CN104674596A - Preparation method of touch paper - Google Patents
Preparation method of touch paper Download PDFInfo
- Publication number
- CN104674596A CN104674596A CN201510060705.7A CN201510060705A CN104674596A CN 104674596 A CN104674596 A CN 104674596A CN 201510060705 A CN201510060705 A CN 201510060705A CN 104674596 A CN104674596 A CN 104674596A
- Authority
- CN
- China
- Prior art keywords
- paper
- slurry
- coating
- agent
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of papermaking and in particular relates to a preparation method of a piece of touch paper. Compared with the prior art, the preparation method has the advantages that a new preparation technology and a new preparation formula are adopted, so that scratch resistance, water resistance and solvent resistance of the touch paper are improved, meanwhile, the working efficiency in a touch paper production process is improved, the overflow of waste is reduced, and the whole economic benefit of the touch paper is increased.
Description
Technical field
The present invention relates to pulp technology for making paper, is a kind of preparation method of sense of touch paper concretely.
Background technology
Sense of touch paper is the upgrade version of environmental protection paper for covering books, and by layer of surface coating, making paper surface have sub-photochromic coloured silk hand touch has fairly obvious silk or matte sensation, and has the anti-scratch solvent resistance of certain water resistant.Series of products are formed according to different colours, different lines.Not only can print but also can be gold stamping on the surface of paper, therefore be widely used in the surface material of senior notebook, picture album, gift box.Sense of touch paper has following three point patterns:
1, feel, cunning and exquisiteness, have obvious thick and heavy sense;
2, color is full, without the site vestige that intaglio plate stays, has class;
3, good weatherability, anti-scratch, folding, color-change resistant, light become, solvent resistance is good.
Sense of touch paper on the make will be manufactured paper with pulp through body paper, chromatograph coating, embossed, surface layer coating and complete processing this five steps, and the sense of touch paper prepared at present often has anti-scratch performance does not easily cause finished product to wear and tear by force, not folding easily produces explosion, natural daylight or light-illuminating variable color, become during product introduction and become paint face, solvent resistance is not by force when packages printing is produced, keep away problems such as unavoidably cleaning, so just cause semi-finished product when producing to be scrapped, expand loss.
The present invention a kind ofly can improve the operating efficiency of sense of touch paper and the preparation method of product quality sense of touch paper for this reason.
Summary of the invention
Instant invention overcomes the deficiencies in the prior art, provide and a kind ofly can improve the operating efficiency of sense of touch paper and the preparation method of product quality sense of touch paper.
In order to achieve the above object, the present invention devises a kind of manufacture method of sense of touch paper, comprise that body paper is manufactured paper with pulp, chromatograph coating, embossed and surface layer coating, it is characterized in that: described surface layer coating, comprises the steps:
Step 1, the preparation of finished surface coating in a reservoir, investment precoat is by weight ratio by the sense of touch resin of 30-50 part, the dumb light resin of 10-35 part, the water of 10-35 part, the auxiliary agent composition of 0-4 part, described auxiliary agent is levelling agent, defoamer and scratch resistance agent, described sense of touch resin is the water-based PU resin being furnished with elasticity powder, and dumb light resin is the aliphatic modified water-based PU resin of a kind of anion; Levelling agent is a kind of polyethers oxosilane copolymer; Defoamer is conventional water paint defoamer, silicone based surfactant, the surfactant of aliphatic alcohols, and ion-type is that anion or nonionic all can be used as defoamer, and scratch resistance agent is a kind of trifunctional group cross-linking agent;
Step 2, puts into embossed paper in Kohler coater, in employing material roller by through 200 eye mesh screens filter after investment precoat apply on paper, with airblade coating by coating weight control at 8-15g/m
2, utilize blast to be blown out by unnecessary coating at the air knife of 7-12kpa simultaneously, form coating, the one-tenth paper moisture after completing surface layer coating is dried to 4%-6% at the drying room of 110-130 DEG C by serviceability temperature afterwards, form sense of touch paper, and rolling is preserved.
