CN104593103B - 一种用于水煤浆的添加剂 - Google Patents

一种用于水煤浆的添加剂 Download PDF

Info

Publication number
CN104593103B
CN104593103B CN201410856457.2A CN201410856457A CN104593103B CN 104593103 B CN104593103 B CN 104593103B CN 201410856457 A CN201410856457 A CN 201410856457A CN 104593103 B CN104593103 B CN 104593103B
Authority
CN
China
Prior art keywords
water slurry
coal water
additive
reaction
aniline
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410856457.2A
Other languages
English (en)
Other versions
CN104593103A (zh
Inventor
凌江
闫芳
朱桂生
唐丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Haiqiao Chemical Co ltd
Original Assignee
Shanghai Haiqiao Chemical Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Haiqiao Chemical Co ltd filed Critical Shanghai Haiqiao Chemical Co ltd
Priority to CN201410856457.2A priority Critical patent/CN104593103B/zh
Publication of CN104593103A publication Critical patent/CN104593103A/zh
Application granted granted Critical
Publication of CN104593103B publication Critical patent/CN104593103B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于水煤浆的添加剂，按照质量百分比含量由：羧甲基纤维素为20～50％，聚马来酸酐磺化苯胺为3～20％，月桂酸有机锡为0.5～3％，磺化苯乙烯马来酸酐共聚物为20～50％，吐温80为0.5～3％，三聚磷酸钠为1～5％，乙二醇丁醚为5～10％组成。本发明具有良好的稳定性，能防止水煤浆的煤粒沉降，使水煤浆悬浮稳定性好，贮存时间长，制备方法简单，原料来源广泛，价格低廉，市场前景好。

Description

一种用于水煤浆的添加剂
技术领域
本发明属于煤炭能源应用技术领域，涉及一种添加剂，更具体是涉及一种用于水煤浆的添加剂。
背景技术
高浓度水煤浆作为现代化电站锅炉的新型流体燃料,越来越受到人们的关注。从1973年美国首先提出用水煤浆代替石油和天然气的设想以来,水煤浆就成为各国火力发电厂燃料研究方面的重要课题。美国、瑞典、加拿大、日本、联邦德国都进行了广泛的研究。水煤浆是70年代石油危机中发展起来的一种煤基流体燃料。它是由约70％左右的煤粉、29％左右的水和1％左右的化学添加剂组成的混合体。水煤浆是一种含有水和少量添加剂与煤粉组成的非牛顿流体。目前，研究的水煤浆是把煤炭粉碎成8％通过200目的煤粉的含水煤浆。它作为液体燃料,显示出固液分散系所特有的流动特性。其中水煤浆添加剂是制浆的关键组成部分。添加剂组合物有利于水煤浆的稳定性。传统的添加剂包括萘系、木质素系、腐植酸系以及聚羧酸系。这些体系不同程度解决了水煤浆分散、稳定、助燃等一些问题。但是，在使用这些体系过程中，仍然存在煤粒沉降，煤粉浓度不高，出现分层等稳定性不好的问题，导致煤燃烧不充分的问题。因而严重影响了水煤浆的广泛应用。
发明内容
本发明的目的是为了解决水煤浆在使用过程中，浆体稳定性差、煤粉浓度不高的问题，而提供一种用于水煤浆的添加剂。本发明添加能防止水煤浆的煤粒沉降，使水煤浆悬浮稳定性好，贮存时间长。
为达到上述目的，本发明实现目的采用的技术方案是：
一种用于水煤浆的添加剂，各组分的质量百分比含量为：
其中，所述磺化苯乙烯马来酸酐共聚物是指利用苯乙烯-马来酸酐共聚物与发烟浓硫酸反应的产物，其分子的结构为：
其中，m与n比为1：1，x为小于m与n的数值；
其中，所述的聚马来酸酐磺化苯胺是聚马来酸酐与氨基苯磺酸反应的产物，其分子结构为：
上述所述的磺化苯乙烯马来酸酐共聚物，是采用发烟浓硫酸与苯乙烯马来酸酐共聚物进行磺化反应的产物，其质量比为50：3，反应的温度为5小时，反应温度为60℃。
上述所述苯乙烯马来酸酐共聚物，其中苯乙烯与马来酸酐摩尔比为任意比，最优为1：1，其分子量为任意值，最优值为0.5-5万。
上述所述聚马来酸酐磺化苯胺是通过对氨基苯磺酸与聚马来酸酐反应的产物，其反应的物质聚马来酸酐与氨基苯磺酸反应质量比为100：8，反应温度为70℃，反应时间为5-6小时。
上述所述聚马来酸酐磺化苯胺是通过对氨基苯磺酸与聚马来酸酐反应的产物，其反应的物质聚马来酸酐的分子量为任意量，最优分子量为2300。
上述所述聚马来酸酐磺化苯胺是通过对氨基苯磺酸与聚马来酸酐反应的产物，其所述的氨基苯磺酸为邻位氨基苯磺酸或对位氨基苯磺酸，最优为对位氨基苯磺酸。
一种用于水煤浆的添加剂的制备方法，将上述所述组分按照比例称量，将组分中的液体组分混合均匀，然后加入固体组分搅拌均匀，最后包装，得到成品。
本发明的特点和有益效果
本发明的一种用于水煤浆的添加剂，具有良好的稳定性，能防止水煤浆的煤粒沉降，使水煤浆悬浮稳定性好，贮存时间长，制备方法简单，原料来源广泛，价格低廉，市场前景好。
具体实施方式
下面结合实施例对本发明作更进一步的详细说明。
实施例1：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法为：将上述组分按照比例称量，将配方组分中的液体组分混合均匀，然后加入固体组分搅拌均匀，得到水煤浆添加剂的带锈涂料的组合物，使用时依据需要加入5％的水进行施工。
实施例效果：稳定水煤浆时间为50天。
实施例2：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为70天。
实施例3：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为80天。
实施例4：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为60天。
实施例5：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为78天。
实施例6：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为100天。
实施例7：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为50天。
实施例8：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为50天。
实施例9：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为81天。
实施例10：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为87天。
实施例11：
一种用于水煤浆的添加剂，按质量百分比含量由如下组分制成：
制备方法同实施例1。
实施例效果：稳定水煤浆时间为105天。

