CN104789075B - Hard information coating for screen protective film as well as preparation method and application of hard information coating - Google Patents
Hard information coating for screen protective film as well as preparation method and application of hard information coating Download PDFInfo
- Publication number
- CN104789075B CN104789075B CN201510175972.9A CN201510175972A CN104789075B CN 104789075 B CN104789075 B CN 104789075B CN 201510175972 A CN201510175972 A CN 201510175972A CN 104789075 B CN104789075 B CN 104789075B
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- coating
- weight portion
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a hard information coating for a screen protective film as well as a preparation method and application of the hard information coating. The coating comprises the following components in parts by weight: 14 parts of methyl methacrylate, 9 parts of 3-glycidoxypropyltrimethoxysilane, 27 parts by ethyl alcohol solvent, 0.17 part of benzoyl peroxide, 30 parts of ethyl orthosilicate hydrolyzed in advance, 0.12 part of Yb2O3 with the characteristic of particle size being 4 [mu]m, 0.12 part of Er2O3 with the characteristic of particle size being 4 [mu]m, 0.7 part of polyvinylpyrrolidone, 1.1 parts of propylcnc glycol monobutyl ether and 0.6 part of block polyoxyethylene- polyoxypropylene ether. The hard information coating for the screen protective film, provided by the invention, can be applied to a base material of a screen protective film, can quickly form a transparent gradient functional thin film through ultraviolet curing, is especially suitable for being used on a PET base material, can improve the harness of the base material and the visible light transmittance, and further has fluorescent falsification-preventing and anti-ultraviolet capabilities.
Description
Technical field
The present invention relates to screen protector hardening information coating and its preparation method and application.
Background technology
Gradually stepping up with people's living standard, the electric touch screen equipment such as mobile phone, panel computer is increasingly popularized, and electricity
The resolution ratio more and more higher of sub- product, color is also distinct all the more true to nature, and screen size is larger, and thus brings a lot " face "
Problem, such as easily scraped drawn, mirror is anti-more apparent etc. has had a strong impact on the attractive in appearance of screen and used, the screen guarantor that it arises at the historic moment
Cuticula also emerges in an endless stream, and species is various, and quality is uneven.
At present, the screen protector on market mainly has PP material, PVC material and three kinds of PET material.The patch of PP material
Film is softer it is seen that light transmission rate is relatively low, and anti-scratch, anti-wear effect are poor, only dust protection, so substantially being consumed now
Person " forgets ".PVC material pad pasting is soft but easily pastes, but pad pasting itself is very thick, and therefore translucency is general, and
If tearing pad pasting, mobile phone screen then can leave cull it is difficult to process.The pad pasting of PET material has higher translucency, tears
After there is no cull, be also not easy to occur the minute bubbles in the middle of pad pasting;But, the hardness of this pad pasting is low, reflectance is high, can lead to
User does not see the word on screen, or even can injure eyes, and the illuminance of mobile phone screen itself has been just under normal circumstances
Very low, patch last layer pad pasting can increase the fatigue of eyes, also easily leave the vestiges such as fingerprint and oil stain from the teeth outwards simultaneously.Cause
How this, improve abrasion resistance, light transmittance, anti-glare and the uvioresistant performance of display screen, is that coatings art is in the urgent need to address
Technical problem.In addition, the counterfeit and shoddy goods on market are relatively more, harmful competition is unfavorable for the protection of product and opens further
Send out, it is necessary for increasing product self anti-counterfeiting function.
Content of the invention
It is an object of the invention to provide a kind of screen protector hardening information coating and its preparation method and application,
This coating can be coated on screen protector film base material, by ultra-violet curing, can quickly form transparent gradient function film, especially
It is applied in PET base material, can improve base material hardness, visible light transmissivity, also has fluorescence falsification preventing, uvioresistant performance.
For achieving the above object, the present invention provides a kind of screen protector hardening information coating, by weight by
Following components forms:
14 parts by weight of methylmethacrylate,
9 weight portion γ-(methacryloxypropyl) propyl trimethoxy silicane,
27 parts by weight of ethanol solvents,
0.17 weight portion benzoyl peroxide,
The tetraethyl orthosilicate that 30 weight portions hydrolyze in advance,
0.12 weight portion grain diameter characteristic is 4 μm of Yb2O3,
0.12 weight portion grain diameter characteristic is 4 μm of Er2O3,
0.7 weight account polyethylene pyrrolidones,
1.1 parts by weight of propylene glycol butyl ether,
0.6 weight parts of block polyoxyethylene polyoxypropylene ether.
The present invention also provides the preparation method that screen protector hardens information coating, comprises the steps:
1)Take 14 parts by weight of methylmethacrylate, 9 weight portion γ-(methacryloxypropyl) propyl trimethoxy silicane,
27 parts by weight of ethanol solvents and 0.17 weight portion benzoyl peroxide, add reactor to mix, little in 58 DEG C of confined reactions 4
When;
2)Add the teos solution that 30 weight portions hydrolyze in advance in reaction system, continue reaction 3 in 62 DEG C
Hour;
3)The Yb that 0.12 weight portion grain diameter characteristic is 4 μm is sequentially added again in reaction system2O3, 0.12 weight portion particle diameter
It is characterized as 4 μm of Er2O3, 0.7 weight account polyethylene pyrrolidones, 1.1 parts by weight of propylene glycol butyl ether, 0.6 weight parts of block polyoxy
Ethene-polyethenoxy ether, ball milling disperses, prepared coating material.