Described body paper is manufactured paper with pulp, and comprises the steps:
Step 1, the preparation of slurry comprises the steps:
(1) ratio is selected to be the softwood pulp of 1:1 and hardwood pulp composition masson pine, described masson pine carries out fibration in hydrabrusher, then Fibrotic masson pine is delivered to upper storage stock tank one and carry out making beating process, in pulping process, the masson pine accomplished fluently is put into lower storage stock tank simultaneously, by pump for mortar transmission the masson pine accomplished fluently delivered in conical refiner and carry out defibrination, masson pine after defibrination forms slurry, slurry is delivered to upper storage stock tank two, recycling slurry position controls switch and slurry is put into lower storage stock tank, carry out repetition defibrination, until the beating degree of slurry reaches within the scope of 22-24 ° of SR, again deliver in storage stock tank two stand-by, and make the refining concentration of slurry remain on 3.5%-4.0%, form defibrination slurry,
(2) select dye formulation according to the demand of required dyeing, take dyestuff and color-fixing agent, re-using temperature is that dyestuff and color-fixing agent dissolve and heat preservation for standby use by the hot water of 90-95 DEG C in a reservoir completely, and color-fixing agent 10 times of water dilute stand-by; The consumption of described dyestuff is within the scope of 0.0-1.5%, and described color-fixing agent consumption is within the scope of 0.0-5.0%; Described dyestuff belongs to direct dyes type, and described color-fixing agent is a kind of cationic surfactant of resinous type;
(3) weigh relevant auxiliary agent and carry out dissolving or diluting in special container, and it is for subsequent use to form auxiliary material liquid, the consumption of various auxiliary material liquid is at 0.2%-3.0%; Described relevant auxiliary agent comprises sizing agent, aluminum sulfate, reinforcing agent, retention agent, and wherein sizing agent is primarily of emulsification rosin, alkyl ketene dimer, modified resin composition; Reinforcing agent, retention agent, mainly high molecular high molecular weight water soluble polymer and cationic starch type;
(4) first the slurry of milled is sent in pond with slurry, then the dye solution filtered through 200 eye mesh screens is slowly added in pond with slurry, powerful propeller is provided with in described pond with slurry, by propeller slurry fully mixed with dyestuff and maintain 10 minutes, then color-fixing agent liquid is added to end of dyeing, auxiliary material liquid slowly added in order in pond with slurry, auxiliary material order of addition is sizing agent, aluminum sulfate, reinforcing agent, retention agent again; Different auxiliary material adds and is spaced apart 5-10 minute, should first be filtered by 200 eye mesh screens before auxiliary material liquid adds.Keep pond with slurry concentration within the scope of 3.0%-3.5%, with slurry complete after formation slurry, slurry is delivered to and destroies forebay one and destroy forebay two;
Step 2, adopt consistencyregulator by the concentration dilution copying slurry in forebay two and be stabilized in about 1.5%, flow control valve is adopted to deliver in fan pump with constant slurry amount in the slurry of adjusted good concentration, the slurry that flow control valve is sent here by fan pump and recycle-water are diluted within the scope of 0.06%-0.20%, utilize the cushioning effect of slurry-stablizing case that pulp flow is carried out to the system of manufacturing paper with pulp process of manufacturing paper with pulp;
Step 3, treatment step of manufacturing paper with pulp is as follows:
(1) use two following currents in the net multi-cylinder paper machine of two gardens to overflow paddle garden net former, slurry enters in the net of garden that to utilize liquid level difference to carry out drainage shaping, and produce l Water Paper page, the online concentration of slurry is within the scope of 0.06%-0.20%;
(2) utilize a pair pressure roller in the net multi-cylinder paper machine of two gardens and carrying roller to be squeezed out by the portion of water of l Water Paper page, after squeezing, the moisture content of l Water Paper page is 60-65%;
(3) using many surface temperatures to carry out continuous drying to completing the l Water Paper page after squeezing for 70-115 DEG C of drying cylinder, making the one-tenth paper moisture after drying be 2%-4%;
(4) cooling cylinder is used to carry out ornamenting to one-tenth paper paper;
(5) the one-tenth paper after ornamenting is preserved as a roll formation reel and become paper.
