CN104862589A - 一种低温焊接性能优良的风电塔筒用钢及生产方法 - Google Patents
一种低温焊接性能优良的风电塔筒用钢及生产方法 Download PDFInfo
- Publication number
- CN104862589A CN104862589A CN201510314693.6A CN201510314693A CN104862589A CN 104862589 A CN104862589 A CN 104862589A CN 201510314693 A CN201510314693 A CN 201510314693A CN 104862589 A CN104862589 A CN 104862589A
- Authority
- CN
- China
- Prior art keywords
- temperature
- steel
- steel plate
- equal
- power tower
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种低温性能优良的风电塔筒用钢,其组分及wt%为:C:0.10~0.15%,Si:0.25~0.35%,Mn:0.85~1.20%,P:≤0.015%,S:≤0.008%,Nb:0.013~0.032%,Als:0.025~0.045%,Pr:0.03~0.07%;生产步骤:经冶炼并连铸成坯后对铸坯加热并常规保温;分段热轧;层流冷却;自然冷却至室温;正火;再次自然冷却至室温。本发明采用热轧+正火状态交货,使生产的钢板屈服强度≥355MPa,抗拉强度:490~630MPa,延伸率A≥30%,-50℃KV2≥260J,-60℃KV2≥220J,而且碳当量<0.32,在低温状态下具有优良的焊接性能。可缩短在冬季温度相对较低时制备风力发电塔结构的工期,也能使出现的小规模修补更为便捷。
Description
技术领域
本发明涉及一种风电塔用钢及生产方法,具体地属于一种低温焊接性能优良的风电塔筒用钢及生产方法。
背景技术
我国风电场建设已遍布全国各省市自治区。风电成为继火电、水电之后的第三大电源。风电能够带动各地区传统能源消费比重的逐渐下调,风电产业的发展对于国家能源结构的调整意义重大,困扰我国多个地区的雾霾,若要从根本上加以解决,风电必将是最为关键的环节之一。风电有望成为雾霾克星,与光伏、燃气等一起为清洁能源行业的发展壮大做出积极贡献。
现有技术中有关于低温韧性优异的结构用钢有许多报道,经检索:
中国专利公开号为CN101831586A的文献,公开了一种低温韧性优异的低碳当量高强度厚钢板及其生产方法。该发明采用控轧控冷工艺,通过控制冷却速率生产钢板屈服强度在345MPa以上,其低温冲击性能虽然较好,但其碳当量在0.33~0.36。
中国专利公开为CN102899569A的文献,公开了一种超低温韧性优异的海上风电用宽厚钢板制造方法。该发明钢采用控轧控冷+正火工艺,生产出钢板屈服强度在355~410MPa,抗拉强度在470~550MPa,延伸率在26%~36%,-60 ℃冲击功100~240J。虽然该发明钢板性能较好,但其碳当量在0.38~0.43,焊接性能较差。
中国专利公开号为CN101906579A的文献,公开了一种耐低温、高焊接性能、高强度的风电法兰用钢。该发明钢使用了Nb、V、Ti合金,正火后延伸率在28%~39%,-50℃冲击功值为110J~180J。虽然钢板力学性能较为理想,但其碳当量在0.40~0.43,焊接性能较差。
风电塔筒是通过钢板卷制焊接而成,如不经正火,往往会出现强度较低的部分已经弯曲,强度高的部分还未变形的现象。正火后钢板各部分强度均匀,有益于卷制。上述专利文献,在控轧控冷工艺生产的钢板采用的C、Mn含量相对较低,能够将CEV控制到较低水平,但当进行正火热处理后,强度性能将得不到保障。如若将钢板中C、Mn含量上调,则钢板正火后性能较好,但焊接性能又较差。
发明内容
