CN104556934A - 一种可吸附有毒有害气体的加气砌块及其制备方法 - Google Patents
一种可吸附有毒有害气体的加气砌块及其制备方法 Download PDFInfo
- Publication number
- CN104556934A CN104556934A CN201410792321.XA CN201410792321A CN104556934A CN 104556934 A CN104556934 A CN 104556934A CN 201410792321 A CN201410792321 A CN 201410792321A CN 104556934 A CN104556934 A CN 104556934A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminium powder
- aerated concrete
- concrete block
- modified aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可吸附有毒有害气体的加气砌块及其制备方法,其由以下重量份的原料制成:黄砂42-68、纳米乌金石10-15、沸石分子筛12-16、水铝英石18-26、木屑22-28、重钙粉15-20、海泥26-34、凹凸棒土16-22、α型半水石膏10-15、卡波树脂3-6、改性铝粉1-2、硫代硫酸钠2-3、硫酸锌2-3、偶氮二异丁腈1-2。本发明加气砌块中添加了纳米乌金石、沸石分子筛等物理吸附功能突出的物质,使得加气砌块可以吸附甲醛、苯系物、硫氧化物、氮氧化物、一氧化碳、硫化氢、氨气、异戊酸、甲烷硫醇、三甲胺(鱼腥味)、TVOC等有害气体,起到净化空气的作用,同时本发明加气砌块具有强度高,隔热保温性好,隔音效果好,耐热,防潮,耐酸碱腐蚀等特点,市场前景广阔。
Description
技术领域
本发明涉及一种可吸附有毒有害气体的加气砌块及其制备方法,属于建筑材料领域。
背景技术
加气砌块是以硅质材料(砂、粉煤灰及含硅尾矿等)和钙质材料(石灰、水泥等)为主要原料,掺加发气剂(铝粉),经加水搅拌,由化学反应形成孔隙,通过浇注成型、预养切割、蒸压养护等工艺过程制成的多孔硅酸盐制品。加气砌块具有质轻、保温隔热、可加工性好、原料来源广、生产效率高、生产能耗低等特点,广泛应用于工业和民用建筑的承重或围护、填充等,受到世界各国的普遍重视,成为许多国家大力推广和发展的优选建筑材料。随着我国建筑行业的快速发展,对加气砌块的性能要求越来越高,然而传统加气砌块不具有吸附有毒气体、净化空气的作用,无法满足人们对环保生活的更高要求。因此,急需开发一种可吸附有毒有害气体的加气砌块。
发明内容
本发明的目的在于提供一种可吸附有毒有害气体的加气砌块及其制备方法。
为实现上述目的,本发明采用如下技术方案:
一种可吸附有毒有害气体的加气砌块,由以下重量份的原料制成:黄砂42-68、纳米乌金石10-15、沸石分子筛 12-16、水铝英石18-26、木屑 22-28、重钙粉15-20、海泥26-34、凹凸棒土16-22、α型半水石膏10-15、卡波树脂3-6、改性铝粉1-2、硫代硫酸钠2-3、硫酸锌2-3、偶氮二异丁腈1-2;
