CN104761802A - Heat-resistant weather-resistant flame-retarding rubber insulating cable material - Google Patents

Heat-resistant weather-resistant flame-retarding rubber insulating cable material Download PDF

Info

Publication number
CN104761802A
CN104761802A CN201510120139.4A CN201510120139A CN104761802A CN 104761802 A CN104761802 A CN 104761802A CN 201510120139 A CN201510120139 A CN 201510120139A CN 104761802 A CN104761802 A CN 104761802A
Authority
CN
China
Prior art keywords
parts
resistant
cable material
heat
ethylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510120139.4A
Other languages
Chinese (zh)
Inventor
管新元
张新
曹卫建
陈文博
张仲韬
邬振林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Hengtong Power Cable Co Ltd
Original Assignee
Jiangsu Hengtong Power Cable Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Hengtong Power Cable Co Ltd filed Critical Jiangsu Hengtong Power Cable Co Ltd
Publication of CN104761802A publication Critical patent/CN104761802A/en
Pending legal-status Critical Current

Abstract

The invention discloses a heat-resistant weather-resistant flame-retarding rubber insulating cable material which is composed of following components, by weight: 8-14 parts of chlorinated polyethylene (CPE), 15-21 parts of ethylene-octylene copolymer elastomer, 3-6 parts of fumed silica, 15-19 parts of aluminum hydroxide, 13-18 parts of calcined argil, 5-8 parts of 800# paraffin-based rubber oil, 0.5-1 part of activated magnesium oxide, 4-7 parts of ultrafine talcum powder, 1-2 parts of zinc oxide, 0.3-0.6 parts of an environmental-protective stabilizing agent, 1-2 parts of microcrystalline wax, 0.5-1 part of titanium dioxide, 0.5-0.8 parts of 4,4'-bis([alpha],[alpha]-dimethylbenzyl)diphenylamine, 1-2 parts of dicumyl peroxide, and 1-1.5 parts of triallyl cyanurate. In the ethylene-octylene copolymer elastomer, the mass percentage of octylene monomer is 20-30%. The cable material is beneficial to uniformity of addition of organic powders, is wide in technical range, can maintain a high elongation at break even at a continuous vulcanizing temperature of 190-210 DEG C. With addition of same filling materials, the cable material requires less plasticizing agent and can improve heat-resistant and weather-resistant performances of rubber compound.

