CN104592266B - Two triazole cadmium nitrate title complex of oxygen ether with potential fluorescent material and preparation method thereof - Google Patents
Two triazole cadmium nitrate title complex of oxygen ether with potential fluorescent material and preparation method thereof Download PDFInfo
- Publication number
- CN104592266B CN104592266B CN201510088025.6A CN201510088025A CN104592266B CN 104592266 B CN104592266 B CN 104592266B CN 201510088025 A CN201510088025 A CN 201510088025A CN 104592266 B CN104592266 B CN 104592266B
- Authority
- CN
- China
- Prior art keywords
- triazole
- cadmium nitrate
- oxygen ether
- title complex
- phenyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses two triazole cadmium nitrate title complex of the oxygen ether with potential fluorescent material and preparation method thereof, wherein two triazole cadmium nitrate title complex { [Cd (the L) (NO of oxygen ether
3)] 3H
2o}? the structural motif of (<b>1</bGreatT.Gr eaT.GT) as shown in Figure 1.Also disclose { [Cd (L) (NO simultaneously
3)] 3H
2o}? (<b>1</bGreatT.Gr eaT.GT)? (L?=? 1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole) preparation method.It adopts " solvent-thermal method ", i.e. Cd (NO
3)
26H
2o, L, CHCl
3, CH
3oH and H
2is O 90?
ounder C, the colourless bulk crystals that room temperature obtains applicable X-ray single crystal diffraction is slowly down in reaction for three days afterwards.The present invention further discloses the application of the two triazole cadmium nitrate title complex of oxygen ether as potential fluorescent material aspect.
Description
The present invention obtains state natural sciences fund general project (21471113), young top-notch personnel's support plan, Tianjin Education Commission general project (20140506), Tianjin Normal University Middl-age and youth faculty Academic innovations advance planning item (52XC1401), the subsidy of Tianjin State Scientific and Technological Commission general project (11JCYBJC03600) and Tianjin innovation team of institution of higher education training plan (TD12-5038).
Technical field
The invention belongs to organic and Inorganic synthese technical field, relate to and state two triazole cadmium nitrate title complex { [Cd (the L) (NO of oxygen ether
3)] 3H
2the preparation method of O} (1) (L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole) and the application as potential fluorescent material.
Background technology
1,2,4-triazole and derivative thereof have the coordination feature of pyrazoles and imidazoles concurrently, are the bridgingligands that coordination ability is stronger, have synthesized at present and have characterized a large amount of monokaryons, multinuclear and multidimensional compound.These parts can with 1, nitrogen-atoms on 2 and metallic ion coordination form N1, N2-bridging pattern, for 4 unsubstituted 1,2,4-triazole derivative is by 2, nitrogen-atoms on 4 forms N2, N4-bridging pattern, this N2, N4-bridging pattern is with the N1 of imidazoles in metalloenzyme, and N3-bridging mode class seemingly.Special purpose for triazole class compounds also shows in the design of molecular device, and the metal complexes that synthesis has different dimension has been the vital step of device.
The present invention adopts " solvent-thermal method ", i.e. Cd (NO
3)
26H
2o, L, CHCl
3, CH
3oH and H
2o is 90
ounder C, colourless bulk crystals { [Cd (the L) (NO that room temperature obtains applicable X-ray single crystal diffraction is slowly down in reaction for three days afterwards
3)] 3H
2o} (1) (L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole).This title complex also can be used as potential fluorescent material aspect and is applied.
Summary of the invention
Another object of the present invention is to provide a kind of oxygen ether two triazole cadmium nitrate title complex { [Cd (L) (NO
3)] 3H
2o} (1) (L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole) monocrystalline and preparation method thereof.
Current inventor provides following technical scheme for this reason:
Two triazole cadmium nitrate title complex { [Cd (the L) (NO of oxygen ether
3)] 3H
2the structural motif of O} (1) (L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole) as shown in Figure 1.
