CN104695824B - Veneer facing lines frame decorative anti-theft door and its production technology - Google Patents
Veneer facing lines frame decorative anti-theft door and its production technology Download PDFInfo
- Publication number
- CN104695824B CN104695824B CN201510092271.9A CN201510092271A CN104695824B CN 104695824 B CN104695824 B CN 104695824B CN 201510092271 A CN201510092271 A CN 201510092271A CN 104695824 B CN104695824 B CN 104695824B
- Authority
- CN
- China
- Prior art keywords
- veneer
- shop front
- door
- recessed lattice
- antitheft door
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Invention is related to window technology field, refers to a kind of veneer facing lines frame decorative anti-theft door and its production technology.It includes the shop front, and shop front surface is pasted with veneer by glue-line, and veneer is natural veneer or recombinant decorative veneer, and veneer surface scribbles skin of paint.It includes step：1) selection is carried out；2) recessed lattice are manufactured；3) the preceding shop front and the rear shop front of the shop front are manufactured；4) gluing or glue spraying；5) spliced natural veneer or recombinant decorative veneer are overlayed on to the surface of the antitheft door shop front and recessed lattice；6) paint；7) to aluminum-alloy line molding powder, natural veneer coiled material is coated on aluminum-alloy line with lines coating machine；8) laid-on moulding frame；9) decoration is installed.Compared with prior art, the advantage of invention is：The fire prevention anti-damage ability equal with traditional anti-theft door can be retained from different materials by door-plate；Its manufacturing process is simple, reduces manufacturing cost, while improving production efficiency, product is possessed stronger competitiveness.
Description
Technical field
Invention is related to window technology field, refers to a kind of antitheft door, especially a kind of veneer facing lines frame decorative anti-theft door
And its production technology.
Background technology
The full name of antitheft door is " anti-theft safety door ".It has both antitheft and safe performance.According to《Anti-theft safety door is general
Technical conditions》Regulation, qualified antitheft door utilized ordinary hand tools and the electric hand drills such as chisel, screwdriver, crowbar in 15 minutes
It can not be pried open Deng portable power tool or one 615 square millimeters of opening is opened on door leaf, or in 150 squares of keyed end
The opening of one 38 square millimeters of opening in the semicircle of millimeter.And the lockset used on antitheft door must be examined by the Ministry of Public Security
Measured center detects the qualified Special purpose lock for anti-theft door with anti-drilling function.Traditional antitheft door, using steel plate as stock, through punching
Welding fabrication is pressed, after degreasing and rust removal processing, then in superficial layer the processing of transfer-coated or pad pasting is done；Steel wood armoured door is in steel
The surface of external door panel first overlays a density board, then in the surface veneer overlay of density board and moulding.Tradition print antitheft door
Texture color and luster prints from machine, therefore texture is stiff, the single shortage stereovision of tone.The density board sheet that steel wood armoured door is used
The easy moisture absorption dilatancy of body, is that a kind of stability is general, the poor material of weather resistance, causes the wooden easy warpage of armoured door of steel to become
Shape, while open paint effect can not be done, it is impossible to build the high-end effect of wood, density board belongs to combustible material, shadow
Ring the overall fire-proof function of antitheft door.
The content of the invention
The purpose of invention be in view of the above-mentioned problems, there is provided it is a kind of not only have Anti-theft door made of steel fire-proof and theft-proof function,
Also there is the texture of high-grade Solid Door, the veneer facing lines frame decoration for meeting consumer to high-grade antitheft door product demand is antitheft
Door.
To reach above-mentioned purpose, invention employs following technical proposal：Veneer facing lines frame decorative anti-theft door, including door
Face, the shop front includes the preceding shop front and the rear shop front, and added with its internal substantial inserts is made between the preceding shop front and the rear shop front, its feature exists
In the described preceding shop front is provided with above several recessed lattice, described recessed lattice and is provided with decoration, between described recessed lattice and decoration
Provided with lines frame, described lines frame includes outer lines frame and interior lines frame, joint face therebetween；Described shop front surface
Veneer is pasted with by glue-line, veneer surface scribbles skin of paint.
In a kind of above-mentioned veneer facing lines frame decorative anti-theft door, between described outer lines frame and interior lines frame
Joint face forms 0 ° -90 ° of angle with shop front surface.
In a kind of above-mentioned veneer facing lines frame decorative anti-theft door, described recessed lattice are rectangular.
In a kind of above-mentioned veneer facing lines frame decorative anti-theft door, described decoration and the area of interior lines inframe
It is equal in magnitude.
