CN104805525A - High-performance fishing line - Google Patents
High-performance fishing line Download PDFInfo
- Publication number
- CN104805525A CN104805525A CN201510133792.4A CN201510133792A CN104805525A CN 104805525 A CN104805525 A CN 104805525A CN 201510133792 A CN201510133792 A CN 201510133792A CN 104805525 A CN104805525 A CN 104805525A
- Authority
- CN
- China
- Prior art keywords
- extruder
- fishing line
- sections
- nylon
- ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-performance fishing line. A preparation method of the fishing line comprises steps as follows: (1) drying of nylon; (2) drying of additives; (3) mixing and granulation; (4) extrusion molding; (5) cooling molding. During processing, multiple additives are added to the nylon raw material, the processability of the nylon is improved, the wear resistance, the corrosion resistance and the tensile property of the fishing line are improved, and the processing efficiency is improved.
Description
Technical field
The invention belongs to fishing gear field, be specifically related to a kind of high-performance fishing line.
Background technology
Fishing line, is used to the silk thread coupled together by fishing tackle accessory, is mainly used for connecting fishing rod and fish hook.The fishing line in past, be mostly that the natural fabrics such as cotton, fiber crops, silk are made, intensity be not high, transparency is bad, pliability and ABRASION RESISTANCE inadequate.Modern fishing line mainly nylon is made, and improves a lot in intensity, transparency and abrasion resistance etc.Because nylon-type fishing line transparency is high, flexibility good, more wear-resisting, make nylon fishing line become the main force in fishing line market, occupy the share in fishing line market more than 80%.But in fishing line production process, often use extruder for shaping, but due to the water sorption of nylon, cause and produce bubble in process of production, the fishing line intensity made is uneven, affects product quality.
Summary of the invention
The object of this invention is to provide a kind of high-performance fishing line, improve the uniformity of fishing line, also improve the ABRASION RESISTANCE of fishing line, also improve fishing line yield rate.
The present invention is achieved through the following technical solutions:
A kind of high-performance fishing line, uses following steps preparation: (1), by nylon 6 dry 20min under 105 DEG C of vacuum conditions; (2), by alum, chlorosulfonated polyethylene, nano titanium oxide, precipitated calcium carbonate drying; (3), nylon 6, neopelex, chlorosulfonated polyethylene, nano phase ag_2 o, precipitated calcium carbonate, Nano-sized Alumina Powder are mixed by weight the ratio of 85:0.8:3.2:2.5:1.2:1.7, use single screw extrusion machine is extruded, granulation, extruder draw ratio 30:1, extruder adopts 4 sections of mode of heatings, and 4 sections of temperature are respectively 240 DEG C, 240 DEG C, 243 DEG C, 245 DEG C; (4), raw material good for step (3) granulation is used the extruder for shaping that draw ratio is 25:1, extruder end is provided with spinning dies, extruder adopts 5 sections of mode of heatings, extruder 5 sections of temperature are respectively 237 DEG C, 239 DEG C, 240 DEG C, 242 DEG C, 244 DEG C, mold temperature is 109 DEG C, and screw rod and machine barrel gap are 0.18mm; (5), after extrusion molding, at 110 DEG C, draw stretching 10s in cooling fluid, TENSILE STRENGTH is 87.5kg/mm
2, cooling fluid is turpentine oil, carbon tetrachloride, tetrabutyl tribromide ammonium are mixed by weight the ratio of 60:50:0.2, has processed rear cooling winding.
Beneficial effect of the present invention: the present invention is adding man-hour, multiple auxiliary agent is added in nylon raw material, by the proportions of individual middle auxiliary agent and the synergy of each raw material, the performance of nylon fishing line is promoted greatly, improve the processing characteristics of nylon, improve its ABRASION RESISTANCE, antiseptic property and tensile property, add the elasticity that calcium carbonate and nano aluminium oxide can reduce fishing line, and adopt 2 step extrusion methods, each raw material is fully mixed, extrude at a higher temperature, extrusion efficiency is high, and the fishing line even thickness extruded, quality is good, and do not produce bubble, the yield rate of fishing line processing improves more than 20%, after extrusion molding, in cooling fluid stretch after can make fishing line intensity evenly, and process can prevent fishing line fragility from increasing in cooling fluid, affect fishing line and use, the inventive method process diameter 0.1mm nylon monofilament TENSILE STRENGTH can promote more than 35%.
Detailed description of the invention
A kind of high-performance fishing line, uses following methods preparation: (1), by nylon 6 dry 20min under 105 DEG C of vacuum conditions; (2), by alum, chlorosulfonated polyethylene, nano titanium oxide, precipitated calcium carbonate drying; (3), nylon 6, neopelex, chlorosulfonated polyethylene, nano phase ag_2 o, precipitated calcium carbonate, Nano-sized Alumina Powder are mixed by weight the ratio of 85:0.8:3.2:2.5:1.2:1.7, use single screw extrusion machine is extruded, granulation, extruder draw ratio 30:1, extruder adopts 4 sections of mode of heatings, and 4 sections of temperature are respectively 240 DEG C, 240 DEG C, 243 DEG C, 245 DEG C; (4), raw material good for step (3) granulation is used the extruder for shaping that draw ratio is 25:1, extruder end is provided with spinning dies, extruder adopts 5 sections of mode of heatings, extruder 5 sections of temperature are respectively 237 DEG C, 239 DEG C, 240 DEG C, 242 DEG C, 244 DEG C, mold temperature is 109 DEG C, and screw rod and machine barrel gap are 0.18mm; (5), after extrusion molding, at 110 DEG C, draw stretching 10s in cooling fluid, TENSILE STRENGTH is 87.5kg/mm
2, cooling fluid is turpentine oil, carbon tetrachloride, tetrabutyl tribromide ammonium are mixed by weight the ratio of 60:50:0.2, has processed rear cooling winding.
Claims (1)
1. a high-performance fishing line, is characterized in that, uses following steps preparation: (1), by nylon 6 dry 20min under 105 DEG C of vacuum conditions; (2), by alum, chlorosulfonated polyethylene, nano titanium oxide, precipitated calcium carbonate drying; (3), nylon 6, neopelex, chlorosulfonated polyethylene, nano phase ag_2 o, precipitated calcium carbonate, Nano-sized Alumina Powder are mixed by weight the ratio of 85:0.8:3.2:2.5:1.2:1.7, use single screw extrusion machine is extruded, granulation, extruder draw ratio 30:1, extruder adopts 4 sections of mode of heatings, and 4 sections of temperature are respectively 240 DEG C, 240 DEG C, 243 DEG C, 245 DEG C; (4), raw material good for step (3) granulation is used the extruder for shaping that draw ratio is 25:1, extruder end is provided with spinning dies, extruder adopts 5 sections of mode of heatings, extruder 5 sections of temperature are respectively 237 DEG C, 239 DEG C, 240 DEG C, 242 DEG C, 244 DEG C, mold temperature is 109 DEG C, and screw rod and machine barrel gap are 0.18mm; (5), after extrusion molding, at 110 DEG C, draw stretching 10s in cooling fluid, TENSILE STRENGTH is 87.5kg/mm
2, cooling fluid is turpentine oil, carbon tetrachloride, tetrabutyl tribromide ammonium are mixed by weight the ratio of 60:50:0.2, has processed rear cooling winding.