CN104589728B - Cold stamping solid medicinal composite hard sheet - Google Patents
Cold stamping solid medicinal composite hard sheet Download PDFInfo
- Publication number
- CN104589728B CN104589728B CN201410852827.5A CN201410852827A CN104589728B CN 104589728 B CN104589728 B CN 104589728B CN 201410852827 A CN201410852827 A CN 201410852827A CN 104589728 B CN104589728 B CN 104589728B
- Authority
- CN
- China
- Prior art keywords
- layer
- aluminium foil
- hard sheet
- composite hard
- urethane resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to cold stamping solid medicinal composite hard sheet, belong to acceptable packaging material technical field, including the aramid layer set gradually, aluminium foil layer, polyvinyl chloride layer, glue layer it is provided with between aluminium foil layer and polyvinyl chloride layer, the surface of aluminium foil layer includes aluminum phosphate thin film and rough layer, urethane resin layer and urethane resin layer it is coated with between aluminium foil layer and aramid layer on aluminium foil layer surface, maleic anhydride modified polyethylene layer and acrylic acid modified polyethylene layer also it is disposed with between aramid layer and aluminium foil layer, acrylic acid modified polyethylene layer and urethane resin layer, adhesive layer it is equipped with between aluminium foil layer and urethane resin layer, glue layer glue density is 4.9 5.1g/cm3, polyamide thickness 28 32 μm, aluminium foil thickness 48 53 μm, polrvinyl chloride thickness 52 58 μm, the gross thickness of described composite hard sheet is 140 143 μm.This composite hard sheet length in service life, steam, OTR oxygen transmission rate are little.
Description
Technical field
The invention belongs to acceptable packaging material technical field, press solidly particularly to a kind of cold punching
Body medicinal composite hard sheet.
Background technology
PVC plastic uptake and medical aluminum foil PTP is used to carry out heat seal in existing drug packaging industry
Packaging, there is the obstruct performance deficiency such as water vapour, oxygen, medicine, health product, food in PVC
The resting periods such as product are short, and the light transmission of PVC can not effectively intercept ultraviolet, and at purple
Outside line is the most aging under irradiating, and produces toxic gas.Although China's pharmaceuticals industry and health product,
Food service industry develops rapidly, and drug packing material have also been obtained and develops rapidly, but industry at present
The hot belt type cold stamping composite hard sheet structure of interior existence is nylon layer (both aramid layers), aluminum
Layers of foil, after molding, hot pressing seals with plastic uptake PVC, and this series products is easily made during cold stamping
Becoming causes aluminium foil layer damaged in layering and punching course between nylon layer and aluminium foil layer, and impact is produced
Product shelf-life and reduction production efficiency.Additionally, the material property in existing drug packing material
Typically, 3003 alloys or 8011 alloys are generally used such as the aluminium foil in drug packing material.With
The aluminium foil of 3003 alloy production, has good punching performance, but due to Mn in alloy
Constituent content is too high, and when carrying out homogenizing annealing, crystal grain is easily grown up, and is being rolled down to into
During product thickness, surface inevitably there will be coarse-grain striped, and impact is normal to be used.Another
Aspect, due to the characteristic of 3003 alloys self, the intensity of material is higher, to rolling equipment with
And the loss of punching device is relatively big, simultaneously need to add substantial amounts of copper, manganese metal, increase enterprise
The production cost of industry.With the tableware aluminium foil of 8011 alloy production, although 3003 can be overcome
The some shortcomings of alloy, but due in 8011 alloys alloying element content relatively low, but performance is inclined
Soft, be not suitable for high-speed punching, and the punching degree of depth is not enough, its range is by the biggest limit
System.
Summary of the invention
It is an object of the invention to there are the problems referred to above for existing technology, it is proposed that a kind of
Service life length, steam, OTR oxygen transmission rate reduce cold stamping solid medicinal composite hard
Sheet.