The present invention also provides the application of hardening information coating of above-mentioned screen protector, and coating material is coated in screen
On curtain protector film base material, transparent gradient function film is solidify to form on base material.
Preferably, the build of described coating is 3 ~ 4 μm.
Preferably, the mode of described coating is coated with for bar, and the mode of described solidification is ultra-violet curing, and described base material is
PET cuts into slices.
Advantages of the present invention and having the beneficial effects that:A kind of screen protector hardening information coating and its preparation are provided
Methods and applications, this coating can be coated on screen protector film base material, by ultra-violet curing, can quickly form transparent gradient
Function film, is particularly suited in PET base material, can improve base material hardness, visible light transmissivity, also has fluorescence falsification preventing performance,
The built-in fluorescence falsification preventing information of energy, also has uvioresistant performance.
The film being formed after coating material solidification of the present invention, has the hardness of 4H, anti-zoned ability is strong, has stronger screen
Protective capability.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
The present invention provides a kind of screen protector hardening information coating, composed of the following components by weight:
14 parts by weight of methylmethacrylate,
9 weight portion γ-(methacryloxypropyl) propyl trimethoxy silicane,
27 parts by weight of ethanol solvents,
0.17 weight portion benzoyl peroxide,
The tetraethyl orthosilicate that 30 weight portions hydrolyze in advance,
0.12 weight portion grain diameter characteristic is 4 μm of Yb2O3,
0.12 weight portion grain diameter characteristic is 4 μm of Er2O3,
0.7 weight account polyethylene pyrrolidones,
1.1 parts by weight of propylene glycol butyl ether,
0.6 weight parts of block polyoxyethylene polyoxypropylene ether.
The present invention also provides the preparation method that screen protector hardens information coating, comprises the steps:
1)Take 14 parts by weight of methylmethacrylate, 9 weight portion γ-(methacryloxypropyl) propyl trimethoxy silicane,
27 parts by weight of ethanol solvents and 0.17 weight portion benzoyl peroxide, add reactor to mix, little in 58 DEG C of confined reactions 4
When;
2)Add the teos solution that 30 weight portions hydrolyze in advance in reaction system, continue reaction 3 in 62 DEG C
Hour;
3)The Yb that 0.12 weight portion grain diameter characteristic is 4 μm is sequentially added again in reaction system2O3, 0.12 weight portion particle diameter
It is characterized as 4 μm of Er2O3, 0.7 weight account polyethylene pyrrolidones, 1.1 parts by weight of propylene glycol butyl ether, 0.6 weight parts of block polyoxy
Ethene-polyethenoxy ether, ball milling disperses, prepared coating material.
The present invention also provides the application of hardening information coating of above-mentioned screen protector, and coating material is coated in screen
On curtain protector film base material, transparent gradient function film is solidify to form on base material.
The build of described coating is 3 ~ 4 μm.
The mode of described coating is coated with for bar, and the mode of described solidification is ultra-violet curing, and described base material is cut into slices for PET.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (5)
1. screen protector hardening information coating is it is characterised in that composed of the following components by weight:
14 parts by weight of methylmethacrylate,
9 weight portion γ-(methacryloxypropyl) propyl trimethoxy silicane,
27 parts by weight of ethanol solvents,
0.17 weight portion benzoyl peroxide,
The tetraethyl orthosilicate that 30 weight portions hydrolyze in advance,
0.12 weight portion grain diameter characteristic is 4 μm of Yb2O3,
0.12 weight portion grain diameter characteristic is 4 μm of Er2O3,
0.7 weight account polyethylene pyrrolidones,
1.1 parts by weight of propylene glycol butyl ether,
0.6 weight parts of block polyoxyethylene polyoxypropylene ether.
2. the preparation method of screen protector hardening information coating is it is characterised in that comprise the steps:
1)Take 14 parts by weight of methylmethacrylate, 9 weight portion γ-(methacryloxypropyl) propyl trimethoxy silicane, 27 weights
Amount part alcohol solvent and 0.17 weight portion benzoyl peroxide, added reactor to mix, in 58 DEG C of confined reactions 4 hours;
2)Add the teos solution that 30 weight portions hydrolyze in advance in reaction system, continue reaction 3 hours in 62 DEG C;
3)The Yb that 0.12 weight portion grain diameter characteristic is 4 μm is sequentially added again in reaction system2O3, 0.12 weight portion grain diameter characteristic
For 4 μm of Er2O3, 0.7 weight account polyethylene pyrrolidones, 1.1 parts by weight of propylene glycol butyl ether, 0.6 weight parts of block polyoxy second
Alkene-polyethenoxy ether, ball milling disperses, prepared coating material.
3. screen protector described in claim 1 or 2 with the application of hardening information coating it is characterised in that by coating material
Material is coated on screen protector film base material, solidify to form transparent gradient function film on base material.
4. screen protector according to claim 3 with the application of anti-fingerprint hardening coat it is characterised in that described painting
The build of layer is 3 ~ 4 μm.
5. screen protector according to claim 4 with the application of hardening information coating it is characterised in that described coating
Mode be bar coating, the mode of described solidification is ultra-violet curing, and described base material is PET section.