CN104650923A - Liquid crystal composition and application thereof - Google Patents
Liquid crystal composition and application thereof Download PDFInfo
- Publication number
- CN104650923A CN104650923A CN201510082268.9A CN201510082268A CN104650923A CN 104650923 A CN104650923 A CN 104650923A CN 201510082268 A CN201510082268 A CN 201510082268A CN 104650923 A CN104650923 A CN 104650923A
- Authority
- CN
- China
- Prior art keywords
- carbonatoms
- fluorine
- substituted
- independently
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a liquid crystal composition comprising a cyclopropyl-containing liquid crystal compound. The cyclopropyl-containing liquid crystal compound not only has positive dielectric anisotropy (delta epsilon), proper optical anisotropy (delta n), proper clearing point (CP), good low-temperature intersolubility with other liquid crystal and low rotary viscosity, but also has good ultraviolet stability and high temperature stability. Moreover, the liquid crystal compound can solve the problems of weakening of alignment force, non-uniform display, light leak and the like caused in the present panel manufacturing process, and can improve the contrast and the response time of a TFT panel at a low temperature. The liquid crystal composition can be used for active matrix displays.
Description
Technical field
The invention belongs to field of application of liquid crystal, be specifically related to the application of a kind of liquid-crystal composition and this liquid-crystal composition.
Background technology
Since Austrian scientist Lai Nicier first time in 1888 has been synthesized liquid crystal, the real development of liquid crystal industry is the thing of nearly more than 30 years, because liquid crystal display material has obvious advantage, as driving voltage is low, power consumption is small, reliability is high, display contains much information, colored display, flicker free, flat pannel display etc. can be realized, liquid crystal monomer and liquid-crystal display all experienced by huge development, liquid crystal monomer has synthesized 10,000 plurality of liquid crystals materials at present, wherein conventional liquid crystal display material has thousands of kinds, classify by the center bridged bond of liquid crystal molecule and the feature of ring, mainly contain biphenyl liquid crystal, Santosol 360 liquid crystal, ester liquid crystal, alkynes class, difluoromethoxy bridge, ethane and heterocyclic etc.Liquid-crystal display also develops into TN-TFT, VA-TFT, IPS-TFT, PDLC etc. of present large color screen from TN, the STN of the black and white the small screen before 30 years.
Main novel liquid crystal display mode has optical compensation bending mode (OCB), coplanar transformation liquid-crystal display (IPS), vertical alignment mode (VA), rotational symmetry microstructure liquid-crystal display (ASM), the display of multidomain twisted liquid crystal etc.
The design of various display mode liquid crystal cell is different, type of drive is different, liquid crystal molecule director is different with glass substrate direction, optical compensation bending mode (OCB), coplanar transformation liquid-crystal display (IPS) liquid crystal molecule director are parallel with glass substrate direction, and vertical alignment mode (VA), rotational symmetry microstructure liquid-crystal display (ASM) is vertical with glass substrate direction without liquid crystal molecule director under electric field status.
The IPS of parallel arrangement mode, the dielectric anisotropy (△ ε) of liquid crystal both can be positive, also can be negative.
Vertical alignment mode (VA) all liquid crystal molecules are vertical with glass substrate direction when null field, with vertical incidence light ray parallel.When polaroid is orthogonal, can show good dark-state, so such device has good contrast gradient, the dielectric anisotropy (△ ε) using liquid crystal must be negative.The optical anisotropy (△ n) of liquid crystal, the thickness (d) of liquid crystal cell, the wavelength (λ) of incident light almost do not affect contrast gradient.The time of response of vertical alignment mode (VA) wants much shorter than meander configuration device, about being about half.Under applied voltages affect, the Bending Deformation of what VA device mainly produced is liquid crystal molecule, what ECB produced is the curved change of exhibition of liquid crystal molecule, and distortion display produces is the twist distortion of liquid crystal molecule, its time of response is also inversely proportional to bending, Zhan Qu, distortion elastic constant respectively, bend elastic constant due to most liquid crystal liquid crystal is in normal circumstances greater than the bent elastic constant of exhibition, and open up bent elastic constant and be greater than again distortion elastic constant, this is also VA response device time reason faster.
