CN104845729B - Chain road dry lubricant and preparation method thereof - Google Patents
Chain road dry lubricant and preparation method thereof Download PDFInfo
- Publication number
- CN104845729B CN104845729B CN201510215497.3A CN201510215497A CN104845729B CN 104845729 B CN104845729 B CN 104845729B CN 201510215497 A CN201510215497 A CN 201510215497A CN 104845729 B CN104845729 B CN 104845729B
- Authority
- CN
- China
- Prior art keywords
- chain road
- dry lubricant
- weight
- parts
- isooctanol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of chain road dry lubricant, include the composition of following parts by weight：Di-phosphorus pentonide 0.5 15, APEO 0.1 5, MEA 0.5 5, triethanolamine 0.5 5, silicone emulsion 60 80.The chain road of the present invention is that stoste is used with dry lubricant, and it is directly painted in conveyer chain, and consumption is small compared with similar products, cost-effective, and each composition is water solubility, and lubricant contacts Hou Lian roads with chain road clearly, and cleaning soluble in water is easy to operate.
Description
Technical field
The invention belongs to field of lubricant, it is related to food industry production chain road lubrication class product, it is more particularly to a kind of new
Chain road dry lubricant and preparation method thereof.
Background technology
In the food productions such as beer beverage, packing container has part packaging on chain road topples over, and can cause packaging
The damage of container；Packing container is transmitted on the bad chain road of lubricant effect can cause the abrasion of part packing container.Current city
Lubricant on field is generally that moistening is sliding, it is necessary to which a large amount of water dilutions, use cost is higher, and production environment is poor；The existing chain in market
Road is mostly glycerine with dry lubricant main component, and this series lubricant agent is more greasy, and chain road needs frequent cleaning, directly increases
Production cost.
The content of the invention
In order to solve the above-mentioned technical problem, the invention provides a kind of new chain road dry lubricant.
The chain road dry lubricant of the present invention, includes the composition of following parts by weight：
Di-phosphorus pentonide 0.5-15,
APEO 0.1-5,
MEA 0.5-5,
Triethanolamine 0.5-5,
Silicone emulsion 60-80.
Preferably, described chain road dry lubricant, in addition to 10 ~ 35 parts of water.
Preferably, the Di-phosphorus pentonide be one of isooctanol phosphate monoester and isooctanol phosphate diester or its
The mixture of meaning ratio.
Preferably, the Di-phosphorus pentonide is the mixture of isooctanol phosphate monoester and isooctanol phosphate diester, wherein
The parts by weight of isooctanol phosphate monoester are 0.5-10, and the parts by weight of isooctanol phosphate diester are 0.1-5.It is highly preferred that institute
The parts by weight for stating isooctanol phosphate monoester are 1-7, and the parts by weight of the isooctanol phosphate diester are 0.2-3.
Preferably, the parts by weight of the silicone emulsion are 65-75.
Preferably, the parts by weight of the MEA are 0.5-3, and the parts by weight of the triethanolamine are 1-3.
Preferably, the parts by weight of the APEO are 0.2-3.
Preferably, above-mentioned chain road dry lubricant, is made up of the composition of following parts by weight：
Isooctanol phosphate monoester 1,
Isooctanol phosphate diester 1,
APEO 0.5,
MEA 0.5,
Triethanolamine 2,
Silicone emulsion 70,
Deionized water 25.
The present invention provides the preparation method of above-mentioned chain road dry lubricant：Each composition is mixed by the amount, stirred
Produce.
The present invention can reach following technique effect：
Lubricant of the present invention can be used for the packagings such as food industry production chain road and vial, PET bottle and pop can to hold
The lubrication of device, lubricant effect is substantially better than existing chain road dry lubricant and moistening lubrication prescription.
The chain road of the present invention is with dry lubricant compared with the existing chain road dry lubricant in market, and the present invention makes for stoste
With it is directly painted in conveyer chain, and consumption is small compared with similar products, cost-effective, and each composition is water solubility, lubrication
Ji Yulian roads contact Hou Lian roads are salubrious, and cleaning soluble in water is easy to operate.