The purpose of the present invention can be realized by following technical proposal: a kind of cold stamping solid medicine
With composite hard sheet, including the aramid layer set gradually, aluminium foil layer, polyvinyl chloride layer, institute
Stating and be provided with a dry re-glue water layer between aluminium foil layer and described polyvinyl chloride layer, its feature exists
In, the surface of described aluminium foil layer includes aluminum phosphate thin film and rough layer, is coated with on aluminium foil layer surface
It is furnished with urethane resin layer and described urethane resin layer is positioned at aluminium foil layer and aramid layer
Between, also it is disposed with maleic anhydride modified between described aramid layer and described aluminium foil layer
Polyethylene layer and acrylic acid modified polyethylene layer, described acrylic acid modified polyethylene layer is with described
Adhesive layer it is equipped with between urethane resin layer, aluminium foil layer and urethane resin layer, described
The density of dry re-glue water layer glue is 4.9-5.1g/cm3, the thickness of described aramid layer is
28-32 μm, the thickness of aluminium foil layer is 48-53 μm, and the thickness of polyvinyl chloride layer is 52-58 μm,
The gross thickness of described cold stamping solid medicinal composite hard sheet is 140-143 μm.
In above-mentioned cold stamping solid medicinal composite hard sheet, as preferably, described aluminium foil layer aluminum
The composition of foil material and percentage by weight be: Si:0.35-0.50%, Fe:0.9-1.20%,
Cu:0.05-0.12%, Mn:0.50-0.60%, Mg:0.02-0.05%, Cr:0.02-0.05%,
Zn:0.02-0.05%, Ti:0.02-0.05%, Al surplus.
Component and content thereof, on the basis of 8011 alloys, have been carried out excellent by the present invention
Change, reduce Si constituent content, improve the content of Mn element, material can be improved
Intensity, simultaneously the most again with the Fe element of high-load, reduce Mn degree of supersaturation in aluminum,
Reduce the microsegregation of Mn, it is to avoid what aluminium foil crystal grain when homogenizing annealing was grown up shows
As.And reasonable compatibility other elements and content thereof, the advantage of having gathered 8011 alloys,
Not only increasing aluminium foil intensity, rupture strength, the rolling simultaneously also improving aluminium foil is stable
Property, production efficiency and yield rate, improve the surface quality of aluminium foil.
In above-mentioned cold stamping solid medicinal composite hard sheet, as preferably, described aluminium foil
Can prepare by the following method:
S1, melting, casting: according to described in above-mentioned aluminium foil composition and weight hundred
Proportion by subtraction weighs raw material, the raw material weighed is carried out at 730-760 DEG C melting, then enters
Row casting obtains blank, and the sotck thinkness after casting is 7.2 ± 0.3mm;
S2, homogenizing annealing: above-mentioned blank is carried out at 560-580 DEG C homogenizing annealing
Processing, isothermal holding is come out of the stove after 18-23 hour and is cooled to room temperature;
S3, cold rolling: the blank after cooling is carried out cold rolling, when rolling the first passage, processing
Rate is 60-80%, and back pass working modulus is maintained at 35-45%, through 5-6 passes
To carrying out intermediate annealing during 0.6-0.8mm under the conditions of 320-380 DEG C, it is incubated 25-28 hour;
S4, paper tinsel roll, and the aluminum strip after intermediate annealing are arrived through 2-3 passes
The aluminium foil of 0.20-0.26mm thickness.
In above-mentioned cold stamping solid medicinal composite hard sheet, as preferably, described adhesive layer
Binding agent be made up of each component of following weight percentage ratio: acetone: 25-32%;Chloroethene
Alkene-vinyl acetate-maleic terpolymer resin: 18-25%;Ethylene glycol-dimethyltrimethylene glycol-
The copolymer of terephthalate-last of the ten Heavenly stems diester: 30-40%;Polyurethane: 5-10%;Poly-carbon
Acid esters: 5-10%;Polyestercarbonate: 5-10%.
The shortcoming the most thoroughly overcoming existing non-environment-friendly adhesive, maintains again this medicine simultaneously
The comprehensive serviceability that product composite film for foods package is good, thus it is multiple to improve this well
Close the production technology quality grade of soft packing material product, achieve good environment protection modification effect.
