CN104859234A - Machining process of jacquard fabric and spun-bonded non-woven fabric composite wall cloth fabrics - Google Patents

Machining process of jacquard fabric and spun-bonded non-woven fabric composite wall cloth fabrics Download PDF

Info

Publication number
CN104859234A
CN104859234A CN201510227654.2A CN201510227654A CN104859234A CN 104859234 A CN104859234 A CN 104859234A CN 201510227654 A CN201510227654 A CN 201510227654A CN 104859234 A CN104859234 A CN 104859234A
Authority
CN
China
Prior art keywords
spun
jacquard
fabrics
bonded non
woven fabrics
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510227654.2A
Other languages
Chinese (zh)
Inventor
韩玥
徐佳丽
刘东婷
朱容
周玲玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Sci Tech University ZSTU
Zhejiang University of Science and Technology ZUST
Original Assignee
Zhejiang Sci Tech University ZSTU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Sci Tech University ZSTU filed Critical Zhejiang Sci Tech University ZSTU
Priority to CN201510227654.2A priority Critical patent/CN104859234A/en
Publication of CN104859234A publication Critical patent/CN104859234A/en
Pending legal-status Critical Current

Abstract

The invention discloses a machining process of jacquard fabric and spun-bonded non-woven fabric composite wall cloth fabrics. The machining process comprises the following steps of selecting appropriate jacquard fabrics as a surface layer and selecting raw materials of spun-bonded non-woven fabrics as a bottom layer according to product demands; designing jacquard patterns and reasonable process parameters and formulating the technological process; bonding the jacquard fabric surface layer and the spun-bonded non-woven fabric bottom layer by a composite technology to eventually form the composite wall cloth fabrics which are good in air permeability and moisture resistance, easy to clean and environmentally-friendly. According to the machining process of the jacquard fabric and spun-bonded non-woven fabric composite wall cloth fabrics, the non-toxic, sound-absorbing and air permeability performance of textile fiber wall paper is achieved, and the characteristics of smoothness, ageing resistance, convenient pasting, certain air permeability and moisture resistance, scrubbing and fastness of non-woven wall cloth are achieved, the way that a cloth cover and wood pulp base paper are bonded through textile fiber wall paper is abandoned, the jacquard cloth cover and the non-woven fabrics are directly bonded through a hot melt adhesive, and accordingly the environment-friendly effect is achieved.

Description

The processing technology of a kind of jacquard fabrics and spun-bonded non-woven fabrics composite wall cloth fabric
Technical field
The present invention relates to environmental protection breathable and the composite wall cloth fabric processing technology of decoration function can be played in indoor, belonging to the processing method of functional and ornamental weaving face fabric, the processing technology of the composite wall cloth fabric of espespecially a kind of jacquard fabrics and spun-bonded non-woven fabrics.
Background technology
In the epoch that this is growing, people require to increase to life each side, are not only confined to meeting of material, also pursue aesthetic breakthrough and lifting.Wall paper, as a kind of house decorative material, is more and more subject to liking of household decoration person with the decorative pattern of its gracefulness, abundant texture and long-lived characteristic.And on wall paper is selected, first concern point is exactly attractive in appearance, and as the ornamental material of one, having good outward appearance commercially could cause good sale repercussion; Next is performance, if wall paper does not have good gas permeability and situation that is mouldy, that come off will in use occur lower hygroscopicity, affects texture and outward appearance.
At present, with base material classification, wall paper is mainly divided into 4 large classes by domestic market: at the bottom of cloth-faced paper, at the bottom of cloth glue, at the bottom of cloth starch adhesive and at the bottom of cloth cover acupuncture cotton.Wall paper at the bottom of paper is using the 100% bleached wood pulp hanging raw stock that is raw material as base, although the not good and moisture-sensitive of the cheap feature of environmental protection of price comparison easily comes off.The wall paper back side at the bottom of glue uses colloid material, and by large molecular composition, therefore gas permeability is not good, and adopts chemical method more, Prof. Du Yucang, and the colloid feature of environmental protection has much room for improvement.Slurry end wall paper generally adds fire retardant, antistatic agent, the coating paste starching overleaf of anti-fluffing and anti-pilling by adopting, although have certain functional, and the poor and moisture-sensitive of gas permeability.By contrast, at the bottom of cloth cover acupuncture cotton, the combination property of wall paper is best, and pattern is also abundanter, but adopts cotton material to do the end because of it, and higher hygroscopicity and partially expensive price reduce its market advantage.
