CN104611801A - Aramid fiber 1313 blended high-temperature-resistant and flame-resistant material - Google Patents
Aramid fiber 1313 blended high-temperature-resistant and flame-resistant material Download PDFInfo
- Publication number
- CN104611801A CN104611801A CN201510072130.0A CN201510072130A CN104611801A CN 104611801 A CN104611801 A CN 104611801A CN 201510072130 A CN201510072130 A CN 201510072130A CN 104611801 A CN104611801 A CN 104611801A
- Authority
- CN
- China
- Prior art keywords
- fiber
- aramid fiber
- resistant
- weight portion
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an aramid fiber 1313 blended high-temperature-resistant and flame-resistant material. The aramid fiber 1313 blended high-temperature-resistant and flame-resistant material is blended by the following fibers in part by weight: 40-50 parts of aramid fibers 1313, 40-50 parts of acrylonitrile-vinylidene chloride copolymer fibers and 5-15 parts of flame-resistant cotton fibers. The aramid fiber 1313 blended high-temperature-resistant and flame-resistant material simultaneously has properties of the aramid fibers 1313, the acrylonitrile-vinylidene chloride copolymer fibers and the flame-resistant cotton fibers; and the high-temperature-resistant property and the flame-resistant property of the aramid fiber 1313 blended high-temperature-resistant and flame-resistant material are high.
Description
Technical field
The present invention relates to a kind of aramid fiber 1313 blending heat-resistant fireproof material, belong to Functional Chemical Fibers technical field.
Background technology
Along with improving constantly of people's living standard, the requirement of people to the comfortableness of dress is also more and more higher, people not only pursue beautiful outward appearance for fabric, fabric is also needed to possess other function, such as in some cases can anti-flaming thermal-insulation, this has higher requirement to the anti-flaming thermal-insulation function of fabric.
Aramid fiber 1313 is a kind of polyamide fiber.Be mainly used in the atomproof energy aspect such as radiation, high speed flight at high altitude material.Also can be used for the tire window line of particular/special requirement.Be mainly used in radiation proof dress material processed, space flight dress material, also for making high temperature resistant dress material, honeycomb product, high temperature spool, fuel tanker, fire wall, reverse osmosis membrane or doughnut etc.
Polyacrylic and polyester fiber is a kind of modified acrylic fibres, is that acrylonitrile monemer forms with the vinyl compound copolymerization containing ignition-proof element, has similar fleecy feel and high flame retardant, and have acidproof and chemically-resistant medicament.As a kind of functional fiber, in Japan and American-European countries, this fiber is widely used, for household textiles, protective garment fabric, decorative textile product material etc.
Flame-retardant cotton fiber is the microcellular structure utilizing cotton fiber to have, Ba^2+ iontophoretic injection is inner to cotton fiber. again with PO3^3-contacted with ions, phosphoric acid barium and phosphoric acid hydrogen barium crystalline deposit is generated in the micropore of cotton fiber, thus by phosphoric acid barium and phosphoric acid hydrogen barium particle assembling in the internal structure of cotton fiber, form inorganic particulate/cotton fiber composite.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art part, a kind of aramid fiber 1313 blending heat-resistant fireproof material is provided.
Aramid fiber 1313 blending heat-resistant fireproof material of the present invention, is formed by following fiber blend: aramid fiber 1313 40-50 weight portion, polyacrylic and polyester fiber 40-50 weight portion and flame-retardant cotton fiber 5-15 weight portion.
Described aramid fiber 1313 blending heat-resistant fireproof material is formed by llowing group of materials blending: aramid fiber 1313 45 weight portion, polyacrylic and polyester fiber 45 weight portion and flame-retardant cotton fiber 10 weight portion.
Prepare the method for aramid fiber 1313 blending heat-resistant fireproof material, it is characterized in that, step is as follows:
(1) blowing: raw material is made three kinds of volumes by scutcher;
(2) comb and parallel cotton fibers prior to spinning: three kinds of volumes are made the carded sliver respectively by carding machine;
(3) drafting: the different carded slivers is merged ripe bar by drawing frame;
(4) rove: the ripe bar merged is stretched oneself and yawn to attenuate and become rove bar by Speed frames;
(5) spun yarn: rove stretched oneself and yawn the yarn into certain number by fine spining machine;
(6) winder: by bobbin winder by spinning volume coning cheese;
(7) to weigh packing finished product.
Claims (3)
1. aramid fiber 1313 blending heat-resistant fireproof material, is characterized in that, is formed by following fiber blend: aramid fiber 1313 40-50 weight portion, polyacrylic and polyester fiber 40-50 weight portion and flame-retardant cotton fiber 5-15 weight portion.
2. aramid fiber 1313 blending heat-resistant fireproof material according to claim 1, is characterized in that, formed by llowing group of materials blending: aramid fiber 1313 45 weight portion, polyacrylic and polyester fiber 45 weight portion and flame-retardant cotton fiber 10 weight portion.
3. prepare the method for aramid fiber 1313 blending heat-resistant fireproof material as claimed in claim 1 or 2, it is characterized in that, step is as follows:
(1) blowing: raw material is made three kinds of volumes by scutcher;
(2) comb and parallel cotton fibers prior to spinning: three kinds of volumes are made the carded sliver respectively by carding machine;
(3) drafting: the different carded slivers is merged ripe bar by drawing frame;
(4) rove: the ripe bar merged is stretched oneself and yawn to attenuate and become rove bar by Speed frames;
(5) spun yarn: rove stretched oneself and yawn the yarn into certain number by fine spining machine;
(6) winder: by bobbin winder by spinning volume coning cheese;
(7) to weigh packing finished product.