CN104609818A - 一种含硅酸锂高强度耐水加气砖及其制备方法 - Google Patents
一种含硅酸锂高强度耐水加气砖及其制备方法 Download PDFInfo
- Publication number
- CN104609818A CN104609818A CN201510017788.1A CN201510017788A CN104609818A CN 104609818 A CN104609818 A CN 104609818A CN 201510017788 A CN201510017788 A CN 201510017788A CN 104609818 A CN104609818 A CN 104609818A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- powder
- lithium silicate
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种含硅酸锂高强度耐水加气砖,由下列重量份的原料制成:煤矸石粉4-5、可再分散乳胶粉0.7-1、甲酸钙0.3-0.5、石膏7-9、粉煤灰50-60、加气铝粉6-7、水泥8-9、高炉灰4-6、生石灰9-11、改性煤灰7-8、硅粉6-8、硬脂酸0.6-1、硅酸锂0.8-1.2、水适量;本发明加气砖通过使用硅酸锂、可再分散乳胶粉,增加了加气砖的强度和耐水性,通过添加硅粉,增加了加气砖的耐磨性,同时该加气砖还具有良好的耐腐蚀性、耐火性、保温性、隔音性和尺寸稳定性;通过使用改性煤灰,增强了隔热效果,耐水性好,减少了环境污染,同时减水效果好。
Description
技术领域
本发明属于砖领域,尤其涉及一种含硅酸锂高强度耐水加气砖及其制备方法。
背景技术
加气砖也叫做加气混凝土砌块,应用非常的广泛,主要用在机械厂房和民用建筑中的墙体材料、填充墙、楼板和屋面板等承重墙材以及非承重材料和周围的填充围墙。
目前加气砖已成为建筑材料行业的主导产品,国家已经逐步禁止使用粘土实心砖,逐渐取而代之的就是加气混凝土砌块,蒸压砖。
加气砖具有重量轻、保温隔热性能好、抗震能力强、加工性能好、具有一定的耐高温性、隔音性能好、适应性强的特点,可根据当地不同原材料,不同条件来量身定造,原材料来源广泛,可选择河沙、粉煤灰、矿砂等,因地制宜,可以废物利用,有利环保,真正变废为宝。
但是随着建筑行业的发展,建筑物越来越高、造型越来越奇特,对加气砖的强度、密度、收缩值、抗冻性等要求都有所提高,另外随着人们生活水平的不断提高,对环境的要求也越来越高,对建筑物的保温性能、吸音性能、放射性都有更高的要求,甚至要求建筑物具有有益身体健康的性能,因此根据需要,研制更加性能优异的加气砖势在必行。
发明内容
本发明的目的在于提供一种含硅酸锂高强度耐水加气砖及其制备方法,该加气砖强度高,耐水性好,耐磨性好,还具有良好的耐腐蚀性、耐火性、保温性、隔音性和尺寸稳定性。
本发明的技术方案如下:
一种含硅酸锂高强度耐水加气砖,其特征在于由下列重量份的原料制成:煤矸石粉4-5、可再分散乳胶粉0.7-1、甲酸钙0.3-0.5、石膏7-9、粉煤灰50-60、加气铝粉6-7、水泥8-9、高炉灰4-6、生石灰9-11、改性煤灰7-8、硅粉6-8、硬脂酸0.6-1、硅酸锂0.8-1.2、水适量;
所述改性煤灰由下列重量份的原料制成:煤灰13-15、硅酸锂0.5-0.7、氟硅酸镁1-2、硬脂酸铝0.5-0.7、糖钙0.5-0.8、甲基丙烯酸缩水甘油酯0.5-0.7、偶氮二异丁腈0.1-0.2、丙烯酸酯1-1.3、茶籽饼1-2、泡沫玻璃粉1-2、聚羧酸高效减水剂2-3、双戊烯0.4-0.7、粉煤灰2-4、亚硫酸钙0.5-0.7、废机油2-3;制作方法为:将煤灰、茶籽饼粉碎成100-200目颗粒,边搅拌边喷入双戊烯、废机油、硬脂酸铝,混合均匀后放置5-7个小时,再与其他剩余成分混合,加热至75-80℃,分散研磨30-40分钟,即得。
所述的含硅酸锂高强度耐水加气砖的制备方法,其特征在于包括以下步骤:
(1)将煤矸石粉、水泥、硅粉、高炉灰、生石灰、石膏、粉煤灰混合,送入球磨机中研磨成100-200目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57-0.58加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;