In a kind of above-mentioned veneer facing lines frame decorative anti-theft door, described door-plate is manufactured using steel plate, described
The shop front is manufactured using steel plate；Inserts uses honeycomb aluminum, honeycomb paper, anti-guncotton or expanded perlite.
In a kind of above-mentioned veneer facing lines frame decorative anti-theft door, described veneer is natural veneer or recombinant decorative
Veneer.
In a kind of above-mentioned veneer facing lines frame decorative anti-theft door, described glue-line is made up of adhesive, adhesive
For one kind in PUR glue, all-purpose adhesive, epoxide-resin glue, polyurethane adhesive.
It is preferred that, described adhesive PUR glue；Cloth glue amount is 40-200 grams/m.
In a kind of above-mentioned veneer facing lines frame decorative anti-theft door, the paint in described skin of paint uses haze tallow
One kind in oil, PU paints, water paint, F-C paint.
In a kind of above-mentioned veneer facing lines frame decorative anti-theft door, described veneer thickness is 0.1-1mm.
In a kind of above-mentioned veneer facing lines frame decorative anti-theft door, described natural veneer includes several natural thins
Combined between wooden chunk, natural veneer chunk by piece gemel connection.
Another purpose of invention is in view of the above-mentioned problems, there is provided a kind of easy to use, efficient veneer facing of production
The production technology of lines frame decorative anti-theft door.
In a kind of production technology of above-mentioned veneer facing lines frame decorative anti-theft door, including step：
1) by thickness be 0.1-1mm, moisture content 6-12% natural veneer carry out selection, cut out removal knot, white edge,
Lack the defect part such as side, natural veneer is combined into the width that antitheft door needs with splicing machine, according to natural veneer thickness, material
Difference, can natural veneer back side composite kraft paper or non-woven fabrics, make natural veneer not cracky, cracking；
2) recessed lattice are manufactured；By two pieces of steel plate bendings downward vertically, the both sides vertical bending upwards of one block of steel plate, upwards and to
Lower bending edges width is identical, and bending edges width is the depth of recessed lattice, then the parallel clasp joint of bending edges of three blocks of steel plates, to
The interior bending part of lower bending steel plate is welded and fixed obtained groove；Or with bender one block of steel plate to vertical under recessed lattice depth direction
Bending, then to vertical bending before recessed lattice width, then to vertical bending on recessed lattice depth direction, finally vertical bending system forward
Groove is obtained, is used by the collocation of horizontal cover plate and perpendicular cover plate and groove is divided into some recessed lattice；
3) the steel door-plate by stamped, bending, welding does oil removing, derusting, phosphorating treatment, is used separately as the front door of the shop front
Face and the rear shop front, by the preceding shop front after processing and rear shop front brush coating, centre adds honeycomb aluminum, honeycomb paper, anti-guncotton or expansion
After perlite welding, with the Hot gluing machine curing molding antitheft door shop front, make the shop front smooth indeformable；
4) to the glue amount of antitheft door shop front surface coating or glue spraying to 40-200g/ ㎡；
5) spliced natural veneer or recombinant decorative veneer are overlayed on to the surface of the antitheft door shop front and recessed lattice, according to the shop front
Moulding, size, Adhensive performance veneer overlay can using overlaying by hand, the method for roll-in or press hot pressing, using press heat
The antitheft door shop front for being covered with veneer is sent into the press that temperature is 30 DEG C -120 DEG C, pressure is 0.01-0.5MPa during pressure, warp
30S-300S hot pressing is combined into the veneer facing antitheft door shop front；
6) antitheft door shop front surface is polished, repaired and repaiied after color processing, equilibrium moisture content to 6-12%, using many
The technique of road spray painting polishing, 150-600g/ ㎡ paint is sprayed on its surface；
7) to aluminum-alloy line molding powder, natural veneer coiled material is coated on aluminum-alloy line with lines coating machine, to day
Right veneer cladding lines surface veneer is polished, repaired and repaiied after color processing, equilibrium moisture content to 6-12%, is sprayed using multiple tracks
The technique for painting polishing, 150-600g/ ㎡ paint is sprayed on its surface；The lines screw and connector or adhesive after paint
45° angle is spliced into lines frame；
8) lines frame is fixed on PUR glue or glass cement the edge of the recessed lattice of the veneer facing antitheft door shop front；Cloth glue amount 60-
300g/㎡。
9) decoration is installed；Decoration is put into recessed lattice, is attached by 30-200g/ ㎡ glue amount and recessed lattice；
Described step 3) in, plastic-spraying processing is done to the antitheft door shop front, the bonding strength of veneer overlay is further improved.
