CN104531272B - Tourmalinite-assistant molybdenum disulfide lubrication additive and preparation method thereof - Google Patents
Tourmalinite-assistant molybdenum disulfide lubrication additive and preparation method thereof Download PDFInfo
- Publication number
- CN104531272B CN104531272B CN201410740117.3A CN201410740117A CN104531272B CN 104531272 B CN104531272 B CN 104531272B CN 201410740117 A CN201410740117 A CN 201410740117A CN 104531272 B CN104531272 B CN 104531272B
- Authority
- CN
- China
- Prior art keywords
- oil
- molybdenum bisuphide
- soluble
- tourmaline
- molybdenum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a tourmalinite-assistant molybdenum disulfide lubrication additive and a preparation method thereof and belongs to the technical field of mechanical lubrication. The tourmalinite-assistant molybdenum disulfide lubrication additive comprises, by mass, 70-90% of an oily solvent, 5-25% of oil-soluble molybdenum disulfide and 5-10% of oil-soluble tourmalinite powder. The preparation method comprises the following steps of adding oil-soluble molybdenum disulfide and oil-soluble tourmalinite powder into the oily solvent at a temperature of 5-60 DEG C with stirring according to the above ratio, carrying out uniform mixing, transferring the mixture to an ultrasonic container and carrying out ultrasonic treatment for 5-20min. The tourmalinite-assistant molybdenum disulfide lubrication additive has good dispersibility and stability. Through assistant action of tourmalinite powder, a use temperature and a service life of molybdenum disulfide are substantially improved.
Description
Technical field
The present invention relates to a kind of tourmaline auxiliary molybdenum bisuphide class lubricating additive and preparation method thereof, belongs to mechanical lubrication
Technical field.
Background technology
Kollag and fluid lubricant have synergism for the lubrication of machinery, and lubricating oil and grease easily steam
Send out, when high load capacity is born, oil film can wreck, and lubricating ability will be lost at high temperature;By kollag and lubrication
Oil, fat are used in combination, and can meet the lubrication problem under harsh conditions, expand the use temperature range of lubricant, improve lubrication
The bearing capacity of oils and fatss, strengthens the aging performance of lubricant grease, protects plant equipment, increases economic efficiency.Molybdenum bisuphide is mesh
Front most widely used solid lubricant, the form and method for being adopted is more, such as powder, oil preparation, water preparation, or and other
Metal or macromolecular material constitute composite lubricated material.Patent CN 1513959A discloses a kind of molybdenum bisuphide oil based emulsions, by
The suspension of the two kinds of oil preparationes composition in molybdenum bisuphide and mineral oil, artificial oil or vegetable oil, as the additive of lubricating oil
Use.Find in actual use, simple molybdenum bisuphide suspension is easily settled, affect using effect.Patent CN
1468945A discloses a kind of method for preparing oil-soluble molybdenum bisuphide, adopts molybdenum trioxide for molybdenum source, using Oleic acid or hard
Fat acid is dressing agent, obtains the nanometer MOS 2 particle through modifying.In the case where there is air existence condition, molybdenum bisuphide makes
With temperature not above 400 DEG C, this is because molybdenum bisuphide is easily oxidized under the high temperature conditions molybdenum trisulfide;Do not occurring
In the ar gas environment of Oxidation, the coefficient of friction of molybdenum bisuphide is slightly above 0.2 at 1000 DEG C.It can be seen that, how to suppress lubrication
The oxidizing process of molybdenum bisuphide in oil additive, the use to molybdenum bisuphide is most important.To solve this problem, use at present
Method be addition from consumption-type antioxidant, such as Sb2O3, but this antioxidant consumes very rapid, economically impracticable.
Tourmaline (Tourmaline) crystal belongs to family's circulus borosilicate mineral of trigonal system, with pyroelectricity
And piezoelectricity, form weak electric field around under pressurized or heating condition, empty gas and water exist situation under promote bear from
The formation of son, mainly O2-(H2O)n、OH-(H2O)n, process do not consume energy;In addition, the bioactive molecule H for producing3O+Impurity can be attracted
Dirt.Tourmaline is a kind of using quite varied ideal green material.