Description

Heat-resisting weathering resistance flame retardant rubber insulated cable material
Technical field
The present invention relates to flame retardant rubber insulated cable material, be specifically related to a kind of heat-resisting weathering resistance flame retardant rubber insulated cable material.
Background technology
What commonly use in rubber insulation is that Ethylene Propylene Terpolymer is as base-material, with vulcanizing agent DCP and vulcanization accelerator TAC, the shortcoming of rubber unvulcanizate is: elongation at break lower (elongation at break is generally 150% ~ 250%), in sulfidation, processing range is narrower, is easy to elongation at break defective during steam vulcanization.
Summary of the invention
The object of this invention is to provide a kind of heat-resisting weathering resistance flame retardant rubber insulated cable material, be conducive to inorganic powder dispersed, processing range is wide, and endless vulcanization temperature still keeps higher elongation at break between 190 DEG C ~ 210 DEG C, can greatly reduce costs simultaneously;
For achieving the above object, the technical solution used in the present invention is: a kind of heat-resisting weathering resistance flame retardant rubber insulated cable material, is characterized in that: be made up of the component of following weight part:
Chlorinatedpolyethylene (CPE) 12 ~ 14 parts,
18 ~ 20 parts, ethylene-octene copolymer elastomerics (POE)
Thermal silica 3 ~ 6 parts,
15 ~ 19 parts, aluminium hydroxide,
Calcinated argil 13 ~ 18 parts,
800# paraffinic base rubber oil 5 ~ 7 parts,
Activated magnesia 0.8 part,
Superfine talcum powder 5 ~ 7 parts,
1 ~ 1.5 part, zinc oxide,
Stabilizer 0.45 ~ 0.55 part,
Microcrystalline Wax 1.5 ~ 2 parts,
Titanium dioxide 0.7 ~ 0.9 part,
4,4 ' two (α, α dimethyl benzyl) pentanoic 0.5 ~ 0.6 part,
Dicumyl peroxide 1.5 parts,
Triallyl cyanurate 1.2 ~ 1.3 parts;
In described ethylene-octene copolymer elastomerics, the mass fraction of octene monomers is between 20% ~ 30%.
Further improvement project in above-mentioned fabricating technology scheme is as follows:
In such scheme, in described step 4, filter screen is three metafiltration nets, is respectively 40 orders, 80 orders and 40 orders.
Due to the utilization of technique scheme, the present invention compared with prior art has following advantages:
1. the present invention's heat-resisting weathering resistance flame retardant rubber insulated cable material, its adopt the mass fraction of octene monomers 20% ~ 30% 15 ~ 21 parts, ethylene-octene copolymer elastomerics (POE) and chlorinatedpolyethylene (CPE) 8 ~ 14 parts as base-material, due to mass fraction 20% ~ 30% the elastomeric Mooney of ethylene-octene copolymer be that 17 viscosity are lower, when temperature raises, sizing material deliquescing; Like this can moistening inorganic powder, be conducive to inorganic powder to be scattered in uniformly in base-material, improve consistency, and after with the addition of chlorinatedpolyethylene (CPE), because chlorinatedpolyethylene (CPE) Mooney is higher, overcome POE when mixing, put glue difficulty, avoid defect tri-roll press machine opened bar slice and easily break, improve physical and mechanical properties, under the prerequisite ensureing electrical property, processing performance is greatly improved; POE excellent electrical property, and chlorinated polyethylene compound can improve and use the electric property of rubber unvulcanizate; Secondly, 15 ~ 21 parts, the ethylene-octene copolymer elastomerics (POE) of mass fraction 20% ~ 30% and chlorinatedpolyethylene (CPE) 8 ~ 14 parts are as base-material, mooney viscosity is lower, adding identical packing material, softening agent required when reaching identical mooney viscosity is less, can improve heat-resisting, the weather resistance of rubber unvulcanizate like this.Finally, CPE as body material a part due in its molecular chain containing chlorine element, decomposes, generates non-flammable gases, inflammable gas and oxygen dilution is reached flame retardant effect.
2. the present invention's heat-resisting weathering resistance flame retardant rubber insulated cable material, its ethylene-octene copolymer elastomerics (POE) and chlorinatedpolyethylene (CPE) are all the not double bond containing saturated rubber of main chain, they have covulcanization characteristic, select DCP as vulcanizing agent, add co-curing agent triallyl cyanurate (TAC); When adopting DCP as vulcanization system, crosslinked and fracture occurs simultaneously, and for suppressing cleavage reaction, can add the common sulphur agent with functional group, co-curing agent can accelerate vulcanization rate greatly, improves cross-linking density, improves the heat resistance of cross-linked rubber.CPE itself does not have double bond, the point of crosslinking structure is not had yet, be cross-linked by superoxide completely, the radical that high temperature when sulfuration makes peroxide breakdown produce, capture the hydrogen on CPE long chain molecule and occur the radical of CPE, under the help of vulcanization aid TAC, the radical of two macromolecular chains being coupled together, form cross-linked structure, thus make the CPE vulcanization of rubber.In the process because the effect of polar molecule has the generation of HCl molecule, this HCl gas not only hampers colloid sulfuration, and easily makes CPE rubber produce similar sponge-type porosity but its physical and mechanical properties worsens.Adding of activated magnesia effectively overcomes this problem.So magnesium oxide is good acid-acceptor, vulcanization accelerator, CPE thermo-stabilizer.Zinc oxide can significantly improve vulcanization rate and the crosslinking degree of POE.
3. the present invention's heat-resisting weathering resistance flame retardant rubber insulated cable material, it is long-pending large that its thermal silica has particle diameter small specific surface, and the feature that surfactivity is high, has good strengthening action to rubber unvulcanizate, substantially increases the physical and mechanical properties of blend rubber; Aluminium hydroxide decomposes can absorb heat; be conducive to cooling; promote dehydrogenation reaction and protection carbon-coating; decompose the water of releasing and be not only a refrigerant, or a thinner, decompose under aluminium hydroxide high temperature and generate aluminium sesquioxide tectum; be covered in the surface of superpolymer; isolated heat, oxygen transmission, make the combustibility of material decline, and oxygen index increases.Aluminium hydroxide is added to the oxygen index that can improve rubber unvulcanizate in chlorinated polyethylene rubber; Calcinated argil is a kind of inorganic filler taking out crystal water more than 900 DEG C, its stable chemical performance, extruded product smooth in appearance, there is thermotolerance, the feature of resistance to acids and bases and good electrical property, and play strengthening action equally, and cost is lower, cost is made greatly to reduce like this.