所述改性铝粉的制备方法如下:(a)、取以下重量份的原料:活性铝粉60-80、亚甲基二萘磺酸钠3-6、椰油酰胺丙基甜菜碱2-4、十四烷基二甲基氧化胺1.5-2.5、十二烷基苯磺酸钠4.5-6.5、月桂酰二乙醇胺4-7、松香酸钠5-8、鲸蜡硬脂基葡糖苷2-4、茶皂素1-3;(b)、取铝粉加适量的水,搅拌制成浓度为50-60%的浆液,然后加入亚甲基二萘磺酸钠、椰油酰胺丙基甜菜碱、十四烷基二甲基氧化胺和十二烷基苯磺酸钠,在50-80r/min的转速下搅拌1-2h,抽滤,烘干;(c)、取1/3-1/2量的上述烘干的铝粉与月桂酰二乙醇胺、茶皂素混合,在40-60r/min的转速下搅拌2-3h,得改性铝粉A;(d)、取余下的铝粉与松香酸钠、鲸蜡硬脂基葡糖苷混合,在30-50r/min的转速下搅拌3-4h,得改性铝粉B;(e)、将改性铝粉A和改性铝粉B混合均匀,即得所需的改性铝粉。
上述改性铝粉采用传统铝粉与月桂酰二乙醇胺、松香酸钠、鲸蜡硬脂基葡糖苷、茶皂素等多种原料复合,能显著增加料浆稠度,大幅度提高铝粉的发气效率,有效解决了传统铝粉发气剂发气效率低的缺点。
一种可吸附有毒有害气体的加气砌块的制备方法,由下列步骤组成:
(1)取黄砂、水铝英石、木屑混合均匀,粉碎,过200-300目筛,加水使得混合料的含水量控制在55-65%,然后加入硫代硫酸钠、硫酸锌、重钙粉,1000-1500rpm研磨10-15min后加入纳米乌金石、沸石分子筛、海泥、凹凸棒土、α型半水石膏、卡波树脂,搅拌均匀后再调整混合料的含水量至70-80%,500-1000rpm搅拌4-6min;
(2)将改性铝粉、偶氮二异丁腈加入步骤(1)制得的浆料中,搅拌均匀后在60-70℃温度下发泡35-45min;
(3)将步骤(2)得到的发泡浆料注入成型模具中,自然养护45-55h,拆模,得生坯;
(4)将步骤(3)得到的生坯在温度为65-75℃、压力为0.6-0.9MPa的条件下蒸汽养护12-16h,即得加气砌块成品。
本发明的有益效果:
本发明加气砌块中添加了纳米乌金石、沸石分子筛等物理吸附功能突出的物质,使得加气砌块可以吸附甲醛、苯系物、硫氧化物、氮氧化物、一氧化碳、硫化氢、氨气、异戊酸、甲烷硫醇、三甲胺(鱼腥味)、TVOC等有害气体,起到净化空气的作用,同时本发明加气砌块具有强度高,隔热保温性好,隔音效果好,耐热,防潮,耐酸碱腐蚀等特点,市场前景广阔。
具体实施方式
一种可吸附有毒有害气体的加气砌块,由以下重量(kg)的原料制成:黄砂56、纳米乌金石12、沸石分子筛 14、水铝英石22、木屑 26、重钙粉18、海泥32、凹凸棒土18、α型半水石膏12、卡波树脂4.5、改性铝粉1.5、硫代硫酸钠2.5、硫酸锌2.5、偶氮二异丁腈1.5;
所述改性铝粉的制备方法如下:(a)、取以下重量(kg)的原料:活性铝粉65、亚甲基二萘磺酸钠3.5、椰油酰胺丙基甜菜碱2.5、十四烷基二甲基氧化胺2、十二烷基苯磺酸钠5、月桂酰二乙醇胺4.5、松香酸钠6、鲸蜡硬脂基葡糖苷2.5、茶皂素1.5;(b)、取铝粉加适量的水,搅拌制成浓度为50%的浆液,然后加入亚甲基二萘磺酸钠、椰油酰胺丙基甜菜碱、十四烷基二甲基氧化胺和十二烷基苯磺酸钠,在65r/min的转速下搅拌1.5h,抽滤,烘干;(c)、取1/3量的上述烘干的铝粉与月桂酰二乙醇胺、茶皂素混合,在50r/min的转速下搅拌2.5h,得改性铝粉A;(d)、取余下的铝粉与松香酸钠、鲸蜡硬脂基葡糖苷混合,在50r/min的转速下搅拌3h,得改性铝粉B;(e)、将改性铝粉A和改性铝粉B混合均匀,即得所需的改性铝粉。
