CN104671834A - Ceramic stained paper printing method - Google Patents
Ceramic stained paper printing method Download PDFInfo
- Publication number
- CN104671834A CN104671834A CN201310650666.7A CN201310650666A CN104671834A CN 104671834 A CN104671834 A CN 104671834A CN 201310650666 A CN201310650666 A CN 201310650666A CN 104671834 A CN104671834 A CN 104671834A
- Authority
- CN
- China
- Prior art keywords
- windrow
- ceramic
- ball milling
- parts
- marble paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a ceramic stained paper printing method. The ceramic stained paper printing method is characterized by comprising the following steps: firstly, preparing a windrow, namely, calcining a material at high temperature to be 1500 DEG C, then ball milling the calcined material for 24h, and filtering the material after ball milling to obtain the windrow; printing the windrow on a bottom paper by adopting a silk screen rendering mode, preparing a finished stained paper by adopting the silk screen rendering mode, adhering the finished stained paper to a ceramic body, and carrying out decorating firing at high temperature to be 1250-1300 DEG C to obtain a finished ceramic product, wherein the windrow is prepared from the following components in parts by weight: 38 parts of zirconia, 27 parts of feldspar, 8 parts of calcined talc and 3 parts of zinc oxide and is prepared by the following steps: mixing the components by virtue of a dry method, calcining for many times at the temperature of 1250-1300 DEG C into crushed blocks, ball milling for 24h, and filtering to obtain a powder, serving as the windrow. According to ceramic stained paper printing method disclosed by the invention, the windrow is printed on a membrane paper firstly and then colored with a primary color, so that a burnt ceramic product is strong in stained surface stereoscopic sense and bright in color.
Description
Technical field
The invention belongs to Ceramic Production technique, be specifically related to a kind of ceramic marble paper printing process.
Background technology
The printing process of traditional ceramics marble paper is first in film paper printed thereon pattern and color, then at pattern and color printed thereon windrow, its defect is: film paper is attached to after on ceramic body, in sintering procedure, a lot of color can disappear, the ceramic stereoscopic sensation burnt out is poor, color is beautiful not, and printing cost is high.
Summary of the invention
The present invention is intended to overcome the deficiencies in the prior art, provides a kind of ceramic marble paper printing process, and the ceramic flower face stereoscopic sensation through this method gained is strong, and color is beautiful.
Ceramic marble paper printing process of the present invention, technical scheme adopted for achieving the above object is: first prepare windrow, high temperature 1500 DEG C of calcined materials, then the material after ball milling calcining 24 hours, windrow is obtained again by after the filtration of material after ball milling, the mode adopting silk screen to play up on base stock afterwards prints windrow, then the mode adopting silk screen to play up produces finished product marble paper, finally finished product marble paper is attached on ceramic body and obtains finished product ceramic through 1250-1300 DEG C of high temperature decoration firing.
For reach in film paper, first print windrow after print the object of design and color, the present invention's windrow used is formed by component proportioning by following material:
Zirconium dioxide 30-50 part
Feldspar 20-40 part
Calcination of talc 4-15 part
Zinc oxide 1-6 part,
Above material is pressed component dry mixed, is repeatedly sintered into fragment through 1250-1300 DEG C, then ball milling 24h, sift out powder after filtering, windrow can be done and use.
Ceramic marble paper printing process of the present invention, film paper first prints windrow, after do primary colors, the ceramic burnt out like this, flower face stereoscopic sensation is strong, and color is beautiful.
embodiment:
embodiment 1
This ceramic marble paper printing process, first windrow is prepared, high temperature 1500 DEG C of calcined materials, then the material after ball milling calcining 24 hours, windrow is obtained again by after the filtration of material after ball milling, the mode adopting silk screen to play up on base stock afterwards prints windrow, and the mode then adopting silk screen to play up produces finished product marble paper, finally finished product marble paper is attached on ceramic body and obtains finished product ceramic through 1250-1300 DEG C of high temperature decoration firing.
Windrow used is formed by component proportioning by following material:
Zirconium dioxide 38 parts
Feldspar 27 parts
Calcination of talc 8 parts
3 parts, zinc oxide,
Above material is pressed component dry mixed, is repeatedly sintered into fragment through 1250-1300 DEG C, then ball milling 24h, sift out powder after filtering, windrow can be done and use.
embodiment 2
This ceramic marble paper printing process, first windrow is prepared, high temperature 1500 DEG C of calcined materials, then the material after ball milling calcining 24 hours, windrow is obtained again by after the filtration of material after ball milling, the mode adopting silk screen to play up on base stock afterwards prints windrow, and the mode then adopting silk screen to play up produces finished product marble paper, finally finished product marble paper is attached on ceramic body and obtains finished product ceramic through 1250-1300 DEG C of high temperature decoration firing.
Windrow used is formed by component proportioning by following material:
Zirconium dioxide 30 parts
Feldspar 20 parts
Calcination of talc 4 parts
1 part, zinc oxide.
Above material is pressed component dry mixed, is repeatedly sintered into fragment through 1250-1300 DEG C, then ball milling 24h, sift out powder after filtering, windrow can be done and use.
embodiment 3
This ceramic marble paper printing process, first windrow is prepared, high temperature 1500 DEG C of calcined materials, then the material after ball milling calcining 24 hours, windrow is obtained again by after the filtration of material after ball milling, the mode adopting silk screen to play up on base stock afterwards prints windrow, and the mode then adopting silk screen to play up produces finished product marble paper, finally finished product marble paper is attached on ceramic body and obtains finished product ceramic through 1250-1300 DEG C of high temperature decoration firing.
Windrow used is formed by component proportioning by following material:
Zirconium dioxide 50 parts
Feldspar 40 parts
Calcination of talc 15 parts
6 parts, zinc oxide.
Above material is pressed component dry mixed, is repeatedly sintered into fragment through 1250-1300 DEG C, then ball milling 24h, sift out powder after filtering, windrow can be done and use.
Claims (2)
1. a ceramic marble paper printing process, it is characterized in that: first prepare windrow, high temperature 1500 DEG C of calcined materials, then the material after ball milling calcining 24 hours, windrow is obtained again by after the filtration of material after ball milling, the mode adopting silk screen to play up on base stock afterwards prints windrow, and the mode then adopting silk screen to play up produces finished product marble paper, finally finished product marble paper is attached on ceramic body and obtains finished product ceramic through 1250-1300 DEG C of high temperature decoration firing.
2. a kind of ceramic marble paper printing process as claimed in claim 1, is characterized in that: windrow used is formed by component proportioning by following material:
Zirconium dioxide 30-50 part
Feldspar 20-40 part
Calcination of talc 4-15 part
Zinc oxide 1-6 part,
Above material is pressed component dry mixed, is repeatedly sintered into fragment through 1250-1300 DEG C, then ball milling 24h, sift out powder after filtering, windrow can be done and use.