CN104827245A - 一种轴承套圈的锻造工艺 - Google Patents

一种轴承套圈的锻造工艺 Download PDF

Info

Publication number
CN104827245A
CN104827245A CN201510055336.2A CN201510055336A CN104827245A CN 104827245 A CN104827245 A CN 104827245A CN 201510055336 A CN201510055336 A CN 201510055336A CN 104827245 A CN104827245 A CN 104827245A
Authority
CN
China
Prior art keywords
ingot
machined
dec
machined ingot
heated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510055336.2A
Other languages
English (en)
Other versions
CN104827245B (zh
Inventor
葛艳明
黄�俊
彭振
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Jinyuan Forging Co Ltd
Original Assignee
Jiangsu Jinyuan Forging Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Jinyuan Forging Co Ltd filed Critical Jiangsu Jinyuan Forging Co Ltd
Priority to CN201510055336.2A priority Critical patent/CN104827245B/zh
Publication of CN104827245A publication Critical patent/CN104827245A/zh
Application granted granted Critical
Publication of CN104827245B publication Critical patent/CN104827245B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种轴承套圈的锻造工艺，该工艺包括如下步骤：1)第一火将钢锭采用中频感应加热炉加热温度至1200℃，压钳口，倒棱，错水口；2)第二火再次加热，镦粗，拔长；3)第三火再次加热，镦粗，旋转压平，冲孔，扩孔；4)第四火再次加热，模圈中镦粗至工艺尺寸，出模，扩孔至工艺尺寸，控制总锻造比＞5；5)车削沟槽，在闭成型扩孔机上冷辗扩整径，滚道、倒角一次成型，修整，软磨两端面；6)热处理：预热800℃～850℃，探伤检查后，在小于450℃时装炉预热至600~650℃保温后，再放入950~1000℃的炉子内进行快速加热至1140～1200℃，采用水淬后立即550～600℃回火，在炉中冷却至400~450℃后，再出炉空冷。该工艺消除金属内在缺陷，延长了轴承的使用寿命。