Described chromatograph coating, comprises the steps:
Step 1, carry out the preparation of white material in a reservoir, described white material is by weight ratio by the water of 40-60 part, the kaolin of 15-40 part, the calcium carbonate of 0-30 part, the titanium dioxide of 0-20 part, the dispersant composition of 0.05-0.5 part, and the coating solids of the white material of composition is 40%-60%, in described white material, kaolin, calcium carbonate and titanium dioxide are coating rank, and its whiteness is greater than or equals 90 °, and powder granule is less than 2 μm, the content of powder granule is more than or equal to 90%, and described dispersant is the dispersant that aqueous pigment is conventional;
Step 2, the white material that chromatograph coating has been prepared by 25-45 part by weight ratio, the mill base of 0-20 part, the link stuff of 30-60 part, 0-20 part water is made in a reservoir, and the coating solids of the chromatograph coating prepared is 25%-50%, and described mill base is water color ink mill base, described link stuff is the synthetic resin emulsion that bond properties is good, such as emulsion acrylic resin or carboxylic styrene butadiene latex;
Step 3, carry out in coating machine chromatograph coating process, in coating machine, put into reel become paper, employings in material roller by through 200 eye mesh screens filtrations after chromatograph coating applying on paper, with airblade coating by coating weight control at 10-15g/m
2, utilize simultaneously blast 7-12kpa air knife by unnecessary coating blow out, formed coating, afterwards serviceability temperature 110-130 DEG C drying room by complete chromatograph coating after one-tenth paper moisture dry to 4%-6%, formed coated paper.
Described embossed, be first placed in embossing machine by the coated paper that rolling is preserved, and carry out damping to it, damping moisture is 5-10g/m
2, carry out embossing subsequently, utilize drying cylinder to be dried by the paper after embossing after embossing completes, and rolling form embossed paper.
The present invention compared with the existing technology, devise a kind of preparation method of sense of touch paper, have employed new preparation technology to fill a prescription with preparation, not only improve the resistance to scraping of sense of touch paper, WATER RESISTANCE and solvent resistance, improve the operating efficiency in sense of touch paper production process simultaneously, reduce the spilling of waste material, improve the economic benefit of sense of touch paper entirety.
Accompanying drawing explanation
Fig. 1 is that in the present invention, body paper is manufactured paper with pulp detail flowchart.
Fig. 2 is chromatograph coating in the present invention, embossing, surface layer coating and product handling system process chart.
Detailed description of the invention
By reference to the accompanying drawings to now the invention will be further described.
Embodiment 1: for red sense of touch paper:
The present invention devises a kind of manufacture method of sense of touch paper, comprise that body paper is manufactured paper with pulp, chromatograph coating, embossed and surface layer coating, described surface layer coating, comprises the steps:
Step 1, the preparation of finished surface coating in a reservoir, investment precoat is by the sense of touch resin of 30 parts, the dumb light resin of 40 parts, the water of 23.5 parts, 3.0 parts of levelling agents, 0.5 part of defoamer, 3.0 parts of scratch resistance agents compositions, described sense of touch resin is the water-based PU resin being furnished with elasticity powder, and dumb light resin is the aliphatic modified water-based PU resin of a kind of anion; Levelling agent is a kind of polyethers oxosilane copolymer; Defoamer is water paint defoamer; Scratch resistance agent is a kind of trifunctional group cross-linking agent;
Step 2, puts into embossed paper in Kohler coater, in employing material roller by through 200 eye mesh screens filter after investment precoat apply on paper, with airblade coating by coating weight control at 14g/m
2, utilize blast to be blown out by unnecessary coating at the air knife of 8kpa simultaneously, form the coating of smooth even, the one-tenth paper moisture after completing surface layer coating is dried to 5% at the drying room of 115 DEG C by serviceability temperature afterwards, form sense of touch paper, and rolling is preserved.
