CN104789156A - Novel paperboard adhesive and preparation method thereof - Google Patents
Novel paperboard adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN104789156A CN104789156A CN201510232856.6A CN201510232856A CN104789156A CN 104789156 A CN104789156 A CN 104789156A CN 201510232856 A CN201510232856 A CN 201510232856A CN 104789156 A CN104789156 A CN 104789156A
- Authority
- CN
- China
- Prior art keywords
- tackiness agent
- water
- tapioca
- flour
- borax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a novel paperboard adhesive and a preparation method thereof. The adhesive is composed of the following components in percentage by mass: 75-85% of water, 13-21% of cassava starch, 0.2-1.0% of sodium hydroxide, 0.7-2.0% of reinforcer and 0.2-1.0% of borax. The adhesive has the advantages of high adhesive capacity, favorable compression resistance, favorable moisture resistance and high drying speed, and can enhance the quality of the bonded paperboard and improve the production efficiency. The preparation method of the adhesive is scientific and reasonable, and fully considers the property characteristics of the components. Reasonable steps and processes are adopted to obtain the adhesive with excellent properties.
Description
Technical field
The invention belongs to paperboard bonding agent and preparation method thereof technical field.
Background technology
Tackiness agent is a kind of requisite material of production enterprise, and existing paperboard bonding agent viscosity is poor, resistance to compression, moisture resistance poor-performing, and bonding is longer for time of drying, is difficult to meet Production requirement.
Summary of the invention
The object of the invention is to solve the deficiency of prior art, provide that a kind of degree of adhesion is strong, resistance to compression moisture resistance and drying paperboard bonding agent fast.The present invention also provides the preparation method of this tackiness agent.
Object of the present invention is achieved through the following technical solutions.
A kind of Novel paperboard tackiness agent, this tackiness agent is mixed formed by water, tapioca (flour), sodium hydroxide, toughener, borax, and the mass ratio of each component is: water 75 ~ 85%, tapioca (flour) 13 ~ 21%, sodium hydroxide 0.2 ~ 1.0%, toughener 0.7 ~ 2.0%, borax 0.2 ~ 1.0%.
The preferred mass ratio of each component of tackiness agent is: water 78 ~ 82%, tapioca (flour) 16 ~ 20.5%, sodium hydroxide 0.3 ~ 0.5%, toughener 0.9 ~ 1.2%, borax 0.3 ~ 0.5%.The mass ratio of each component of tackiness agent is specifically as follows: water 80%, tapioca (flour) 18%, sodium hydroxide 0.5%, toughener 1%, borax 0.5%.The mass ratio of each component of tackiness agent also can be specifically: water 82%, tapioca (flour) 16%, sodium hydroxide 0.4%, toughener 1.2%, borax 0.4%.The mass ratio of each component of tackiness agent can also be specifically: water 78%, tapioca (flour) 20.5%, sodium hydroxide 0.3%, toughener 0.9%, borax 0.3%.Described toughener is epoxy resin or its analogue.
The preparation method of a kind of Novel paperboard tackiness agent of the present invention, includes following steps:
A. in the first a mixing bowl, add water, first add 1/7th of tapioca (flour) total amount, stir;
B. in the first a mixing bowl, add sodium hydroxide, stir, make ripe glue;
C. in the second a mixing bowl, inject water, add toughener, then add the tapioca (flour) of 6/7ths remaining parts, be uniformly mixed, make rubber;
D. the ripe glue in the first a mixing bowl is injected in the second a mixing bowl, stir 15-20 minute;
E. the modulation of dilute with water borax is finally injected and the borax water that obtains.
Add described in above-mentioned steps a after in the water of 1 to the first/7th a mixing bowls of tapioca (flour) total amount, stir 10-15 minute, make it mix.Toughener described in the inventive method is epoxy resin or its analogue.
Paperboard bonding agent degree of adhesion of the present invention is strong, and resistance to compression, moisture resistance performance are good, and fast drying, can improve the quality of bonded cardboard, enhance productivity.Preparation method of the present invention is scientific and reasonable, has taken into full account the performance characteristics of each component, has taken reasonable steps and method, the tackiness agent of excellent.
Embodiment
Embodiment 1: a kind of Novel paperboard tackiness agent, this tackiness agent is mixed formed by water, tapioca (flour), sodium hydroxide, toughener, borax, and the mass ratio of each component is: water 84%, tapioca (flour) 13%, sodium hydroxide 1%, toughener 1.8%, borax 0.2%.Toughener available epoxy or its analogue.The present embodiment adopts epoxy resin.