Described step 6) in, the technique of described multi-coat lacquer polishing includes polishing-wiping color to 50-100g/ ㎡-spray bottom
Paint is repaiied color to 50-200g/ ㎡-polishing-spray and painted to 50-150g/ ㎡-polishing-topcoating to 50-150g/ ㎡.
Compared with prior art, the advantage of invention is：It can retain anti-with tradition from different materials by door-plate
Steal the fire prevention anti-damage ability of door on an equal basis；The combination with decorative surfaces of natural veneer not only easily melts as one with the overall decoration style of building
Body.Compared with imitation wood line antitheft door, the class of antitheft door is improved, the appropriate thickness of veneer can achieve the same of effect
When can also save usage amount, the internal stress when temperature of material, moisture content change is small, at the same veneer be in interior adhesive
In the protection of layer and outer skin of paint, veneer facing lines frame decorative anti-theft door has good product stability；Natural veneer can
The veneer layer different by splicing composition size, makes it wider using scope；Timber usage amount is about the wooden armoured door of steel
1/10th, about 1st/20th of Wooden composite antitheft door timber usage amount, a large amount of timber resources of saving.Manufacturing process letter
Single, the cycle is short, reduces manufacturing cost, while improving production efficiency, product is possessed stronger competitiveness, make surface more
Smooth, color and luster is good-looking, and the thickness of each layer is appropriate, reduces the integral thickness of door, it appears less heavy, while can also make
Connection two aspects more consolidation, firmly.The structure of lines frame and the application of decoration highlight third dimension, improve antitheft door
Class.
Brief description of the drawings
, below will be to embodiment or existing in order to illustrate more clearly of inventive embodiments or technical scheme of the prior art
The accompanying drawing used required in technology description is briefly described, it should be apparent that, drawings in the following description are only invention
Some embodiments, for those of ordinary skill in the art, without having to pay creative labor, can be with root
Other accompanying drawings are obtained according to these accompanying drawings.
Fig. 1 is the structural representation of invention；
Fig. 2 is Fig. 1 sectional view；
Fig. 3 is two recessed lattice structural representations；
Fig. 4 is three recessed lattice structural representations；
Fig. 5 is six recessed lattice structural representations.
Embodiment
Below in conjunction with the accompanying drawing in inventive embodiments, the technical scheme in inventive embodiments is carried out clearly and completely
Description, it is clear that described embodiment is only to invent a part of embodiment, rather than whole embodiments.Based in invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made,
Belong to the scope of invention protection.
Embodiment 1
As shown in Figure 1, 2, 3, veneer facing lines frame decorative anti-theft door, including the shop front 1, the shop front are manufactured using steel plate.It is logical
Crossing steel plate enables to the shop front to have stronger rigidity, while reducing the timber required for the general shop front.The shop front includes the preceding shop front
11 and the rear shop front 12, added with making its internal substantial inserts 13 between the preceding shop front and the rear shop front.Described shop front surface passes through
Glue-line 2 is bonded with natural veneer 3 or recombinant decorative veneer, and glue-line is made up of adhesive, and adhesive is PUR glue, all-purpose adhesive, epoxy
One kind in resin glue, polyurethane adhesive, adhesive PUR glue；Using outdoor wood wax oil, weather-proof PU paints, weather resistant water-thinned paint, fluorine carbon
Paint can obtain preferable color fastness to light grade.
Natural veneer surface scribbles skin of paint 4.Described natural veneer includes several natural veneer chunks, natural veneer
Combined between chunk by piece gemel connection.The area of general door-plate will directly obtain respective area all than larger
Natural veneer is unpractical, costs rather expensive, therefore is easy to implement using multiple natural veneer chunks composition, is reduced simultaneously
Cost.Required according to the style of specific antitheft door and user, the length and width of veneer can be more than the size of the shop front, after redundance bending
For the faced deorative on shop front both sides, the outward appearance for the antitheft door that the shop front and shop front both sides are manufactured with same veneer overlay is more certainly
So, associative perception is stronger.Paint in skin of paint is using one kind in wood wax oil, PU paints, water paint, F-C paint.
The preceding shop front, which is provided with above several recessed lattice 5, described recessed lattice, is provided with decoration 42, described recessed lattice and decoration it
Between be provided with lines frame 43, described lines frame includes outer lines frame 44 and interior lines frame 45.Decoration and the face of interior lines inframe
Product is equal in magnitude, is easy to what decoration can coincide to be put into interior lines inframe, it is to avoid excessive gap, described outer lines occur
Joint face 445 between frame and interior lines frame forms 0 ° of angle with shop front surface.