一种可吸附有毒有害气体的加气砌块的制备方法,由下列步骤组成:
(1)取黄砂、水铝英石、木屑混合均匀,粉碎,过250目筛,加水使得混合料的含水量控制在60%,然后加入硫代硫酸钠、硫酸锌、重钙粉,1500rpm研磨10min后加入纳米乌金石、沸石分子筛、海泥、凹凸棒土、α型半水石膏、卡波树脂,搅拌均匀后再调整混合料的含水量至80%,1000rpm搅拌5min;
(2)将改性铝粉、偶氮二异丁腈加入步骤(1)制得的浆料中,搅拌均匀后在70℃温度下发泡35min;
(3)将步骤(2)得到的发泡浆料注入成型模具中,自然养护50h,拆模,得生坯;
(4)将步骤(3)得到的生坯在温度为70℃、压力为0.8MPa的条件下蒸汽养护12h,即得加气砌块成品。
上述实施例制得的加气砌块的的主要性能检测见下表:
项目 | 单位 | 检测结果 |
常温耐压强度 | Mpa | 5.3 |
干燥收缩值 | mm/m | 0.5 |
导热系数 | W/m.K | 0.17 |
有害气体吸附率 | % | 97.8 |
Claims (2)
1.一种可吸附有毒有害气体的加气砌块,其特征在于,由以下重量份的原料制成:黄砂42-68、纳米乌金石10-15、沸石分子筛 12-16、水铝英石18-26、木屑 22-28、重钙粉15-20、海泥26-34、凹凸棒土16-22、α型半水石膏10-15、卡波树脂3-6、改性铝粉1-2、硫代硫酸钠2-3、硫酸锌2-3、偶氮二异丁腈1-2;
所述改性铝粉的制备方法如下:(a)、取以下重量份的原料:活性铝粉60-80、亚甲基二萘磺酸钠3-6、椰油酰胺丙基甜菜碱2-4、十四烷基二甲基氧化胺1.5-2.5、十二烷基苯磺酸钠4.5-6.5、月桂酰二乙醇胺4-7、松香酸钠5-8、鲸蜡硬脂基葡糖苷2-4、茶皂素1-3;(b)、取铝粉加适量的水,搅拌制成浓度为50-60%的浆液,然后加入亚甲基二萘磺酸钠、椰油酰胺丙基甜菜碱、十四烷基二甲基氧化胺和十二烷基苯磺酸钠,在50-80r/min的转速下搅拌1-2h,抽滤,烘干;(c)、取1/3-1/2量的上述烘干的铝粉与月桂酰二乙醇胺、茶皂素混合,在40-60r/min的转速下搅拌2-3h,得改性铝粉A;(d)、取余下的铝粉与松香酸钠、鲸蜡硬脂基葡糖苷混合,在30-50r/min的转速下搅拌3-4h,得改性铝粉B;(e)、将改性铝粉A和改性铝粉B混合均匀,即得所需的改性铝粉。
2.根据权利要求1所述的可吸附有毒有害气体的加气砌块的制备方法,其特征在于,由下列步骤组成:
(1)取黄砂、水铝英石、木屑混合均匀,粉碎,过200-300目筛,加水使得混合料的含水量控制在55-65%,然后加入硫代硫酸钠、硫酸锌、重钙粉,1000-1500rpm研磨10-15min后加入纳米乌金石、沸石分子筛、海泥、凹凸棒土、α型半水石膏、卡波树脂,搅拌均匀后再调整混合料的含水量至70-80%,500-1000rpm搅拌4-6min;
(2)将改性铝粉、偶氮二异丁腈加入步骤(1)制得的浆料中,搅拌均匀后在60-70℃温度下发泡35-45min;
(3)将步骤(2)得到的发泡浆料注入成型模具中,自然养护45-55h,拆模,得生坯;
(4)将步骤(3)得到的生坯在温度为65-75℃、压力为0.6-0.9MPa的条件下蒸汽养护12-16h,即得加气砌块成品。