Preparation method is as follows:
A. in the first a mixing bowl, add water, first add 1/7th of tapioca (flour) total amount, stir 10-15 minute, make it mix;
B. in the first a mixing bowl, add sodium hydroxide, stir, make ripe glue;
C. in the second a mixing bowl, inject water, add toughener, then add the tapioca (flour) of 6/7ths remaining parts, be uniformly mixed, make rubber;
D. the ripe glue in the first a mixing bowl is injected in the second a mixing bowl, stir 15-20 minute;
E. the modulation of dilute with water borax is finally injected and the borax water that obtains.
Embodiment 2: a kind of Novel paperboard tackiness agent, this tackiness agent is mixed formed by water, tapioca (flour), sodium hydroxide, epoxy resin, borax, and the mass ratio of each component is: water 81%, tapioca (flour) 17%, sodium hydroxide 0.5%, epoxy resin 1%, borax 0.5%.The preparation method of tackiness agent is with embodiment 1.
Embodiment 3: a kind of Novel paperboard tackiness agent, the component of this tackiness agent and mass ratio are: water 80%, tapioca (flour) 18%, sodium hydroxide 0.5%, toughener 1%, borax 0.5%.The preparation method of tackiness agent is with embodiment 1.
Embodiment 4: a kind of Novel paperboard tackiness agent, the component of this tackiness agent and mass ratio are: water 82%, tapioca (flour) 16%, sodium hydroxide 0.4%, toughener 1.2%, borax 0.4%.The preparation method of tackiness agent is with embodiment 1.
Embodiment 5: a kind of Novel paperboard tackiness agent, the component of this tackiness agent and mass ratio are: water 78%, tapioca (flour) 20.5%, sodium hydroxide 0.3%, toughener 0.9%, borax 0.3%.The preparation method of tackiness agent is with embodiment 1.
Embodiment 6: a kind of Novel paperboard tackiness agent, the component of this tackiness agent and mass ratio are: water 75%, tapioca (flour) 21%, sodium hydroxide 1%, toughener 2%, borax 1%.The preparation method of tackiness agent is with embodiment 1.
Embodiment 7: a kind of Novel paperboard tackiness agent, the component of this tackiness agent and mass ratio are: water 80%, tapioca (flour) 18.6%, sodium hydroxide 0.2%, toughener 1%, borax 0.2%.The preparation method of tackiness agent is with embodiment 1.
Embodiment 8: a kind of Novel paperboard tackiness agent, the component of this tackiness agent and mass ratio are: water 81%, tapioca (flour) 17.2%, sodium hydroxide 0.5%, toughener 0.8%, borax 0.5%.The preparation method of tackiness agent is with embodiment 1.
Claims (9)
1. a Novel paperboard tackiness agent, it is characterized in that, this tackiness agent is mixed formed by water, tapioca (flour), sodium hydroxide, toughener, borax, the mass ratio of each component is: water 75 ~ 85%, tapioca (flour) 13 ~ 21%, sodium hydroxide 0.2 ~ 1.0%, toughener 0.7 ~ 2.0%, borax 0.2 ~ 1.0%.
2. a kind of Novel paperboard tackiness agent according to claim 1, it is characterized in that, the preferred mass ratio of each component of this tackiness agent is: water 78 ~ 82%, tapioca (flour) 16 ~ 20.5%, sodium hydroxide 0.3 ~ 0.5%, toughener 0.9 ~ 1.2%, borax 0.3 ~ 0.5%.
3. a kind of Novel paperboard tackiness agent according to claim 2, is characterized in that, the mass ratio of each component of this tackiness agent is: water 80%, tapioca (flour) 18%, sodium hydroxide 0.5%, toughener 1%, borax 0.5%.
4. a kind of Novel paperboard tackiness agent according to claim 2, is characterized in that, the mass ratio of each component of this tackiness agent is: water 82%, tapioca (flour) 16%, sodium hydroxide 0.4%, toughener 1.2%, borax 0.4%.
5. a kind of Novel paperboard tackiness agent according to claim 2, is characterized in that, the mass ratio of each component of this tackiness agent is: water 78%, tapioca (flour) 20.5%, sodium hydroxide 0.3%, toughener 0.9%, borax 0.3%.
6. a kind of Novel paperboard tackiness agent according to any one of claim 1-5, is characterized in that, described toughener is epoxy resin or its analogue.
7. the preparation method of a kind of Novel paperboard tackiness agent as described in any one of claim 1-6, is characterized in that, include following steps:
A. in the first a mixing bowl, add water, first add 1/7th of tapioca (flour) total amount, stir;
B. in the first a mixing bowl, add sodium hydroxide, stir, make ripe glue;
C. in the second a mixing bowl, inject water, add toughener, then add the tapioca (flour) of 6/7ths remaining parts, be uniformly mixed, make rubber;
D. the ripe glue in the first a mixing bowl is injected in the second a mixing bowl, stir 15-20 minute;
E. the modulation of dilute with water borax is finally injected and the borax water that obtains.
8. the preparation method of a kind of Novel paperboard tackiness agent according to claim 7, is characterized in that, adds after in the water of 1 to the first/7th a mixing bowls of tapioca (flour) total amount described in above-mentioned steps a, stirs 10-15 minute, makes it mix.
9. the preparation method of a kind of Novel paperboard tackiness agent according to claim 7 or 8, is characterized in that, described toughener is epoxy resin or its analogue.