Embodiment
The heat-resisting weathering resistance flame retardant rubber insulated cable material of embodiment 1. 1 kinds, material each component formula is: chlorinatedpolyethylene (CPE) 12 kilograms, 19 kilograms, ethylene-octene copolymer elastomerics (POE), 800# paraffinic base rubber oil 5 kilograms, activated magnesia 0.8 kilogram, 1.5 kilograms, zinc oxide, superfine talcum powder 5 kilograms, stabilizer 0.5 kilogram, Microcrystalline Wax 1.5 kilograms, titanium dioxide 0.8 kilogram, thermal silica 3 kilograms, calcinated argil 13 kilograms, 19 kilograms, aluminium hydroxide, 4, 4 ' two (α, α dimethyl benzyl) pentanoic 0.6 kilogram, dicumyl peroxide 1.5 kilograms, triallyl cyanurate 1.2 kilograms.
In above-mentioned ethylene-octene copolymer elastomerics, the mass fraction of octene monomers is 20% ~ 30%.
Preparation method: first by chlorinatedpolyethylene (CPE), ethylene-octene copolymer elastomerics (POE) percentage ratio mixing 4-5min in 90 ~ 110 DEG C of Banbury mixeies by weight, bi-material mixes; 800# paraffinic base rubber oil, activated magnesia, zinc oxide, stabilizer, Microcrystalline Wax, titanium dioxide, anti-aging agent 4,4 ' two (α, α dimethyl benzyl) pentanoic, mixing 2-3min; Then by calcinated argil, thermal silica, aluminium hydroxide, superfine talcum powder, mixing 3-5min; Banbury mixer discharge, by rubber unvulcanizate thin-pass 1 ~ 2 time on a mill until, put glue 2 ~ 3 times simultaneously, then rubber (the order number of three metafiltration nets is respectively: 40 orders, 80 orders, 40 orders) is filtered, after the rubber filtered is deposited 24 hours, sizing material is reentered into mixer mixing, add vulcanizing agent dicumyl peroxide, mixing about the 2 ~ 3min discharge of vulcanization aid triallyl cyanurate simultaneously, by rubber unvulcanizate thin-pass 1 ~ 2 time on a mill until, put glue 2 ~ 3 times simultaneously, tri-roll press machine is opened bar slice, rubber page cools through cooling roller, obtained finished product after powder case.
The high strength prepared of this example is high stretches rate flame retardant rubber insulated cable material, and performance detection data is as follows:
Aging condition: 135 ± 1 DEG C × 168 hours.
The heat-resisting weathering resistance flame retardant rubber insulated cable material of embodiment 2. 1 kinds, material each component formula is: chlorinatedpolyethylene (CPE) 12 kilograms, 19 kilograms, ethylene-octene copolymer elastomerics (POE), 800# paraffinic base rubber oil 7 kilograms, activated magnesia 0.8 kilogram, 1.5 kilograms, zinc oxide, superfine talcum powder 7 kilograms, stabilizer 0.5 kilogram, Microcrystalline Wax 1.5 kilograms, titanium dioxide 0.8 kilogram, thermal silica 3 kilograms, calcinated argil 17 kilograms, 19 kilograms, aluminium hydroxide, 4, 4 ' two (α, α dimethyl benzyl) pentanoic 0.6 kilogram, dicumyl peroxide 1.5 kilograms, triallyl cyanurate 1.2 kilograms.
In above-mentioned ethylene-octene copolymer elastomerics, the mass fraction of octene monomers is 22% ~ 24%.
Preparation method is in the same manner as in Example 1.
The high strength prepared of this example is high stretches rate flame retardant rubber insulated cable material, and performance detection data is as follows:
Aging condition: 135 ± 1 DEG C × 168 hours.
The heat-resisting weathering resistance flame retardant rubber insulated cable material of embodiment 3. 1 kinds, material each component formula is: chlorinatedpolyethylene (CPE) 14 kilograms, 18 kilograms, ethylene-octene copolymer elastomerics (POE), 800# paraffinic base rubber oil 5 kilograms, activated magnesia 0.8 kilogram, 1.0 kilograms, zinc oxide, superfine talcum powder 5 kilograms, stabilizer 0.5 kilogram, Microcrystalline Wax 2 kilograms, titanium dioxide 0.8 kilogram, thermal silica 5 kilograms, calcinated argil 17 kilograms, 19 kilograms, aluminium hydroxide, 4, 4 ' two (α, α dimethyl benzyl) pentanoic 0.6 kilogram, dicumyl peroxide 1.5 kilograms, triallyl cyanurate 1.2 kilograms.
In above-mentioned ethylene-octene copolymer elastomerics, the mass fraction of octene monomers is 25% ~ 26%.
The high strength prepared of this example is high stretches rate flame retardant rubber insulated cable material, and the detection data of performance are as follows:
Aging condition: 135 ± 1 DEG C × 168 hours.
To sum up, the present invention's heat-resisting weathering resistance flame retardant rubber insulated cable material, its adopt the mass fraction of octene monomers 20% ~ 30% 15 ~ 21 parts, ethylene-octene copolymer elastomerics (POE) and chlorinatedpolyethylene (CPE) 8 ~ 14 parts as base-material, due to mass fraction 20% ~ 30% the elastomeric Mooney of ethylene-octene copolymer be that 17 viscosity are lower, when temperature raises, rubber unvulcanizate becomes very soft; Being conducive to inorganic powder interpolation is mixed in its base-material uniformly, improve consistency, and after with the addition of chlorinatedpolyethylene (CPE), because chlorinatedpolyethylene (CPE) Mooney is higher, overcome rubber unvulcanizate when mixing, put glue difficulty, avoid defect tri-roll press machine opened bar slice and easily break, improve physical and mechanical properties, under the prerequisite ensureing electrical property, processing performance is greatly improved; Secondly, mass fraction 20% ~ 30% 15 ~ 21 parts, ethylene-octene copolymer elastomerics (POE) and chlorinatedpolyethylene (CPE) 8 ~ 14 parts as base-material, mooney viscosity is lower, adding identical packing material, softening agent required when reaching identical mooney viscosity is less, can improve the heat-resisting, weather-proof of rubber unvulcanizate like this.
Above-described embodiment, only for technical conceive of the present invention and feature are described, its object is to person skilled in the art can be understood content of the present invention and implement according to this, can not limit the scope of the invention with this.All equivalences done according to spirit of the present invention change or modify, and all should be encompassed within protection scope of the present invention.