Description

一种轴承套圈的锻造工艺
技术领域
本发明属于锻造技术领域，尤其涉及一种轴承套圈的锻造工艺。
背景技术
轴承套圈是具有一个或几个滚道的滚动轴承的重要环形零件，其重量一般约占轴承总重量的60~70％，套圈毛坯有锻件、冷挤件、温挤件、管料和棒料等，其中锻件约占套圈毛坯总数的85%左右。套圈的内部质量包括材料的致密度、金属纤维流线分布、晶粒度和形变热处理等，对轴承寿命有较大的影响，所以套圈毛坯质量的好坏，生产率的高低，将对轴承产品的质量、性能、寿命及企业的经济效益产生重要的影响。轴承套圈 属于薄壁环类锻件，在锻造过程中容易出现壁厚不均、折叠、椭圆等问题，从而造成轴承精度不够，影响轴承的使用寿命。
发明内容
本发明的目的为了解决上述技术问题，提供一种轴承套圈的锻造工艺，该工艺可以消除金属内在缺陷，改善金属组织，使金属流线分布合理，金属紧密度好，延长了轴承的使用寿命；提高锻件的几何精度和尺寸精度，消除壁厚差，并使锻件形状最大限度地接近套圈的成品形状，因而可以降低锻件的留量和公差，提高材料利用率，减小机械加工工作量，降低了成本。其技术方案如下：一种轴承套圈 的锻造工艺，其特征在于，所述轴承套圈 以重量百分比计由下列组份组成： C ：0.17～0.23 Si：0.17～0.37 Mn：0.30～0.60 S ：≤0.035 P ：≤0.035 Cr：1.25～1.65 Ni：3.25～3.65，余量为Fe；所述的锻造工艺包括如下步骤：1)、第一火将具有上述组成的钢锭采用中频感应加热炉󰀃加热温度至1200℃，压钳口，倒棱，错水口；2)、第二火对1)步获得的坯材进行再次加热，加热至1120~1150℃，镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1050~1100℃，镦粗，旋转压平，冲孔，扩孔；4)、第四火对3)步获得的坯材进行再次加热，加热至1020~1050℃，模圈中镦粗至工艺尺寸，出模，扩孔至工艺尺寸，控制总锻造比＞5，装炉升温到795℃，保温7h，快速冷却到720℃，保温5h，以20℃/h冷却速度降至650℃出炉空冷；5)、车削沟槽，在闭成型扩孔机上冷辗扩整径，滚道、倒角一次成型，修整，软磨两端面；6)、热处理：预热800℃～850℃，探伤检查后，在小于450℃时装炉预热至600~650℃保温后，再放入950~1000℃的炉子内进行快速加热至1140～1200℃，采用水淬后立即550～600℃回火，在炉中冷却至400~450℃后，再出炉空冷。
与现有技术相比，本发明的优点是：该工艺可以消除金属内在缺陷，改善金属组织，使金属流线分布合理，金属紧密度好，延长了轴承的使用寿命；提高锻件的几何精度和尺寸精度，消除壁厚差，并使锻件形状最大限度地接近套圈的成品形状，因而可以降低锻件的留量和公差，提高材料利用率，减小机械加工工作量，降低了轴承套圈的加工成本。
具体实施方式
实施例一
一种轴承套圈的锻造工艺，其特征在于，所述轴承套圈以重量百分比计由下列组份组成： C ：0.17 Si：0.17 Mn：0.30 S ： 0.015 P ： 0.015 Cr：1.25 Ni：3.25，余量为Fe；所述的锻造工艺包括如下步骤：1)、第一火将具有上述组成的钢锭采用中频感应加热炉󰀃加热温度至1200℃，压钳口，倒棱，错水口；2)、第二火对1)步获得的坯材进行再次加热，加热至1120℃，镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1050℃，镦粗，旋转压平，冲孔，扩孔；4)、第四火对3)步获得的坯材进行再次加热，加热至1020℃，模圈中镦粗至工艺尺寸，出模，扩孔至工艺尺寸，控制总锻造比5.1，装炉升温到795℃，保温7h，快速冷却到720℃，保温5h，以20℃/h冷却速度降至650℃出炉空冷；5)、车削沟槽，在闭成型扩孔机上冷辗扩整径，滚道、倒角一次成型，修整，软磨两端面；6)、热处理：预热800℃℃，探伤检查后，在小于450℃时装炉预热至600℃保温后，再放入950℃的炉子内进行快速加热至1140℃，采用水淬后立即550℃回火，在炉中冷却至400℃后，再出炉空冷。
实施例二
一种轴承套圈的锻造工艺，其特征在于，所述轴承套圈以重量百分比计由下列组份组成： C ：0.19 Si：0.27 Mn：0.50 S ： 0.025 P ： 0.025 Cr：1.45 Ni：3.50，余量为Fe；所述的锻造工艺包括如下步骤：1)、第一火将具有上述组成的钢锭采用中频感应加热炉󰀃加热温度至1200℃，压钳口，倒棱，错水口；2)、第二火对1)步获得的坯材进行再次加热，加热至1130℃，镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1080℃，镦粗，旋转压平，冲孔，扩孔；4)、第四火对3)步获得的坯材进行再次加热，加热至1030℃，模圈中镦粗至工艺尺寸，出模，扩孔至工艺尺寸，控制总锻造比5.2，装炉升温到795℃，保温7h，快速冷却到720℃，保温5h，以20℃/h冷却速度降至650℃出炉空冷；5)、车削沟槽，在闭成型扩孔机上冷辗扩整径，滚道、倒角一次成型，修整，软磨两端面；6)、热处理：预热820℃，探伤检查后，在小于450℃时装炉预热至620℃保温后，再放入980℃的炉子内进行快速加热至1180℃，采用水淬后立即580℃回火，在炉中冷却至420℃后，再出炉空冷。
实施例三
一种轴承套圈的锻造工艺，其特征在于，所述轴承套圈以重量百分比计由下列组份组成： C ： 0.23 Si： 0.37 Mn： 0.60 S ： 0.035 P ： 0.035 Cr： 1.65 Ni： 3.65，余量为Fe；所述的锻造工艺包括如下步骤：1)、第一火将具有上述组成的钢锭采用中频感应加热炉󰀃加热温度至1200℃，压钳口，倒棱，错水口；2)、第二火对1)步获得的坯材进行再次加热，加热至1150℃，镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1100℃，镦粗，旋转压平，冲孔，扩孔；4)、第四火对3)步获得的坯材进行再次加热，加热至1050℃，模圈中镦粗至工艺尺寸，出模，扩孔至工艺尺寸，控制总锻造比5.5，装炉升温到795℃，保温7h，快速冷却到720℃，保温5h，以20℃/h冷却速度降至650℃出炉空冷；5)、车削沟槽，在闭成型扩孔机上冷辗扩整径，滚道、倒角一次成型，修整，软磨两端面；6)、热处理：预热850℃，探伤检查后，在小于450℃时装炉预热至600~650度保温后，再放入1000℃的炉子内进行快速加热至1200℃，采用水淬后立即600℃回火，在炉中冷却至450℃后，再出炉空冷。

Claims (1)

1.一种轴承套圈的锻造工艺，其特征在于，所述轴承套圈以重量百分比计由下列组份组成： C ：0.17～0.23 Si：0.17～0.37 Mn：0.30～0.60 S ：≤0.035 P ：≤0.035 Cr：1.25～1.65 Ni：3.25～3.65，余量为Fe；所述的锻造工艺包括如下步骤：1)、第一火将具有上述组成的钢锭采用中频感应加热炉󰀃加热温度至1200℃，压钳口，倒棱，错水口；2)、第二火对1)步获得的坯材进行再次加热，加热至1120~1150℃，镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1050~1100℃，镦粗，旋转压平，冲孔，扩孔；4)、第四火对3)步获得的坯材进行再次加热，加热至1020~1050℃，模圈中镦粗至工艺尺寸，出模，扩孔至工艺尺寸，控制总锻造比＞5，装炉升温到795℃，保温7h，快速冷却到720℃，保温5h，以20℃/h冷却速度降至650℃出炉空冷；5)、车削沟槽，在闭成型扩孔机上冷辗扩整径，滚道、倒角一次成型，修整，软磨两端面；6)、热处理：预热800℃～850℃，探伤检查后，在小于450℃时装炉预热至600~650℃保温后，再放入950~1000℃的炉子内进行快速加热至1140～1200℃，采用水淬后立即550～600℃回火，在炉中冷却至400~450℃后，再出炉空冷。
CN201510055336.2A 2015-02-03 2015-02-03 一种轴承套圈的锻造工艺 Active CN104827245B (zh)