In a kind of production technology of above-mentioned veneer facing lines frame decorative anti-theft door, including step：
1) it is 0.1mm by thickness, moisture content carries out selection in 6% natural veneer, cuts out removal knot, white edge, lacks side
Deng defect part, natural veneer is combined into the width that antitheft door needs with splicing machine, according to natural veneer thickness, material not
Together, can natural veneer back side composite kraft paper or non-woven fabrics, make natural veneer not cracky, cracking；
2) recessed lattice are manufactured；By two pieces of steel plate bendings downward vertically, the both sides vertical bending upwards of one block of steel plate, upwards and to
Lower bending edges width is identical, and bending edges width is the depth of recessed lattice, then the parallel clasp joint of bending edges of three blocks of steel plates, to
The interior bending part of lower bending steel plate, which is welded and fixed, obtains groove；Or with bender one block of steel plate to vertical under recessed lattice depth direction
Bending, then to vertical bending before recessed lattice width, then to vertical bending on recessed lattice depth direction, finally vertical bending system forward
Obtain groove；Groove is divided into two recessed lattice by the two ends and centre that groove is fixed on three pieces of horizontal cover plates；
3) the steel door-plate by stamped, bending, welding does oil removing, derusting, phosphorating treatment, is used separately as the front door of the shop front
Face and the rear shop front, by the preceding shop front after processing and rear shop front brush coating, centre adds honeycomb aluminum, honeycomb paper, anti-guncotton or expansion
After perlite welding, with the Hot gluing machine curing molding antitheft door shop front, make the shop front smooth indeformable；Plastic-spraying is done to the antitheft door shop front
Processing, further improves the bonding strength of veneer overlay；
4) to the glue amount of antitheft door shop front surface coating or glue spraying to 40g/ ㎡；
5) spliced natural veneer or recombinant decorative veneer are overlayed on to the surface of the antitheft door shop front and recessed lattice, according to the shop front
Moulding, size, Adhensive performance veneer overlay can using overlaying by hand, the method for roll-in or press hot pressing, using press heat
The antitheft door shop front for being covered with veneer is sent into the press that temperature is 30 DEG C, pressure is 0.01MPa during pressure, it is compound through 30S hot pressing
Into the veneer facing antitheft door shop front；
6) antitheft door shop front surface is polished, repaired and repaiied after color processing, equilibrium moisture content to 6%, using multiple tracks
The technique of spray painting polishing, 150g/ ㎡ paint is sprayed on its surface；The technique of described multi-coat lacquer polishing includes polishing-wiping color
Color is repaiied to 50g/ ㎡-primer spray to 50g/ ㎡-polishing-spray to paint to 50g/ ㎡-polishing-topcoating to 50g/ ㎡；
7) to aluminum-alloy line molding powder, natural veneer coiled material is coated on aluminum-alloy line with lines coating machine, to day
Right veneer cladding lines surface veneer is polished, repaired and repaiied after color processing, equilibrium moisture content to 6%, using multi-coat lacquer
The technique of polishing, 150g/ ㎡ paint is sprayed on its surface；Lines after paint are spliced into line with screw and connector 45° angle
Bar frame；
8) lines frame is fixed on PUR glue or glass cement the edge of the recessed lattice of the veneer facing antitheft door shop front；Cloth glue amount
60g/㎡。
9) decoration is installed；Decoration is put into recessed lattice above, be attached by 30g/ ㎡ glue amount and recessed lattice；
Embodiment 2
As shown in Fig. 1,2,4, veneer facing lines frame decorative anti-theft door, including the shop front 1, the shop front is using steel plate manufacture.It is logical
Crossing steel plate enables to the shop front to have stronger rigidity, while reducing the timber required for the general shop front.The shop front includes the preceding shop front
11 and the rear shop front 12, added with making its internal substantial inserts 13 between the preceding shop front and the rear shop front.Described shop front surface passes through
Glue-line 2 is bonded with natural veneer 3 or recombinant decorative veneer, and glue-line is made up of adhesive, and adhesive is PUR glue, all-purpose adhesive, epoxy
One kind in resin glue, polyurethane adhesive, adhesive PUR glue；Using outdoor wood wax oil, weather-proof PU paints, weather resistant water-thinned paint, fluorine carbon
Paint can obtain preferable color fastness to light grade.
Natural veneer surface scribbles skin of paint 4.Described natural veneer includes several natural veneer chunks, natural veneer
Combined between chunk by piece gemel connection.The area of general door-plate will directly obtain respective area all than larger
Natural veneer is unpractical, costs rather expensive, therefore is easy to implement using multiple natural veneer chunks composition, is reduced simultaneously
Cost.Required according to the style of specific antitheft door and user, the length and width of veneer can be more than the size of the shop front, after redundance bending
For the faced deorative on shop front both sides, the outward appearance for the antitheft door that the shop front and shop front both sides are manufactured with same veneer overlay is more certainly
So, associative perception is stronger.Paint in skin of paint is using one kind in wood wax oil, PU paints, water paint, F-C paint.
