CN104610887A - High performance carton adhesive - Google Patents
High performance carton adhesive Download PDFInfo
- Publication number
- CN104610887A CN104610887A CN201310541244.6A CN201310541244A CN104610887A CN 104610887 A CN104610887 A CN 104610887A CN 201310541244 A CN201310541244 A CN 201310541244A CN 104610887 A CN104610887 A CN 104610887A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive
- paper box
- performance adhesive
- dry starch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a high performance carton adhesive, which comprises, by weight, 75-85 parts of dry starch, 0.01-0.03 part of potassium permanganate, 0.01-0.03 part of borax, 7-15 parts of sodium hydroxide, 0.01-0.03 part of a catalyst, 0.001-0.002 part of a tackifier, and 4-8 parts of bentonite. According to the present invention, the high performance carton adhesive has the stable product performance, the cost is lower than the cost of the conventional sodium silicate, the use amount is reduced by 50-60%, the adhesion fastness is good, the moisture resistance is good, and the prepared product has the brittleness resistance; the adhesive does not produce the conditions such as the insufficient corrugating height, the thread drawing and the skinning, has characteristics of rapid drying, easy packaging, easy storage, east use, long shelf life, low cost and simple production process, and is suitable for the adhesion of a variety of carton products; and the adhesive preparation does not produce three-waste.
Description
Technical field
The invention belongs to adhesive field technical field, especially a kind of high-performance adhesive for paper box.
Background technology
Current domestic making carton, paper bag, the bonding of mulberry paper goods still generally uses sodium silicate or general amylan, the former used till today from the thirties, its alkalescence is large, after sticky paper because of the accumulation of salt in the surface soil moisture absorption, easy yellowing is come unstuck and stupefied, ultimate compression strength is little, the easy moldy metamorphism of in-built commodity or get rusty, include again alkali poison, food and daily life product adopt sodium silicate to seal sticky packaging, be detrimental to health, because of life-time service sodium silicate, hand is rotten poisoning aborning for workman, in use cost, sodium silicate is than great, easy precipitation, glue consumption is many, production cost is high, in order to overcome the above problems, recent year is proposed the amylan of liquid-type, although ultimate compression strength increases, the nonhygroscopic accumulation of salt in the surface soil, but production technique is more complicated, dry slow, easily collapse stupefied, cohesive strength is low, easy to crack, cost is high, storage period is extremely short, easily there is the deficiencies such as crisp folding in the carton of bonding, extensively cannot substitute sodium silicate.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art part, there is provided one to have not run stupefied, not wire drawing, not skinning, rate of drying be fast, packaging, storage, use all extremely convenient, storage period is long, and with low cost, the simple high-performance adhesive for paper box of production technique.
The technical scheme that the present invention realizes object is:
A kind of high-performance adhesive for paper box, its composition and parts by weight as follows:
Dry starch 75 ~ 85 parts, 0.01 ~ 0.03 part, potassium permanganate, borax 0.01 ~ 0.03 part, 7 ~ 15 parts, sodium hydroxide, catalyzer 0.01 ~ 0.03 part, tackifier 0.001 ~ 0.002 part, wilkinite 4 ~ 8 parts.
And the fineness requirement of each component of described high-performance adhesive for paper box is crossed 200 and is sieved.
And the preparation method of described high-performance adhesive for paper box is as follows:
After first potassium permanganate, borax, sodium hydroxide, catalyzer, tackifier, wilkinite being pulverized respectively, sieving, again sodium hydroxide fine powder is mixed obtained gelatinization dry starch with dry starch, again the fineness of potassium permanganate, borax, catalyzer, tackifier each component is added gelatinization dry starch successively to mix, obtain high-performance adhesive for paper box.
Advantage of the present invention and beneficial effect are:
The product performance of adhesive for paper box of the present invention are stablized, and cost is lower than traditional sodium silicate, and consumption reduces 50-60%; Bonding firmness is good, humidity resistance is good, finished product are crisp folding not easily, this tackiness agent does not run stupefied, not wire drawing, not skinning, rate of drying is fast, packaging, storage, uses all extremely convenient, and storage period is long, and it is with low cost, production technique is simple, and its preparation is suitable for the bonding of various box paper product without the generation of the three wastes.
Embodiment
Below by specific embodiment, the invention will be further described, and following examples are descriptive, is not determinate, can not limit protection scope of the present invention with this.
If no special instructions, the reagent used in the present invention is conventional reagent; If no special instructions, the method used is ordinary method.
Embodiment 1:
A kind of high-performance adhesive for paper box, its composition and parts by weight as follows:
Dry starch 75 parts, 0.01 part, potassium permanganate, borax 0.01 part, 7 parts, sodium hydroxide, catalyzer 0.01 part, tackifier 0.001 part, wilkinite 4 parts.
The fineness requirement of above-mentioned each component is crossed 200 and is sieved.
The preparation method of above-mentioned high-performance adhesive for paper box, step is as follows:
After first potassium permanganate, borax, sodium hydroxide, catalyzer, tackifier, wilkinite being pulverized respectively, sieving, again sodium hydroxide fine powder is mixed obtained gelatinization dry starch with dry starch, again the fineness of potassium permanganate, borax, catalyzer, tackifier each component is added gelatinization dry starch successively to mix, obtain high-performance adhesive for paper box.
Embodiment 2:
A kind of high-performance adhesive for paper box, its composition and parts by weight as follows:
Dry starch 80 parts, 0.02 part, potassium permanganate, borax 0.02 part, 11 parts, sodium hydroxide, catalyzer 0.02 part, tackifier 0.0015 part, wilkinite 6 parts.
The preparation method of above-mentioned high-performance adhesive for paper box is with embodiment 1.
Embodiment 3
A kind of high-performance adhesive for paper box, its composition and parts by weight as follows:
Dry starch 85 parts, 0.03 part, potassium permanganate, borax 0.03 part, 15 parts, sodium hydroxide, catalyzer 0.03 part, tackifier 0.002 part, wilkinite 8 parts.
The preparation method of above-mentioned high-performance adhesive for paper box is with embodiment 1.
Claims (3)
1. a high-performance adhesive for paper box, is characterized in that: its composition and parts by weight as follows:
Dry starch 75 ~ 85 parts, 0.01 ~ 0.03 part, potassium permanganate, borax 0.01 ~ 0.03 part, 7 ~ 15 parts, sodium hydroxide, catalyzer 0.01 ~ 0.03 part, tackifier 0.001 ~ 0.002 part, wilkinite 4 ~ 8 parts.
2. high-performance adhesive for paper box according to claim 1, is characterized in that: the fineness requirement of each component of described high-performance adhesive for paper box is crossed 200 and sieved.
3. high-performance adhesive for paper box according to claim 1 and 2, is characterized in that: the preparation method of described high-performance adhesive for paper box is as follows:
After first potassium permanganate, borax, sodium hydroxide, catalyzer, tackifier, wilkinite being pulverized respectively, sieving, again sodium hydroxide fine powder is mixed obtained gelatinization dry starch with dry starch, again the fineness of potassium permanganate, borax, catalyzer, tackifier each component is added gelatinization dry starch successively to mix, obtain high-performance adhesive for paper box.