CN104630511A - High-strength wear resistant complex brass melting technology - Google Patents
High-strength wear resistant complex brass melting technology Download PDFInfo
- Publication number
- CN104630511A CN104630511A CN201310549002.1A CN201310549002A CN104630511A CN 104630511 A CN104630511 A CN 104630511A CN 201310549002 A CN201310549002 A CN 201310549002A CN 104630511 A CN104630511 A CN 104630511A
- Authority
- CN
- China
- Prior art keywords
- melting technology
- technology
- complex brass
- wear resistant
- strength wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength wear resistant complex brass melting technology. The technology comprises the following steps: adopting a line-frequency cored induction furnace to melt alloy, wherein the alloy comprises 2.8-3.4% of Mn, 2.8-3.2% of Al, 0.7-1.1% of Si, 0.3-0.5% of Ni, 0.15-0.25% of Cr, 61-63% of Cu, and the balance of Zn; adding 2/3 of Cu; adding charcoal; fusing; sequentially adding Si, Mn, Cr, Al, 1/3 of Cu and Zn; stirring; adding cryolite; and extracting slag, and discharging. The technology is based on hot working, and has the advantages of short process flow and high added values. The inside of ingot blanks difficultly has slag inclusion, loosening, segregation and other defects, and has stable quality.
Description
Technical field
The invention belongs to the raw melting technology of brass, be specifically related to a kind of high-strength wearable complex brass melting technology.
Background technology
Brass is most important alloy kind in copper alloy, is world-famous for, is widely used in the every field of national economy with low-cost and high-performance.But people are widely used is for a long time market brass alloy, the less of application is studied to high zinc complex brass.High zinc complex brass because of its good performance applications more and more extensive.But its production is very high to the stability requirement of technique, and its performance depends on the accurate control of various Processes and apparatus, and therefore such alloy production technical difficulty is large.
Summary of the invention
In order to overcome the above-mentioned defect that prior art field exists, the object of the invention is to, a kind of high-strength wearable complex brass melting technology is provided, easy to operate.
High-strength wearable complex brass melting technology provided by the invention, adopt frequency cored induction furnace melting, alloying constituent is the Cu of Cr, 61-63% of Ni, 0.15-0.25% of Si, 0.3-0.5% of Al, 0.7-1.1% of Mn, 2.8-3.2% of 2.8-3.4%, surplus is zinc, material alloying order is for first to add 2/3Cu, add charcoal fusing, then add Si, Mn, Cr, Al, 1/3Cu, Zn successively, stir, add sodium aluminum fluoride, drag for slag and come out of the stove.
High-strength wearable complex brass melting technology provided by the invention, its beneficial effect is, based on hot-work, technical process is short, and added value is high.Ingot blank inside not easily produces the defects such as slag inclusion, loose, segregation, and internal soundness is more stable.
Embodiment
Below in conjunction with an embodiment, high-strength wearable complex brass melting technology provided by the invention is described in detail.
Embodiment
Adopt frequency cored induction furnace melting, alloying constituent is the Cu of Cr, 61-63% of Ni, 0.15-0.25% of Si, 0.3-0.5% of Al, 0.7-1.1% of Mn, 2.8-3.2% of 2.8-3.4%, surplus is zinc, material alloying order is for first to add 2/3Cu, add charcoal fusing, add Si, Mn, Cr, Al, 1/3Cu, Zn successively again, stir, add sodium aluminum fluoride, drag for slag and come out of the stove.
Claims (1)
1. a high-strength wearable complex brass melting technology, it is characterized in that: adopt frequency cored induction furnace melting, alloying constituent is the Cu of Cr, 61-63% of Ni, 0.15-0.25% of Si, 0.3-0.5% of Al, 0.7-1.1% of Mn, 2.8-3.2% of 2.8-3.4%, and surplus is zinc; Material alloying order, for first to add 2/3Cu, adds charcoal fusing, then adds Si, Mn, Cr, Al, 1/3Cu, Zn successively, stir, add sodium aluminum fluoride, drag for slag and come out of the stove.