CN104711105A - 透明水基切削液及生产方法 - Google Patents
透明水基切削液及生产方法 Download PDFInfo
- Publication number
- CN104711105A CN104711105A CN201310678357.0A CN201310678357A CN104711105A CN 104711105 A CN104711105 A CN 104711105A CN 201310678357 A CN201310678357 A CN 201310678357A CN 104711105 A CN104711105 A CN 104711105A
- Authority
- CN
- China
- Prior art keywords
- water
- cutting fluid
- based cutting
- production method
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种透明水基切削液,所用原料及质量百分比如下:硝酸钾2~4%、硝酸钠2~4%、三乙醇胺6~9%、甘油3~5%、聚乙二醇2~4%、磷化水质调节剂3~5%及水余量。生产方法按如下步骤进行:将计算称量的水加入到反应釜中,加热到70~80℃开动搅拌器,控制转速40转/min,然后将计算称量的硝酸钾、硝酸钠、三乙醇胺、甘油、聚乙二醇及磷化水质调节剂依次徐徐加入到反应釜中,每加一种原料需搅拌30min,全部原料加完后继续搅拌3~4H,待温度降到室温时,放料过滤包装。
Description
技术领域
本发明涉及一种金属切削液,尤其是一种具有良好的冷却性能、润滑性能、清洗性能和防锈性能的透明水基切削液及生产方法。
背景技术
在金属切削加工过程中,刀具与工件之间的摩擦力会使工件加工区域温度上升到1000℃以上,刀具与工件表面凹凸不平处相接触的部位表面负荷可达到5000N/mm2,所以工件在切削时会造成局部熔焊现象。为了降低切削温度与切削力,在金属切削加工过程中就必需使用切削液,水基切削液是常用的一种,但目前切削加工过程中所使用的水基切削液所存在的最大问题就是防锈能力较差,工件表面容易发生锈蚀。
发明内容
本发明是为了解决现有技术所存在的上述技术问题,提供一种具有良好的冷却性能、润滑性能、清洗性能和防锈性能的透明水基切削液及生产方法。
本发明的技术解决方案是:一种透明水基切削液,其特征在于所用原料及质量百分比如下:
硝酸钾 2~4%
硝酸钠 2~4%
三乙醇胺 6~9%
甘油 3~5%
聚乙二醇 2~4%
磷化水质调节剂 3~5%
水 余量。
一种上述的透明水基切削液的生产方法,其特征在于按如下步骤进行:将计算称量的水加入到反应釜中,加热到70~80℃开动搅拌器,控制转速40转/min,然后将计算称量的硝酸钾、硝酸钠、三乙醇胺、甘油、聚乙二醇及磷化水质调节剂依次徐徐加入到反应釜中,每加一种原料需搅拌30min,全部原料加完后继续搅拌3~4H,待温度降到室温时,放料过滤包装。
本发明优化组合了相关的优质原材料,各组分相互配伍作用,同现有技术相比,具有良好的冷却性能、润滑性能、清洗性能和防锈性能。 具体实施方式
实施例1:
所用原料及质量百分比如下:
硝酸钾 2~4%
硝酸钠 2~4%
三乙醇胺 6~9%
甘油 3~5%
聚乙二醇 2~4%
磷化水质调节剂 3~5%
水 余量。
上述原料中的磷化水质调节剂为大连三达奥克化学股份有限公司的产品,产品型号为TS-300。
生产方法按如下步骤进行:将计算称量的水加入到反应釜中,加热到70~80℃开动搅拌器,控制转速40转/min,然后将计算称量的硝酸钾、硝酸钠、三乙醇胺、甘油、聚乙二醇及磷化水质调节剂依次徐徐加入到反应釜中,每加一种原料需搅拌30min,全部原料加完后继续搅拌3~4H,待温度降到室温时,放料过滤包装。
实施例2:
所用原料及质量百分比如下:
硝酸钾 3%
硝酸钠 3%
三乙醇胺 8%
甘油 4%
聚乙二醇 3%
磷化水质调节剂 4%
水 余量。
生产方法同实施例1。
使用时,将本发明实施例1、2配制质量百分比10~20%的gon工作液,分别作为铬钢工件的车削、钻削、螺纹加工等,冷却性能、润滑性能、清洗性能及防锈性能得到了显著的提高,防锈期超过两周。
Claims (2)
1.一种透明水基切削液,其特征在于所用原料及质量百分比如下:
硝酸钾 2~4%
硝酸钠 2~4%
三乙醇胺 6~9%
甘油 3~5%
聚乙二醇 2~4%
磷化水质调节剂 3~5%
水 余量。
2.一种如权利要求1所述的透明水基切削液的生产方法,其特征在于按如下步骤进行:将计算称量的水加入到反应釜中,加热到70~80℃开动搅拌器,控制转速40转/min,然后将计算称量的硝酸钾、硝酸钠、三乙醇胺、甘油、聚乙二醇及磷化水质调节剂依次徐徐加入到反应釜中,每加一种原料需搅拌30min,全部原料加完后继续搅拌3~4H,待温度降到室温时,放料过滤包装。