CN104610576A - 一种塑胶用高流动性改性碳酸钙及其制备方法 - Google Patents

一种塑胶用高流动性改性碳酸钙及其制备方法 Download PDF

Info

Publication number
CN104610576A
CN104610576A CN201510013654.2A CN201510013654A CN104610576A CN 104610576 A CN104610576 A CN 104610576A CN 201510013654 A CN201510013654 A CN 201510013654A CN 104610576 A CN104610576 A CN 104610576A
Authority
CN
China
Prior art keywords
calcium carbonate
parts
minute
modified calcium
magnesium stearate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510013654.2A
Other languages
English (en)
Inventor
疏林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Yutang Rain Gear Co Ltd
Original Assignee
Anhui Yutang Rain Gear Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Yutang Rain Gear Co Ltd filed Critical Anhui Yutang Rain Gear Co Ltd
Priority to CN201510013654.2A priority Critical patent/CN104610576A/zh
Publication of CN104610576A publication Critical patent/CN104610576A/zh
Pending legal-status Critical Current

Abstract

一种塑胶用高流动性改性碳酸钙,由下列重量份的原料制成：碳酸氢钠0.3-0.4、氯化亚锡0.5-0.8、聚丙烯酸钠1-1.3、纳米铁矿渣2-3、棕榈酸异丙酯1-2、预胶化淀粉0.5-0.8、硬脂酸镁0.7-1、二氧化铈0.5-0.8、重质碳酸钙200-220、助剂5-9、水20-30；本发明的改性方法简单，碳酸钙改性均匀，通过添加氯化亚锡、棕榈酸异丙酯、预胶化淀粉、白糊精、硬脂酸镁，增加了碳酸钙的流动性、可压性，有利于在压片阶段，使片重均匀，同等条件下降低了片剂的尺寸；通过添加二氧化铈，能够增加塑胶的耐氧化和耐磨性能。

Description

一种塑胶用高流动性改性碳酸钙及其制备方法
技术领域
本发明属于塑胶领域，特别涉及一种塑胶用高流动性改性碳酸钙及其制备方法。
背景技术
塑胶应用非常广泛，是家电、汽车、手机、PC、医疗器械、照明电器中不可或缺的部件。近年来我国经济实现了持续稳定的增长，家电、汽车、手机、PC、医疗器械等行业受益于良好的外部环境也实现了快速发展，下游行业的发展进一步拉动了对塑胶的需求，但是和国外先进水平相比，我国合成树脂工业仍存在一定差距，国内一些高端产品数量不能满足市场需求，质量也有待改进和提高。目前塑胶存在的性能缺陷表现在耐磨性、耐老化、耐油、耐高温、强度、化学稳定性、弯曲强度、蠕变性能等方面，需要不断的改进。改进的途径有对原料、工艺的改进，还有就是通过添加填料进行改进，填料的性能从某种程度上改善了塑胶 的性能，所以研究填料的改进工艺很重要。
发明内容
本发明的目的在于提供一种塑胶用高流动性改性碳酸钙及其制备方法，该碳酸钙的流动性、可压性好，有利于在压片阶段，使片重均匀，同等条件下降低了片剂的尺寸，能够增加塑胶的耐氧化和耐磨性能。
本发明的技术方案如下：
一种塑胶用高流动性改性碳酸钙,其特征在于由下列重量份的原料制成：碳酸氢钠0.3-0.4、氯化亚锡0.5-0.8、聚丙烯酸钠1-1.3、纳米铁矿渣2-3、棕榈酸异丙酯1-2、预胶化淀粉0.5-0.8、硬脂酸镁0.7-1、二氧化铈0.5-0.8、重质碳酸钙200-220、助剂5-9、水20-30；
所述助剂由下列重量份的原料制成：硬脂酸镁0.2-0.3、癸二酸二辛酯0.2-0.3、乙撑双油酸酰胺0.4-0.6、氧化聚乙烯蜡0.3-0.5、妥尔油0.3-0.4、氧化石墨烯0.3-0.5、羊毛脂醇聚氧乙烯醚0.2-0.3、纳米二氧化钛2-3、聚酰胺蜡微粉0.2-0.3、聚氨酯丙烯酸酯0.3-0.5、烯丙基缩水甘油醚0.2-0.3、甲苯二异氰酸酯0.1-0.2、磷酸酯0.2-0.3、二缩三丙二醇二丙烯酸酯13-16；制备方法为：将聚氨酯丙烯酸酯、烯丙基缩水甘油醚加入至二缩三丙二醇二丙烯酸酯中，加热至50-55℃，搅拌20-30分钟，加入硬脂酸镁、癸二酸二辛酯、乙撑双油酸酰胺、氧化聚乙烯蜡、妥尔油、氧化石墨烯、羊毛脂醇聚氧乙烯醚、纳米二氧化钛、聚酰胺蜡微粉、磷酸酯，搅拌均匀后继续升温至70-80℃，搅拌反应30-40分钟，降温至35-40℃，再加入其他剩余成分，搅拌反应50-60分钟，即得。
所述的塑胶用高流动性改性碳酸钙的制备方法，其特征在于包括以下步骤：
（1）将碳酸氢钠、氯化亚锡、聚丙烯酸钠、二氧化铈加入水中，充分搅拌均匀，得到浆料；
（2）向重质碳酸钙吹70-80℃的热空气使其翻腾，再向翻腾的粉末中喷入雾状的第（1）步得到的浆料，使二者充分混合后，保持温度为70-80℃，继续翻腾30-40分钟；
(3)将第（2）步得到的混合物料烘干，加入高速捏合机中，加入其他剩余成分，再升温至110-120℃，保温捏合15-20分钟，再研磨成5-40μm的颗粒，即得。
本发明的有益效果
本发明的改性方法简单，碳酸钙改性均匀，通过添加氯化亚锡、棕榈酸异丙酯、预胶化淀粉、白糊精、硬脂酸镁，增加了碳酸钙的流动性、可压性，有利于在压片阶段，使片重均匀，同等条件下降低了片剂的尺寸；通过添加二氧化铈，能够增加塑胶的耐氧化和耐磨性能。
具体实施方式
一种塑胶用高流动性改性碳酸钙,由下列重量份(公斤)的原料制成：碳酸氢钠0.3、氯化亚锡0.7、聚丙烯酸钠1.2、纳米铁矿渣2.5、棕榈酸异丙酯1.5、预胶化淀粉0.7、硬脂酸镁0.9、二氧化铈0.6、重质碳酸钙210、助剂7、水25；
所述助剂由下列重量份（公斤）的原料制成：硬脂酸镁0.2、癸二酸二辛酯0.2、乙撑双油酸酰胺0.5、氧化聚乙烯蜡0.4、妥尔油0.3、氧化石墨烯0.4、羊毛脂醇聚氧乙烯醚0.2、纳米二氧化钛2.5、聚酰胺蜡微粉0.2、聚氨酯丙烯酸酯0.4、烯丙基缩水甘油醚0.2、甲苯二异氰酸酯0.2、磷酸酯0.2、二缩三丙二醇二丙烯酸酯15；制备方法为：将聚氨酯丙烯酸酯、烯丙基缩水甘油醚加入至二缩三丙二醇二丙烯酸酯中，加热至58℃，搅拌25分钟，加入硬脂酸镁、癸二酸二辛酯、乙撑双油酸酰胺、氧化聚乙烯蜡、妥尔油、氧化石墨烯、羊毛脂醇聚氧乙烯醚、纳米二氧化钛、聚酰胺蜡微粉、磷酸酯，搅拌均匀后继续升温至75℃，搅拌反应35分钟，降温至38℃，再加入其他剩余成分，搅拌反应55分钟，即得。
所述的塑胶用高流动性改性碳酸钙的制备方法，包括以下步骤：
（1）将碳酸氢钠、氯化亚锡、聚丙烯酸钠、二氧化铈加入水中，充分搅拌均匀，得到浆料；
（2）向重质碳酸钙吹75℃的热空气使其翻腾，再向翻腾的粉末中喷入雾状的第（1）步得到的浆料，使二者充分混合后，保持温度为75℃，继续翻腾35分钟；
(3)将第（2）步得到的混合物料烘干，加入高速捏合机中，加入其他剩余成分，再升温至115℃，保温捏合18分钟，再研磨成5-40μm的颗粒，即得。
实验数据：
将该实施例填料用于双组份聚氨酯塑胶跑道，添加量为10%，测得试验数据如下：
硬度（HS）: 55
抗拉强度（Mpa): 28
撕裂强度（Mpa):12
伸长率%： 277%
压缩永久变形率%:39%。