(2)将第(1)步得到的浆料倒入模具中,得到砖胚体;
(3)将砖胚体放入蒸养釜进行抽真空,然后在1.7-1.9小时内均匀地通入蒸汽,使蒸养室内的温度升至170-180℃,压力达到11-13MPa,保持恒定10-11小时;
(4)在1.7-1.9小时内均匀地放出蒸汽,使蒸养室内的温度降至70℃以下,出釜,放置28-30天即得。
本发明的有益效果
本发明加气砖通过使用硅酸锂、可再分散乳胶粉,增加了加气砖的强度和耐水性,通过添加硅粉,增加了加气砖的耐磨性,同时该加气砖还具有良好的耐腐蚀性、耐火性、保温性、隔音性和尺寸稳定性;通过使用改性煤灰,增强了隔热效果,耐水性好,减少了环境污染,同时减水效果好。
具体实施方式
一种含硅酸锂高强度耐水加气砖,由下列重量份(公斤)的原料制成:煤矸石粉4.5、可再分散乳胶粉0.9、甲酸钙0.4、石膏8、粉煤灰55、加气铝粉6.5、水泥8.6、高炉灰5、生石灰10、改性煤灰7.5、硅粉7、硬脂酸0.8、硅酸锂1、水适量;
所述改性煤灰由下列重量份(公斤)的原料制成:煤灰14、硅酸锂0.6、氟硅酸镁1.5、硬脂酸铝0.6、糖钙0.6、甲基丙烯酸缩水甘油酯0.6、偶氮二异丁腈0.1、丙烯酸酯1.2、茶籽饼1.5、泡沫玻璃粉1.5、聚羧酸高效减水剂2.5、双戊烯0.6、粉煤灰3、亚硫酸钙0.6、废机油2.6;制作方法为:将煤灰、茶籽饼粉碎成160目颗粒,边搅拌边喷入双戊烯、废机油、硬脂酸铝,混合均匀后放置6个小时,再与其他剩余成分混合,加热至78℃,分散研磨36分钟,即得。
所述的含硅酸锂高强度耐水加气砖的制备方法,包括以下步骤:
(1)将煤矸石粉、水泥、硅粉、高炉灰、生石灰、石膏、粉煤灰混合,送入球磨机中研磨成160目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;
(2)将第(1)步得到的浆料倒入模具中,得到砖胚体;
(3)将砖胚体放入蒸养釜进行抽真空,然后在1.7小时内均匀地通入蒸汽,使蒸养室内的温度升至176℃,压力达到12MPa,保持恒定11小时;
(4)在1.8小时内均匀地放出蒸汽,使蒸养室内的温度降至70℃,出釜,放置29天即得。
实验数据:
该加气砖的密度为640kg/m3,耐火温度为700℃,导热系数为0.14W /(m·℃),采用淋浴喷头分别向240mm厚的粘土砖墙和加气砖墙喷淋,粘土砖墙12小时后全部浸透,加气砖墙喷淋72小时后渗水深度为50mm,抗压强度为 6.2Mpa,吸声系数0.4。
Claims (2)
1.一种含硅酸锂高强度耐水加气砖,其特征在于由下列重量份的原料制成:煤矸石粉4-5、可再分散乳胶粉0.7-1、甲酸钙0.3-0.5、石膏7-9、粉煤灰50-60、加气铝粉6-7、水泥8-9、高炉灰4-6、生石灰9-11、改性煤灰7-8、硅粉6-8、硬脂酸0.6-1、硅酸锂0.8-1.2、水适量;
所述改性煤灰由下列重量份的原料制成:煤灰13-15、硅酸锂0.5-0.7、氟硅酸镁1-2、硬脂酸铝0.5-0.7、糖钙0.5-0.8、甲基丙烯酸缩水甘油酯0.5-0.7、偶氮二异丁腈0.1-0.2、丙烯酸酯1-1.3、茶籽饼1-2、泡沫玻璃粉1-2、聚羧酸高效减水剂2-3、双戊烯0.4-0.7、粉煤灰2-4、亚硫酸钙0.5-0.7、废机油2-3;制作方法为:将煤灰、茶籽饼粉碎成100-200目颗粒,边搅拌边喷入双戊烯、废机油、硬脂酸铝,混合均匀后放置5-7个小时,再与其他剩余成分混合,加热至75-80℃,分散研磨30-40分钟,即得。
2.根据权利要求1所述的含硅酸锂高强度耐水加气砖的制备方法,其特征在于包括以下步骤:
(1)将煤矸石粉、水泥、硅粉、高炉灰、生石灰、石膏、粉煤灰混合,送入球磨机中研磨成100-200目颗粒,再与除加气铝粉之外的成分混合,按水料比为0.57-0.58加入水,搅拌均匀,再加入加气铝粉,搅拌均匀得到浆料;
(2)将第(1)步得到的浆料倒入模具中,得到砖胚体;
(3)将砖胚体放入蒸养釜进行抽真空,然后在1.7-1.9小时内均匀地通入蒸汽,使蒸养室内的温度升至170-180℃,压力达到11-13MPa,保持恒定10-11小时;
(4)在1.7-1.9小时内均匀地放出蒸汽,使蒸养室内的温度降至70℃以下,出釜,放置28-30天即得。