CN104858562B - 一种耐热药芯焊丝 - Google Patents

一种耐热药芯焊丝 Download PDF

Info

Publication number
CN104858562B
CN104858562B CN201510227462.1A CN201510227462A CN104858562B CN 104858562 B CN104858562 B CN 104858562B CN 201510227462 A CN201510227462 A CN 201510227462A CN 104858562 B CN104858562 B CN 104858562B
Authority
CN
China
Prior art keywords
welding
flux
medicinal powder
cored wire
effect
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510227462.1A
Other languages
English (en)
Other versions
CN104858562A (zh
Inventor
郭寅斌
刘小军
张德远
安毕军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guizhou kaihong Huida Cooling System Co. Ltd.
Original Assignee
Guizhou Kaihong Huida Cooling System Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guizhou Kaihong Huida Cooling System Co Ltd filed Critical Guizhou Kaihong Huida Cooling System Co Ltd
Priority to CN201510227462.1A priority Critical patent/CN104858562B/zh
Publication of CN104858562A publication Critical patent/CN104858562A/zh
Application granted granted Critical
Publication of CN104858562B publication Critical patent/CN104858562B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐热药芯焊丝包括碳钢外皮和填充在碳钢外皮内的药粉，所述药粉占焊丝总重量的百分比为：Cr：0.04‑0.1％、Mo：0.06‑0.12％、Mn：1.2‑1.8％、Si：1.4‑2％。本药芯焊丝中加入C的作用是保证焊接金属的强度，Si的作用是减少熔敷金属内的氧含量，提高熔敷金属的流动性Mo的作用是在高热量输入焊和高层间温度条件下的焊接中使焊接金属组织变得稳定，保障焊接金属的韧性及强度，S的作用是将熔池流动从外部转移到内部，将焊渣集中到内部，使得焊渣的消除工作更加容易，提高了焊道的整洁度。通过调整药粉中的成分和含量，使得制备出来的药芯焊丝具有焊接强度高、电弧稳定、脱渣容易、耐高温等特点。

Description

一种耐热药芯焊丝
技术领域
本发明涉及金属焊接材料技术领域，具体涉及一种耐热药芯焊丝。
背景技术
药芯焊丝也称为管状焊丝或粉芯焊丝，是20世纪50年代发展起来的高效率焊接材料，可以通过调整药芯添加物的种类和比例，很方便地设计各种不同用途的焊接材料，以适于不同工矿、不同条件设备部件的要求，用来焊接各种类型钢材。药芯焊丝既具有药皮焊条的配方可调性，同时又具有实芯焊丝连续焊接的特点。药芯焊丝正以其无可比拟的技术和经济性，受到国内外焊接界的极大关注。
现有的焊丝中在稳定性方面都比较成功，但是其耐热性和焊接部位的完整性则比较差强人意，因此本发明人通过研究药芯焊丝中药粉的成分和含量提供了一种耐热性较强，能够有效抑制焊接过程焊渣量保证其焊接面完整整洁的药芯焊丝。
发明内容
为解决上述技术问题，本发明提供了一种耐热药芯焊丝。
本发明是通过以下技术方案予以实现的：
一种耐热药芯焊丝包括碳钢外皮和填充在碳钢外皮内的药粉，所述药粉占焊丝总重量的百分比为：Cr：0.04-0.1％、Mo：0.06-0.12％、Mn：1.2-1.8％、Si：1.4-2％。
所述药粉中还含有C其含量占焊丝总重量的百分比为：0.06-0.12％。
所述药粉中还含有TiO2其含量占焊丝总重量的百分比为：5.0-9.0％。
所述药粉中还含有S其含量占焊丝总重量的百分比为：0.3-0.6％。
本发明提供的C的作用是保证焊接金属的强度，保障焊接部位的质量，避免氧化副产物渗入焊接金属的内部。
Si是脱氧剂，其作用是减少熔敷金属内的氧含量，提高熔敷金属的流动性。
Mo的作用是在高热量输入焊和高层间温度条件下的焊接中使焊接金属组织变得稳定，保障焊接金属的韧性及强度。
S的作用是将熔池流动从外部转移到内部，将焊渣集中到内部，使得焊渣的消除工作更加容易，提高了焊道的整洁度。
本发明的有益效果在于：本药芯焊丝中加入C的作用是保证焊接金属的强度，Si的作用是减少熔敷金属内的氧含量，提高熔敷金属的流动性Mo的作用是在高热量输入焊和高层间温度条件下的焊接中使焊接金属组织变得稳定，保障焊接金属的韧性及强度，S的作用是将熔池流动从外部转移到内部，将焊渣集中到内部，使得焊渣的消除工作更加容易，提高了焊道的整洁度。通过调整药粉中的成分和含量，使得制备出来的药芯焊丝具有焊接强度高、电弧稳定、脱渣容易、耐高温等特点。
具体实施方式
以下结合实施例对本发明的技术方案作进一步描述，但要求保护的范围并不局限于所述。
实施例一
按照药粉占焊丝总重量的百分比为：Cr：0.04％、Mo：0.06％、Mn：1.2％、Si：1.4％、C：0.06％。TiO2：5.0％、S：0.3％的比例将该药粉加入到碳钢外皮中，使药粉包裹在其中，然后通过拉丝机处理即得到本发明耐蚀药芯焊丝。
实施例二
按照药粉占焊丝总重量的百分比为：Cr：0.1％、Mo：0.12％、Mn：1.8％、Si：2％、C：0.12％。TiO2：9.0％、S：0.6％的比例将该药粉加入到碳钢外皮中，使药粉包裹在其中，然后通过拉丝机处理即得到本发明耐蚀药芯焊丝。
实施例三
按照药粉占焊丝总重量的百分比为：Cr：0.07％、Mo：0.09％、Mn：1.5％、Si：1.7％、C：0.09％。TiO2：7.0％、S：0.45％的比例将该药粉加入到碳钢外皮中，使药粉包裹在其中，然后通过拉丝机处理即得到本发明耐蚀药芯焊丝。

Claims (1)

1.一种耐热药芯焊丝，包括碳钢外皮和填充在碳钢外皮内的药粉，其特征在于：所述药粉占焊丝总重量的百分比为：Cr：0.04-0.1％、Mo：0.06-0.12％、Mn：1.2-1.8％、Si：1.4-2％；
所述药粉中还含有C其含量占焊丝总重量的百分比为：0.06-0.12％；
所述药粉中还含有TiO2其含量占焊丝总重量的百分比为：5.0-9.0％；
所述药粉中还含有S其含量占焊丝总重量的百分比为：0.3-0.6％。
CN201510227462.1A 2015-05-06 2015-05-06 一种耐热药芯焊丝 Expired - Fee Related CN104858562B (zh)