In above-mentioned cold stamping solid medicinal composite hard sheet, as preferably, described adhesive
The binding agent of layer can prepare by the following method: makees solvent with acetone, add vinyl chloride-
Vinyl acetate-maleic terpolymer resin is as main body adhesion substance, at 55-65 DEG C
In temperature range, stirring is to being completely dissolved, and adds ethylene glycol-dimethyltrimethylene glycol-to benzene two
The copolymer of formic acid esters-last of the ten Heavenly stems diester and polyurethane, Merlon, polyestercarbonate, mixing
Uniformly form.
Compared with prior art, the invention have the advantages that
1, inter-layer bonding force increases, and steam, OTR oxygen transmission rate reduce, and barrier property increases
Greatly, global formation performance improves;Can with stable prod quality, extend product service life and
Improving product security performance.
2, maleic anhydride modified polyethylene layer and the acrylic acid extruded by coextrusion mode is changed
Property polyethylene layer, not only have and have higher with each accompanying aluminium foil layer, aramid layer
Peel strength, and whole extruding layer is soft, toughness is strong, has high hot strength
And elongation at break, the aluminum that can effectively prevent product to be likely to occur during cold stamping split and
The problems such as absciss layer.
3, aluminum foil material is on the basis of 8011 alloys, enters component and content thereof
Go optimization, reduced Si constituent content, improve the content of Mn element, Ji Nengti
The intensity of high material, the most again with the Fe element of high-load, reduces Mn mistake in aluminum
Saturation, reduces the microsegregation of Mn, it is to avoid aluminium foil crystal grain when homogenizing annealing
The phenomenon grown up, and reasonable compatibility other elements and content thereof, gathered 8011 alloys
Advantage, not only increase aluminium foil intensity, rupture strength, also improve aluminium foil simultaneously
Rolling stability, production efficiency and yield rate, improve the surface quality of aluminium foil.
4, the binding agent of adhesive phase is by its composition of reasonable compatibility, compounding interpolation polyurethane,
Merlon, polyestercarbonate, improve the thermal property of binding agent and engineering properties and good
Tack, and ensure the impact of binding agent and the balance of mobility.
Accompanying drawing explanation
Fig. 1 is the structural representation of the present invention.
In figure, 1, aramid layer;2, aluminium foil layer;3, polyvinyl chloride layer;4, dry multiple
Glue layer;5, urethane resin layer;6, maleic anhydride modified polyethylene layer;7, propylene
Acid modified poly ethylene layer;8, adhesive layer.
Detailed description of the invention
The following is the specific embodiment of the present invention and combine accompanying drawing, the technical side to the present invention
Case is further described, but the present invention is not limited to these embodiments.
As it is shown in figure 1, this cold stamping solid medicinal composite hard sheet includes the polyamides set gradually
Amine layer 1, aluminium foil layer 2, polyvinyl chloride layer 3, between aluminium foil layer 2 and described polyvinyl chloride layer 3
Being provided with a dry re-glue water layer 4, the surface of aluminium foil layer 2 includes aluminum phosphate thin film and rough layer,
It is coated with urethane resin layer 5 on aluminium foil layer 2 surface and described urethane resin layer 5 is positioned at
Between aluminium foil layer 2 and aramid layer 1, also depend between described aramid layer 1 and described aluminium foil layer 2
Secondary it is provided with maleic anhydride modified polyethylene layer 6 and acrylic acid modified polyethylene layer 7, acrylic acid
Between modified poly ethylene layer 7 and urethane resin layer 5, aluminium foil layer 2 and urethane resin layer 5 all
Being provided with adhesive layer 8, the density of described dry re-glue water layer 4 glue is 4.9-5.1g/cm3, institute
The thickness stating aramid layer 1 is 28-32 μm, and the thickness of aluminium foil layer 2 is 48-53 μm, polychlorostyrene
The thickness of pvdf layer 3 is 52-58 μm, the total thickness of described cold stamping solid medicinal composite hard sheet
Degree is 140-143 μm.