OLED adopts organic electro luminescent layer initiatively reflective as light source as a kind of emerging display format, panel can be made more frivolous simultaneously, can be reduced operating voltage simultaneously, and high temperature performance does not affect by the change of material.Its display black is purer simultaneously.But cause human eye directly to receive the stimulation of light source due to its active illuminating, long-time viewing can feel tired out, be unfavorable for health, and liquid crystal material well avoids light source irradiation eyes in liquid-crystal display, simultaneously by thinning backlight, its frivolous degree and OLED can be made to match in excellence or beauty with glass substrate, but due to the reason of liquid crystal material, impact by temperature is comparatively large, and simultaneously responsive to photo-thermal, process of alignment causes contrast gradient to be declined to become LCD short slab simultaneously
Cyclopropyl structure is applied to liquid crystalline cpd also has bibliographical information, but on the compounds property in document, defect is comparatively large, and such as structural stability is poor, viscosity is very large, synthesis difficulty is large, does not thus obtain practical application so far.
Summary of the invention
The invention provides a kind of liquid-crystal composition, by the component A containing cyclopropyl structure, and the B component of twin nuclei, realize at good low temperature intersolubility and low rotary viscosity, with the demand of high reliability aspect, simultaneously by two kinds of structure matchings, the degree of order of whole liquid crystal system is promoted, enhance the globality with liquid crystal arrangement, improve the uneven and light leak of display that liquid crystal panel easily produces in the fabrication process.
The invention provides a kind of liquid-crystal composition, described liquid-crystal composition comprises component A and B component, and described component A is made up of compound shown in one or more formula I, formula II and/or formula III,
Wherein, R
1represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5;
Y
1represent F, OCF independently of one another
3, CF
3, the halo carbonatoms alkyl that is 1-5, the halo carbonatoms alkoxyl group that is 1-5, halo carbonatoms be the alkene oxygen base of 2-5 or halo carbonatoms be the thiazolinyl of 2-5;
Y
2, Y
3represent H or F independently of one another;
Z
1, Z
2represent singly-bound ,-CF independently of one another
2o-,-CH
2cH
2-,-CH
2o-,-C ≡ C-,-OCH
2-or-OCF
2-;
represent one or two disjunct-CH in phenylene, cyclohexylidene or cyclohexylidene that phenylene, fluorine replace independently of one another
2-by-O-replace the group that formed;
N represents 0,1,2,3 or 4 independently of one another, and R
1institute's carbon atom quantity+n≤5;
Described B component is made up of compound shown in one or more formula IV
Wherein, R
2, R
3represent that the substituted or unsubstituted carbonatoms of fluorine is the alkyl of 1-5 independently of one another, the substituted or unsubstituted carbonatoms of fluorine is the alkoxyl group of 1-5, the substituted or unsubstituted carbonatoms of fluorine is the thiazolinyl of 2-5, and the substituted or unsubstituted carbonatoms of fluorine is the alkene oxygen base of 2-5.
Surprisingly, the liquid crystalline cpd containing cyclopropyl with structure shown in formula I feature not only has positive dielectric anisotropy (△ ε), the optical anisotropy (△ n) be applicable to, higher clearing point (CP), low temperature intersolubility that is good and other liquid crystal, low rotary viscosity, and have good in ultraviolet stability, to the stability of high temperature, and be easy to solve the orientation power caused in current panel manufacturing process weaken, display is uneven, light leak, improve TFT panel in the contrast gradient of low temperature-30 DEG C and time of response simultaneously.Thus be with a wide range of applications
Liquid-crystal composition provided by the present invention, preferred described component A is made up of two or more in compound shown in formula I, formula II and/or formula III.
Liquid-crystal composition provided by the present invention, all right preferred described component A is at least containing the compound contained by a kind of formula II.Further preferred described component A is also at least containing the compound shown in a kind of formula II I on this basis.
Shown in described formula I, compound is preferably compound shown in formula I-1 to formula I-6
Wherein, R
1represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5;
Y
1represent F, OCF independently of one another
3, CF
3, the halo carbonatoms alkyl that is 1-5, the halo carbonatoms alkoxyl group that is 1-5, halo carbonatoms be the alkene oxygen base of 2-5 or halo carbonatoms be the thiazolinyl of 2-5;
N expression independently of one another 0,1,2 or 3, and R
1institute's carbon atom quantity+n≤5.