Claims (6)

1.一种用于水煤浆的添加剂，其特征是，组成添加剂各组分的质量百分比含量为：
其中，所述磺化苯乙烯马来酸酐共聚物是指利用苯乙烯-马来酸酐共聚物与发烟浓硫酸反应的产物，其分子的结构为：
其中，m与n比为1：1，x为小于m与n的数值；
其中，所述的聚马来酸酐磺化苯胺是聚马来酸酐与氨基苯磺酸反应的产物，其分子结构为：
2.根据权利要求1所述的用于水煤浆的添加剂，其特征在于：所述的磺化苯乙烯马来酸酐共聚物是采用发烟浓硫酸与苯乙烯马来酸酐共聚物进行磺化反应的产物，其质量比为50：3，反应时间为5小时，反应温度为60℃；所述苯乙烯马来酸酐共聚物，其中苯乙烯与马来酸酐的摩尔比为任意比，其分子量为任意值。
3.根据权利要求2所述的用于水煤浆的添加剂，其特征在于：所述的苯乙烯与马来酸酐的摩尔比为1：1；所述的分子量为0.5-5万。
4.根据权利要求1所述的用于水煤浆的添加剂，其特征在于：所述聚马来酸酐磺化苯胺是通过氨基苯磺酸与聚马来酸酐反应的产物，其反应的物质聚马来酸酐与氨基苯磺酸反应质量比为100：8，反应温度为70℃，反应时间为5-6小时；所述聚马来酸酐的分子量为任意量。
5.根据权利要求4所述的用于水煤浆的添加剂，其特征在于：所述的聚马来酸酐的分子量为2300。
6.根据权利要求4所述的用于水煤浆的添加剂，其特征在于：所述的氨基苯磺酸为邻位氨基苯磺酸或对位氨基苯磺酸。
CN201410856457.2A 2014-12-29 2014-12-29 一种用于水煤浆的添加剂 Expired - Fee Related CN104593103B (zh)