The present invention further discloses two triazole cadmium nitrate title complex { [Cd (the L) (NO of oxygen ether
3)] 3H
2o} (1) (L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole) monocrystalline, it is characterized in that this single crystal structure adopts APEXIICCD single crystal diffractometer, use through graphite monochromatised Mok alpha-ray (λ=0.71073) be incident radiation, point diffraction is collected with ω-2 θ scan mode, obtain unit cell parameters through least-squares refinement, utilize SHELXL-97 direct method to solve single crystal data from difference Fourier electron density map:
The crystallographic data of table 1. title complex 1
Two triazole cadmium nitrate title complex { [Cd (the L) (NO of oxygen ether of the present invention
3)] 3H
2o} (1) (L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole) preparation method of monocrystalline, its feature is at employing " solvent-thermal method ", i.e. Cd (NO
3)
26H
2o, L, CHCl
3, CH
3oH and H
2o is 90
ounder C, reaction is slowly down to room temperature for three days afterwards to prepare this title complex
L。
The present invention's preferred example:
The preparation of 1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole (L)
Adopt " one kettle way " at polar solvent, by 4,4 '-dibromodiphenyl ether, 1H-1,2,4-triazole, salt of wormwood and cupric oxide are prepared in a heated condition; The wherein bromo-4-of 1-(4-bromine phenoxy group) benzene: 1H-1,2,4-triazole: salt of wormwood: the mol ratio of cupric oxide is 2:10:30:1;
4,4 '-dibromodiphenyl ether 1H-1,2,4-triazole
The present invention preferably 4,4 '-dibromodiphenyl ether: 1H-1,2,4-triazole: salt of wormwood: the mol ratio of cupric oxide is 2:10:30:1; Temperature of reaction 80-200 DEG C, reaction times 12-120 hour.In polar solvent, adopt " one kettle way ", by 4,4 '-dibromodiphenyl ether, 1H-1, this organic compound prepared in a heated condition by 2,4-triazole, salt of wormwood and cupric oxide;
Another preferred embodiment of the present invention
1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole (L) (0.1mmol), Cd (NO
3)
26H
2o (0.2mmo), CHCl
3(1mL), CH
3oH (8mL) and H
2o (1mL), is put in 23mL water heating kettle.90
oc heats and is slowly down to room temperature afterwards in three days, obtains the colourless bulk crystals of applicable X-ray single crystal diffraction after driving still.Productive rate: 20%.Ultimate analysis (C
32h
30cdN
14o
11) theoretical value (%): C, 42.75; H, 3.36; N, 21.81.Measured value: C, 42.71; H, 3.34; N, 21.77.
The present invention further discloses two triazole cadmium nitrate title complex { [Cd (the L) (NO of oxygen ether
3)] 3H
2o} (1) (L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole) can be used as potential fluorescent material aspect and is applied.
Two triazole cadmium nitrate title complex { [Cd (the L) (NO of a kind of oxygen ether disclosed by the invention
3)] 3H
2the advantage and disadvantage that O} (1) (L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole) monocrystalline has is:
(1) operation is simple and easy to do.
(2) reaction yield is high, and the purity of products obtained therefrom is high.
(3) { [Cd (the L) (NO prepared by the present invention
3)] 3H
2o} (1) (L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole) production cost is low, and method is easy, is applicable to scale operation.
Accompanying drawing explanation
Fig. 1: the crystalline structure primitive figure of title complex 1;
Fig. 2: the one-dimensional catenary structure figure of title complex 1.
Embodiment
Below in conjunction with embodiment, the present invention is described further, and embodiment is only indicative, never means that it limits the scope of the invention by any way.Raw materials used 4,4 '-dibromodiphenyl ether, 1H-1,2,4-triazole, salt of wormwood and cupric oxide etc. all have commercially available.All raw materials are all buy from chemical reagents corporation both domestic and external, through continuation purify but directly use.
Embodiment 1
4,4 '-dibromodiphenyl ether: 1H-1,2,4-triazole: salt of wormwood: the mol ratio of cupric oxide is 2:10:30:1
CuO (0.5mmol), salt of wormwood (15mmol), 1H-1 is added respectively in 50mL tri-mouthfuls of round-bottomed flasks that magneton, reflux exchanger and thermometer are housed, 2,4-triazole (5mmol), 4,4 '-dibromodiphenyl ether (1mmol) and 20mLDMF.Start and be stirred in 100
oc, reacts 24 hours.After reaction terminates, reaction solution is down to room temperature, filter, filtrate adds 100mL water, separate out a large amount of precipitation, suction filtration, collect filter cake 1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole (L).Yield 60%.
Embodiment 2
1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole (L) (0.1mmol), Cd (NO
3)
26H
2o (0.2mmo), CHCl
3(1mL), CH
3oH (8mL) and H
2o (1mL), is put in 23mL water heating kettle.90
oc heats and is slowly down to room temperature afterwards in three days, obtains the colourless bulk crystals of applicable X-ray single crystal diffraction after driving still.Productive rate: 20%.Ultimate analysis (C
32h
30cdN
14o
11) theoretical value (%): C, 42.75; H, 3.36; N, 21.81.Measured value: C, 42.71; H, 3.34; N, 21.77.Embodiment 3
Crystal structure determination adopts APEXIICCD single crystal diffractometer, use through graphite monochromatised Mok alpha-ray (λ=0.71073) be incident radiation, point diffraction is collected with ω-2 θ scan mode, unit cell parameters is obtained through least-squares refinement, software is utilized to solve crystalline structure from difference Fourier electron density map, and through Lorentz lorentz and polarizing effect correction.All H atom are synthesized by difference Fourier and are determined through desirable position calculation.Detailed axonometry data are in table 1.Structural motif is shown in Fig. 1, and one-dimensional catenary structure is shown in Fig. 2.