Shown in described formula II, compound is preferably compound shown in formula II-1 to formula II-6
Wherein, R
1represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5;
Y
1represent F, OCF independently of one another
3, CF
3, the halo carbonatoms alkyl that is 1-5, the halo carbonatoms alkoxyl group that is 1-5, halo carbonatoms be the alkene oxygen base of 2-5 or halo carbonatoms be the thiazolinyl of 2-5;
Z
1independently represent singly-bound ,-CF separately
2o-,-CH
2cH
2-,-CH
2o-,-C ≡ C-,-OCH
2-or-OCF
2-
(F) F or H is represented independently of one another;
N expression independently of one another 0,1,2 or 3, and R
1institute's carbon atom quantity+n≤5.
Shown in described formula III, compound is preferably compound shown in formula III-1 to formula III-6
Wherein, R
1represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5;
Y
1represent F, OCF independently of one another
3, CF
3, the halo carbonatoms alkyl that is 1-5, the halo carbonatoms alkoxyl group that is 1-5, halo carbonatoms be the alkene oxygen base of 2-5 or halo carbonatoms be the thiazolinyl of 2-5;
Z
1independently represent singly-bound ,-CF separately
2o-,-CH
2cH
2-,-CH
2o-,-C ≡ C-,-OCH
2-or-OCF
2-
(F) F or H is represented independently of one another;
N expression independently of one another 0,1,2 or 3, and R
1institute's carbon atom quantity+n≤5.
Shown in described formula IV, compound is preferably compound shown in IV-1 to IV-4
Wherein, R
2represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5.
In described component A, the mass percentage that described formula II compound accounts for described liquid-crystal composition gross weight is preferably 5-70%.
In described component A, the mass percentage that compound shown in described formula I accounts for described liquid-crystal composition gross weight is preferably 30-95%.
Present invention also offers a kind of electro-optical display containing above-mentioned arbitrary described liquid-crystal composition.
Described electro-optical display is preferably VA indicating meter, IPS indicating meter, FFS indicating meter, TN indicating meter or OCB display.
Liquid-crystal composition provided by the present invention, realize at good low temperature intersolubility and low rotary viscosity, with the demand of high reliability aspect, simultaneously by two kinds of structure matchings, the degree of order of whole liquid crystal system is promoted, enhances the globality with liquid crystal arrangement.And based on the composition of this type, ring third ring own tension can be avoided excessive and the situation of self structure instability that causes occurs, the overall degree of order can also be improved under the help of twin nuclei simultaneously, and low-temperature performance, can improve at IPS., in TN, OCB display format, and the dark-state light leak that cause bad due to Liquid Crystal Molecules Alignment and the uneven situation of display occur.
Embodiment
Below in conjunction with specific embodiment, the present invention is further elaborated, but the present invention is not limited to following examples.Described method is ordinary method if no special instructions.Described raw material all can obtain from open commercial sources if no special instructions.Described per-cent if no special instructions, is mass percent.
In following embodiment,
CP represents clearing point, and directly use the micro-thermal analyzer of WRX-1S to measure, setting temperature rise rate is 3 DEG C/min.
Δ n represents optical anisotropy (589nm, 20 DEG C),
Δ ε represents dielectric anisotropy (25 DEG C, 1KHz, HP4284A, 5.2 microns of left-handed boxes of TN),
γ
1rotary viscosity (mpas) when representing 20 DEG C.VHR (%) represents electric charge conservation rate (5V, 60Hz, 20 DEG C); ρ (× 10
13Ω cm) represent resistivity (20 DEG C)
The tester of voltage retention VHR (%) and electricalresistivityρ (× 10
13Ω cm) be TOYO06254 and TOYO6517 type liquid crystal evaluation of physical property system (probe temperature 20 DEG C.Time 16ms testing cassete is 7.0 microns)
RT represents that response time tester device is DMS-501 (probe temperature 25 DEG C)
T stores (my god) at a set temperature, be stored to the time of partial crystallization, low temperature storage stability (-20 ,-30 ,-40 ,-50), testing cassete (7.0 microns)
T dark (%) represents transmitance during test darkest state.Test cell (3.3 microns) uses DMS-501
T bright (%) represents transmitance when testing most on state of.Test cell (3.3 microns) uses DMS-501
CR=T is bright/and T is dark
Be expressed as with following all temperature above DEG C, percentage ratio is that mass percent all values relates to 25 DEG C,
Embodiment 1
Comparative example 1
Comparative example 2
Time of response
RT | Embodiment 1 | Comparative example 1 | Comparative example 2 |
25 | 4.5V 25.36ms | 4.5V 31.25ms | 4.5V 37.26ms |
-20 | 4.5V 215ms | 4.5V 298.12ms | 4.5V 235.27ms |
-30 | 4.5V 350ms | 4.5V 415.26ms | 4.5V 430.03ms |
Low temperature stores
T stores | Embodiment 1 | Comparative example 1 | Comparative example 2 |
-20 | 42 days | 31 days | 9 days |
-30 | 42 days | 28 days | 6 days |
-40 | 42 days | 15 days | 1 day |
-50 | 42 days | 5 days | 1 day |
Reliability
Transmitance
Embodiment 1 | Comparative example 1 | Comparative example 2 | |
T is bright | 6.5029% | 6.3083% | 6.0151% |
T is dark | 0.0053% | 0.0081% | 0.0085% |
CR | 1226.96 | 778.80 | 707.66 |
As can be seen from embodiment, the mixture of this patent indication compares that to have low temperature reliability with other comparative example good, photo-thermal reliability is excellent, and time of response and contrast gradient significantly promote, and the advantage simultaneous contrast that rotary viscosity obviously reduces and dark-state brightness significantly improve.