Maleic anhydride modified polyethylene layer 6 and the acrylic acid extruded by coextrusion mode are changed
Property polyethylene layer 7, not only have with each accompanying aluminium foil layer 2, aramid layer 1
There is higher peel strength, and whole extruding layer is soft, toughness strong, has high
Hot strength and elongation at break, can effectively prevent product during cold stamping may
The aluminum occurred splits and the problem such as absciss layer.
Wherein, cold stamping solid medicinal composite hard sheet of the present invention uses the aluminium foil of specific materials,
Composition and the percentage by weight of described aluminium foil layer aluminum foil material be: Si:0.35-0.50%,
Fe:0.9-1.20%, Cu:0.05-0.12%, Mn:0.50-0.60%, Mg:0.02-0.05%,
Cr:0.02-0.05%, Zn:0.02-0.05%, Ti:0.02-0.05%, surplus are Al.
And can method make as follows:
S1, melting, casting: according to described in above-mentioned aluminium foil composition and weight hundred
Proportion by subtraction weighs raw material, the raw material weighed is carried out at 730-760 DEG C melting, then enters
Row casting obtains blank, and the sotck thinkness after casting is 7.2 ± 0.3mm;
S2, homogenizing annealing: above-mentioned blank is carried out at 560-580 DEG C homogenizing annealing
Processing, isothermal holding is come out of the stove after 18-23 hour and is cooled to room temperature;
S3, cold rolling: the blank after cooling is carried out cold rolling, then 320-380 DEG C of condition
Under carry out intermediate annealing, after being incubated 25-28 hour prepare aluminium foil.
Additionally, the binding agent of adhesive phase described in cold stamping solid medicinal composite hard sheet of the present invention
It is made up of each component of following weight percentage ratio: acetone: 25-32%;Vinyl chloride-acetic acid second
Alkene-maleic acid terpolymer resin: 18-25%;Ethylene glycol-dimethyltrimethylene glycol-terephthaldehyde
The copolymer of acid esters-last of the ten Heavenly stems diester: 30-40%;Polyurethane: 5-10%;Merlon: 5-10%;
Polyestercarbonate: 5-10%.
The binding agent of described adhesive phase can prepare by the following method: makees with ketones solvent
Solvent, adds chloroethylene-vinyl acetate-maleic acid terpolymer resin and bonds as main body
Material, stirs to being completely dissolved within the temperature range of 55-65 DEG C, add ethylene glycol-
The copolymer of dimethyltrimethylene glycol-terephthalate-last of the ten Heavenly stems diester and polyurethane, Merlon,
Polyestercarbonate, mix homogeneously forms.
Embodiment 1
A kind of cold stamping solid medicinal composite hard sheet includes aramid layer 1, the aluminum set gradually
Layers of foil 2, polyvinyl chloride layer 3, be provided with one between aluminium foil layer 2 and described polyvinyl chloride layer 3 dry
Re-glue water layer 4, the surface of aluminium foil layer 2 includes aluminum phosphate thin film and rough layer, at aluminium foil layer 2
Surface is coated with urethane resin layer 5 and described urethane resin layer 5 is positioned at aluminium foil layer 2 He
Between aramid layer 1, also it is disposed with between described aramid layer 1 and described aluminium foil layer 2
Maleic anhydride modified polyethylene layer 6 and acrylic acid modified polyethylene layer 7, acrylic acid modified poly-second
It is equipped with gluing between alkene layer 7 and urethane resin layer 5, aluminium foil layer 2 and urethane resin layer 5
Oxidant layer 8, the density of described dry re-glue water layer 4 glue is 5.0g/cm3, described aramid layer 1
Thickness be 30 μm, the thickness of aluminium foil layer 2 is 50 μm, and the thickness of polyvinyl chloride layer 3 is
55 μm, the gross thickness of described cold stamping solid medicinal composite hard sheet is 142 μm.