The preceding shop front is provided with several recessed lattice 5, and the edge of described recessed lattice is provided with lines frame 43, and described lines frame includes outer
Lines frame 44 and interior lines frame 45.Joint face 445 and shop front surface shape between described outer lines frame and interior lines frame is in 90 °
Angle.
In a kind of production technology of above-mentioned veneer facing lines frame decorative anti-theft door, including step：
1) it is 1mm by thickness, moisture content carries out selection in 12% natural veneer, cuts out removal knot, white edge, lacks side etc.
Defect part, the width that antitheft door needs is combined into splicing machine by natural veneer, according to natural veneer thickness, the difference of material,
Can natural veneer back side composite kraft paper or non-woven fabrics, make natural veneer not cracky, cracking；
2) recessed lattice are manufactured；By two pieces of steel plate bendings downward vertically, the both sides vertical bending upwards of one block of steel plate, upwards and to
Lower bending edges width is identical, and bending edges width is the depth of recessed lattice, then the parallel clasp joint of bending edges of three blocks of steel plates, to
The interior bending part of lower bending steel plate, which is welded and fixed, obtains groove；Or with bender one block of steel plate to vertical under recessed lattice depth direction
Bending, then to vertical bending before recessed lattice width, then to vertical bending on recessed lattice depth direction, finally vertical bending system forward
Obtain groove；Groove is divided into 3 recessed lattice by the two ends and centre that groove is fixed on 4 pieces of horizontal cover plates；
3) the steel door-plate by stamped, bending, welding does oil removing, derusting, phosphorating treatment, is used separately as the front door of the shop front
Face and the rear shop front, by the preceding shop front after processing and rear shop front brush coating, centre adds honeycomb aluminum, honeycomb paper, anti-guncotton or expansion
After perlite welding, with the Hot gluing machine curing molding antitheft door shop front, make the shop front smooth indeformable；Plastic-spraying is done to the antitheft door shop front
Processing, further improves the bonding strength of veneer overlay；
4) to the glue amount of antitheft door shop front surface coating or glue spraying to 200g/ ㎡；
5) surface for overlaying on spliced natural veneer or recombinant decorative veneer beyond the recessed lattice of the antitheft door shop front, according to door
Face moulding, size, Adhensive performance veneer overlay can using overlaying by hand, the method for roll-in or press hot pressing, using press
The antitheft door shop front for being covered with veneer is sent into the press that temperature is 120 DEG C, pressure is 0.5MPa during hot pressing, it is multiple through 300S hot pressing
Synthesize the veneer facing antitheft door shop front；
6) antitheft door shop front surface is polished, repaired and repaiied after color processing, equilibrium moisture content to 12%, using multiple tracks
The technique of spray painting polishing, 600g/ ㎡ paint is sprayed on its surface；The technique of described multi-coat lacquer polishing includes polishing-wiping color
Color is repaiied to 100g/ ㎡-primer spray to 200g/ ㎡-polishing-spray to paint to 150g/ ㎡-polishing-topcoating to 150g/ ㎡；
7) to aluminum-alloy line molding powder, natural veneer coiled material is coated on aluminum-alloy line with lines coating machine, to day
Right veneer cladding lines surface veneer is polished, repaired and repaiied after color processing, equilibrium moisture content to 12%, using multi-coat lacquer
The technique of polishing, 600g/ ㎡ paint is sprayed on its surface；Lines after paint are spliced into line with screw and connector 45° angle
Bar frame；
8) lines frame is fixed on PUR glue or glass cement the edge of the recessed lattice of the veneer facing antitheft door shop front；Cloth glue amount
300g/㎡。
Embodiment 3
As shown in Figure 1, 2, 3, veneer facing lines frame decorative anti-theft door, including the shop front 1, the shop front are manufactured using steel plate.It is logical
Crossing steel plate enables to the shop front to have stronger rigidity, while reducing the timber required for the general shop front.The shop front includes the preceding shop front
11 and the rear shop front 12, added with making its internal substantial inserts 13 between the preceding shop front and the rear shop front.Described shop front surface passes through
Glue-line 2 is bonded with natural veneer 3 or recombinant decorative veneer, and glue-line is made up of adhesive, and adhesive is PUR glue, all-purpose adhesive, epoxy
One kind in resin glue, polyurethane adhesive, adhesive PUR glue；Using outdoor wood wax oil, weather-proof PU paints, weather resistant water-thinned paint, fluorine carbon
Paint can obtain preferable color fastness to light grade.