Embodiment
With reference to specific embodiment, the invention will be further described, so that those skilled in the art can be more preferable
Understand the present invention and can be practiced, but illustrated embodiment is not as a limitation of the invention.
Embodiment 1
The chain road dry lubricant of the present embodiment, is made up of the component of following parts by weight：
Isooctanol phosphate monoester 1,
Isooctanol phosphate diester 1,
APEO 0.5,
MEA 0.5,
Triethanolamine 2,
Silicone emulsion 70,
Deionized water 25.
Preparation method：
1. sequentially add 25 parts of the deionized water measured, 1 part of isooctanol phosphate monoester, 1 part of isooctanol phosphate diester, different
0.5 part of octanol polyoxyethylene ether phosphate, 0.5 part of MEA, 2 parts of triethanolamine stir, and add 70 parts of silicone emulsion,
It is stirred at room temperature 20 minutes.
2. filtered and packaged with 300 mesh filter screens.
Application method：The chain road dry lubricant prepared is added in lubricant liquid storing barrel, to food transport chain road
Spray in 30 minutes is once.
Using effect：The chain road of the present embodiment is with after dry lubricant use, and without greasy in conveyer chain, and each composition is molten
Yu Shui, need to only be wiped during cleaning with wet rag to clean up, and usage amount is few, and saving largely uses water.Use in existing chain road
Dry lubricant needs spray in 5-20 minutes once, and usage amount is big.Same chain road, using existing moistening lubrication prescription, needs when using
It is diluted to 0.4% to use, field ground there are a large amount of ponding, workman easily slips, and easily produces mould.
Embodiment 2
The chain road dry lubricant of the present embodiment, is made up of the component of following parts by weight：
Isooctanol phosphate monoester 2,
Isooctanol phosphate diester 2,
APEO 1.5,
MEA 1,
Triethanolamine 2,
Silicone emulsion 65,
Deionized water 26.5.
Preparation method：
1. sequentially add 26.5 parts of the deionized water measured, 2 parts of isooctanol phosphate monoester, 2 parts of isooctanol phosphate diester,
1.5 parts of Phosphate of Polyoxyethylene Isooctyl Ether, 1 part of MEA, 2 parts of triethanolamine stir, and add 65 parts of silicone emulsion,
It is stirred at room temperature 20 minutes.
2. filtered and packaged with 300 mesh filter screens.
Application method：The chain road dry lubricant prepared is added in lubricant liquid storing barrel, to food transport chain road
Spray in 30 minutes is once.
Using effect：The chain road of the present embodiment is with after dry lubricant use, and without greasy in conveyer chain, and each composition is molten
Yu Shui, need to only be wiped during cleaning with wet rag to clean up, and usage amount is few, and saving largely uses water.
Embodiment 3
The chain road dry lubricant of the present embodiment, is made up of the component of following parts by weight：
Isooctanol phosphate monoester 7,
Isooctanol phosphate diester 3,
APEO 0.5,
MEA 2,
Triethanolamine 1,
Silicone emulsion 75,
Deionized water 12.5.
Preparation method：
1. sequentially add the deionized water measured, isooctanol phosphate monoester, isooctanol phosphate diester, isooctanol polyoxy second
Alkene ether phosphate, MEA, triethanolamine stir, and add silicone emulsion, are stirred at room temperature 20 minutes.
2. filtered and packaged with 300 mesh filter screens.
Application method：The chain road dry lubricant prepared is added in lubricant liquid storing barrel, to food transport chain road
Spray in 30 minutes is once.
Using effect：The chain road of the present embodiment is with after dry lubricant use, and without greasy in conveyer chain, and each composition is molten
Yu Shui, need to only be wiped during cleaning with wet rag to clean up, and usage amount is few, and saving largely uses water.
Embodiment 4
The chain road dry lubricant of the present embodiment, is made up of the component of following parts by weight：
Isooctanol phosphate monoester 5,
Isooctanol phosphate diester 0.2,
APEO 0.2,
MEA 3,
Triethanolamine 3,
Silicone emulsion 68,
Deionized water 21.6.