Wherein, described aluminium foil prepares by the following method:
Melting, casting: according to described in following aluminium foil composition and percentage by weight claim
Take raw material: Si:0.40%, Fe:1.10%, Cu:0.08%, Mn:0.55%, Mg:
0.03%, Cr:0.03%, Zn:0.03%, Ti:0.03%, surplus are Al, will weigh
Good raw material carries out melting at 740 DEG C, and then carrying out casting obtains blank, the base after casting
Material thickness is 7.2mm;
Homogenizing annealing: above-mentioned blank carries out at 570 DEG C homogenizing annealing process, protects
Temperature is come out of the stove after processing 20 hours and is cooled to room temperature;
Cold rolling: the blank after cooling is carried out cold rolling, in then carrying out under the conditions of 360 DEG C
Between anneal, prepared aluminium foil after be incubated 26 hours.
The binding agent of described adhesive phase prepares by the following method: make solvent with acetone, adds
Enter chloroethylene-vinyl acetate-maleic acid terpolymer resin as main body adhesion substance, 60
Stir within the temperature range of DEG C to being completely dissolved, add ethylene glycol-dimethyltrimethylene glycol-to benzene
The copolymer of dicarboxylic acid esters-last of the ten Heavenly stems diester and polyurethane, Merlon, polyestercarbonate, mixed
Close and uniformly form.Wherein, binding agent is made up of each component of following weight percentage ratio: acetone:
25%;Chloroethylene-vinyl acetate-maleic acid terpolymer resin: 25%;Ethylene glycol-new penta
The copolymer of base glycol-terephthalate-last of the ten Heavenly stems diester: 30%;Polyurethane: 10%;Poly-
Carbonic ester: 5%;Polyestercarbonate: 5%.
Embodiment 2
A kind of cold stamping solid medicinal composite hard sheet includes aramid layer 1, the aluminum set gradually
Layers of foil 2, polyvinyl chloride layer 3, be provided with one between aluminium foil layer 2 and described polyvinyl chloride layer 3 dry
Re-glue water layer 4, the surface of aluminium foil layer 2 includes aluminum phosphate thin film and rough layer, at aluminium foil layer 2
Surface is coated with urethane resin layer 5 and described urethane resin layer 5 is positioned at aluminium foil layer 2 He
Between aramid layer 1, also it is disposed with between described aramid layer 1 and described aluminium foil layer 2
Maleic anhydride modified polyethylene layer 6 and acrylic acid modified polyethylene layer 7, acrylic acid modified poly-second
It is equipped with gluing between alkene layer 7 and urethane resin layer 5, aluminium foil layer 2 and urethane resin layer 5
Oxidant layer 8, the density of described dry re-glue water layer 4 glue is 4.9g/cm3, described aramid layer 1
Thickness be 32 μm, the thickness of aluminium foil layer 2 is 48 μm, and the thickness of polyvinyl chloride layer 3 is
58 μm, the gross thickness of described cold stamping solid medicinal composite hard sheet is 143 μm.
Wherein, described aluminium foil prepares by the following method:
Melting, casting: according to described in following aluminium foil composition and percentage by weight claim
Take raw material: Si:0.35%, Fe:1.20%, Cu:0.05%, Mn:0.60%, Mg:
0.02%, Cr:0.05%, Zn:0.02%, Ti:0.05%, surplus are Al, will weigh
Good raw material carries out melting at 730 DEG C, and then carrying out casting obtains blank, the base after casting
Material thickness is 7.5mm;
Homogenizing annealing: above-mentioned blank carries out at 580 DEG C homogenizing annealing process, protects
Temperature is come out of the stove after processing 18 hours and is cooled to room temperature;
Cold rolling: the blank after cooling is carried out cold rolling, in then carrying out under the conditions of 380 DEG C
Between anneal, prepared aluminium foil after be incubated 25 hours.
