CN104861804A - Fire retardant coating for bus duct - Google Patents
Fire retardant coating for bus duct Download PDFInfo
- Publication number
- CN104861804A CN104861804A CN201510231630.4A CN201510231630A CN104861804A CN 104861804 A CN104861804 A CN 104861804A CN 201510231630 A CN201510231630 A CN 201510231630A CN 104861804 A CN104861804 A CN 104861804A
- Authority
- CN
- China
- Prior art keywords
- parts
- bus duct
- retardant coating
- fire retardant
- frie retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fire retardant coating for a bus duct. The fire retardant coating for the bus duct is composed of compositions of, by quality part, 25-45 parts of acrylic emulsion, 17-25 parts of ammonium polyphosphate, 3-15 parts of melamine, 6-12 parts of pentaerythrite, 1-5 parts of chlorinated paraffin cobalt, 3-8 parts of titanium dioxide and 2-3 parts of P-19 thickening agent. The fire retardant coating for the bus duct can effectivity prevent the bus duct from melting due to a high temperature, avoids the bus duct exploding caused by electric short circuit, improves safety performance, abrasion performance, extensive fireproof performance and solvent resistance, and has an advantageous construction characteristic under a plurality of atmosphere circumstance conditions.
Description
Technical field
The present invention relates to a kind of bus duct frie retardant coating, in particular, particularly relate to a kind of bus duct frie retardant coating.
Background technology
Modern high-rise building and large-scale workshop need huge electric energy, and the powerful electric current of hundreds and thousands of amperes will select safe and reliable transmission equipment needed for this huge load.Bus duct is mainly used in envrionment temperature-20
0c is to+40
0between C, relative humidity of atomsphere is not more than 90%, and elevation is highly not more than 2000 meters, more than voltage rating 10KV, and frequency is the electrical power trans mission/distribution systems such as the large power plant of 50-60HZ, meets high temperature easily melt due to traditional bus duct.Cause whole system short circuit or blast; So design a kind of fire-type bus duct, it is current those skilled in the art's urgent problem.
summary of the invention:
In order to solve the problem, the object of this invention is to provide a kind of bus duct frie retardant coating.
Technical scheme of the present invention is: a kind of bus duct frie retardant coating, and wherein, its moiety is as follows according to the mass fraction:
ACRYLIC EMULSION 25-45 part
Ammonium polyphosphate 17-25 part
Trimeric cyanamide 3-15 part
Tetramethylolmethane 6-12 part
Clorafin cobalt 1-5 part
Titanium dioxide 3-8 part
P-19 thickening material 2-3 part.
Above-mentioned a kind of bus duct frie retardant coating, wherein, preferably, its moiety is as follows according to the mass fraction:
ACRYLIC EMULSION 38 parts
Ammonium polyphosphate 23 parts
Trimeric cyanamide 16 parts
Tetramethylolmethane 7 parts
Clorafin cobalt 5 parts
Titanium dioxide 8 parts
P-19 thickening material 3 parts
Above-mentioned a kind of bus duct frie retardant coating, until all raw materials fully mix reach viscosity to 8000mp.s, both obtained bus duct frie retardant coating.
The invention has the beneficial effects as follows: the present invention adopts new formulation, unique formula composition is adopted to accomplish effective fire prevention, adopt the frie retardant coating that the present invention obtains, can effectively avoid high temperature melt bus duct, avoid electric short circuit, cause the generation that bus explodes, improve safety performance, wear resistance and widely fire line and solvent resistance, have superior construction property under multiple Atmospheric Condition.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
A kind of bus duct frie retardant coating, 38 parts of ACRYLIC EMULSION are put into reactor with 23 parts of ammonium polyphosphates mix, mixing time is 1h, mixing temperature is 50 degree, mixing rate is 120r/min, 16 parts of trimeric cyanamides are added after mixing terminates, continue to stir 30min, then 7 parts of tetramethylolmethanes, 5 parts of clorafin cobalts, 3 parts of P-19 thickening materials and 8 parts of titanium dioxides are added, mixing temperature is 60 degree, mixing rate is 140r/min, until all raw materials fully mix reach viscosity to 8000mp.s, naturally cools to normal temperature.
Embodiment 2:
A kind of bus duct frie retardant coating, 37 parts of ACRYLIC EMULSION are put into reactor with 24 parts of ammonium polyphosphates mix, mixing time is 1h, mixing temperature is 50 degree, mixing rate is 120r/min, 16 parts of trimeric cyanamides are added after mixing terminates, continue to stir 30min, then 7 parts of tetramethylolmethanes, 5 parts of clorafin cobalts, 3 parts of P-19 thickening materials and 8 parts of titanium dioxides are added, mixing temperature is 60 degree, mixing rate is 140r/min, until all raw materials fully mix reach viscosity to 8000mp.s, naturally cools to normal temperature.
Embodiment 3:
A kind of bus duct frie retardant coating, 36 parts of ACRYLIC EMULSION are put into reactor with 25 parts of ammonium polyphosphates mix, mixing time is 1h, mixing temperature is 50 degree, mixing rate is 120r/min, 16 parts of trimeric cyanamides are added after mixing terminates, continue to stir 30min, then 7 parts of tetramethylolmethanes, 5 parts of clorafin cobalts, 3 parts of P-19 thickening materials and 8 parts of titanium dioxides are added, mixing temperature is 60 degree, mixing rate is 140r/min, until all raw materials fully mix reach viscosity to 8000mp.s, naturally cools to normal temperature.
Beneficial effect: the present invention adopts new formulation, unique formula composition is adopted to accomplish effective fire prevention, adopt the frie retardant coating that the present invention obtains, can effectively avoid high temperature melt bus duct, avoid electric short circuit, cause the generation that bus explodes, improve safety performance, wear resistance and widely fire line and solvent resistance, have superior construction property under multiple Atmospheric Condition.
The above; be only the present invention's preferably embodiment, but protection scope of the present invention is not limited thereto, is anyly familiar with those skilled in the art in the technical scope that the present invention discloses; the change that can expect easily or replacement, all should be encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain of claims.
Claims (2)
1. a bus duct frie retardant coating, is characterized by, and its moiety is as follows according to the mass fraction:
ACRYLIC EMULSION 25-45 part
Ammonium polyphosphate 17-25 part
Trimeric cyanamide 3-15 part
Tetramethylolmethane 6-12 part
Clorafin cobalt 1-5 part
Titanium dioxide 3-8 part
P-19 thickening material 2-3 part.
2. as claim 1 bus duct frie retardant coating, it is characterized by, until all raw materials fully mix reach viscosity to 8000mp.s, both obtained bus duct frie retardant coating.