CN104786622A - 一种pe易撕型高阻隔复合发泡膜的加工方法 - Google Patents
一种pe易撕型高阻隔复合发泡膜的加工方法 Download PDFInfo
- Publication number
- CN104786622A CN104786622A CN201510216186.9A CN201510216186A CN104786622A CN 104786622 A CN104786622 A CN 104786622A CN 201510216186 A CN201510216186 A CN 201510216186A CN 104786622 A CN104786622 A CN 104786622A
- Authority
- CN
- China
- Prior art keywords
- pet
- composite
- film
- processing method
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种PE易撕型高阻隔复合发泡膜的加工方法,其特征在于:该复合发泡膜由PET12/PE147/PE45/PET12/AL20/PE45组成。通过:(1)PET12与PE147预合;(2)PET12与AL12预合;(3)PET12/AL20复合材料与PE45预合;(4)PET12与PE147复合材料和PET12/AL20/PE45复合材料复合;(5)切分成捆五个步骤完成。有益效果:本发明PE易撕型高阻隔复合发泡膜提高了膜体本身的强度,克服了传统产品延展性差、易撕破、折叠时易断裂等缺陷。进一步提高了膜体的硬度,并且还具备适应外部温湿度等环境状况的性能,产品具有良好的隔气、阻水性能。
Description
技术领域
本发明涉及一种高阻隔复合包装膜,尤其是涉及一种PE易撕型高阻隔复合发泡膜的加工方法。
背景技术
日前,现有的PE复合发泡膜的透明性、光泽度、机械强度、伸缩性、耐磨性、耐寒性和表面强度等都不理想。再者,铝箔层是目前复合发泡膜包装材料中唯一的金属箔类,其阻水、阻气、遮光等阻隔保护性能是其它包装材料所难以匹敌的。然而,一般铝箔的延展性不佳、厚度很低、折叠时易断裂,单位面积的重量比较重,因而易产生孔眼等自身性能缺陷,导致其阻隔保护性能不理想。
发明内容
本发明的目的是提供一种高阻隔农药级复合包装膜的制造方法,解决现有的PE易撕型高阻隔复合发泡膜延展性不佳、厚度低、单位面积重量比较重、撕取不方便的问题。
本发明解决其技术问题所采用的技术方案是:
一种PE易撕型高阻隔复合发泡膜的加工方法,其特征在于,该复合发泡膜由PET12、PE147、PET12、AL12、PE45组成,所述的PE45为聚乙烯膜层,所述的PE147为发泡型聚乙烯膜层,该复合包装膜通过以下步骤完成:
(1)PET12与PE147预合; PET12材料和PE147材料各在50℃-60℃的干燥间中干燥24小时,PET12与PE147之间通过加入有机胶水后,再经50℃-60℃的干燥间中干燥24小时;
(2)PET12与AL12预合;PET12材料和PE147材料各在50℃-60℃的干燥间中干燥24小时,PET12与PE147之间通过加入有机胶水后,再经50℃-60℃的干燥间中干燥24小时;
(3)PET12/AL20复合材料与PE45预合;PET12/AL20复合材料在经40℃-60℃的干燥间中干燥24小时后入薄膜复合机,PE45材料与ET12/AL20复合材料用复合胶水整平压合在一起;薄膜复合机的复合气压在0.4-0.6MPa之间,转速为55-65rpm;
(4)PET12与PE147复合材料和PET12/AL20/PE45复合材料复合:PET12与PE147复合材料和PET12/AL20/PE45的复合材料入薄膜复合机,再加入醋酸乙脂胶合剂整平压合成型;
(5)切分成捆。
本发明的有益效果:该PE易撕型高阻隔复合发泡膜提高了膜体本身的强度,克服了传统产品延展性差、易撕破、折叠时易断裂等缺陷。进一步提高了膜体的硬度,并且还具备适应外部温湿度等环境状况的性能,产品具有良好的隔气、阻水性能。
具体实施方式
实施例1:
一种PE易撕型高阻隔复合发泡膜的加工方法,其特征在于:该复合发泡膜由PET12、PE147、PET12、AL12、PE45组成,
所述的PE45为聚乙烯膜层,所述的PE147为发泡型聚乙烯膜层,
该复合包装膜通过以下步骤完成:
(1)PET12与PE147预合; PET12材料和PE147材料各在50℃-60℃的干燥间中干燥24小时,PET12与PE147之间通过加入有机胶水后,再经50℃-60℃的干燥间中干燥24小时,
(2)PET12与AL12预合;PET12材料和PE147材料各在50℃-60℃的干燥间中干燥24小时,PET12与PE147之间通过加入有机胶水后,再经50℃-60℃的干燥间中干燥24小时,
(3)PET12/AL20复合材料与PE45预合;PET12/AL20复合材料在经40℃-60℃的干燥间中干燥24小时后入薄膜复合机,PE45材料与ET12/AL20复合材料用复合胶水整平压合在一起;薄膜复合机的复合气压在0.4-0.6MPa之间,转速为60-70rpm,
(4)PET12与PE147复合材料和PET12/AL20/PE45复合材料复合:PET12与PE147复合材料和PE45与PET12/AL20/PE45的复合材料入薄膜复合机再加入醋酸乙脂胶合剂整平压合成型。
(5)检测:检测复合的膜体上出现的爆筋、皱纹、气泡、划***、穿孔、粘边、异物、层间分层。
(6)切分成捆。
以上的实施例仅仅是对本发明的优选实施方式进行描述,并非对本发明的范围进行限定,在不脱离本发明设计精神的前提下,本领域普通工程技术人员对本发明的技术方案做出的各种变形和改进,均应落入本发明的权利要求书确定的保护范围内。
本发明未涉及部分均与现有技术相同或可采用现有技术加以实现。
Claims (1)
1. 一种PE易撕型高阻隔复合发泡膜的加工方法,其特征在于,该复合发泡膜由PET12、PE147、PET12、AL12、PE45组成,所述的PE45为聚乙烯膜层,所述的PE147为发泡型聚乙烯膜层,该复合包装膜通过以下步骤完成:
(1)PET12与PE147预合: PET12材料和PE147材料各在50℃-60℃的干燥间中干燥24小时,PET12与PE147之间通过加入有机胶水后,再经50℃-60℃的干燥间中干燥24小时;
(2)PET12与AL12预合:PET12材料和PE147材料各在50℃-60℃的干燥间中干燥24小时,PET12与PE147之间通过加入有机胶水后,再经50℃-60℃的干燥间中干燥24小时;
(3)PET12/AL20复合材料与PE45预合:PET12/AL20复合材料在经40℃-60℃的干燥间中干燥24小时后入薄膜复合机,PE45材料与ET12/AL20复合材料用复合胶水整平压合在一起,薄膜复合机的复合气压为0.4-0.6MPa,转速为为55-65rpm;
(4)PET12与PE147复合材料和PET12/AL20/PE45复合材料的复合:PET12与PE147复合材料和PET12/AL20/PE45的复合材料入薄膜复合机,再加入醋酸乙脂胶合剂整平压合成型;
(5)切分成捆。