The binding agent of described adhesive phase prepares by the following method: make solvent with acetone, adds
Enter chloroethylene-vinyl acetate-maleic acid terpolymer resin as main body adhesion substance, 65
Stir within the temperature range of DEG C to being completely dissolved, add ethylene glycol-dimethyltrimethylene glycol-to benzene
The copolymer of dicarboxylic acid esters-last of the ten Heavenly stems diester and polyurethane, Merlon, polyestercarbonate, mixed
Close and uniformly form.Wherein, binding agent is made up of each component of following weight percentage ratio: acetone:
32%;Chloroethylene-vinyl acetate-maleic acid terpolymer resin: 18%;Ethylene glycol-new penta
The copolymer of base glycol-terephthalate-last of the ten Heavenly stems diester: 30%;Polyurethane: 5%;Poly-carbon
Acid esters: 5%;Polyestercarbonate: 10%.
Embodiment 3
A kind of cold stamping solid medicinal composite hard sheet includes aramid layer 1, the aluminum set gradually
Layers of foil 2, polyvinyl chloride layer 3, be provided with one between aluminium foil layer 2 and described polyvinyl chloride layer 3 dry
Re-glue water layer 4, the surface of aluminium foil layer 2 includes aluminum phosphate thin film and rough layer, at aluminium foil layer 2
Surface is coated with urethane resin layer 5 and described urethane resin layer 5 is positioned at aluminium foil layer 2 He
Between aramid layer 1, also it is disposed with between described aramid layer 1 and described aluminium foil layer 2
Maleic anhydride modified polyethylene layer 6 and acrylic acid modified polyethylene layer 7, acrylic acid modified poly-second
It is equipped with gluing between alkene layer 7 and urethane resin layer 5, aluminium foil layer 2 and urethane resin layer 5
Oxidant layer 8, the density of described dry re-glue water layer 4 glue is 5.1g/cm3, described aramid layer 1
Thickness be 28 μm, the thickness of aluminium foil layer 2 is 53 μm, and the thickness of polyvinyl chloride layer 3 is
52 μm, the gross thickness of described cold stamping solid medicinal composite hard sheet is 140 μm.
Wherein, described aluminium foil prepares by the following method:
Melting, casting: according to described in following aluminium foil composition and percentage by weight claim
Take raw material: Si:0.35%, Fe:1.20%, Cu:0.05%, Mn:0.60%, Mg:
0.02%, Cr:0.05%, Zn:0.02%, Ti:0.05%, surplus are Al, will weigh
Good raw material carries out melting at 730 DEG C, and then carrying out casting obtains blank, the base after casting
Material thickness is 7.5mm;
Homogenizing annealing: above-mentioned blank carries out at 580 DEG C homogenizing annealing process, protects
Temperature is come out of the stove after processing 18 hours and is cooled to room temperature;
Cold rolling: the blank after cooling is carried out cold rolling, in then carrying out under the conditions of 380 DEG C
Between anneal, prepared aluminium foil after be incubated 25 hours.
The binding agent of described adhesive phase prepares by the following method: make solvent with acetone, adds
Enter chloroethylene-vinyl acetate-maleic acid terpolymer resin as main body adhesion substance, 65
Stir within the temperature range of DEG C to being completely dissolved, add ethylene glycol-dimethyltrimethylene glycol-to benzene
The copolymer of dicarboxylic acid esters-last of the ten Heavenly stems diester and polyurethane, Merlon, polyestercarbonate, mixed
Close and uniformly form.Wherein, binding agent is made up of each component of following weight percentage ratio: acetone:
32%;Chloroethylene-vinyl acetate-maleic acid terpolymer resin: 18%;Ethylene glycol-new penta
The copolymer of base glycol-terephthalate-last of the ten Heavenly stems diester: 30%;Polyurethane: 5%;Poly-carbon
Acid esters: 5%;Polyestercarbonate: 10%.
