改性纤维素纤维如乙酸纤维素、合成纤维如衍生自聚酯、聚酰胺、聚丙烯酸的那些、生物相容/生物可降解的纤维如聚内酯,或其复合材料。这类背衬材料的实例还可包括聚酯(Mylar或穿孔Telfa膜)、聚氨酯、聚硅氧烷片材、聚丙烯(PP)、聚乙烯(PE)、聚氯乙烯(PVC)及其复合材料。
敷裹材料的实施例
胶粘制品还可包括敷裹材料。敷裹材料的一些实例为纱网、无纺布、编织物等。敷裹材料的其它实例为水胶体、水凝胶和海藻酸盐。聚氨酯和/或硅酮泡沫也可用作敷裹材料。抗微生物敷裹材料为敷裹材料的其它实例。这类敷裹材料可包含以离子或纳米晶体形式的抗微生物剂,例如银。敷裹材料的其它实例公开在出版物Jones等“伤口愈合基础知识.伤口敷料(ABC of Wound Healing.Wound Dressings),”BMJ,777~780页,332卷,2006年4月1日中。该公开文本的全部内容通过引用结合到本文中。
胶粘制品的例示性应用
胶粘制品可用于多种应用中。例如,它们可用于医学应用。医学应用的实例为手术屏障、外科贴片(例如,硬脑膜贴片)、外科包裹物(例如,血管、血管周围、外膜、外膜周围的包裹物和外膜片材)、外科敷料、网(例如,血管周围网)、绷带、胶带、组织覆盖物等。其它实例为用于处理烧伤皮肤的医学敷料、造口术的覆盖物、用于固持医疗装置如导管、管子、心电图电极就位的胶粘制品、用于褥疮的覆盖物等。
尽管上文通过医学应用描述了胶粘制品,但是其可适合在其它领域中的应用。例如,该胶粘制品用于修复、替换、复位或附着电子、光学、电光组件或甚至汽车组件。
包括可逆胶粘剂和不可逆胶粘剂的上文公开的实施方式或实施例的任何组合可适合形成本公开的胶粘制品。
已经讨论的组件、步骤、特征、目的、益处和优势仅为说明性的。其中哪一个都并非旨在以任何方式限制保护范围,关于它们的论述中也是如此。还预期许多其它实施方式。这些包括具有较少、另外和/或不同的组件、步骤、特征、目的、益处和优势的实施方式。这些还包括其中不同地配置和/或定序组件和/或步骤的实施方式。
除非另有说明,否则在本说明书中,包括在权利要求书中,阐述的所有测量、值、等级、位置、量值、尺寸及其它规格皆为近似的,而不是精确的。它们旨在具有符合与它们相关且在它们所属领域中常用的功能的合理范围。
Claims (12)
1.一种胶粘制品,其包括:
至少一个可逆胶粘层,其当经历温度改变时基本上减少其胶粘力;
至少一个不可逆胶粘层,其当经历温度改变时基本上不减少其胶粘力;和
至少一个背衬材料,
其中所述至少一个背衬材料包含至少一个正面,所述可逆胶粘层和所述不可逆胶粘层与该正面胶粘;
其中所述至少一个不可逆胶粘层包围所述至少一个可逆胶粘层;以及
其中当所述胶粘制品与材料表面接触时,所述至少一个可逆胶粘层和所述至少一个不可逆胶粘层二者各自具有与所述材料表面胶粘的表面。
2.根据权利要求1所述的胶粘制品,其中所述至少一个可逆胶粘层覆盖所述背衬材料的所述至少一个正面的至少0.1%的表面积。
3.根据权利要求2所述的胶粘制品,其中所述至少一个不可逆胶粘层覆盖所述背衬材料的所述至少一个正面的至少0.1%的表面积。
4.根据权利要求3所述的胶粘制品,其中所述至少一个可逆胶粘层不与所述至少一个不可逆胶粘层接触。
5.根据权利要求3所述的胶粘制品,其中所述至少一个可逆胶粘层与所述至少一个不可逆胶粘层接触。
6.根据权利要求5所述的胶粘制品,其中所述至少一个可逆胶粘层和所述至少一个不可逆胶粘层重叠,使得所述至少一个可逆胶粘层部分地覆盖所述至少一个不可逆胶粘层或者使得所述至少一个不可逆胶粘层部分地覆盖所述至少一个可逆胶粘层。
7.根据权利要求6所述的胶粘制品,其中所述至少一个可逆胶粘层覆盖所述至少一个不可逆胶粘层的一部分。
8.根据权利要求6所述的胶粘制品,其中所述至少一个不可逆胶粘层覆盖所述至少一个可逆胶粘层的一部分。
9.根据权利要求1所述的胶粘制品,其中所述至少一个可逆胶粘层具有的胶粘强度高于所述至少一个不可逆胶粘层的胶粘强度。
10.根据权利要求1所述的胶粘制品,其中所述至少一个可逆胶粘层具有的胶粘强度低于所述至少一个不可逆胶粘层的胶粘强度。
11.根据权利要求1所述的胶粘制品,其中所述不可逆胶粘层完全包围所述可逆胶粘层。
12.根据权利要求1所述的胶粘制品,其中所述不可逆胶粘层不完全包围所述可逆胶粘层。