CN104585897A - Multicolor rubber infant pinny and manufacturing method thereof - Google Patents
Multicolor rubber infant pinny and manufacturing method thereof Download PDFInfo
- Publication number
- CN104585897A CN104585897A CN201510029308.3A CN201510029308A CN104585897A CN 104585897 A CN104585897 A CN 104585897A CN 201510029308 A CN201510029308 A CN 201510029308A CN 104585897 A CN104585897 A CN 104585897A
- Authority
- CN
- China
- Prior art keywords
- rubber
- bib
- infant
- colorful
- pinny
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a multicolor rubber infant pinny, a material constituent and a manufacturing method for the multicolor rubber infant pinny. The multicolor rubber infant pinny comprises an elliptical upper chest rubber sheet (6), and a first neck rubber band (1) and a second neck rubber band which are integrally connected with the upper side of the upper chest rubber sheet. The multicolor rubber infant pinny comprises the following raw materials: rubber, white carbon black, a structural control agent and a crosslinking agent. The rubber pinny can well prevent food residues, residual liquid and infant saliva from polluting clothes, and the material selection is scientific, injury to an infant is avoided, and the pinny is colorful. The rubber pinny is simple in structure, convenient to form and process and low in cost and is larger in popularization and application value.
Description
Technical field
The present invention relates to a kind of bib and material composition thereof, specifically a kind of colorful infant's rubber bib and manufacture method thereof, belong to small stores field.
Background technology
Along with the quickening of the live and work rhythm in modern times, in the daily routines of people, need the daily necessities of more convenience, quick and health.Young man is when bringing up infant, and owing to cutting out, the articles for use such as infant clothes need online or solid shop/brick and mortar store purchase.And infant is at play, clothes of often making dirty when having a meal.This just needs infant's bib protected or protect.
In prior art, infant's bib is that muslin makes substantially.Because cotton has stronger water imbibition and oil absorption, once do dirty, not only pollute bib, also likely pollute clothes.In the family that a lot of young man can not do housework, need repeatedly buy infant clothes and bib.Cause not little waste like this.
Summary of the invention
For above-mentioned prior art Problems existing, the invention provides a kind of colorful infant's rubber bib and manufacture method thereof, by changing moulding and the bib material of bib, can be good at preventing the solid, liquid body pollution thing drippage pollution clothes such as saliva of the grain of rice, gruel, dish juice, fruit juice and infant, the nonpoisonous and tasteless multi-colour rubber sheet material that rubber bib material selection is corrosion-resistant, high temperature resistant, ageing-resistant, hardness is moderate, machine-shaping process is simple, and practicality is better.
To achieve these goals, the technical solution used in the present invention is: a kind of colorful infant's rubber bib, comprise oval upper chest film, the the first muffler adhesive tape linked into an integrated entity on the upside of the film of described upper chest and the second muffler adhesive tape, wherein, first muffler adhesive tape is provided with band eye, and the second muffler adhesive tape is provided with and the bracelet matched with eye; Be connected with the lower bib of pocket shape on the downside of the film of described upper chest, described upper chest film is provided with three identical eyelets, by eyelet can be connected with described lower bib with the use of; And described lower bib is point sheet rubber that two areas do not wait, and large area sheet rubber is provided with three can be connected the rubber salient point of arranging in pairs or groups with described eyelet.The raw material of colorful infant's rubber bib comprise silicon rubber, white carbon, constitution controller and crosslinking agent.
Raw material for colorful infant's rubber bib, it comprises silicon rubber, white carbon, constitution controller and crosslinking agent; Various raw-material weight part is: 100 parts, silicon rubber, white carbon 30-55 part, constitution controller 3-6 part, crosslinking agent 0.6-2 part.
Further, White Carbon black comprises Fumed silica and precipitation method White Carbon black.
Further, described constitution controller is any one in diphenyl silanediol, low-molecular-weight hydroxyl silicone oil, aminomethyl phenyl diethoxy silane, tetramethyl ethylidene dioxy dimethylsilane, silazane.
Further, described crosslinking agent is any one in 2,5-dimethyl-2,5-di-t-butyl peroxy hexane, cumyl peroxide, benzoyl peroxide, bis-p-chlorobenzoyl peroxide and di-t-butyl peroxide (DTBP) peroxide.
The manufacture method of colorful infant's rubber bib comprises the steps:
1), according to common compounding process, various raw material are mixed by formula rate after, take appropriate elastomeric compound put into there is bib shape mould in;
2), at pressure be greater than 5MPa, sulfidization molding under the condition of temperature 150-190 DEG C, after shaping, at normal pressure, under the condition of temperature 190-220 DEG C, post-cure 2-10 hour can be carried out;
3), mold pressing, bib after sulfuration without the need to cutting, make and press, can directly to use or different parts are connected and use;
4), rubber bib can go out the individual character space patterns such as the cartoon character liked as name, birthday, symbolic animal of the birth year or individual by mould molding.Also as required, colouring agent can be added, makes the colorful bib of different colours.