Natural veneer surface scribbles skin of paint 4.Described natural veneer includes several natural veneer chunks, natural veneer
Combined between chunk by piece gemel connection.The area of general door-plate will directly obtain respective area all than larger
Natural veneer is unpractical, costs rather expensive, therefore is easy to implement using multiple natural veneer chunks composition, is reduced simultaneously
Cost.Required according to the style of specific antitheft door and user, the length and width of veneer can be more than the size of the shop front, after redundance bending
For the faced deorative on shop front both sides, the outward appearance for the antitheft door that the shop front and shop front both sides are manufactured with same veneer overlay is more certainly
So, associative perception is stronger.Paint in skin of paint is using one kind in wood wax oil, PU paints, water paint, F-C paint.
The preceding shop front is provided with several recessed lattice 5, and described recessed lattice edge is provided with lines frame 43, and described lines frame includes outside line
Bar frame 44 and interior lines frame 45.Joint face 445 between described outer lines frame and interior lines frame forms 0 ° with shop front surface
Angle.
In a kind of production technology of above-mentioned veneer facing lines frame decorative anti-theft door, including step：
1) it is 0.5mm by thickness, moisture content carries out selection in 11% natural veneer, cuts out removal knot, white edge, lacks side
Deng defect part, natural veneer is combined into the width that antitheft door needs with splicing machine, according to natural veneer thickness, material not
Together, can natural veneer back side composite kraft paper or non-woven fabrics, make natural veneer not cracky, cracking；
2) recessed lattice are manufactured；By two pieces of steel plate bendings downward vertically, the both sides vertical bending upwards of one block of steel plate, upwards and to
Lower bending edges width is identical, and bending edges width is the depth of recessed lattice, then the parallel clasp joint of bending edges of three blocks of steel plates, to
The interior bending part of lower bending steel plate, which is welded and fixed, obtains groove；Or with bender one block of steel plate to vertical under recessed lattice depth direction
Bending, then to vertical bending before recessed lattice width, then to vertical bending on recessed lattice depth direction, finally vertical bending system forward
Obtain groove；Groove is divided into 6 recessed lattice with 4 pieces of horizontal cover plates and 3 pieces of perpendicular cover plates；
3) the steel door-plate by stamped, bending, welding does oil removing, derusting, phosphorating treatment, is used separately as the front door of the shop front
Face and the rear shop front, by the preceding shop front after processing and rear shop front brush coating, centre adds honeycomb aluminum, honeycomb paper, anti-guncotton or expansion
After perlite welding, with the Hot gluing machine curing molding antitheft door shop front, make the shop front smooth indeformable；Plastic-spraying is done to the antitheft door shop front
Processing, further improves the bonding strength of veneer overlay；
4) to the glue amount of antitheft door shop front surface coating or glue spraying to 100g/ ㎡；
5) spliced natural veneer or recombinant decorative veneer are overlayed on to the surface of the antitheft door shop front and recessed lattice, according to the shop front
Moulding, size, Adhensive performance veneer overlay can using overlaying by hand, the method for roll-in or press hot pressing, using press heat
The antitheft door shop front for being covered with veneer is sent into the press that temperature is 111 DEG C, pressure is 0.09MPa during pressure, it is compound through 39S hot pressing
Into the veneer facing antitheft door shop front；
6) antitheft door shop front surface is polished, repaired and repaiied after color processing, equilibrium moisture content to 11%, using multiple tracks
The technique of spray painting polishing, 180g/ ㎡ paint is sprayed on its surface；The technique of described multi-coat lacquer polishing includes polishing-wiping color
Color is repaiied to 59g/ ㎡-primer spray to 58g/ ㎡-polishing-spray to paint to 140g/ ㎡-polishing-topcoating to 140g/ ㎡；
7) to aluminum-alloy line molding powder, natural veneer coiled material is coated on aluminum-alloy line with lines coating machine, to day
Right veneer cladding lines surface veneer is polished, repaired and repaiied after color processing, equilibrium moisture content to 9%, using multi-coat lacquer
The technique of polishing, 180g/ ㎡ paint is sprayed on its surface；Lines after paint are spliced into lines frame with adhesive 45° angle；
8) lines frame is fixed on PUR glue or glass cement the edge of the recessed lattice of the veneer facing antitheft door shop front；Cloth glue amount
200g/㎡。
Embodiment 4
As shown in Figure 1, 2, veneer facing lines frame decorative anti-theft door, including the shop front 1, the shop front are manufactured using steel plate.Pass through
Steel plate enables to the shop front to have stronger rigidity, while reducing the timber required for the general shop front.The shop front includes the preceding shop front 11
With the rear shop front 12, added with making its internal substantial inserts 13 between the preceding shop front and the rear shop front.Described shop front surface passes through glue
Layer 2 is bonded with natural veneer 3 or recombinant decorative veneer, and glue-line is made up of adhesive, and adhesive is PUR glue, all-purpose adhesive, asphalt mixtures modified by epoxy resin
One kind in fat glue, polyurethane adhesive, adhesive PUR glue；Using outdoor wood wax oil, weather-proof PU paints, weather resistant water-thinned paint, F-C paint
Preferable color fastness to light grade can be obtained.
