CN104591659A - Rapidly hardening mortar for binding and jointing sticker mosaic tile - Google Patents
Rapidly hardening mortar for binding and jointing sticker mosaic tile Download PDFInfo
- Publication number
- CN104591659A CN104591659A CN201410809285.3A CN201410809285A CN104591659A CN 104591659 A CN104591659 A CN 104591659A CN 201410809285 A CN201410809285 A CN 201410809285A CN 104591659 A CN104591659 A CN 104591659A
- Authority
- CN
- China
- Prior art keywords
- mortar
- parts
- paster
- bonding
- joint filling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a rapidly hardening mortar for binding and jointing a sticker mosaic tile. The mortar comprises the following components in parts by weight: 300-480 parts of aluminate cement, 50-150 parts of ordinary Portland cement, 400-550 parts of sand, 30.0-70.0 parts of kaolin, 18.0-28.0 parts of rubber powder, 2.0-3.5 parts of cellulose ether, 1.0-2.0 parts of a water reducer, 3.0-6.0 parts of a water repellent and 0.4-1.0 part of a retarder. The rapidly hardening mortar disclosed by the invention has the advantages of high construction efficiency, strong bonding force and dense and full tile joint, is rapidly hardening and early strong and the like and is especially suitable for face tile facing engineering using sticker mosaic tile as the face tile.
Description
Technical field
The present invention relates to the fast rigid mortar of bonding for paster leatheroid brick and joint filling.
Background technology
Traditional paster leatheroid brick construction process is the sticking veneer being first layered on leatheroid brick with the Wall or floor tile tackiness agent mortar be stirred, and is then attached to metope, pats with strength, makes itself and base course wall paste jail, and mortar is poured in seam.Then with water, paper is fully wetting, observe the joint filling situation of brickwork joint, by brickwork joint insatiable hunger everywhere again row to squeegee compacting.Wholely surface-veneer engineeredly bring security-hidden trouble in order to avoid above-mentioned traditional method is given, following 4 problems must be solved:
1, during decorating surface brick engineering, the stickup dedicated mortar of face brick and each have their own operative norm of joint filling dedicated mortar and specific targets requirement, can not mutually replace, above-mentioned situation is exactly that tackiness agent instead of spackling.
2, paster leatheroid brick is before paper-tear picture, is soaked by leatheroid, could thoroughly be torn with a large amount of water, exposes whole finishing effect.Joint filling mortar is a kind of mortar of cement based, after the initial stage washes with water, is easy to the situation occurring the accumulation of salt in the surface soil.
3, workmen wash by water wetting while, mortar now does not reach certain intensity, be unable to undergo water punching, joint filling place only having torn paper to side brings damage in varying degrees, and is flushed to by mortar on brick face, finally causes a seam place mortar to be flushed away, stitch not full, brick is be rushed out the slurry come, the material such as grout, sand can be seen, cause the effect of whole finish coat to have a greatly reduced quality.
Although after 4 paper-tear pictures, carried out measure of squeegeeing, still had a large amount of places of squeegeeing not tamp, particularly in winter, rainwater passes through the not place of tamping and permeates inwards, and meeting freezing and expansion after low temperature, whole finish coat will produce the phenomenon of the brick that comes off.
Summary of the invention
In order to solve the problems of the technologies described above, the invention provides a kind of for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling.
Provided by the invention for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling, comprise the composition of following parts by weight:
Under two kinds of cementitious composite systems, mortar strength both can be made to stablize, fully effectively can absorb again the Free Ca that normal silicate aquation produces
2+, alkali burnout resistance can reach JC/T1024-2007 standard.Add sand, rubber powder, ether of cellulose, kaolin, water reducer and hydrophober in addition, play thickening function, give mortar plasticity-, can significantly improve the filling effect of mortar at brickwork joint place, make product have operating efficiency high, cohesive force is strong, brickwork joint is closely knit full, the advantages such as high-early-strength.Mortar belongs to fast gravity die mortar, after only adding retardant, just can ensure the engineering time of mortar.
Preferably, described aluminate cement is aluminate cement CA60.Aluminate cement CA60, hydration rate is fast, and early strength is high, and hydrated product not only can not produce Ca
2+, and the Ca of 42.5R ordinary Portland cement generation can be consumed
2+, reduce accumulation of salt in the surface soil risk.
Preferably, described ordinary Portland cement is 42.5R ordinary Portland cement.42.5R ordinary Portland cement not only has the feature of snap cure, with the use of aluminate cement CA60, can also improve the stability of mortar strength.
