Summary of the invention
The object of the invention is for the problems referred to above, develop a kind of preparation method of the ceramic mosquito coil plate containing herbal medicine, first various herbal medicine is rationally processed, obtain having sterilization, antibacterial, refresh oneself, the Chinese herbal medicine powder of environmental protection, then herbal medicine is incorporated in ceramic mosquito coil plate, and regulates the various materials composition of ceramic mosquito coil plate, obtain having the ceramic mosquito coil plate of sterilization, antibacterial, performance of refreshing oneself, smell is pure and fresh, health environment-friendly.
A preparation method for ceramic mosquito coil plate containing herbal medicine, this ceramic mosquito coil plate weight is composed as follows:
River sand fine sand 60-100 part; Purple clay 50-80 part; Alumine 30-40 part; Black mud 20-40 part; Unslaked lime 20-30 part; Slaked lime 8-20 part; Silicon powder 5-8 part; Nano aluminium oxide 5-8 part; Clay 5-8 part; Zirconium silicate 1-2 part; Thanomin 1-2 part; Repone K 1-2 part; Sodium carbonate 1-2 part; Chinese herbal medicine powder 1-3 part; Water reducer 1-2 part;
The preparation method of Chinese herbal medicine powder is:
Take Spica Prunellae 8-15 part by weight, garden burnet 8-12 part, dark plum 8-10 part, blue fragrant stone 8-12 part, Siberian Cocklour Fruit 6-9 part, cloves 6-8 part, pomegranate rind 5-10 part, Towel Gourd Stem 1-3 part, tarragon 6-10 part, skunk bush 5-8 part, psyllium 8-15 part, Turkey-galls 8-15 part, cassia bark 20-30 part, chrysanthemum 3-4 part, Triquetrous Tadehagi Herb 3-4 part, aloe 3-4 part, santal 3-4 part, rhizome of cyrtomium 3-4 part, Japanese Honeysuckle 3-4 part, orange peel 3-4 part, first carry out drying, then pulverize, obtain Chinese herbal medicine powder.
The preparation method that should contain the ceramic mosquito coil plate of herbal medicine prepares by the following method:
(1) each raw material is prepared burden according to weight composition, and adopt shredder to grind 2h, stir, obtain batch mixing;
(2) batch mixing is added appropriate water and carry out rolling, and stir;
(3) through pugging and old after, make type at 30Mpa pressure;
(4) at temperature is 25 DEG C, relative humidity is natural curing under the environment of 95%, can obtain the preparation method of the ceramic mosquito coil plate containing herbal medicine.
Beneficial effect of the present invention:
Generally speaking, using herbal medicine as the raw material of ceramic mosquito coil plate, make traditional ceramic mosquito coil plate have sterilization, antibacterial, refresh oneself, the effect of environmental protection.Simultaneously by reasonably allocating raw material, herbal medicine can be mated with traditional raw material, and, herbal medicine also can play reinforced effects for the bonding of each raw material, then the physical and chemical performance of ceramic mosquito coil plate is improved, the ceramic mosquito coil plate ultimate compression strength of the finished product of the application is greater than 23Mpa, and folding strength is greater than 6Mpa, and apparent density is greater than 1023kg/m3.
Embodiment
Below in conjunction with specific embodiment, and comparable data describes in further detail the present invention.Should be understood that these embodiments just in order to demonstrate the invention, but not limit the scope of the invention by any way.
Embodiment 1:
A preparation method for ceramic mosquito coil plate containing herbal medicine, is characterized in that:
This ceramic mosquito coil plate weight is composed as follows:
River sand fine sand 90 parts; Purple clay 70 parts; Alumine 40 parts; Black mud 30 parts; Unslaked lime 25 parts; Slaked lime 10 parts; Silicon powder 7 parts; Nano aluminium oxide 7 parts; Clay 7 parts; Zirconium silicate 2 parts; Thanomin 2 parts; 2 parts, Repone K; 2 parts, sodium carbonate; Chinese herbal medicine powder 3 parts; Water reducer 1 part
The preparation method of Chinese herbal medicine powder is:
Take Spica Prunellae 15 parts by weight, garden burnet 12 parts, dark plum 10 parts, blue 12 parts, fragrant stone, Siberian Cocklour Fruit 9 parts, cloves 8 parts, pomegranate rind 10 parts, Towel Gourd Stem 3 parts, tarragon 10 parts, skunk bush 8 parts, psyllium 8 parts, 8 parts, Turkey-galls, 20 parts, cassia bark, chrysanthemum 3 parts, Triquetrous Tadehagi Herb 3 parts, aloe 3 parts, 3 parts, santal, rhizome of cyrtomium 3 parts, Japanese Honeysuckle 3 parts, orange peel 3 parts, first carry out drying, then pulverize, obtain Chinese herbal medicine powder.
The preparation method that should contain the ceramic mosquito coil plate of herbal medicine prepares by the following method:
(1) each raw material is prepared burden according to weight composition, and adopt shredder to grind 2h, stir, obtain batch mixing;
(2) batch mixing is added appropriate water and carry out rolling, and stir;
(3) through pugging and old after, make type at 30Mpa pressure;
(4) at temperature is 25 DEG C, relative humidity is natural curing under the environment of 95%, can obtain the preparation method of the ceramic mosquito coil plate containing herbal medicine.