Preparation method：
1. sequentially add the deionized water measured, isooctanol phosphate monoester, isooctanol phosphate diester, isooctanol polyoxy second
Alkene ether phosphate, MEA, triethanolamine stir, and add silicone emulsion, are stirred at room temperature 20 minutes.
2. filtered and packaged with 300 mesh filter screens.
Application method：The chain road dry lubricant prepared is added in lubricant liquid storing barrel, to food transport chain road
Spray in 30 minutes is once.
Using effect：The chain road of the present embodiment is with after dry lubricant use, and without greasy in conveyer chain, and each composition is molten
Yu Shui, need to only be wiped during cleaning with wet rag to clean up, and usage amount is few, and saving largely uses water.
Embodiment 5
The chain road dry lubricant of the present embodiment, is made up of the component of following parts by weight：
Isooctanol phosphate monoester 2,
Isooctanol phosphate diester 4,
APEO 5,
MEA 0.5,
Triethanolamine 5,
Silicone emulsion 60,
Deionized water 21.5.
Preparation method：
1. sequentially add the deionized water measured, isooctanol phosphate monoester, isooctanol phosphate diester, isooctanol polyoxy second
Alkene ether phosphate, MEA, triethanolamine stir, and add silicone emulsion, are stirred at room temperature 20 minutes.
2. filtered and packaged with 300 mesh filter screens.
Application method：The chain road dry lubricant prepared is added in lubricant liquid storing barrel, to food transport chain road
Spray in 30 minutes is once.
Using effect：The chain road of the present embodiment is with after dry lubricant use, and without greasy in conveyer chain, and each composition is molten
Yu Shui, need to only be wiped during cleaning with wet rag to clean up, and usage amount is few, and saving largely uses water.
Embodiment 6
The chain road dry lubricant of the present embodiment, is made up of the component of following parts by weight：
Isooctanol phosphate monoester 9,
Isooctanol phosphate diester 0.1,
APEO 0.1,
MEA 5,
Triethanolamine 2,
Silicone emulsion 70,
Deionized water 13.8.
Preparation method：
1. sequentially add the deionized water measured, isooctanol phosphate monoester, isooctanol phosphate diester, isooctanol polyoxy second
Alkene ether phosphate, MEA, triethanolamine stir, and add silicone emulsion, are stirred at room temperature 20 minutes.
2. filtered and packaged with 300 mesh filter screens.
Application method：The chain road dry lubricant prepared is added in lubricant liquid storing barrel, to food transport chain road
Spray in 30 minutes is once.
Using effect：The chain road of the present embodiment is with after dry lubricant use, and without greasy in conveyer chain, and each composition is molten
Yu Shui, need to only be wiped during cleaning with wet rag to clean up, and usage amount is few, and saving largely uses water.
Embodiment 7
The chain road dry lubricant of the present embodiment, is made up of the component of following parts by weight：
Isooctanol phosphate monoester 12,
APEO 4,
MEA 4,
Triethanolamine 4,
Silicone emulsion 61,
Deionized water 15.
Preparation method：
1. sequentially add the deionized water measured, isooctanol phosphate monoester, Phosphate of Polyoxyethylene Isooctyl Ether, Dan Yi
Hydramine, triethanolamine stir, and add silicone emulsion, are stirred at room temperature 20 minutes.
2. filtered and packaged with 300 mesh filter screens.
Application method：The chain road dry lubricant prepared is added in lubricant liquid storing barrel, to food transport chain road
Spray in 30 minutes is once.
Using effect：The chain road of the present embodiment is with after dry lubricant use, and without greasy in conveyer chain, and each composition is molten
Yu Shui, need to only be wiped during cleaning with wet rag to clean up, and usage amount is few, and saving largely uses water.
Embodiment 8
The chain road dry lubricant of the present embodiment, is made up of the component of following parts by weight：
Isooctanol phosphate diester 7,
APEO 3,
MEA 4,
Triethanolamine 1,
Silicone emulsion 65,
Deionized water 20.
Preparation method：
1. sequentially add the deionized water measured, isooctanol phosphate diester, Phosphate of Polyoxyethylene Isooctyl Ether, Dan Yi
Hydramine, triethanolamine stir, and add silicone emulsion, are stirred at room temperature 20 minutes.