Embodiment 2
Comparative example 3
Comparative example 4
Time of response
RT | Embodiment 2 | Comparative example 3 | Comparative example 4 |
25 | 4.5V 18.26ms | 4.5V 27.26ms | 4.5V 32.32ms |
-20 | 4.5V 189.18ms | 4.5V 253.28ms | 4.5V 222.17ms |
-30 | 4.5V 289.36ms | 4.5V 387.28ms | 4.5V 398.76ms |
Low temperature stores
Embodiment 2 | Comparative example 3 | Comparative example 4 | |
-20 | 42 days | 29 days | 15 days |
-30 | 42 days | 18 days | 10 days |
-40 | 42 days | 15 days | 1 day |
-50 | 42 days | 10 days | 1 day |
Reliability
Transmitance
Embodiment 2 | Comparative example 3 | Comparative example 4 | |
T is bright | 6.4042 | 6.3926 | 6.0512% |
T is dark | 0.0051 | 0.0085 | 0.0071% |
CR | 1255.73 | 752.07 | 852.28 |
As can be seen from embodiment, the mixture of this patent indication compares that to have low temperature reliability with other comparative example good, photo-thermal reliability is excellent, and time of response and contrast gradient significantly promote, and the advantage simultaneous contrast that rotary viscosity obviously reduces and dark-state brightness significantly improve.
Embodiment 3
Embodiment 4
Embodiment 5
Embodiment 6
Embodiment 7
Embodiment 8
Embodiment 9
Embodiment 10
Embodiment 11
From embodiment 1 ~ embodiment 11, this Nematic phase liquid crystal composition can maintain the fast time of response at low-temperature region, the use temperature of TN, IPS liquid crystal mode can be widened, and there is time of response and wider angular field of view faster, especially improve low-temperature performance, and have outstanding advantage in contrast gradient and reliability
Although the present invention only lists concrete material and the proportioning mass percent of above-mentioned 11 embodiments, and the performance of the liquid-crystal composition of composition is tested, but liquid-crystal composition of the present invention can on the basis of above-described embodiment, utilize general formula I involved in the present invention, II, III, IV, representative compound and general formula I, II, III, IV preferred compound expand further and revise, all can reach object of the present invention.
Claims (12)
1. a liquid-crystal composition, is characterized in that, described liquid-crystal composition comprises component A and B component, and described component A is made up of compound shown in one or more formula I, formula II and/or formula III,
Wherein, R
1represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5;
Y
1represent F, OCF independently of one another
3, CF
3, the halo carbonatoms alkyl that is 1-5, the halo carbonatoms alkoxyl group that is 1-5, halo carbonatoms be the alkene oxygen base of 2-5 or halo carbonatoms be the thiazolinyl of 2-5;
Y
2, Y
3represent H or F independently of one another;
Z
1, Z
2represent singly-bound ,-CF independently of one another
2o-,-CH
2cH
2-,-CH
2o-,-C ≡ C-,-OCH
2-or-OCF
2-;
represent one or two disjunct-CH in phenylene, cyclohexylidene or cyclohexylidene that phenylene, fluorine replace independently of one another
2-by-O-replace the group that formed;
N represents 0,1,2,3 or 4 independently of one another, and R
1institute's carbon atom quantity+n≤5;
Described B component is made up of compound shown in one or more formula IV
Wherein, R
2, R
3represent that the substituted or unsubstituted carbonatoms of fluorine is the alkyl of 1-5 independently of one another, the substituted or unsubstituted carbonatoms of fluorine is the alkoxyl group of 1-5, the substituted or unsubstituted carbonatoms of fluorine is the thiazolinyl of 2-5, and the substituted or unsubstituted carbonatoms of fluorine is the alkene oxygen base of 2-5.
