CN104844079A - 一种水泥基渗透结晶型防水材料及其制备方法 - Google Patents
一种水泥基渗透结晶型防水材料及其制备方法 Download PDFInfo
- Publication number
- CN104844079A CN104844079A CN201510156462.7A CN201510156462A CN104844079A CN 104844079 A CN104844079 A CN 104844079A CN 201510156462 A CN201510156462 A CN 201510156462A CN 104844079 A CN104844079 A CN 104844079A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- ether
- latex powder
- waterproofing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水泥基渗透结晶型防水材料，其原料组分及组分如下：水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份，触变剂；2.0份，硅粉：10份，防水剂：1.0份，消泡剂；1.0份，可再分散乳胶粉：5份-15份，纤维素醚：0.5份-1.5份；还公开了其制备方法，原材料按配比通过电子称自动计量，混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。本发明的目的在于提供一种可再分散乳胶粉的还原率高，避免可再分散乳胶粉的粒子过早结合，可以与混凝土反应，产生二次渗透以填充空隙，使防水效果更强的水泥基渗透结晶型防水材料及其制备方法。
Description
技术领域
本发明涉及一种水泥基渗透结晶型防水材料及其制备方法。
背景技术
国标“GB18445（2001）水泥基渗透结晶型防水材料”自2002年3月1日实施以来，推动了该材料的研究发展和工程应用，提高了防水工程的工作效率，降低了防水工程的综合成本；某种程度上，满足了现代建筑物对耐久性的要求。可以说，水泥基渗透结晶型防水材料以其综合优势，赢得各方面人士的青睐，在刚性防水材料、堵漏止水材料系列中，确立了自己重要的地位。
水泥基渗透结晶型防水材料的防水原理是填充密实结构混凝土的孔隙和微裂缝而达到防水目的，所以该防水材料还能延缓结构内钢筋生锈，提高混凝土结构的耐久性能。
但是目前市场的水泥基渗透结晶型防水材料中可再分散乳胶粉的还原率低，可再分散乳胶粉的粒子结合过早，未使用极发生结合，致使无法保证防水效果，对混凝土内的空隙渗透能力较差，防水效果较差，急需加强。
发明内容
针对现有技术存在的不足，本发明的目的在于提供一种可再分散乳胶粉的还原率高，避免可再分散乳胶粉的粒子过早结合，可以与混凝土反应，产生二次渗透以填充空隙，使防水效果更强的水泥基渗透结晶型防水材料及其制备方法。
为实现上述目的，本发明提供了如下技术方案：一种水泥基渗透结晶型防水材料，其原料组分及组分如下：
水泥：400份-500份
石英砂：550份-600份
高效减水剂；1.5份
触变剂；2.0份
硅粉：10份
防水剂：1份
消泡剂；1.0份
可再分散乳胶粉：5份-15份
纤维素醚：0.5份-1.5份。
本发明进一步设置为： 所述可再分散乳胶粉为10.份；
所述纤维素醚为1.0份。
本发明进一步设置为：所述防水剂为高分子材料超低粘度限位素醚。
本发明进一步设置为：所述高分子材料超低粘度限位素醚的组分如下：
普硅水泥 42.5R 28份
高铝水泥 CA-50 10份
70-140目的石英砂 40份
500目的碳酸钙 16.8份
半 水 石 膏 1份
无水石膏 6份
自流平专用乳胶粉 1.5份
纤维素醚 0.07份
聚羧酸减水剂 0.4份
自流平专用消泡剂 0.4份
200目的酒石酸 0.18份
碳酸锂 0.12份
熟 石 灰 2份。
本发明还提供了一种该水泥基渗透结晶型防水材料的制备方法，原材料按配比通过电子称自动计量，混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
本发明的有益效果：高分子材料超低粘度限位素醚可以防止水泥基过多过快系吸收水分并阻止水分的蒸发，以保证水泥基具有足够的水，同时与高效减水剂的配合使用，可以减少对水的敏感性，减少泌水沉底，保证自流平砂浆的流动度；而且由于水泥基成互穿网络结构，可再分散乳胶粉可以加强水泥基内骨料的之间的粘结，可以堵塞水泥基内的空隙，改善水泥基的各项性能，可再分散乳胶粉在水中分散后，可再分散乳胶粉的粒径分布更接近于原来的乳液，以保证可再分散乳胶粉与原来的乳液性质相近；并且可再分散乳胶粉与纤维素醚相结合，可以避免可再分散乳胶粉的粒子二次团聚，使其具有较好的粒子还原性，避免可再分散乳胶粉的粒子在未使用时发生结合；从而达到了本发明的可再分散乳胶粉的还原率高，避免可再分散乳胶粉的粒子过早结合，可以与混凝土反应，产生二次渗透以填充空隙，使防水效果更强的目的。
具体实施方式
实施例一：
一种水泥基渗透结晶型防水材料，其其原料组分及组分如下：
水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份
，触变剂；2.0份，硅粉：10份，高分子材料超低粘度限位素醚：1份，消泡剂；1.0份，可再分散乳胶粉：5份，纤维素醚：0.5。混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