Cold stamping solid medicinal composite hard sheet uses the rational aluminum foil material of compatibility to make aluminium foil
Layer, uses compatibility rational, compounding interpolation polyurethane, Merlon, polyestercarbonate
Binding agent make adhesive phase, which floor hyaline membrane is after compound, and whole structure is the most saturating
Bright, steam and oxygen are suffered from high barrier property, and inter-layer bonding force increases,
Steam, OTR oxygen transmission rate reduce, and barrier property increases, and global formation performance improves;
Product service life and improving product security performance can be extended with stable prod quality.
Specific embodiment described herein is only to present invention spirit theory for example
Bright.Those skilled in the art can be to described specific embodiment
Make various amendment or supplement or use similar mode to substitute, but without departing from
The spirit of the present invention or surmount scope defined in appended claims.
Claims (4)
1. a cold stamping solid medicinal composite hard sheet, including the aramid layer set gradually, aluminium foil layer, polyvinyl chloride layer, a dry re-glue water layer it is provided with between described aluminium foil layer and described polyvinyl chloride layer, it is characterized in that, the surface of described aluminium foil layer includes aluminum phosphate thin film and rough layer, urethane resin layer and described urethane resin layer it is coated with between aluminium foil layer and aramid layer on aluminium foil layer surface, maleic anhydride modified polyethylene layer and acrylic acid modified polyethylene layer also it is disposed with between described aramid layer and described aluminium foil layer, described acrylic acid modified polyethylene layer and described urethane resin layer, adhesive layer it is equipped with between aluminium foil layer and urethane resin layer, the density of described dry re-glue water layer glue is 4.9-5.1g/cm3, the thickness of described aramid layer is 28-32 μm, and the thickness of aluminium foil layer is 48-53 μm, and the thickness of polyvinyl chloride layer is 52-58 μm, and the gross thickness of described cold stamping solid medicinal composite hard sheet is 140-143 μm;Composition and the percentage by weight of described aluminium foil layer aluminum foil material be: Si:0.35-0.50%, Fe:0.9-1.20%, Cu:0.05-0.12%, Mn:0.50-0.60%, Mg:0.02-0.05%, Cr:0.02-0.05%, Zn:0.02-0.05%, Ti:0.02-0.05%, Al surplus.
Cold stamping solid medicinal composite hard sheet the most according to claim 1, it is characterised in that described aluminium foil prepares by the following method:
S1, melting, casting: weigh raw material according to the composition described in aluminium foil and percentage by weight, carry out melting at 730-760 DEG C by the raw material weighed, and then carries out casting and obtains blank, and the sotck thinkness after casting is 7.2 ± 0.3mm;
S2, homogenizing annealing: above-mentioned blank carries out at 560-580 DEG C homogenizing annealing process, isothermal holding is come out of the stove after 18-23 hour and is cooled to room temperature;
S3, cold rolling: the blank after cooling is carried out cold rolling, when rolling the first passage, working modulus is 60-80%, and back pass working modulus is maintained at 35-45%, under the conditions of 320-380 DEG C, carry out intermediate annealing through 5-6 passes to 0.6-0.8mm, be incubated 25-28 hour prepared aluminium foil.
Cold stamping solid medicinal composite hard sheet the most according to claim 1, it is characterised in that the binding agent of described adhesive layer is made up of each component of following weight percentage ratio: acetone: 25-32%;Chloroethylene-vinyl acetate-maleic acid terpolymer resin: 18-25%;The copolymer of ethylene glycol-dimethyltrimethylene glycol-terephthalate-last of the ten Heavenly stems diester: 30-40%;Polyurethane: 5-10%;Merlon: 5-10%;Polyestercarbonate: 5-10%.
Cold stamping solid medicinal composite hard sheet the most according to claim 3, it is characterized in that, the binding agent of described adhesive layer prepares by the following method: make solvent with acetone, add chloroethylene-vinyl acetate-maleic acid terpolymer resin as main body adhesion substance, stir within the temperature range of 55-65 DEG C to being completely dissolved, adding copolymer and polyurethane, Merlon, the polyestercarbonate of ethylene glycol-dimethyltrimethylene glycol-terephthalate-last of the ten Heavenly stems diester, mix homogeneously forms.