The invention has the beneficial effects as follows: this rubber bib well can prevent the pollution clothes such as swill, residual night and infant's saliva, and its material selection has science, can not to infant have injury and bright in luster; This rubber bib structure is simple, and processing and forming is convenient, cheap, has larger application value;
Silicon rubber is selected in this rubber bib material.Silicon rubber has softness, biological biocidal property is good, nontoxic, water-fast, corrosion-resistant, resistance to ozone aging, resistance to oxygen aging, light aging resisting and Weather-resistant, electrical insulation capability is good, colorable feature, after adding additive, there is good intensity, adopt the compression molding of common rubber processing method, do not need cutting, make and press, can also be gone out as individual character space patterns such as name, birthday, symbolic animal of the birth year by mould molding.
Accompanying drawing explanation
Fig. 1 is overall structure schematic diagram of the present invention;
In figure: 1, the first muffler adhesive tape, 2, bracelet, the 3, second muffler adhesive tape, 4, band eye, 5, perisotomice, 6, upper chest film, 7, eyelet, 8, lower bib.
Detailed description of the invention
Below in conjunction with accompanying drawing, the invention will be further described.
As shown in Figure 1: a kind of colorful infant's rubber bib, comprise chest film 6, upper chest film 6 is oval film, and being specifically of a size of with infant is standard.For making upper chest film handsome in appearance, applicable infant wears, and can be printed on cartoon character on the film of upper chest, selects in order to the head of a family and infant.The eyelet of three same sizes can be had on the downside of the film of upper chest, object be connected with lower bib with the use of.
Have on the upside of upper chest film 6 and the first muffler adhesive tape 1 that upper chest film 6 links into an integrated entity and the 3rd muffler adhesive tape 3.Wherein, the first muffler adhesive tape 1 is brought be provided with band eye 4, second muffler adhesive tape 3 and be provided with and the bracelet 2 matched with eye 4.First muffler adhesive tape 1, second muffler adhesive tape 3 and upper chest film 6 surround a perisotomice 5, and this perisotomice 5 can fit like a glove the neck of child.Buckle well when band eye 1 and bracelet 2 are connected, upper chest film is just fixed on infant's upper body.
Lower bib 8 is the rubber sheet of a pocket shape, and wherein a lateral area is greater than opposite side.Three rubber salient points can be designed with, to need the eyelet on the downside of used time and upper chest film to be connected hasp in large area side.
Use colorful infant's rubber bib process in, because film has certain pliability and own wt thereof, substantially can be docile protect infant shirtfront.The swill that such infant produces when eating the foods such as rice, biscuit, steamed bun will be slipped to ground along the upper chest film of front, can not pollute clothes.
Drink water infant, drink gruel, drink fruit juices, when drinking the liquid foods such as dish juice and have saliva to occur, lower bib can be connected and be buckled in upper chest film.At this moment produced liquid can be left in lower bib along upper chest film residual night.Be convenient to the head of a family clear up in time, clean and change clothes.
Infant's rubber bib, owing to have employed oil resistant, high temperature resistant, ageing-resistant, corrosion resistant rubber sheet, is difficult to also with coordinative solvent cleaning and to disinfect with the pollutant of water cleaning.
Infant's rubber bib rubber sheet can make transparence or other colors, to adapt to the different head of a family and infant to aesthetic needs.
The raw material of colorful infant's rubber bib comprise silicon rubber, white carbon, constitution controller and crosslinking agent;
Various raw-material weight part is: 100 parts, silicon rubber, white carbon 30-55 part, constitution controller 3-6 part, crosslinking agent 0.6-2 part;
Further, White Carbon black comprises Fumed silica and precipitation method White Carbon black.
Further, described constitution controller is any one in diphenyl silanediol, low-molecular-weight hydroxyl silicone oil, aminomethyl phenyl diethoxy silane, tetramethyl ethylidene dioxy dimethylsilane, silazane.
Further, described crosslinking agent is any one in 2,5-dimethyl-2,5-di-t-butyl peroxy hexane, cumyl peroxide, benzoyl peroxide, bis-p-chlorobenzoyl peroxide and di-t-butyl peroxide peroxide.
The manufacture method of colorful infant's rubber bib comprises the steps:
1), according to common compounding process, various raw material are mixed by formula rate after, take appropriate elastomeric compound put into there is bib shape mould in;
2), at pressure be greater than 5MPa, sulfidization molding under the condition of temperature 150-190 DEG C, after shaping, at normal pressure, under the condition of temperature 190-220 DEG C, post-cure 2-10 hour can be carried out;
3), mold pressing, bib after sulfuration without the need to cutting, make and press, can directly to use or different parts are connected and use;
4), rubber bib can go out the individual character space patterns such as the cartoon character liked as name, birthday, symbolic animal of the birth year or individual by mould molding; Also as required, colouring agent can be added, makes the colorful bib of different colours.
Embodiment 1,
Select raw-material weight part as follows: 100 parts, silicon rubber, fume colloidal silica 30 parts, diphenyl silanediol 5 parts, 2,5-dimethyl-2,5-di-t-butyl peroxy hexane (two 2,5) 1.0 parts.