Embodiment 2:
A preparation method for ceramic mosquito coil plate containing herbal medicine, is characterized in that:
This ceramic mosquito coil plate weight is composed as follows:
River sand fine sand 80 parts; Purple clay 60 parts; Alumine 40 parts; Black mud 30 parts; Unslaked lime 25 parts; Slaked lime 10 parts; Silicon powder 7 parts; Nano aluminium oxide 7 parts; Clay 7 parts; Zirconium silicate 2 parts; Thanomin 2 parts; 2 parts, Repone K; 2 parts, sodium carbonate; Chinese herbal medicine powder 2 parts; Water reducer 1 part;
The preparation method of Chinese herbal medicine powder is:
Take Spica Prunellae 15 parts by weight, garden burnet 12 parts, dark plum 10 parts, blue 12 parts, fragrant stone, Siberian Cocklour Fruit 9 parts, cloves 8 parts, pomegranate rind 10 parts, Towel Gourd Stem 3 parts, tarragon 10 parts, skunk bush 8 parts, psyllium 8 parts, 8 parts, Turkey-galls, 20 parts, cassia bark, chrysanthemum 4 parts, Triquetrous Tadehagi Herb 4 parts, aloe 4 parts, 4 parts, santal, rhizome of cyrtomium 4 parts, Japanese Honeysuckle 4 parts, orange peel 3 parts, first carry out drying, then pulverize, obtain Chinese herbal medicine powder.
The preparation method that should contain the ceramic mosquito coil plate of herbal medicine prepares by the following method:
(1) each raw material is prepared burden according to weight composition, and adopt shredder to grind 2h, stir, obtain batch mixing;
(2) batch mixing is added appropriate water and carry out rolling, and stir;
(3) through pugging and old after, make type at 30Mpa pressure;
(4) at temperature is 25 DEG C, relative humidity is natural curing under the environment of 95%, can obtain the preparation method of the ceramic mosquito coil plate containing herbal medicine.
Embodiment 3:
A preparation method for ceramic mosquito coil plate containing herbal medicine, is characterized in that:
This ceramic mosquito coil plate weight is composed as follows:
River sand fine sand 90 parts; Purple clay 70 parts; Alumine 40 parts; Black mud 30 parts; Unslaked lime 25 parts; Slaked lime 10 parts; Silicon powder 7 parts; Nano aluminium oxide 7 parts; Clay 7 parts; Zirconium silicate 2 parts; Thanomin 1 part; 1 part, Repone K; 1 part, sodium carbonate; Chinese herbal medicine powder 1 part; Water reducer 1 part;
The preparation method of Chinese herbal medicine powder is:
Take Spica Prunellae 12 parts by weight, garden burnet 10 parts, dark plum 10 parts, blue 12 parts, fragrant stone, Siberian Cocklour Fruit 9 parts, cloves 8 parts, pomegranate rind 10 parts, Towel Gourd Stem 3 parts, tarragon 10 parts, skunk bush 8 parts, psyllium 8 parts, 8 parts, Turkey-galls, 20 parts, cassia bark, chrysanthemum 4 parts, Triquetrous Tadehagi Herb 3 parts, aloe 3 parts, 3 parts, santal, rhizome of cyrtomium 3 parts, Japanese Honeysuckle 3 parts, orange peel 3 parts, first carry out drying, then pulverize, obtain Chinese herbal medicine powder.
The preparation method that should contain the ceramic mosquito coil plate of herbal medicine prepares by the following method:
(1) each raw material is prepared burden according to weight composition, and adopt shredder to grind 2h, stir, obtain batch mixing;
(2) batch mixing is added appropriate water and carry out rolling, and stir;
(3) through pugging and old after, make type at 30Mpa pressure;
(4) at temperature is 25 DEG C, relative humidity is natural curing under the environment of 95%, can obtain the preparation method of the ceramic mosquito coil plate containing herbal medicine.
Embodiment 4:
A preparation method for ceramic mosquito coil plate containing herbal medicine, is characterized in that:
This ceramic mosquito coil plate weight is composed as follows:
River sand fine sand 80 parts; Purple clay 60 parts; Alumine 40 parts; Black mud 30 parts; Unslaked lime 25 parts; Slaked lime 10 parts; Silicon powder 7 parts; Nano aluminium oxide 7 parts; Clay 7 parts; Zirconium silicate 2 parts; Thanomin 1 part; 1 part, Repone K; 1 part, sodium carbonate; Chinese herbal medicine powder 3 parts; Water reducer 1 part;
The preparation method of Chinese herbal medicine powder is:
Take Spica Prunellae 10 parts by weight, garden burnet 10 parts, dark plum 10 parts, blue 12 parts, fragrant stone, Siberian Cocklour Fruit 9 parts, cloves 8 parts, pomegranate rind 10 parts, Towel Gourd Stem 3 parts, tarragon 10 parts, skunk bush 8 parts, psyllium 8 parts, 8 parts, Turkey-galls, 20 parts, cassia bark, chrysanthemum 3 parts, Triquetrous Tadehagi Herb 3 parts, aloe 3 parts, 3 parts, santal, rhizome of cyrtomium 3 parts, Japanese Honeysuckle 3 parts, orange peel 3 parts, first carry out drying, then pulverize, obtain Chinese herbal medicine powder.
The preparation method that should contain the ceramic mosquito coil plate of herbal medicine prepares by the following method:
(1) each raw material is prepared burden according to weight composition, and adopt shredder to grind 2h, stir, obtain batch mixing;
(2) batch mixing is added appropriate water and carry out rolling, and stir;
(3) through pugging and old after, make type at 30Mpa pressure;
(4) at temperature is 25 DEG C, relative humidity is natural curing under the environment of 95%, can obtain the preparation method of the ceramic mosquito coil plate containing herbal medicine.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should embodiment be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.
In addition, be to be understood that, although this specification sheets is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of specification sheets is only for clarity sake, those skilled in the art should by specification sheets integrally, and the technical scheme in each embodiment also through appropriately combined, can form other embodiments that it will be appreciated by those skilled in the art that.