And segment with wall paper cloth cover material, can three major types be divided into again: nonwoven wall paper, chemical fibre wall paper, textile fabric wallpaper.Nonwoven wall paper adopts natural fiber or the synthetic fibers such as terylene, acrylic fibers such as cotton, numb, a kind of new material of shaping through nonwoven, upper resin, stamp, this wall paper has well-pressed, high resiliency, resistance to brute force, ageing-resistant, the moistureproof feature such as ventilative, and simple and convenient in stickup, maintenance, but comparatively dull in appearance.Chemical fibre wall paper is that stamp forms after treatment with the chemical fabric such as terylene, polypropylene fibre for base stock, this wall paper have nontoxic, tasteless, ventilative, wear-resisting, without features such as layerings, but thiner, lack solid sense.Textile fabric wallpaper makes various color and luster, the thickness yarn of fancy or fabric by natural fiber and chemical fibre, bond with wood pulp based paper again and make, this wall paper has nontoxic, sound-absorbing, breathes freely, has certain damping and fungicidal properties, and have good visual effect, but be that base material is not easily arranged with paper, and change destructible cloth cover decorative pattern when tearing.
At present except individual layer wall paper, also have compound wall paper, namely formed by two-layer above Material cladding.Compared with individual layer wall paper, compound wall paper have multi-functional, easily arrange, compared with multiple good performances such as environmental protection, but price is generally higher.
In order to provide a better alternative condition to wall paper user, this just requires to develop not only ventilative but also environmental and durable high performance-price ratio wall paper attractive in appearance, improves common wall paper poor air permeability, the inadequate environmental protection of material and the clean weak point such as inconvenient.Given this, develop composite wall cloth of the present invention, kind of the present invention belongs to compound wall paper with regard to current existing sorting technique.
Summary of the invention
The object of the present invention is to provide the processing technology of a kind of jacquard fabrics and spun-bonded non-woven fabrics composite wall cloth fabric.Composite wall cloth fabric of the present invention had both had that textile fabric wallpaper is nontoxic, sound-absorbing, the performance such as ventilative, also have nonwoven wall paper well-pressed, ageing-resistant, paste convenient, have certain air permeability and moisture resistance, can clean and non-fading characteristic; But abandon the way that cloth cover and wood pulp based paper bond by textile fabric wallpaper, directly utilize the technology that jacquard weave cloth cover and non-woven fabrics bond by PUR, more environmental protection.
For achieving the above object, technical scheme of the present invention is:
A processing technology for jacquard fabrics and spun-bonded non-woven fabrics composite wall cloth fabric, is characterized in that, comprises the steps: first to select suitable jacquard fabrics as top layer according to product demand, and the raw material of spun-bonded non-woven fabrics is as bottom; Then large elaborate pattern tissue and reasonably technological parameter, formulation technological process is designed; Then utilize complex technique to be bonded in the top layer of jacquard fabrics and the bottom of spun-bonded non-woven fabrics, final form one piece there is fine air permeability, moisture resistance, the easy to clean and composite wall cloth fabric of environmental protection.
Colored tissue in described top layer jacquard fabrics has two kinds, is interweaved respectively, cooperatively interact to reach jacquard effect, mainly meet the requirement that composite wall cloth fabric should have good appearance by the one group of warp be made up of two kinds of different colours with two groups of parallels; Wherein said warp selects terylene low elastic interlaced yarn, and first latitude second latitude all selects terylene to have light low stretch yarn, make the jacquard fabrics of the system of knitting have certain bulkiness and glossiness, and the mesh of network yarn has certain permeation functions.Regain due to polyster fibre is low therefore its hygroscopicity is poor, can play certain barrier effect to the moisture in air or environment; Described bottom spun-bonded non-woven fabrics selects hygroscopicity poor but powerful good fiber.
