CN104558894A - PVC cable composite tube - Google Patents
PVC cable composite tube Download PDFInfo
- Publication number
- CN104558894A CN104558894A CN201310495095.4A CN201310495095A CN104558894A CN 104558894 A CN104558894 A CN 104558894A CN 201310495095 A CN201310495095 A CN 201310495095A CN 104558894 A CN104558894 A CN 104558894A
- Authority
- CN
- China
- Prior art keywords
- pvc cable
- pvc
- polyvinyl chloride
- stabilizer
- compound pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PVC cable composite tube which is prepared from 70-80% of polyvinyl chloride resin, 5-10% of a thermal stabilizing agent, 2-5% of a light stabilizing agent, 3-5% of an antioxidant, 2-5% of an auxiliary stabilizing agent, 1-2% of a plasticizer, 1-2% of a coloring agent, 1-2% of a lubricant, 1-2% of an impact-resisting modifier, 1-2% of a biological inhibitor, 1-2% of a fire retardant and 1-2% of other additives, wherein the polyvinyl chloride resin is free of cadmium. The PVC cable composite tube is good in high temperature resistance and anti-aging property, is applicable to high temperature caused by overload short circuit generated when an electric cable is used, is high in insulating strength and volume electrical resistivity, good in flexibility, high in compressive strength, and differential settlement resistant, does not need to be coated by placing concrete in a construction field, and is small in inner wall surface friction coefficient, beneficial to use and long in service life.
Description
Technical field
The present invention relates to cable shoe, be specifically related to a kind of PVC cable compound pipe.
Background technology
Current engineering cable shoe is take polyvinyl chloride (PVC) RESINS as major ingredient, water-ground limestone is mixed for filler and the small powder such as chlorinatedpolyethylene, paraffin, and possess certain corrosion-resistant, high temperature resistant, fire-retardant, insulate the wear-resisting characteristic such as lightweight, pollution-free.But it is poor that its weak point is ultimate compression strength, require gap in addition with construction application, its flame retardant properties is also not ideal enough; Its vicat softening temperature is hovered at about 90 DEG C in addition, and inner and outer pipes wall friction coefficient is large, adds the difficulty of construction usage.
Summary of the invention
For the deficiency that prior art exists, the present invention seeks to the PVC cable compound pipe being to provide a kind of excellent property.
To achieve these goals, the present invention realizes by the following technical solutions: its raw material is made by other auxiliary agents of the tinting material of the softening agent of the auxiliary stabilizer of the oxidation inhibitor of the photostabilizer of the thermal stabilizer of the polyvinyl chloride (PVC) RESINS of 70%-80%, 5%-10%, 2%-5%, 3%-5%, 2%-5%, 1%-2%, 1%-2%, the lubricant of 1%-2%, the impact modifier of 1%-2% and 1%-2%, and described polyvinyl chloride (PVC) RESINS is not containing cadmium.
As preferably, described thermo-stabilizer is one package stabilizer.
As preferably, described one package stabilizer is the mixture of three salt, disalt and metallic soap.
As preferably, described softening agent is DOP.
As preferably, described lubricant is polyester synthetic ester.
As preferably, described impact modifier is MBS.
Product of the present invention has high temperature resistant and ageing resistance is good, and can adapt to the high temperature that power cable use procedure produces because of overload short circuit, material has high insulation resistance and volume specific resistance; Flexible and ultimate compression strength is large, anti-non-uniform settling, need not pouring concrete be encapsulated at the construction field (site); Inner wall surface coefficient of friction is little, is beneficial to use, and product life is long.
The present invention is described in detail below in conjunction with embodiment.
embodiment
The technique means realized for making the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with embodiment, setting forth the present invention further.
This embodiment is by the following technical solutions: PVC cable compound pipe, its raw material is made by other auxiliary agents of the tinting material of the softening agent of the auxiliary stabilizer of the oxidation inhibitor of the photostabilizer of the thermal stabilizer of the polyvinyl chloride (PVC) RESINS of 70%-80%, 5%-10%, 2%-5%, 3%-5%, 2%-5%, 1%-2%, 1%-2%, the lubricant of 1%-2%, the impact modifier of 1%-2% and 1%-2%, and described polyvinyl chloride (PVC) RESINS is not containing cadmium.
It should be noted that described thermo-stabilizer is one package stabilizer.
It should be noted that described one package stabilizer is the mixture of three salt, disalt and metallic soap.
It should be noted that described softening agent is DOP.
It should be noted that described lubricant is polyester synthetic ester.
It should be noted that described impact modifier is MBS.
Product of the present invention has high temperature resistant and ageing resistance is good, and can adapt to the high temperature that power cable use procedure produces because of overload short circuit, material has high insulation resistance and volume specific resistance; Flexible and ultimate compression strength is large, anti-non-uniform settling, need not pouring concrete be encapsulated at the construction field (site); Inner wall surface coefficient of friction is little, is beneficial to use, and product life is long.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (6)
1. a PVC cable compound pipe, it is characterized in that, its raw material is made by other auxiliary agents of the fire retardant of the impact modifier of the lubricant of the tinting material of the softening agent of the auxiliary stabilizer of the oxidation inhibitor of the photostabilizer of the thermal stabilizer of the polyvinyl chloride (PVC) RESINS of 70%-80%, 5%-10%, 2%-5%, 3%-5%, 2%-5%, 1%-2%, 1%-2%, 1%-2%, 1%-2%, 1%-2%, the whipping agent of 1%-2%, the biostats of 1%-2% and 1%-2%, and described polyvinyl chloride (PVC) RESINS is not containing cadmium.
2. a kind of PVC cable compound pipe according to claims 1, is characterized in that, described thermo-stabilizer is one package stabilizer.
3. a kind of PVC cable compound pipe according to claims 1, is characterized in that, described one package stabilizer is the mixture of three salt, disalt and metallic soap.
4. a kind of PVC cable compound pipe according to claims 1, is characterized in that, described softening agent is DOP.
5. a kind of PVC cable compound pipe according to claims 1, is characterized in that, described lubricant is polyester synthetic ester.
6. a kind of PVC cable compound pipe according to claims 1, is characterized in that, described impact modifier is MBS.