2. liquid-crystal composition according to claim 1, is characterized in that, described component A is made up of two or more in compound shown in formula I, formula II and/or formula III.
3. ask the liquid-crystal composition described in 1 according to right, it is characterized in that, described component A is at least containing the compound contained by a kind of formula II.
4. ask the liquid-crystal composition described in 3 according to right, it is characterized in that, described component A is also at least containing the compound shown in a kind of formula II I.
5. according to described liquid-crystal composition arbitrary in claim 1-4, it is characterized in that, compound shown in described formula I is compound shown in formula I-1 to formula I-6
Wherein, R
1represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5;
Y
1represent F, OCF independently of one another
3, CF
3, the halo carbonatoms alkyl that is 1-5, the halo carbonatoms alkoxyl group that is 1-5, halo carbonatoms be the alkene oxygen base of 2-5 or halo carbonatoms be the thiazolinyl of 2-5;
N expression independently of one another 0,1,2 or 3, and R
1institute's carbon atom quantity+n≤5.
6. according to described liquid-crystal composition arbitrary in claim 1-4, it is characterized in that, compound shown in described formula II is compound shown in formula II-1 to formula II-6
Wherein, R
1represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5;
Y
1represent F, OCF independently of one another
3, CF
3, the halo carbonatoms alkyl that is 1-5, the halo carbonatoms alkoxyl group that is 1-5, halo carbonatoms be the alkene oxygen base of 2-5 or halo carbonatoms be the thiazolinyl of 2-5;
Z
1independently represent singly-bound ,-CF separately
2o-,-CH
2cH
2-,-CH
2o-,-C ≡ C-,-OCH
2-or-OCF
2-
(F) F or H is represented independently of one another;
N expression independently of one another 0,1,2 or 3, and R
1institute's carbon atom quantity+n≤5.
7. according to described liquid-crystal composition arbitrary in claim 1-4, it is characterized in that, compound shown in described formula III is compound shown in formula III-1 to formula III-6
Wherein, R
1represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5;
Y
1represent F, OCF independently of one another
3, CF
3, the halo carbonatoms alkyl that is 1-5, the halo carbonatoms alkoxyl group that is 1-5, halo carbonatoms be the alkene oxygen base of 2-5 or halo carbonatoms be the thiazolinyl of 2-5;
Z
1independently represent singly-bound ,-CF separately
2o-,-CH
2cH
2-,-CH
2o-,-C ≡ C-,-OCH
2-or-OCF
2-
(F) F or H is represented independently of one another;
N expression independently of one another 0,1,2 or 3, and R
1institute's carbon atom quantity+n≤5.
8., according to described liquid-crystal composition arbitrary in claim 1-7, it is characterized in that, compound shown in described formula IV is compound shown in IV-1 to IV-4
Wherein, R
2represent fluorine substituted or unsubstituted carbonatoms is the alkyl of 1-5, the substituted or unsubstituted carbonatoms of fluorine is 1-5 alkoxyl group independently of one another, alkene oxygen base that thiazolinyl that the substituted or unsubstituted carbonatoms of fluorine is 2-5, the substituted or unsubstituted carbonatoms of fluorine are 2-5.
9., according to described liquid-crystal composition arbitrary in claim 1-8, it is characterized in that, in described component A, the mass percentage that described formula II compound accounts for described liquid-crystal composition gross weight is 5-70%.
10., according to described liquid-crystal composition arbitrary in claim 1-8, it is characterized in that, in described component A, the mass percentage that compound shown in described formula I accounts for described liquid-crystal composition gross weight is 30-95%.
11. 1 kinds of electro-optical displays containing arbitrary described liquid-crystal composition in claim 1-10.
12. electro-optical displays according to claim 11, is characterized in that, described electro-optical display is VA indicating meter, IPS indicating meter, FFS indicating meter, TN indicating meter or OCB display.