In the present invention, body paper is manufactured paper with pulp, and comprises the steps:
Step 1, the preparation of slurry comprises the steps:
(1) softwood pulp and the hardwood pulp composition whiteness that take each 500kg are high, intensity is good, the masson pine of Yi Shangran, described masson pine carries out fibration in hydrabrusher, then Fibrotic masson pine is delivered to upper storage stock tank one and carry out making beating process, in pulping process, the masson pine accomplished fluently is put into lower storage stock tank simultaneously, by pump for mortar transmission the masson pine accomplished fluently delivered in conical refiner and carry out defibrination, masson pine after defibrination forms slurry, slurry is delivered to upper storage stock tank two, recycling slurry position controls switch and slurry is put into lower storage stock tank, carry out repetition defibrination, until the beating degree of slurry reaches within the scope of 23 ° of SR, again deliver in storage stock tank two stand-by, and make the refining concentration of slurry remain on 3.8% formation defibrination slurry,
(2) select dye formulation according to the demand of red staining, accurately take dyestuff and color-fixing agent, re-using temperature is that dyestuff dissolves completely and heat preservation for standby use by the hot water of 95 DEG C in dye barrel, and color-fixing agent 10 times of water dilute stand-by; Described dyestuff is for redness and consumption is 28kg, and described color-fixing agent consumption is 28kg; Described dyestuff belongs to direct dyes type, and color-fixing agent is a kind of cationic surfactant of resinous type;
(3) auxiliary agent comprises sizing agent, aluminum sulfate, dry reinforcing agent and cationic starch, weigh auxiliary agent carry out dissolving in various special container, dilute stand-by, and form auxiliary material liquid, the consumption of described auxiliary agent is: sizing agent 20kg, aluminum sulfate 20kg, dry reinforcing agent is 30kg, and cationic starch is 10kg, and described sizing agent is emulsification rosin alkyl ketene dimer mainly; Dry reinforcing agent is high molecular high molecular weight water soluble polymer type reinforcing agent;
(4) first the slurry of milled is sent in pond with slurry, then by through 200 eye mesh screens filter dye solution at room temperature according to slowly adding pond with slurry, slurry is fully mixed with dyestuff, and continue dyeing 10 minutes, then auxiliary material liquid is sequentially added into again after adding color-fixing agent, keep the concentration of slurry with slurry 3.3%, with slurry complete after will complete slurry deliver to No. 1 and No. 2 destroy forebay, above-mentioned concentration with slurry refers to the percentage by weight of wood pulp material, described auxiliary material liquid addition sequence is sizing agent, aluminum sulfate, dry reinforcing agent, cationic starch and between each auxiliary material liquid drop into be spaced apart 8 minutes,
Step 2, adopt consistencyregulator that No. 2 are copied the concentration dilution of slurry in forebay and are stabilized in 1.5%, flow control valve is adopted to deliver in fan pump with constant slurry amount in the slurry of adjusted good concentration, the slurry that flow control valve is sent here by fan pump and a large amount of recycle-waters are diluted to 0.08%, utilize the cushioning effect of slurry-stablizing case by slurry reposefully stream deliver to the system of manufacturing paper with pulp and carry out process of manufacturing paper with pulp;
Step 3, treatment step of manufacturing paper with pulp is as follows:
(1) use two following currents in the net multi-cylinder paper machine of two gardens to overflow paddle garden net former, slurry enters in the net of garden that to utilize liquid level difference to carry out drainage shaping, and produce l Water Paper page, the online concentration of slurry is 0.08%;
(2) utilize a pair pressure roller in the net multi-cylinder paper machine of two gardens and carrying roller to be squeezed out by the moisture of l Water Paper page, become the l Water Paper page of moisture 63%;
(3) use many surface temperatures to carry out continuous drying to completing the l Water Paper page after squeezing for 70-115 DEG C of drying cylinder, make the one-tenth paper moisture after drying for the temperature of drying cylinder described in 3%. be raised to 115 DEG C gradually from 70 DEG C finally to get back to 100 DEG C with formation temperature curve;
(4) cooling cylinder is used to carry out ornamenting to one-tenth paper paper, smooth to improve paper;
(5) the one-tenth paper after ornamenting is preserved as a roll formation reel and become paper.
Described chromatograph coating, comprises the steps:
Step 1, carries out the preparation of white material in a reservoir, and described white material is by weight ratio by the water of 43 parts, the kaolin of 25 parts, the calcium carbonate of 15 parts, the titanium dioxide of 15 parts, the dispersant composition of 0.2 part, and the coating solids of the white material of composition is 51%, in described white material, kaolin, calcium carbonate and titanium dioxide are coating rank, and its whiteness is greater than or equals 90 °, and powder granule is less than 2 μm, be not less than 90% containing powder granule amount, described dispersant is the dispersant that aqueous pigment is conventional;
Step 2, the white material that chromatograph coating has prepared by 25 parts, the mill base of 18 parts, the link stuff of 45 parts, the water of 12 parts is made in a reservoir, and the coating solids of the chromatograph coating prepared is about 40%, and described mill base is water color ink mill base, described binder is the synthetic resin emulsion that bond properties is good, such as carboxylic styrene butadiene latex;
Step 3, carry out in coating machine chromatograph coating process, in coating machine, put into reel become paper, employings in material roller by through 200 eye mesh screens filtrations after chromatograph coating applying on paper, with airblade coating by coating weight control at 12g/m
2, utilize blast to be blown out by unnecessary coating at the air knife of 9kpa simultaneously, form the coating of smooth even, the one-tenth paper moisture after completing chromatograph coating is dried to 5% at the drying room of 115 DEG C by serviceability temperature afterwards, forms coated paper;
Described embossed, be first placed in embossing machine by the coated paper that rolling is preserved, and carry out damping to it, damping moisture is 7g/m
2, carry out embossing subsequently, utilize drying cylinder to be dried by the paper after embossing after embossing completes, and rolling form embossed paper.
