CN104651014A - Anti-rust oil and preparation method thereof - Google Patents
Anti-rust oil and preparation method thereof Download PDFInfo
- Publication number
- CN104651014A CN104651014A CN201410263157.3A CN201410263157A CN104651014A CN 104651014 A CN104651014 A CN 104651014A CN 201410263157 A CN201410263157 A CN 201410263157A CN 104651014 A CN104651014 A CN 104651014A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- rust
- viscotrol
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-rust oil and a preparation method thereof and belongs to the technical field of metal rust prevention. The anti-rust oil is prepared from the following raw materials in parts by weight: 10 parts of castor oil, 20 parts of wool fat and 10 parts of Vaseline; the preparation method comprises the following steps: A, adding the castor oil to a reaction kettle for heating at a temperature ranging from 100 to 110 DEG C for 2-5 minutes; B, cooling the castor oil obtained in the step A to 46 degrees, adding the Vaseline and stirring thoroughly and evenly, and then adding the wool fat and stirring evenly, and cooling to obtain the anti-rust oil. The invention provides the anti-rust oil which is convenient to use, good in anti-rust effect, and natural and environmentally friendly, and the preparation method of the anti-rust oil.
Description
Technical field
The present invention relates to technical field of rust prevention, especially a kind of slushing oil and preparation method thereof.
Background technology
Mechanical workout usually uses various cubing and fixture in producing, after cubing and fixture use are over, their bubbles are deposited by people in machine oil, get rusty to prevent them, this antirust method also exists following problem: 1, must be used for holding machine oil with one or more larger container, occupation of land side and use inconvenience.2, because machine oil is synthetic, such as the fragrant same clan of organic compound wherein not only can rest on human lung, also can enter blood operation whole body, the hemopoietic system of interference people, neural system, not only can make people dizzy, feel sick, poor appetite, weak, blood of human body also can be caused sick; Iron is wherein active metal, can cause chronic inflammatory diseases in the respiratory tract and lung of people, and long this can cause pulmonary fibrosis, pulmonary emphysema etc.; And heavy metal is wherein as lead, cadmium etc. can at people's body accumulation, is difficult to discharge health, has a strong impact on neural system and cause human oral cavity ulcer, various focusing depths represented etc., very harmful to human body of therefore long-term contact machine oil.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of easy to use, favorable rust preventing effect and slushing oil of natural environmental-protective and preparation method thereof.
In order to solve the problem, the technical solution adopted in the present invention is: this slushing oil adopts the raw material of following parts by weight proportioning:
Viscotrol C 10 parts, 20 parts, lanolin, 10 parts, Vaseline;
Making step is:
A, to be joined in reactor by Viscotrol C and heat, temperature is 100 degree to 110 degree, 2 to 4 minutes time;
B, Viscotrol C obtained for steps A is cooled to 46 degree, adds Vaseline and stir, then add lanolin and stir, cooling both.
Owing to have employed technique scheme, the present invention compared with prior art has following beneficial effect:
1, because raw material of the present invention is natural animal and the raw material of plant, therefore nontoxic and natural environmental-protective its to human body fanout free region.
Viscotrol C of the present invention is that the mature seed of euphorbia plant castor-oil plant Ricinus communis L. is through squeezing and refining the fatty oil obtained.Uniquely to contain the commodity grease of hydroxyl through base acid.
Lanolin of the present invention is made up of multiple lanolin fatty acid, Wool wax alcohol, is the semi-solid grease of yellow gummy, is a kind of natural animal fat, mainly extracts from the waste liquid of washing wool.
Vaseline of the present invention, chemical name glycerol, performance is highly stable; Colourless, tasteless, transparent, nontoxic and have the gelatin liquid of water-repellancy.
2, heat owing to being joined in reactor by Viscotrol C, temperature is 100 degree to 110 degree, 2 to 4 minutes time; Moisture in Viscotrol C fully can be evaporated, ensure that obtained anti-purity of embroidering oil.
3, the slushing oil owing to making is pasty state, therefore only it need be spread upon on cubing or fixture, and can not run off, so easy to use, and favorable rust preventing effect.
Embodiment
Below in conjunction with embodiment, the invention will be further described:
Embodiment one
This slushing oil adopts the raw material of following weight:
Viscotrol C 10 kilograms, 20 kilograms, lanolin, 10 kilograms, Vaseline, gac 0.2 kilogram;
Making step is:
A, to be joined in reactor by Viscotrol C and heat, temperature is 110 degree, 2 minutes time;
B, Viscotrol C obtained for steps A is cooled to 46 degree, adds Vaseline and stir, then add lanolin and gac stirs, cool and get final product.
Embodiment two
This slushing oil adopts the raw material of following weight:
Viscotrol C 5 kilograms, 10 kilograms, lanolin, 5 kilograms, Vaseline, gac 0.1 kilogram;
Making step is:
A, to be joined in reactor by Viscotrol C and heat, temperature is 100 degree, 4 minutes time;
B, Viscotrol C obtained for steps A is cooled to 46 degree, adds Vaseline and stir, then add lanolin and gac stirs, cool and get final product.
Embodiment three
This slushing oil adopts the raw material of following weight:
Viscotrol C 20 kilograms, 40 kilograms, lanolin, 20 kilograms, Vaseline, gac 0.4 kilogram;
Making step is:
A, to be joined in reactor by Viscotrol C and heat, temperature is 105 degree, 3.3 minutes time;
B, Viscotrol C obtained for steps A is cooled to 46 degree, adds Vaseline and stir, then add lanolin and gac stirs, cool and get final product.
Claims (2)
1. a slushing oil, is characterized in that: the raw material comprising following parts by weight proportioning is made:
Viscotrol C 10 parts, 20 parts, lanolin, 10 parts, Vaseline.
2. a preparation method for slushing oil, is characterized in that: the raw material adopting following parts by weight proportioning:
Viscotrol C 10 parts, 20 parts, lanolin, 10 parts, Vaseline;
Making step is:
A, to be joined in reactor by Viscotrol C and heat, temperature is 100 degree to 110 degree, 2 to 4 minutes time;
B, Viscotrol C obtained for steps A is cooled to 46 degree, adds Vaseline and stir, then add lanolin and stir, cooling both.