2. filtered and packaged with 300 mesh filter screens.
Application method：The chain road dry lubricant prepared is added in lubricant liquid storing barrel, to food transport chain road
Spray in 30 minutes is once.
Using effect：The chain road of the present embodiment is with after dry lubricant use, and without greasy in conveyer chain, and each composition is molten
Yu Shui, need to only be wiped during cleaning with wet rag to clean up, and usage amount is few, and saving largely uses water.
Greasy property is detected：
Detection method：
Sample stoste is uniformly applied on carrier bar with hairbrush（The matter for being applied to lubricant on carrier bar is recorded with Subtraction method
Amount）, will experiment Packaging Bottle be placed on carrier bar one end, for increase data accuracy 500g be packaged as two bottles, 250ml be packaged as four bottles of use
Rope is squeezed in the middle of bottle, is at the uniform velocity pulled with tensiometer to the other end, is now recorded tensiometer and is shown numerical value, parallel ten surveys
It is fixed.Calculation formula：Friction coefficient μ=pulling force g/bottle weight g
The contrast verification result of table 1
| Lubricant | Coefficient of friction |
| Embodiment 1 | 0.0742 |
| Embodiment 2 | 0.0803 |
| Embodiment 3 | 0.0786 |
| Embodiment 4 | 0.0769 |
| Embodiment 5 | 0.0851 |
| Embodiment 6 | 0.0842 |
| Embodiment 7 | 0.0913 |
| Embodiment 8 | 0.0905 |
| Commercially available chain road dry lubricant 1 | 0.1112 |
| Commercially available chain road dry lubricant 2 | 0.0927 |
| Commercially available chain road dry lubricant 3 | 0.1360 |
| Commercially available moistening lubrication prescription 1 | 0.1051 |
| Commercially available moistening lubrication prescription 2 | 0.1250 |
Conclusion：From table 1 it follows that the chain road dry lubricant of the present invention, lubricating ability is better than commercially available chain road
With dry lubricant and commercially available moistening lubrication prescription, lubricant effect is good.
Embodiment described above is only the preferred embodiment to absolutely prove the present invention and being lifted, protection model of the invention
Enclose not limited to this.Equivalent substitute or conversion that those skilled in the art are made on the basis of the present invention, in the present invention
Protection domain within.Protection scope of the present invention is defined by claims.
Claims (7)
1. a kind of chain road dry lubricant, it is characterised in that be made up of the composition of following parts by weight：
Di-phosphorus pentonide 0.5-15,
APEO 0.1-5,
MEA 0.5-5,
Triethanolamine 0.5-5,
Silicone emulsion 60-80,
10 ~ 35 parts of water；
Wherein, the Di-phosphorus pentonide is the mixture of isooctanol phosphate monoester and isooctanol phosphate diester, wherein isooctanol
The parts by weight of phosphate monoester are 0.5-10, and the parts by weight of isooctanol phosphate diester are 0.1-5.
2. chain road according to claim 1 dry lubricant, it is characterised in that the weight of the isooctanol phosphate monoester
Number is 1-7, and the parts by weight of the isooctanol phosphate diester are 0.2-3.
3. chain road according to claim 2 dry lubricant, it is characterised in that the parts by weight of the silicone emulsion are
65-75。
4. chain road according to claim 2 dry lubricant, it is characterised in that the parts by weight of the MEA are
0.5-3, the parts by weight of the triethanolamine are 1-3.
5. chain road according to claim 2 dry lubricant, it is characterised in that the parts by weight of the APEO
For 0.2-3.
6. chain road according to claim 2 dry lubricant, it is characterised in that by the composition structure of following parts by weight
Into：
Isooctanol phosphate monoester 1,
Isooctanol phosphate diester 1,
APEO 0.5,
MEA 0.5,
Triethanolamine 2,
Silicone emulsion 70,
Deionized water 25.
7. the preparation method of the chain road dry lubricant described in any one of claim 1 ~ 6, it is characterised in that will by the amount
Each composition mixing, stirring is produced.