Above raw material mixes by rubber mixing machine; Take appropriate sizing material and put into preheated mould, at pressure 8MPa, with vulcanizing press mold pressing 10min under the condition that temperature is 180 DEG C; Put into the baking oven post-cure 5h of 190 DEG C, namely obtain the bib finished product of white clear.
Embodiment 2,
Select raw-material weight part as follows: 100 parts, silicon rubber, fume colloidal silica 55 parts, hydroxy silicon oil 4 parts, 2,5-dimethyl-2,5-di-t-butyl peroxy hexane (two 2,5) 1.1 parts, bright red 0.8 part of colouring agent rubber.
Above raw material mixes by rubber mixing machine; Take appropriate sizing material and put into preheated mould, at pressure 6MPa, with vulcanizing press mold pressing 5min under the condition that temperature is 190 DEG C; Put into the baking oven post-cure 4h of 210 DEG C, namely obtain red translucent bib finished product.
Embodiment 3,
Select raw-material weight part as follows: 100 parts, silicon rubber, fume colloidal silica 45 parts, hydroxy silicon oil 15 parts, vinyl silicone oil 4 parts, benzoyl peroxide (BP) 0.9 part, colouring agent phthalocyanine blue 0.5 part.
Above raw material mixes by rubber mixing machine; Take appropriate sizing material and put into preheated mould, at pressure 5MPa, with vulcanizing press mold pressing 4min under the condition that temperature is 200 DEG C; Put into the baking oven post-cure 3.5h of 210 DEG C, namely obtain the bib finished product of Blue-Color Semitransparent.
100 parts, embodiment 4, silicon rubber, fume colloidal silica 50 parts, diphenyl silanediol 4 parts, hydroxy silicon oil 14 parts, benzoyl peroxide (BP) 1.2 parts, dark green 0.7 part of colouring agent phthalein.。
Above raw material mixes by rubber mixing machine; Take appropriate sizing material and put into preheated mould, at pressure 7MPa, with vulcanizing press mold pressing 5min under the condition that temperature is 180 DEG C; Put into the baking oven post-cure 3h of 210 DEG C, namely obtain green translucent bib finished product.
The obtained silicon rubber of above-mentioned four techniques is after testing: hot strength is greater than 7.00MPa, and tearing strength is greater than 10KN/m, and hardness 55-65 Shao Er A, tension fracture elongation rate is greater than 350%.
Claims (6)
1. colorful infant's rubber bib, it is characterized in that: comprise oval upper chest film (6), the first muffler adhesive tape (1) that described upper chest film (6) upside links into an integrated entity and the second muffler adhesive tape (3), wherein, first muffler adhesive tape (1) is provided with band eye (4), and the second muffler adhesive tape (3) is provided with and the bracelet (2) matched with eye (4); Described upper chest film (6) downside is connected with the lower bib (8) of pocket shape, described upper chest film (1) is provided with three identical eyelets (7), by eyelet (7) can be connected with described lower bib (8) with the use of; And described lower bib (8) is the sheet rubber dividing two areas not wait, and large area sheet rubber is provided with three can be connected the rubber salient point of arranging in pairs or groups with described eyelet (7).
2. raw material for colorful infant's rubber bib, is characterized in that: it comprises silicon rubber, white carbon, constitution controller and crosslinking agent; Various raw-material weight part is: 100 parts, silicon rubber, white carbon 30-55 part, constitution controller 3-6 part, crosslinking agent 0.6-2 part.
3. the raw material of a kind of colorful infant's rubber bib according to claim 1, is characterized in that: described White Carbon black comprises Fumed silica and precipitation method White Carbon black.
4. the raw material of a kind of colorful infant's rubber bib according to Claims 2 or 3, is characterized in that: described constitution controller is any one in diphenyl silanediol, low-molecular-weight hydroxyl silicone oil, aminomethyl phenyl diethoxy silane, tetramethyl ethylidene dioxy dimethylsilane, silazane.
5. the raw material of a kind of colorful infant's rubber bib according to claim 4, it is characterized in that: described crosslinking agent is 2, any one in 5-dimethyl-2,5-di-t-butyl peroxy hexane, cumyl peroxide, benzoyl peroxide, bis-p-chlorobenzoyl peroxide and di-t-butyl peroxide peroxide.
6. a manufacture method for colorful infant's rubber bib according to claim 1, is characterized in that, comprise the steps:
1), according to common compounding process, various raw material are mixed by formula rate after, take appropriate elastomeric compound put into there is bib shape mould in;
2), at pressure be greater than 5MPa, sulfidization molding under the condition of temperature 150-190 DEG C, after shaping, at normal pressure, under the condition of temperature 190-220 DEG C, post-cure 2-10 hour can be carried out;
3), mold pressing, bib after sulfuration without the need to cutting, make and press, can directly to use or different parts are connected and use;
4), rubber bib can go out the individual character space patterns such as the cartoon character liked as name, birthday, symbolic animal of the birth year or individual by mould molding; Also as required, colouring agent can be added, makes the colorful bib of different colours.