Claims (1)

1. a heat-resisting weathering resistance flame retardant rubber insulated cable material, is characterized in that: be made up of the component of following weight part:
Chlorinatedpolyethylene (CPE) 12 ~ 14 parts,
18 ~ 20 parts, ethylene-octene copolymer elastomerics (POE)
Thermal silica 3 ~ 6 parts,
15 ~ 19 parts, aluminium hydroxide,
Calcinated argil 13 ~ 18 parts,
800# paraffinic base rubber oil 5 ~ 7 parts,
Activated magnesia 0.8 part,
Superfine talcum powder 5 ~ 7 parts,
1 ~ 1.5 part, zinc oxide,
Stabilizer 0.45 ~ 0.55 part,
Microcrystalline Wax 1.5 ~ 2 parts,
Titanium dioxide 0.7 ~ 0.9 part,
4,4 ' two (α, α dimethyl benzyl) pentanoic 0.5 ~ 0.6 part,
Dicumyl peroxide 1.5 parts,
Triallyl cyanurate 1.2 ~ 1.3 parts;
In described ethylene-octene copolymer elastomerics, the mass fraction of octene monomers is between 20% ~ 30%.
CN201510120139.4A 2013-04-22 2013-04-22 Heat-resistant weather-resistant flame-retarding rubber insulating cable material Pending CN104761802A (en)