The crystallographic data of table 1. title complex 1
Embodiment 4
The concrete instance that dyestuff or luminous agent use
Method: the PARSTAT2273 electrochemical workstation of differentiated pulse volt-ampere (DPV) the curve negotiating Princeton Applied Research Laboratory development of dye solution is measured.The DPV test of solution adopts three-electrode system, and glass-carbon electrode is working electrode, and supporting electrode is platinum plate electrode, homemade Ag/AgNO
3electrode is reference electrode; Electrolytic solution is the acetonitrile solution of 0.1molL-1TBAP.Reduce reversible point to for interior mark with Oxidation of Ferrocene, obtains the correction value between test system and standard hydrogen electrode system.
Monochromatic incident light photoelectric transformation efficiency (IPCE) describes the photoelectric transformation efficiency of DSCs under monochromatic ray effect, is transfer to the electronic number of external circuit and the ratio of incident light subnumber.During measurement, use 500W xenon lamp as light source, the monochromatic ray of incident light under the multifunctional assembled grating spectrograph of WDS-5 type obtains different wave length λ; Monochromatic light exposure, in the light anode of battery, reads current value I by Keithley2400 digital sourcemeter.Monochromatic good fortune illumination is measured by USB4000plug-and-play Miniature optical linear light spectrometer.
Step: in order to definitely understand dyestuff at TiO
2adsorptive capacity on film, by dye sensitization TiO
2(geometric area is about 1cm to nanometer crystal film
2) be immersed in 10mL0.01molL
-1sodium hydroxide methanol solution in spend the night, treat that the absorbancy of attached mensuration solution separated completely by dyestuff.Wash one's face and rinse one's mouth according to absorbancy and molar absorptivity and can calculate the adsorptive capacity of dyestuff on unit surface nanometer crystal film.The adsorptive capacity of this title complex is 4.9 × 10
-4mol/cm
2.
Result: compared with the methanol solution of dyestuff, dyestuff is at TiO
2absorption spectrum on film all obviously broadens and red shift.This shows that dye molecule is at TiO
2define the J-aggregate of first also tail.From the principle of work of DSCs, the spectrum broadening that dye aggregation causes and red shift are very favourable for the widening of photoelectric response scope of dyestuff.But meanwhile, dye aggregation cognition reduces its electron injection efficiency greatly, thus causes the degraded performance of DSCs.So, in dye solution, usually add coadsorbent to suppress the gathering of dyestuff.This title complex is in methanol solution and at TiO
2the fluorometric investigation of the purple solution on membrane electrode adopts 2.5 × 10
-5the methanol solution of mol/L, maximum emission wavelength is positioned at 585nm.
After the preferred embodiment described in detail, be familiar with this technology personage can be well understood to, do not departing under above-mentioned claim and spirit and can carry out various change and amendment, all above embodiment is done according to technical spirit of the present invention any simple modification, equivalent variations and modification, all belong to the scope of technical solution of the present invention.And the present invention is not also by the restriction of example embodiment in specification sheets.
Claims (3)
1. the monocrystalline of the two triazole cadmium nitrate title complex of oxygen ether, it is characterized in that this single crystal structure adopts APEXIICCD single crystal diffractometer, use through graphite monochromatised Mok alpha-ray, λ=0.71073 is incident radiation, point diffraction is collected with ω-2 θ scan mode, obtain unit cell parameters through least-squares refinement, utilize software to solve single crystal data from difference Fourier electron density map:
Structure [Cd (the L) (NO of the two triazole cadmium nitrate complex monocrystal of oxygen ether
3)] 3H
2o: wherein L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole.
2. two triazole cadmium nitrate complex monocrystal [Cd (the L) (NO of oxygen ether described in claim 1
3)] 3H
2the preparation method of O, L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole, is characterized in that it adopts " solvent-thermal method ", i.e. Cd (NO
3)
26H
2o, L, CHCl
3, CH
3oH and H
2o is 90
ounder C, reaction is slowly down to room temperature for three days afterwards to prepare this title complex
L。
3. two triazole cadmium nitrate complex monocrystal [Cd (the L) (NO of oxygen ether described in claim 1
3)] 3H
2o, L=1-(4-(4-(1H-1,2,4-triazole-1-base) phenoxy group) phenyl)-1H-1,2,4-triazole is as the application of potential fluorescent material aspect.