实施例二：
一种水泥基渗透结晶型防水材料，其其原料组分及组分如下：
水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份
，触变剂；2.0份，硅粉：10份，高分子材料超低粘度限位素醚：1份，消泡剂；1.0份，可再分散乳胶粉：10份，纤维素醚：0.5。混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
实施例三：
一种水泥基渗透结晶型防水材料，其其原料组分及组分如下：
水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份
，触变剂；2.0份，硅粉：10份，高分子材料超低粘度限位素醚：1份，消泡剂；1.0份，可再分散乳胶粉：15份，纤维素醚：0.5。混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
实施例四：
一种水泥基渗透结晶型防水材料，其其原料组分及组分如下：
水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份
，触变剂；2.0份，硅粉：10份，高分子材料超低粘度限位素醚：1份，消泡剂；1.0份，可再分散乳胶粉：5份，纤维素醚：1。混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
实施例五：
一种水泥基渗透结晶型防水材料，其其原料组分及组分如下：
水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份
，触变剂；2.0份，硅粉：10份，高分子材料超低粘度限位素醚：1份，消泡剂；1.0份，可再分散乳胶粉：10份，纤维素醚：1。混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
实施例六：
一种水泥基渗透结晶型防水材料，其其原料组分及组分如下：
水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份
，触变剂；2.0份，硅粉：10份，高分子材料超低粘度限位素醚：1份，消泡剂；1.0份，可再分散乳胶粉：15份，纤维素醚：1。混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
实施例七：
一种水泥基渗透结晶型防水材料，其其原料组分及组分如下：
水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份
，触变剂；2.0份，硅粉：10份，高分子材料超低粘度限位素醚：1份，消泡剂；1.0份，可再分散乳胶粉：5份，纤维素醚：1.5。混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
实施例八：
一种水泥基渗透结晶型防水材料，其其原料组分及组分如下：
水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份
，触变剂；2.0份，硅粉：10份，高分子材料超低粘度限位素醚：1份，消泡剂；1.0份，可再分散乳胶粉：10份，纤维素醚：1.5。混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
实施例九：
一种水泥基渗透结晶型防水材料，其其原料组分及组分如下：
水泥：400份-500份，石英砂：550份-600份，高效减水剂；1.5份
，触变剂；2.0份，硅粉：10份，高分子材料超低粘度限位素醚：1份，消泡剂；1.0份，可再分散乳胶粉：15份，纤维素醚：1.5。混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。
。
可再生分散乳胶粉的粒子还原率取整数。
以上所述使本发明的优选实施方式，对于本领域的普通技术人员来说不脱离本发明原理的前提下，还可以做出若干变型和改进，这些也应视为本发明的保护范围。
Claims (5)
1.一种水泥基渗透结晶型防水材料，其特征在于其原料组分如下：
水泥：400份-500份
石英砂：550份-600份
高效减水剂；1.5份
触变剂；2.0份
硅粉：10份
防水剂：1.0份
消泡剂；1.0份
可再分散乳胶粉：5份-15份
纤维素醚：0.5份-1.5份。
2.根据权利要求1所述的水泥基渗透结晶型防水材料，其特征是：所述可再分散乳胶粉为10.份；
所述纤维素醚为1.0份。
3.根据权利要求2所述的水泥基渗透结晶型防水材料，其特征是：所述防水剂为高分子材料超低粘度限位素醚。
4.根据权利要求3所述的水泥基渗透结晶型防水材料，其特征是：所述高分子材料超低粘度限位素醚的组分如下：
普硅水泥 42.5R 28份
高铝水泥 CA-50 10份
70-140目的石英砂 40份
500目的碳酸钙 16.8份
半 水 石 膏 1份
无水石膏 6份
自流平专用乳胶粉 1.5份
纤维素醚 0.07份
聚羧酸减水剂 0.4份
自流平专用消泡剂 0.4份
200目的酒石酸 0.18份
碳酸锂 0.12份
熟 石 灰 2份。
5.一种制备如权利要求1所述的水泥基渗透结晶型防水材料的制备方法，其特征在于：原材料按配比通过电子称自动计量，混合后放入磁力搅拌器上搅拌并于60℃加热25-30分钟，搅拌结束进入成品库，通过自动包装机包装入库。