Preferably, described sand is particle diameter 70 ~ 120 object river sand.Use the river sand of this particle size range, the construction workability of mortar can be made to reach best, and wherein the river sand of fine grain size fully can fill the skeleton space that river, coarse grain footpath sand is formed.
Preferably, described kaolin is calcined kaolin, and kaolin take kaolinite as the clay of main component, and be a kind of inorganic salt, its main chemical compositions is Al
2o
3, SiO
2, have soapy feeling, be easily scattered in water.Also the Free Ca that hydrated cementitious produces can be consumed
2+.
Preferably, described hydrophober is Zinic stearas or calcium stearate.Stearate is one inherently water-fast salt material, adds in mortar, without the need to waiting until that mortar solidifies completely, just can significantly improve the hydrophobic nature of mortar.
Hydrophober is the water-intake rate reducing mortar, improves the hydrophobic nature at mortar initial stage.Water reducer can obviously reduce mortar mixing water, reduces porosity, makes mortar more closely knit, improves mortar strength.Both having respective function, is required composition.
Preferably, described retardant is citric acid.Citric acid not only can as cement setting retarder, and what ensure mortar can application property, also can improve the early strength of cement, not affect again the later strength of cement.
Preferably, above-mentioned for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling, the weight fraction of each composition is:
The present invention is as follows relative to the beneficial effect of prior art:
(1) by adding kaolin, under two kinds of cementitious composite systems, the Free Ca that normal silicate aquation produces can fully effectively be absorbed
2+, and can also thickening function, give mortar plasticity-, the filling effect of mortar at brickwork joint place can be significantly improved.
(2) fast rigid mortar except to have add water stir after can have the function of snap cure, also to ensure enough engineering times.According to the mortar obtained by instant component, the time before wall on paster leatheroid brick can either be ensured, also have leatheroid brick fixing after, under mortar no longer obtains External Force Acting, mortar can snap cure, and after 2 hours, ultimate compression strength can reach more than 3MPa, and joint filling place of having torn paper to side when can avoid washing by water wetting brings damage phenomenon in varying degrees, the slurry in seam can be avoided to be flushed to brick face, to pollute the phenomenons such as metope.
(3) to have operating efficiency high in the present invention, and cohesive force is strong, and brickwork joint is closely knit full, the advantages such as high-early-strength, and being specially adapted to facing is the decorating surface brick engineering adopting paster leatheroid brick.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described, can better understand the present invention and can be implemented, but illustrated embodiment is not as a limitation of the invention to make those skilled in the art.
Get kaolin, rubber powder, ether of cellulose, water reducer, retardant, hydrophober and first stir obtained core material, then core material and aluminate cement, ordinary Portland cement and sand are stirred and namely can be made into for 3 ~ 5 minutes.The concrete composition of each embodiment and consumption are see table 1.
Table 1
Embodiment 1-5, spackling Interventions Requested detect according to hydraulic cement base spackling CG1F fast in standard JC/T1004-2006; Inspection project detects according to snap cure coventional type cement-based adhesive C1F in JC/T547-2005; Can 3 be overcome difficulties, special detection " standard test condition 2h ultimate compression strength " this index in order to mortar of the present invention more can be embodied; Alkali burnout resistance project is according to standard JC/T1024-2007 standard detection.Detected result is in table 2.
Table 2
The above embodiment is only that protection scope of the present invention is not limited thereto in order to absolutely prove the preferred embodiment that the present invention lifts.The equivalent alternative or conversion that those skilled in the art do on basis of the present invention, all within protection scope of the present invention.Protection scope of the present invention is as the criterion with claims.
Claims (8)
1., for the bonding of paster leatheroid brick and a fast rigid mortar for joint filling, it is characterized in that, comprise the composition of following parts by weight:
2. according to claim 1ly it is characterized in that for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling, described aluminate cement is aluminate cement CA60.
3. according to claim 1ly it is characterized in that for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling, described ordinary Portland cement is 42.5R ordinary Portland cement.
4. according to claim 1ly it is characterized in that for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling, described sand is particle diameter 70 ~ 120 object river sand.
5. according to claim 1ly it is characterized in that for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling, described kaolin is calcined kaolin.
6. according to claim 1ly it is characterized in that for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling, described hydrophober is Zinic stearas or calcium stearate.
7. according to claim 1ly it is characterized in that for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling, described retardant is citric acid.
8. arbitrary described for the bonding of paster leatheroid brick and the fast rigid mortar of joint filling according to claim 1 ~ 7, it is characterized in that, the weight fraction of each composition is: