CN104827536A - 一种疏水型磁化木的制备方法 - Google Patents
一种疏水型磁化木的制备方法 Download PDFInfo
- Publication number
- CN104827536A CN104827536A CN201510250952.3A CN201510250952A CN104827536A CN 104827536 A CN104827536 A CN 104827536A CN 201510250952 A CN201510250952 A CN 201510250952A CN 104827536 A CN104827536 A CN 104827536A
- Authority
- CN
- China
- Prior art keywords
- wood
- magnetization
- hydrophobic
- preparation
- hydrophobic type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种疏水型磁化木的制备方法,本发明通过低温水热法制备磁化木,并通过FAS-17疏水改性制备了疏水型磁化木,制备工艺简单,原料来源广泛,成本低廉,能耗低。得到的疏水型磁化木在微波吸收、电磁屏蔽、室内外装饰材料、重金属离子吸附等领域具有广泛应用。
Description
技术领域
本发明涉及一种疏水型磁化木的制备方法。
背景技术
磁性NiFe2O4纳米粒子是一种性能优异的磁性纳米粒子,其具有较高的饱和磁化强度和较小的娇顽磁力,广泛的运用于磁记录材料、磁流体、催化剂和医药领域。通过水热法将无机纳米材料高效负载于木材表面来制备功能性无机纳米/木材新型无机-有机物复合材料,这不仅继承了木材天然的物理、化学、力学特性,而且因为无机纳米粒子的小尺寸效应和表面效应衍生出众多新的特殊性能,对木材的高附加值利用和功能化拓展具有重要的研究意义,为制备磁化木复合材料提供了一种新的方法和研究思路。
同时,由于木材是一种亲水性物质,其表面存在大量的羟基,使木材极易产生吸水膨胀、翘曲变形等情况,这极大地限制了木材的应用范围。通过对磁化木进行了疏水处理,在保证磁化木原有磁性不变的基础上在其表面构建了疏水膜层,实现了磁化木的由亲水性到疏水性的转变,从而制备的具有疏水性和磁性的双功能木材,极大的拓展了木材的使用范围。
发明内容
本发明所要解决的技术问题是提供一种疏水型磁化木的制备方法,该方法工艺简单、成本低廉、反应条件温和。
本发明解决其技术问题所采用的技术方案是:
一种疏水型磁化木的制备方法,包括如下步骤:
(1)将木材浸入含有Fe3+和Ni2+的混合盐溶液,在低温60-120℃水热条件下反应2~6h,其中,Fe3+和Ni2+在混合溶液中的摩尔比1∶1~6∶1;
(2)向反应容器内加入适量的NH3·H2O后使其混合溶液的pH值为9-12,反应温度为室温,反应时间为3~12h;
(3)将经步骤(2)处理后的木材于20~110℃条件下真空干燥1~48h,即可制得磁化木;
(4)将步骤(3)制得的磁化木在室温下浸入1H,1H,2H,2H-全氟癸基三甲氧基硅烷(FAS-17)乙醇溶液中磁力搅拌1-100h;
(5)将经过步骤(4)FAS-17改性的磁化木于20~110℃条件下真空干燥1~48h,即制备得到疏水型磁化木。
上述步骤(1)中Fe3+的来源是硝酸铁、氯化铁、硫酸铁中任何一种形式的三价铁盐,NI2+的来源是硝酸镍、氯化镍、硫酸镍中的任何一种含有镍离子的盐。
上述步骤(4)中加入1H,1H,2H,2H-全氟癸基三甲氧基硅烷(FAS-17)的体积为1.0×10-3~1×102mL,加入乙醇体积为1~200mL。
本发明的有益效果是:本发明利用低温水热法制备磁化木,并通过FAS-17疏水改性制备了疏水型磁化木,制备工艺简单,原料来源广泛,成本低廉,能耗低。得到的疏水型磁化木在微波吸收、电磁屏蔽、室内外装饰材料、重金属离子吸附等领域具有广泛应用。
附图说明
图1是实施例1制得的疏水型磁化木的宏观图;
图2是实施例1制得的疏水型磁化木可被磁铁吸起来的宏观图;
图3是实施例1制得的疏水型磁化木表面疏水的宏观图。
具体实施方式
本发明技术方案不局限于以下所列举具体实施方式,还包括各具体实施方式间的任意组合。
一种疏水型磁化木的制备方法,包括如下步骤:
将木浸入含有Fe3+和Ni2+的混合盐溶液,在低温水热条件下,其中,在低温60-120℃水热条件下,其中,Fe3+和Ni2+在混合溶液中的摩尔比1∶1~6∶1,时间为2~6h;
向反应容器内加入适量的NH3·H2O后使其混合溶液的pH值为9-12;
将将经上述处理后的木材在20~110℃条件下真空干燥1~48h后即可制得磁化木;
将制得的磁化木在室温下浸入1H,1H,2H,2H-全氟癸基三甲氧基硅烷(FAS-17)乙醇溶液中不停搅拌,其中,加入FAS-17体积为1.0×10-3~1×102mL,加入甲醇醇体积为1~200mL,处理时间为1~100h;
将经过FAS-17改性的磁化木在20~110℃条件下真空干燥1~48h后即制备得到了疏水型磁化木。
本实施例制得的疏水型磁化木产品见图1,疏水型磁化木被磁铁吸起来的宏观图见图2,疏水型磁化木表面疏水的宏观图见图3。
上述所述的实施例,对本发明的目的、技术方案和有益效果进行了进一步详细说明,所应理解的是,凡在本发明的精神和原则之内所做的任何修改、等同替换。改进等,均应包括在本发明的保护范围之内。
Claims (3)
1.一种疏水型磁化木的制备方法,其特征在于包括如下步骤:
(1)将木材浸入含有Fe3+和Ni2+的混合盐溶液,在低温60-120℃水热条件下反应2~6h,其中,Fe3+和Ni2+在混合溶液中的摩尔比1∶1~6∶1;
(2)向反应容器内加入适量的NH3·H2O后使其混合溶液的pH值为9-12,反应温度为室温,反应时间为3~12h;
(3)将经步骤(2)处理后的木材于20~110℃条件下真空干燥1~48h,即可制得磁化木;
(4)将步骤(3)制得的磁化木在室温下浸入1H,1H,2H,2H-全氟癸基三甲氧基硅烷乙醇溶液中磁力搅拌1-100h;
(5)将经过步骤(4)改性的磁化木于20~110℃条件下真空干燥1~48h,即制备得到疏水型磁化木。
2.根据权利要求1所述的一种疏水型磁化木的制备方法,其特征在于:所述步骤(1)中Fe3+的来源是硝酸铁、氯化铁、硫酸铁中任何一种形式的三价铁盐,NI2+的来源是硝酸镍、氯化镍、硫酸镍中的任何一种含有镍离子的盐。
3.根据权利要求1所述的一种疏水型磁化木的制备方法,其特征在于:步骤(4)中加入1H,1H,2H,2H-全氟癸基三甲氧基硅烷的体积为1.0×10-3~1×102mL,加入乙醇体积为1~200mL。