The present invention devises a kind of preparation method of sense of touch paper, have employed new preparation technology to fill a prescription with preparation, not only improve the resistance to scraping of sense of touch paper, WATER RESISTANCE and solvent resistance, improve the operating efficiency in sense of touch paper production process simultaneously, reduce the spilling of waste material, improve the economic benefit of sense of touch paper entirety.
Claims (4)
1. a manufacture method for sense of touch paper, it is characterized in that comprising the steps: that body paper is manufactured paper with pulp, chromatograph coating, embossed and surface layer coating, it is characterized in that: described surface layer coating, comprises the steps:
Step 1, the preparation of finished surface coating in a reservoir, investment precoat is by weight ratio by the sense of touch resin of 10-40 part, the dumb light resin of 10-50 part, the water of 10-35 part, the auxiliary agent composition of 0-4 part, described auxiliary agent is levelling agent, defoamer and scratch resistance agent, described sense of touch resin is the water-based PU resin being furnished with elasticity powder, and described dumb light resin is the aliphatic modified water-based PU resin of a kind of anion; Described levelling agent is a kind of polyethers oxosilane copolymer; Described defoamer is water paint defoamer, and described scratch resistance agent is a kind of trifunctional group cross-linking agent;
Step 2, puts into embossed paper in Kohler coater, in employing material roller by through 200 eye mesh screens filter after investment precoat apply on paper, with airblade coating by coating weight control at 8-15g/m
2, utilize blast to be blown out by unnecessary coating at the air knife of 7-12kpa simultaneously, form coating, the one-tenth paper moisture after completing surface layer coating is dried to 4%-6% at the drying room of 110-130 DEG C by serviceability temperature afterwards, form sense of touch paper, and rolling is preserved.
2. the manufacture method of a kind of sense of touch paper as claimed in claim 1, is characterized in that described body paper is manufactured paper with pulp, comprises the steps:
Step 1, the preparation of slurry comprises the steps:
Ratio is selected to be that the softwood pulp of 1:1 and hardwood pulp make masson pine, masson pine is carried out fibration in hydrabrusher, then Fibrotic masson pine is delivered to upper storage stock tank one carry out making beating process and the masson pine accomplished fluently is put into lower storage stock tank, by pump for mortar transmission the masson pine accomplished fluently delivered in conical refiner and carry out defibrination, masson pine after defibrination forms slurry, slurry is delivered to upper storage stock tank two, recycling slurry position controls switch and slurry is put into lower storage stock tank, carry out repetition defibrination, until the beating degree of slurry reaches within the scope of 22-24 ° of SR, again deliver in storage stock tank two stand-by, and make the refining concentration of slurry remain on 3.5%-4.0%, form defibrination slurry,
Take dyestuff and color-fixing agent according to dye formulation, re-using temperature is that dyestuff and color-fixing agent dissolve completely and heat preservation for standby use by the hot water of 90-95 DEG C in dye barrel; Color-fixing agent is stand-by with 10 times of water dilutions, and the consumption of described dyestuff is within the scope of 0.0-5.0%, and described color-fixing agent consumption is within the scope of 0.0-5.0%; Described dyestuff belongs to direct dyes type, and described color-fixing agent is a kind of cationic surfactant of resinous type;
Weigh relevant auxiliary agent, carry out dissolving and diluting in special container, and form auxiliary material liquid, the consumption of described auxiliary material liquid is within the scope of 0.2%-3.0%; Described relevant auxiliary agent comprises sizing agent, aluminum sulfate, reinforcing agent, retention agent, and described sizing agent is made up of emulsification rosin, alkyl ketene dimer, modified resin; Described reinforcing agent, retention agent are made up of high molecular high molecular weight water soluble polymer and cationic starch;