Natural veneer surface scribbles skin of paint 4.Described natural veneer includes several natural veneer chunks, natural veneer
Combined between chunk by piece gemel connection.The area of general door-plate will directly obtain respective area all than larger
Natural veneer is unpractical, costs rather expensive, therefore is easy to implement using multiple natural veneer chunks composition, is reduced simultaneously
Cost.Required according to the style of specific antitheft door and user, the length and width of veneer can be more than the size of the shop front, after redundance bending
For the faced deorative on shop front both sides, the outward appearance for the antitheft door that the shop front and shop front both sides are manufactured with same veneer overlay is more certainly
So, associative perception is stronger.Paint in skin of paint is using one kind in wood wax oil, PU paints, water paint, F-C paint.
The preceding shop front is provided with several recessed lattice 5, and described recessed lattice edge is provided with lines frame 43, and described lines frame includes outside line
Bar frame 44 and interior lines frame 45.Joint face 445 between described outer lines frame and interior lines frame is irregular joint face.
In a kind of production technology of above-mentioned veneer facing lines frame decorative anti-theft door, including step：
1) it is 0.3mm by thickness, moisture content carries out selection in 11.1% natural veneer, cuts out removal knot, white edge, lacks
The defect parts such as side, are combined into the width that antitheft door needs, according to natural veneer thickness, material not with splicing machine by natural veneer
Together, can natural veneer back side composite kraft paper or non-woven fabrics, make natural veneer not cracky, cracking；
2) recessed lattice are manufactured；By two pieces of steel plate bendings downward vertically, the both sides vertical bending upwards of one block of steel plate, upwards and to
Lower bending edges width is identical, and bending edges width is the depth of recessed lattice, then the parallel clasp joint of bending edges of three blocks of steel plates, to
The interior bending part of lower bending steel plate is welded and fixed groove；Or one block of steel plate is vertically rolled under recessed lattice depth direction with bender
It is curved, then to vertical bending before recessed lattice width, then to vertical bending on recessed lattice depth direction, finally vertical bending is made forward
Groove；Groove is divided into 1 recessed lattice with 2 pieces of horizontal cover plates；
3) the steel door-plate by stamped, bending, welding does oil removing, derusting, phosphorating treatment, is used separately as the front door of the shop front
Face and the rear shop front, by the preceding shop front after processing and rear shop front brush coating, centre adds honeycomb aluminum, honeycomb paper, anti-guncotton or expansion
After perlite welding, with the Hot gluing machine curing molding antitheft door shop front, make the shop front smooth indeformable；Plastic-spraying is done to the antitheft door shop front
Processing, further improves the bonding strength of veneer overlay；
4) to the glue amount of antitheft door shop front surface coating or glue spraying to 100g/ ㎡；
5) spliced natural veneer or recombinant decorative veneer are overlayed on to the surface of the antitheft door shop front and recessed lattice, according to the shop front
Moulding, size, Adhensive performance veneer overlay can using overlaying by hand, the method for roll-in or press hot pressing, using press heat
The antitheft door shop front for being covered with veneer is sent into the press that temperature is 110 DEG C, pressure is 0.091MPa during pressure, it is multiple through 40S hot pressing
Synthesize the veneer facing antitheft door shop front；
6) antitheft door shop front surface is polished, repaired and repaiied after color processing, equilibrium moisture content to 11%, using multiple tracks
The technique of spray painting polishing, 180.1g/ ㎡ paint is sprayed on its surface；The technique of described multi-coat lacquer polishing includes polishing-wiping
Color to 59.1g/ ㎡-primer spray to 58.1g/ ㎡-polishing-spray is repaiied color and painted to 140.1g/ ㎡-polishing-topcoating to 140.1g/
㎡；
7) to aluminum-alloy line molding powder, natural veneer coiled material is coated on aluminum-alloy line with lines coating machine, to day
Right veneer cladding lines surface veneer is polished, repaired and repaiied after color processing, equilibrium moisture content to 9.1%, is sprayed using multiple tracks
The technique for painting polishing, 180.1g/ ㎡ paint is sprayed on its surface；Lines screw after paint and connector 45° angle are spliced
Into lines frame；
8) lines frame is fixed on PUR glue or glass cement the edge of the recessed lattice of the veneer facing antitheft door shop front；Cloth glue amount
200.1g/㎡。
9) decoration is installed；Decoration is put into recessed lattice, is attached by 100.1g/ ㎡ glue amount and recessed lattice.