Described hygroscopicity is poor but powerful large fiber is terylene or polypropylene fibre; When the moisture in air or external environment infiltrates into nonwoven layer through top layer jacquard fabrics, because fiber hygroscopicity is poor, the effect of isolated moisture can be played, hinder moisture to infiltrate further and cause body of wall to make moist to body of wall; And fiber self brute force is comparatively large, when replacing can be avoided to tear, destroy jacquard fabric decorative pattern.Described composite wall cloth fabric to the action principle of moisture as shown in Figure 1.
Described complex technique adopts the method for contactless PUR coat binding, and PUR system adopts the one in ethene and copolymer systems thereof, unformed poly-alpha olefinic system.
Described ethene and copolymer systems thereof adopt EEA, and namely ethylene-ethyl acrylate copolymer is as matrix, Applicable temperature wider range of EEA resin, all has good caking property to polarity and non-polar substrates, and to human non-toxic; Unformed poly-alpha olefinic system adopts APAO, namely ethylene-propylene-1-butene polymers is as matrix, it has temperate zone widely, excellent ground caking property and firmly cohesive force, it is more extensive that its performance coverage compares other polymeric matrixs, and good with a lot of material combination.Described contactless hot-melt mode for cloth, such as Summ it minor spiral glue spraying or fiber glue spraying.Wherein Summ it minor spiral glue spraying is widely used in non-woven fabrics and coating composite hot melt adhesive spraying coating process, and can obtain maximum combined strength bination under low grammes per square metre, regular helix glue shape, open glue shape makes product have better absorbent properties.Fiber glue spraying then utilizes the many hot-air of glue spraying aperture ejection through humidification having the uprush of equidirectional, collodion silk is produced and constantly shakes and swing and draw very carefully and constantly, the effect of ventilative coating can be produced uniformly and stably, greatly reduce glue-spread.
The invention has the beneficial effects as follows: the wall cloth fabric of the double layer material form of the jacquard fabrics in the present invention and spun-bonded non-woven fabrics compound has good air-permeable dampproof performance, in the double dyed jacquard product of top layer latitude, warp selects terylene low elastic interlaced yarn, and the mesh of network yarn has certain permeation functions; First latitude second latitude all selects terylene to have light low stretch yarn, makes the jacquard fabrics of the system of knitting have certain glossiness; And because the regain of polyster fibre is low therefore its hygroscopicity is poor, certain barrier effect can be played to the moisture in air or environment.The spun-bonded non-woven fabrics of bottom adopts hygroscopicity poor but powerful large fiber, and water repellency is excellent, cost is low, frivolous ventilative; When the moisture penetration in air or external environment is to the effect can playing isolated moisture during nonwoven layer, hinder moisture to infiltrate further and cause body of wall to make moist to body of wall; Bottom adopts non-woven fabrics under the prerequisite ensureing good appearance, strengthen gas permeability and the environmental protection index of wall paper, has more higher cost performance; And be easy to peel off body of wall, damage pattern for surface when avoiding changing, while guarantee aesthetics, there is the spun-bonded non-woven fabrics of water repellency as bottom, can also be convenient for cleaning and environmental and durable.
The jacquard fabrics produced through the present invention and spun-bonded non-woven fabrics composite wall cloth fabric composite material have certain aesthetics and functional, and ornament materials market has vast potential for future development.The present invention makes contributions for the development of wall cloth fabric and the wall paper product of exploitation high performance-price ratio.