First refined stock slurry is sent in pond with slurry, then the dye solution filtered through 200 eye mesh screens is added in pond with slurry, powerful propeller is provided with in described pond with slurry, by propeller slurry fully mixed with dyestuff and maintain 10 minutes, then color-fixing agent is added to end of dyeing, auxiliary material liquid slowly added in order in pond with slurry, described auxiliary material liquid order of addition is sizing agent, aluminum sulfate, reinforcing agent, retention agent again; Different auxiliary feed liquid adds and is spaced apart 5-10 minute, should first be filtered by 200 eye mesh screens before described auxiliary material liquid adds; Keep pond with slurry concentration within the scope of 3.0%-3.5%, with slurry complete after formation slurry, described slurry is delivered to and destroies forebay one and destroy forebay two;
Step 2, adopt consistencyregulator by the concentration dilution copying slurry in forebay two and be stabilized in 1.5%, flow control valve is adopted to deliver in fan pump in the slurry of adjusted good concentration, the slurry that flow control valve is sent here by fan pump and recycle-water are diluted within the scope of 0.06%-0.20%, utilize the cushioning effect of slurry-stablizing case that pulp flow is carried out to the system of manufacturing paper with pulp process of manufacturing paper with pulp;
Step 3, treatment step of manufacturing paper with pulp is as follows:
Use two following currents in the net multi-cylinder paper machine of two gardens to overflow paddle garden net former, slurry enters in the net of garden that to utilize liquid level difference to carry out drainage shaping, and produce l Water Paper page, the online concentration of slurry is within the scope of 0.06%-0.20%;
Utilize a pair pressure roller in the net multi-cylinder paper machine of two gardens and carrying roller to be squeezed out by the portion of water of l Water Paper page, after squeezing, the moisture of l Water Paper page is 60-65%;
Use surface temperature for 70-115 DEG C of drying cylinder to squeezing after l Water Paper page carry out continuous drying, make dry after one-tenth paper moisture be 2%-4%;
Cooling cylinder is used to carry out ornamenting to one-tenth paper paper;
One-tenth paper after ornamenting is preserved as a roll formation reel and become paper.
3. the manufacture method of a kind of sense of touch paper as claimed in claim 1, is characterized in that: described chromatograph coating, comprises the steps:
Step 1, carry out the preparation of white material in a reservoir, described white material is by weight ratio by the water of 20-50 part, the kaolin of 15-40 part, the calcium carbonate of 0-30 part, the titanium dioxide of 0-20 part, the dispersant composition of 0.05-0.5 part, and the coating solids of the white material of composition is 40%-60%, in described white material, kaolin, calcium carbonate and titanium dioxide are coating rank, and its whiteness is greater than or equals 90 °, and powder granule is less than 2 μm, the content of powder granule is more than or equal to 90%, and described dispersant is aqueous pigment common dispersants;
Step 2, the white material that chromatograph coating has been prepared by 25-45 part by weight ratio, the mill base of 0-20 part, the link stuff of 30-60 part, 0-20 part water is made in a reservoir, and the coating solids of the chromatograph coating prepared is 25%-50%, and described mill base is water color ink mill base, described link stuff is the synthetic resin emulsion that bond properties is good, such as emulsion acrylic resin or carboxylic styrene butadiene latex;
Step 3, carry out in coating machine chromatograph coating process, in coating machine, put into reel become paper, employings in material roller by through 200 eye mesh screens filtrations after chromatograph coating applying on paper, with airblade coating by coating weight control at 10-15g/m
2, utilize simultaneously blast 7-12kpa air knife by unnecessary coating blow out, formed coating, afterwards serviceability temperature 110-130 DEG C drying room by complete chromatograph coating after one-tenth paper moisture dry to 4%-6%, formed coated paper.
4. the manufacture method of a kind of sense of touch paper as claimed in claim 1, is characterized in that: described embossed is specific as follows, and be first placed in embossing machine by the coated paper that rolling is preserved, and carry out damping to it, damping moisture is 5-10g/m
2, carry out embossing subsequently, utilize drying cylinder to be dried by the paper after embossing after embossing completes, and rolling form embossed paper.