The preferred embodiment of invention is the foregoing is only, not to limit invention, all spiritual and originals in invention
Within then, any modification, equivalent substitution and improvements made etc. should be included within the protection domain of invention.
Claims (3)
1. a kind of production technology of veneer facing lines frame decorative anti-theft door, it is characterised in that including step：
1) it is 0.1-1mm by thickness, moisture content carries out selection in 6-12% natural veneer, cuts out removal knot, white edge, lacks side
Defect part, the width that antitheft door needs is combined into splicing machine by natural veneer, according to natural veneer thickness, the difference of material,
In the back side composite kraft paper or non-woven fabrics of natural veneer, make natural veneer not cracky, cracking；
2) recessed lattice are manufactured；By two pieces of steel plate bendings downward vertically, the both sides vertical bending upwards of one block of steel plate is rolled over up and down
Crimp width is identical, and bending edges width is the depth of recessed lattice, then the parallel clasp joint of bending edges of three blocks of steel plates, is rolled over downwards
The interior bending part of curved steel plate is welded and fixed obtained groove；Or one block of steel plate is vertically rolled under recessed lattice depth direction with bender
It is curved, then to vertical bending before recessed lattice width, then to vertical bending on recessed lattice depth direction, finally vertical bending is made forward
Groove, is used by the collocation of horizontal cover plate and perpendicular cover plate and groove is divided into some recessed lattice；
3) by stamped, bending, welding steel door-plate do oil removing, derusting, phosphorating treatment, be used separately as the shop front the preceding shop front and
The shop front, middle to add honeycomb aluminum, honeycomb paper, anti-guncotton or expanded pearlite by the preceding shop front after processing and rear shop front brush coating afterwards
After rock welding, with the Hot gluing machine curing molding antitheft door shop front, make the shop front smooth indeformable；
4) to the glue amount of antitheft door shop front surface coating or glue spraying to 40-200g/ ㎡；
5) spliced natural veneer or recombinant decorative veneer are overlayed on to the surface of the antitheft door shop front and recessed lattice, made according to the shop front
Type, size, Adhensive performance veneer overlay using overlaying by hand, the method for roll-in or press hot pressing, during using press hot pressing
The antitheft door shop front for being covered with veneer is sent into the press that temperature is 30 DEG C -120 DEG C, pressure is 0.01-0.5MPa, through 30S-
300S hot pressing is combined into the veneer facing antitheft door shop front；
6) antitheft door shop front surface is polished, repaired and repaiied after color processing, equilibrium moisture content to 6-12%, sprayed using multiple tracks
The technique for painting polishing, 150-600g/ ㎡ paint is sprayed on its surface；
7) to aluminum-alloy line molding powder, natural veneer coiled material is coated on aluminum-alloy line with lines coating machine, to natural thin
Wood cladding lines surface veneer is polished, repaired and repaiied after color processing, equilibrium moisture content to 6-12%, is beaten using multi-coat lacquer
The technique of mill, 150-600g/ ㎡ paint is sprayed on its surface；The lines screw and connector or 45 ° of adhesive after paint
Angle is spliced into lines frame；
8) lines frame is fixed on PUR glue or glass cement the edge of the recessed lattice of the veneer facing antitheft door shop front；Cloth glue amount 60-
300g/㎡；
9) decoration is installed；Decoration is put into recessed lattice, is attached by 30-200g/ ㎡ glue amount and recessed lattice.
2. the production technology of veneer facing lines frame decorative anti-theft door according to claim 1, it is characterised in that described
Step 3) in, plastic-spraying processing is done to the antitheft door shop front, the bonding strength of veneer overlay is further improved.
3. the production technology of veneer facing lines frame decorative anti-theft door according to claim 1, it is characterised in that described
Step 6) in, the technique of described multi-coat lacquer polishing includes polishing-wiping color to 50-100g/ ㎡-primer spray to 50-200g/
㎡-polishing-spray is repaiied color and painted to 50-150g/ ㎡-polishing-topcoating to 50-150g/ ㎡.