Accompanying drawing explanation
Fig. 1 is that composite wall cloth fabric in the embodiment of the present invention is to the action principle figure of moisture;
Fig. 2 is ground five pieces of warp sateen plans of weave of portion first and second latitude combination in the embodiment of the present invention;
Fig. 3 is embodiment of the present invention Zhong Hua district 1 second latitude organization chart;
Fig. 4 is embodiment of the present invention Zhong Hua district 2 first latitude organization chart;
Fig. 5 is embodiment of the present invention Zhong Hua district 2 second latitude organization chart.
Fig. 6 is woven local plan of weave in the embodiment of the present invention;
Fig. 7 is woven grain pattern figure in the embodiment of the present invention.
Detailed description of the invention
Embodiment 1
A kind of jacquard fabrics of the present embodiment and the processing technology of spun-bonded non-woven fabrics composite wall cloth fabric, comprise the steps: first to select suitable jacquard fabrics as top layer according to product demand, the raw material of spun-bonded non-woven fabrics is as bottom; Then large elaborate pattern tissue and reasonably technological parameter, formulation technological process is designed; Then complex technique is utilized to be bonded in the top layer of jacquard fabrics and the bottom of spun-bonded non-woven fabrics, the PUR of unformed poly-alpha olefines system is adopted in complex technique, concrete selection for the PUR of matrix is as adhesive using APAO (ethylene-propylene-1-butene polymers), final form one piece and has fine air permeability, moisture resistance, the easy to clean and composite wall cloth fabric of environmental protection.
Wherein technological parameter is: in the jacquard fabrics of top layer, and flower tissue has two kinds, and flower district 1 is floating long, backing second latitude 1/1 plain weave of first latitude latitude; Flower district 2 is second latitude 1/1 plain weave, backing first latitude filling face 3/1 twill-weave, be organized as first and second latitudes combination five pieces of warp sateens, ground portion first and second latitude combination five pieces of warp sateen plans of weave as shown in Figure 2, in plan of weave black block for flower district 1, grey block is flower district 2, and white block is ground portion; The lifting number of times wherein spending first latitude in district 1 is 0, and be namely organized as latitude floating long, second latitude is organized as shown in Figure 3; In flower district 2, first latitude is organized as shown in Figure 4, and second latitude is organized as shown in Figure 5.
Organizine selects 166.7dtex × 1 (1/150D) terylene low elastic interlaced yarn (dark-brown), 166.7dtex × 1 (1/150D) terylene low elastic interlaced yarn (golden yellow), mainly meets the requirement that composite wall cloth fabric should have good appearance; In latitude combination, first, second latitude selects 333.3dtex × 1 (1/300D) terylene to have light low stretch yarn; Make the jacquard fabrics of the system of knitting have certain bulkiness and glossiness, and the mesh of network yarn have certain permeation functions.Regain due to polyster fibre is low therefore its hygroscopicity is poor, can play certain barrier effect to the moisture in air or environment; Finished product through close be 68/cm, finished product filling density is 12/cm; 2688 electronic jacquard halters are weaved, upper machine through close 62/cm, upper machine filling density 10/cm; Fabric width 144 ± 5cm.Woven local plan of weave as shown in Figure 6; Grain pattern figure as shown in Figure 7.
Wherein said bottom spun-bonded non-woven fabrics, adopt slim PP (polypropylene fibre) non-woven fabrics, when the moisture in air or external environment infiltrates into nonwoven layer through top layer jacquard fabrics, because fiber hygroscopicity is poor, the effect of isolated moisture can be played, hinder moisture to infiltrate further and cause body of wall to make moist to body of wall; And fiber self brute force is comparatively large, when replacing can be avoided to tear, destroy jacquard fabric decorative pattern.Consolidation style is that hot rolling is reinforced.Technical process can be summarized as follows: section-screw extruder-measuring pump-spinneret-cooling quench-air drawing-lapping-be rolled into cloth-winding.Raw material choose HOPP is cut into slices, and finished product grammes per square metre is 17-50g/m 2, thickness is 0.03--0.20mm, and fabric width is 1.5m--3m.PP (polypropylene fibre) specifications parameter is as shown in table 1;
When carrying out hot rolling, should notice that hot-rolled temperature can not, higher than PP fusing point, control within the scope of 135-165 DEG C; Hot rolling time roll temperature is more than 4-5 times, flower roller, but unsuitable too high, otherwise the flexibility of cloth can be made to be deteriorated.Hot Line pressure can set with temperature according to product is surely heavy, and the temperature of flower roller, smooth roll then depends on determines weight and speed.