Claims (2)

1.一种塑胶用高流动性改性碳酸钙,其特征在于由下列重量份的原料制成：碳酸氢钠0.3-0.4、氯化亚锡0.5-0.8、聚丙烯酸钠1-1.3、纳米铁矿渣2-3、棕榈酸异丙酯1-2、预胶化淀粉0.5-0.8、硬脂酸镁0.7-1、二氧化铈0.5-0.8、重质碳酸钙200-220、助剂5-9、水20-30；
所述助剂由下列重量份的原料制成：硬脂酸镁0.2-0.3、癸二酸二辛酯0.2-0.3、乙撑双油酸酰胺0.4-0.6、氧化聚乙烯蜡0.3-0.5、妥尔油0.3-0.4、氧化石墨烯0.3-0.5、羊毛脂醇聚氧乙烯醚0.2-0.3、纳米二氧化钛2-3、聚酰胺蜡微粉0.2-0.3、聚氨酯丙烯酸酯0.3-0.5、烯丙基缩水甘油醚0.2-0.3、甲苯二异氰酸酯0.1-0.2、磷酸酯0.2-0.3、二缩三丙二醇二丙烯酸酯13-16；制备方法为：将聚氨酯丙烯酸酯、烯丙基缩水甘油醚加入至二缩三丙二醇二丙烯酸酯中，加热至50-55℃，搅拌20-30分钟，加入硬脂酸镁、癸二酸二辛酯、乙撑双油酸酰胺、氧化聚乙烯蜡、妥尔油、氧化石墨烯、羊毛脂醇聚氧乙烯醚、纳米二氧化钛、聚酰胺蜡微粉、磷酸酯，搅拌均匀后继续升温至70-80℃，搅拌反应30-40分钟，降温至35-40℃，再加入其他剩余成分，搅拌反应50-60分钟，即得。
2.根据权利要求1所述的塑胶用高流动性改性碳酸钙的制备方法，其特征在于包括以下步骤：
（1）将碳酸氢钠、氯化亚锡、聚丙烯酸钠、二氧化铈加入水中，充分搅拌均匀，得到浆料；
（2）向重质碳酸钙吹70-80℃的热空气使其翻腾，再向翻腾的粉末中喷入雾状的第（1）步得到的浆料，使二者充分混合后，保持温度为70-80℃，继续翻腾30-40分钟；
(3)将第（2）步得到的混合物料烘干，加入高速捏合机中，加入其他剩余成分，再升温至110-120℃，保温捏合15-20分钟，再研磨成5-40μm的颗粒，即得。
CN201510013654.2A 2015-01-12 2015-01-12 一种塑胶用高流动性改性碳酸钙及其制备方法 Pending CN104610576A (zh)