本发明针对现有技术存在的不足,提供一种既能在正火后屈服强度≥355MPa,抗拉强度在490~630MPa,延伸率A≥30%,碳当量<0.32,-50℃KV2≥260J,-60℃KV2≥220J的低温焊接性能优良的风电塔筒用钢及生产方法。
实现上述目的的措施:
一种低温性能优良的风电塔筒用钢,其组分及重量百分比含量为:C:0.10~0.15%,Si:0.25~0.35%,Mn:0.85~1.20%,P:≤0.015%,S:≤0.008%,Nb:0.013~0.032%,Als:0.025~0.045%,Pr:0.03~0.07%,其余为Fe及不可避免的杂质;同时满足CEV<0.32,金相组织为铁素体+珠光体组织,其中铁素体体积比例为50~60%,其余为珠光体组织。
生产一种低温性能优良的风电塔筒用钢的方法,其步骤:
1)经冶炼并连铸成坯后对铸坯加热并常规保温,加热温度为1160~1250℃,加热速率在0.8~1.1min/mm;
2)进行分段热轧,并控制精轧开轧温度在900℃~950℃,终轧温度在800~860℃,累计压下率不低于75%,末三道次压下率不低于40%;
3)进行层流冷却,冷却速率控制在8~15℃/s,返红温度控制在600~680℃;
4)自然冷却至室温;
5)进行正火,正火温度控制在875~908℃,并保温32~47min;
6)再次自然冷却至室温。
本发明中各元素的作用
C是提高钢材强度最有效的元素,随着碳含量的增加,钢的抗拉强度和屈服强度随之提高,但延伸率和冲击韧性下降,而且钢材的焊接热影响区还会出现淬硬现象,导致焊接冷裂纹的产生。当C含量低于0.10%时,正火后强度性能达不到要求,若C含量高于0.15%钢板CEV上升,恶化焊接性能,因此,本发明C选择在0.10~0.15%。
Si是炼钢脱氧的必要元素,以固溶强化形式提高钢的强度,当Si含量低于0.25%时,强度性能偏低,当Si含量高于0.35%时,钢的韧性下降。因此,本发明Si选择在0.25~0.35%。
Mn是重要的强韧化元素,随着Mn含量的增加,钢的强度明显增加,改善钢的加工性能,而冲击转变温度几乎不发生变化,含1%的Mn大约可提高抗拉强度100MPa。Mn含量低于0.85%时,正火后强度性能较低,当Mn含量高于1.20%时,钢板CEV上升。因此,本发明Mn选择在0.85~1.20%。
P、S是钢中难以避免的有害杂质元素。高P会导致偏析,影响钢组织均匀性,降低钢的塑性;S易形成硫化物夹杂对低温韧性不利,且会造成性能的各向异性,同时严重影响钢的应变时效。因此,应严格限制钢中的P、S含量,本发明P控制在≤0.015%, S控制在≤0.008%。
Nb可延迟奥氏体再结晶,降低相变温度,晶粒细化作用明显,并可改善低温韧性。Nb通过固溶强化、相变强化、析出强化等机制来获得要求的强度。当Nb含量低于0.013%时,细化晶粒效果不理想,当Nb含量大于0.032%时,容易产生晶间裂纹。因此,本发明Nb选择在0.013~0.032%。
Als通常作为钢中的脱氧剂。但Als含量低于0.025%时,脱氧不充分,当Als含量高于0.045%时,氧化铝夹杂物增加,降低钢的洁净度。因此,本发明Als选择在0.025~0.045%。
Pr:其是很好的钢中脱硫去气剂,可以清除砷、锑、铋等有害杂质;可以改变钢中夹杂物的形状和分布情况,从而改善钢的质量。在低合金钢中加入适量稀土可以提高低温冲击韧性,改善钢材的各向异性。当Pr含量低于0.03%时,对钢材性能改善效果不明显,当Pr含量高于0.07%时,对钢材性能的改善不再提高,且增加成本。因此,本发明Pr选择在0.03~0.07%。
本发明之所以控制碳当量<0.32,其目的在于保证焊接厚度低于20mm的钢板时,在零度环境下无需预热,同时低的CEV钢板的冷裂纹倾向更低。
本发明之所以控制正火温度在875~908℃,并保温32~47min,其目的在于控制钢板的金相组织中软相和硬相的比例,以保证钢板同时满足强度好,韧性优的特点。