Be that the PUR of matrix carries out compound tense as adhesive with APAO utilizing, APAO has temperate zone widely, excellent ground caking property and firmly cohesive force, it is more extensive that its performance coverage compares other polymeric matrixs, and good with a lot of material combination.Adopt the contactless hot-melt mode for cloth of Summ it minor spiral glue spraying, Summ it minor spiral glue spraying is widely used in non-woven fabrics and coating composite hot melt adhesive spraying coating process, can obtain maximum combined strength bination under low grammes per square metre, regular helix glue shape, open glue shape makes product have better absorbent properties.Certainly should strictly control following technological parameter: the machine open hour, ought to be more short better, and the machine open hour must well below the open hour of PUR, with before preventing the non-compound of PUR cooling curing bonding effect is deteriorated; Gluing temperature, more high better with temperature within the scope of APAO work temperate zone, but may not exceed polypropylene fiber fusing point (160 DEG C), to protect cloth cover integrity; Spread, glue-spread is more few better, according to product requirement, with 35 ~ 50g/m 2be advisable; Composite pressure, under the prerequisite not destroying elaborate pattern and cloth cover, the larger then effect of pressure is better.
Jacquard fabrics in the present embodiment and spun-bonded non-woven fabrics composite wall cloth fabric have good air-permeable dampproof performance, can be covered with gum during use at composite wall cloth fabric backing layer, conveniently tear.
The wall cloth fabric of the double layer material form of the jacquard fabrics in the present embodiment and spun-bonded non-woven fabrics compound has good air-permeable dampproof performance, in the double dyed jacquard product of top layer latitude, warp selects terylene low elastic interlaced yarn, and the mesh of network yarn has certain permeation functions; First latitude second latitude all selects terylene to have light low stretch yarn, makes the jacquard fabrics of the system of knitting have certain glossiness; And because the regain of polyster fibre is low therefore its hygroscopicity is poor, certain barrier effect can be played to the moisture in air or environment.The spun-bonded non-woven fabrics of bottom adopts hygroscopicity poor but powerful large fiber, and water repellency is excellent, cost is low, frivolous ventilative; When the moisture penetration in air or external environment is to the effect can playing isolated moisture during nonwoven layer, hinder moisture to infiltrate further and cause body of wall to make moist to body of wall; Bottom adopts non-woven fabrics under the prerequisite ensureing good appearance, strengthen gas permeability and the environmental protection index of wall paper, has more higher cost performance; And be easy to peel off body of wall, damage pattern for surface when avoiding changing, while guarantee aesthetics, there is the spun-bonded non-woven fabrics of water repellency as bottom, can also be convenient for cleaning and environmental and durable.
Embodiment 2
A kind of jacquard fabrics of the present embodiment and the processing technology of spun-bonded non-woven fabrics composite wall cloth fabric, comprise the steps: first to select suitable jacquard fabrics as top layer according to product demand, the raw material of spun-bonded non-woven fabrics is as bottom; Then large elaborate pattern tissue and reasonably technological parameter, formulation technological process is designed; Then complex technique is utilized to be bonded in the top layer of jacquard fabrics and the bottom of spun-bonded non-woven fabrics, the PUR of ethene and copolymer analog system thereof is adopted in complex technique, concrete selection, using EEA (ethylene-ethyl acrylate copolymer) PUR that is matrix as adhesive, finally forms one piece and has fine air permeability, moisture resistance, the easy to clean and composite wall cloth fabric of environmental protection.
Wherein technological parameter is: in the jacquard fabrics of top layer, and flower tissue has two kinds, and flower district 1 is floating long, backing second latitude 1/1 plain weave of first latitude latitude; Flower district 2 is second latitude 1/1 plain weave, backing first latitude filling face 3/1 twill-weave, be organized as first and second latitudes combination five pieces of warp sateens, ground portion first and second latitude combination five pieces of warp sateen plans of weave as shown in Figure 2, in plan of weave black block for flower district 1, grey block is flower district 2, and white block is ground portion; The lifting number of times wherein spending first latitude in district 1 is 0, and be namely organized as latitude floating long, second latitude is organized as shown in Figure 3; In flower district 2, first latitude is organized as shown in Figure 4, and second latitude is organized as shown in Figure 5.
Organizine selects 166.7dtex × 1 (1/150D) terylene low elastic interlaced yarn (dark-brown), 166.7dtex × 1 (1/150D) terylene low elastic interlaced yarn (golden yellow), mainly meets the requirement that composite wall cloth fabric should have good appearance; In latitude combination, first, second latitude selects 333.3dtex × 1 (1/300D) terylene to have light low stretch yarn; Make the jacquard fabrics of the system of knitting have certain bulkiness and glossiness, and the mesh of network yarn have certain permeation functions.Regain due to polyster fibre is low therefore its hygroscopicity is poor, can play certain barrier effect to the moisture in air or environment; Finished product through close be 68/cm, finished product filling density is 12/cm; 2688 electronic jacquard halters are weaved, upper machine through close 62/cm, upper machine filling density 10/cm; Fabric width 144 ± 5cm.Woven local plan of weave as shown in Figure 6; Grain pattern figure as shown in Figure 7.
Wherein said bottom spun-bonded non-woven fabrics, adopt slim PET (terylene) non-woven fabrics, when the moisture in air or external environment infiltrates into nonwoven layer through top layer jacquard fabrics, because fiber hygroscopicity is poor, the effect of isolated moisture can be played, hinder moisture to infiltrate further and cause body of wall to make moist to body of wall; And fiber self brute force is comparatively large, when replacing can be avoided to tear, destroy jacquard fabric decorative pattern.Consolidation style is that hot rolling is reinforced.Technical process can be summarized as follows: section-screw extruder-measuring pump-spinneret-cooling quench-air drawing-lapping-be rolled into cloth-winding.Raw material choose PET cuts into slices, and finished product grammes per square metre is 17-50g/m 2, thickness is 0.10-0.30mm, and fabric width is 1.5m--3m.PET (terylene) specifications parameter is as shown in table 2;
When carrying out hot rolling, should notice that hot-rolled temperature can not, higher than PET fusing point, control within the scope of 235-250 DEG C; Hot rolling time roll temperature is more than 4-5 times, flower roller, but unsuitable too high, otherwise the flexibility of cloth can be made to be deteriorated.Hot Line pressure can set with temperature according to product is surely heavy, and the temperature of flower roller, smooth roll then depends on determines weight and speed.
Being that the PUR of matrix carries out compound tense as adhesive, Applicable temperature wider range of EEA resin with EEA utilizing, all having good caking property to polarity and non-polar substrates, and to human non-toxic.Adopt the contactless hot-melt mode for cloth of fiber glue spraying, fiber glue spraying can utilize the many hot-air of glue spraying aperture ejection through humidification having the uprush of equidirectional, collodion silk is produced and constantly shakes and swing and draw very carefully and constantly, the effect of ventilative coating can be produced uniformly and stably, greatly reduce glue-spread.Certainly should strictly control following technological parameter: the machine open hour, ought to be more short better, and the machine open hour must well below the open hour of PUR, with before preventing the non-compound of PUR cooling curing bonding effect is deteriorated; Gluing temperature, more high better with temperature within the scope of EEA work temperate zone, but may not exceed polyster fibre fusing point (250 ~ 260 DEG C), to protect cloth cover integrity; Spread, glue-spread is more few better, according to product requirement, with 35 ~ 50g/m 2be advisable; Composite pressure, under the prerequisite not destroying elaborate pattern and cloth cover, the larger then effect of pressure is better.