本发明与现有技术相比,采用热轧+正火状态交货,使生产的钢板屈服强度≥355MPa,抗拉强度:490~630MPa,延伸率A≥30%,-50℃KV2≥260J,-60℃KV2≥220J,而且碳当量<0.32,在低温状态下具有优良的焊接性能。可缩短在冬季温度相对较低时制备风力发电塔结构的工期,同时也使未来可能出现的小规模修补更为便捷。
具体实施方式
下面对本发明予以详细描述:
表1为本发明各实施例及对比例的取值列表;
表2为本发明各实施例及对比例的主要工艺参数列表;
表3为本发明各实施例及对比例性能检测情况列表。
本发明各实施例按照以下步骤生产:
1)经冶炼并连铸成坯后对铸坯加热并常规保温,加热温度为1160~1250℃,加热速率在0.8~1.1min/mm;
2)进行分段热轧,并控制精轧开轧温度在900℃~950℃,终轧温度在800~860℃,累计压下率不低于75%,末三道次压下率不低于40%;
3)进行层流冷却,冷却速率控制在8~15℃/s,返红温度控制在600~680℃;
4)自然冷却至室温;
5)进行正火,正火温度控制在875~908℃,并保温32~47min;
6)再次自然冷却至室温。
表1 本发明实施例与比较例的化学成分列表(wt%)
表2 本发明各实施例及对比例的主要工艺参数列表
表3 本发明各实施例及对比例的力学性能对比列表
实施例 | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 对比例1 | 对比例2 |
ReL/MPa | 355 | 372 | 386 | 398 | 435 | 422 | 408 | 419 | 432 | 312 | 328 |
Rm/MPa | 490 | 532 | 567 | 586 | 630 | 602 | 617 | 585 | 579 | 468 | 476 |
A/% | 35 | 34 | 32 | 30 | 34 | 33 | 31 | 32 | 33 | 25 | 23 |
-50℃KV2/J | 264 | 262 | 260 | 273 | 276 | 265 | 283 | 274 | 268 | 127 | 135 |
-60℃KV2/J | 242 | 235 | 225 | 240 | 231 | 224 | 237 | 230 | 220 | 86 | 103 |
从表3可以看出,本发明钢板进行常温拉伸实验性能,-50℃和-60℃纵向冲击试验,并与对比钢对比发现,本发明钢屈服强度和抗拉强度均优于对比钢,本发明钢延伸率A高于对比钢且均不低于30%,体现出良好的塑韧性。本发明-50℃冲击功值较高在260J以上,-60℃冲击功值较高在220J以上,远高于对比钢,说明本发明钢具有更为优异的低温韧性。
综上所述,本发明钢具有优良低温韧性,高延伸率,低碳当量的特点。本发明钢采用热轧+正火工艺,同一钢板上性能稳定均匀,可广泛应用于风力发电塔工程钢结构。
上述实施例仅为最佳例举,而并非是对本发明的实施方式的限定。
Claims (2)
1.一种低温焊接性能优良的风电塔筒用钢,其组分及重量百分比含量为:C:0.10~0.15%,Si:0.25~0.35%,Mn:0.85~1.20%,P:≤0.015%,S:≤0.008%,Nb:0.013~0.032%,Als:0.025~0.045%, Pr:0.03~0.07%,其余为Fe及不可避免的杂质;同时满足CEV<0.32,金相组织为铁素体+珠光体组织,其中铁素体体积比例为50~60%,其余为珠光体组织。
2.生产权利要求1所述的一种低温焊接性能优良的风电塔筒用钢的方法,其步骤:
1)经冶炼并连铸成坯后对铸坯加热并常规保温,加热温度为1160~1250℃,加热速率在0.8~1.1min/mm;
2)进行分段热轧,并控制精轧开轧温度在900℃~950℃,终轧温度在800~860℃,累计压下率不低于75%,末三道次压下率不低于40%;
3)进行层流冷却,冷却速率控制在8~15℃/s,返红温度控制在600~680℃;
4)自然冷却至室温;
5)进行正火,正火温度控制在875~908℃,并保温32~47min;
6)再次自然冷却至室温。