Jacquard fabrics in the present embodiment and spun-bonded non-woven fabrics composite wall cloth fabric have good air-permeable dampproof performance, can be covered with gum during use at composite wall cloth fabric backing layer, conveniently tear.
The wall cloth fabric of the double layer material form of the jacquard fabrics in the present embodiment and spun-bonded non-woven fabrics compound has good air-permeable dampproof performance, in the double dyed jacquard product of top layer latitude, warp selects terylene low elastic interlaced yarn, and the mesh of network yarn has certain permeation functions; First latitude second latitude all selects terylene to have light low stretch yarn, makes the jacquard fabrics of the system of knitting have certain glossiness; And because the regain of polyster fibre is low therefore its hygroscopicity is poor, certain barrier effect can be played to the moisture in air or environment.The spun-bonded non-woven fabrics of bottom adopts hygroscopicity poor but powerful large fiber, and water repellency is excellent, cost is low, frivolous ventilative; When the moisture penetration in air or external environment is to the effect can playing isolated moisture during nonwoven layer, hinder moisture to infiltrate further and cause body of wall to make moist to body of wall; Bottom adopts non-woven fabrics under the prerequisite ensureing good appearance, strengthen gas permeability and the environmental protection index of wall paper, has more higher cost performance; And be easy to peel off body of wall, damage pattern for surface when avoiding changing, while guarantee aesthetics, there is the spun-bonded non-woven fabrics of water repellency as bottom, can also be convenient for cleaning and environmental and durable.
Table 1
Table 2

Claims (5)

1. a processing technology for jacquard fabrics and spun-bonded non-woven fabrics composite wall cloth fabric, is characterized in that, comprises the steps: first to select suitable jacquard fabrics as top layer according to product demand, and the raw material of spun-bonded non-woven fabrics is as bottom; Then large elaborate pattern tissue and reasonably technological parameter, formulation technological process is designed; Then utilize complex technique to be bonded in the top layer of jacquard fabrics and the bottom of spun-bonded non-woven fabrics, final form one piece there is fine air permeability, moisture resistance, the easy to clean and composite wall cloth fabric of environmental protection.
2. the processing technology of a kind of jacquard fabrics as claimed in claim 1 and spun-bonded non-woven fabrics composite wall cloth fabric, it is characterized in that: the colored tissue in described top layer jacquard fabrics has two kinds, interweaved with two groups of parallels respectively by the one group of warp be made up of two kinds of different colours, cooperatively interact to reach jacquard effect; Wherein said warp selects terylene low elastic interlaced yarn, and first latitude second latitude all selects terylene to have light low stretch yarn; Described bottom spun-bonded non-woven fabrics selects hygroscopicity poor but powerful good fiber.
3. the processing technology of a kind of jacquard fabrics as claimed in claim 2 and spun-bonded non-woven fabrics composite wall cloth fabric, is characterized in that: described hygroscopicity is poor but powerful large fiber is terylene or polypropylene fibre.
4. the processing technology of a kind of jacquard fabrics as claimed in claim 1 and spun-bonded non-woven fabrics composite wall cloth fabric, it is characterized in that: described complex technique adopts the method for contactless PUR coat binding, PUR system adopts the one in ethene and copolymer systems thereof, unformed poly-alpha olefinic system.
5. the processing technology of a kind of jacquard fabrics as claimed in claim 4 and spun-bonded non-woven fabrics composite wall cloth fabric, is characterized in that: described ethene and copolymer systems thereof adopt EEA, and namely ethylene-ethyl acrylate copolymer is as matrix; Unformed poly-alpha olefinic system adopts APAO, and namely ethylene-propylene-1-butene polymers is as matrix.
CN201510227654.2A 2015-05-06 2015-05-06 Machining process of jacquard fabric and spun-bonded non-woven fabric composite wall cloth fabrics Pending CN104859234A (en)