The content of the invention
The problem of high cost is rapidly resulted in for existing molybdenum bisuphide antioxidant consumption, it is an object of the invention to carry
For a kind of tourmaline auxiliary molybdenum bisuphide class lubricating additive and preparation method thereof, the additive is by oil-soluble molybdenum bisuphide and oil
Dissolubility tourmaline powder is constituted.The lubricating additive of the present invention has extraordinary dispersibility and stability, in the auxiliary of tourmaline powder
Help the lower use temperature and service life that can be obviously improved molybdenum bisuphide of effect.
The purpose of the present invention is realized by technical scheme below:
A kind of tourmaline aids in molybdenum bisuphide class lubricating additive, is counted with the gross mass of the additive as 100%, wherein
Each component and its weight/mass percentage composition are as follows:
Oil-based solvent 70%~90%,
Oil-soluble molybdenum bisuphide 5%~25%,
Oil-soluble tourmaline powder 5%~10%,
Wherein, the oil-based solvent is the one kind in mineral oil and artificial oil;
The oil-soluble molybdenum bisuphide is obtained for molybdenum bisuphide through surface organic modification, and oil-soluble tourmaline powder is electric
Stone powder is obtained through surface organic modification.
The surface organic modification is specially:
Under the conditions of 60 DEG C~90 DEG C, molybdenum bisuphide or tourmaline powder are mixed homogeneously with modified organisms, then placed
More than 2h;
The modified organisms be stearic acid, silane coupler, titanate coupling agent and silicone oil in one or two with
On mixture;
The addition of the modified organisms is the 0.5wt%~5wt% of molybdenum bisuphide or tourmaline powder.
Described oil-soluble molybdenum bisuphide particle diameter is 0.5~3 μm;
Described oil-soluble tourmaline powder particle diameter is 0.1~0.3 μm;
Tourmaline of the present invention aids in the preparation method of molybdenum bisuphide class lubricating additive, and step is as follows:At 5~60 DEG C
Under the conditions of, under agitation, oil-soluble molybdenum bisuphide and oil-soluble tourmaline powder being added in oil-based solvent in proportion, mixing is equal
It is even, it is finally transferred to 5~20min of ultrasound in ultrasonic container.
Wherein, mix homogeneously preferably stirs 5~30min.
Beneficial effect
During various machineries are lubricated, emollient component unavoidably bears very big pressure and hot conditionss, merely
In the presence of molybdenum bisuphide, can slowly be oxidized to the oxides such as molybdenum trisulfide, molybdenum trioxide and reduce performance;The present invention is by oil
Dissolubility tourmaline powder is used in mixed way with molybdenum bisuphide, tourmaline powder is pressurized when being heated can and oxygen, moisture form O2-(H2O)n、OH-
(H2O)n, reach and suppress the purpose of molybdenum bisuphide oxidizing process, and itself will not consume, principle is as shown in Figure 1.Can replace disappearing certainly
Consumption type antioxidant, with good economic benefit.
The lubricating additive of the present invention has extraordinary dispersibility and stability, can under the assosting effect of tourmaline powder
It is obviously improved the use temperature and service life of molybdenum bisuphide.
Description of the drawings
Fig. 1 tourmaline lift molybdenum bisuphide oxidation resistance schematic diagram:(A) it is not added with the MoS of tourmaline powder2Surface oxidation
Reaction;(B) MoS after tourmaline is added2Surface reaction.
Specific embodiment
Below in conjunction with the accompanying drawings with specific embodiment describing the present invention, but not limited to this in detail.
Embodiment 1
Molybdenum bisuphide and the modified of tourmaline powder adopt the mixed machine of heat for modified device, and revolution is 900r/min.Take 200g bis-
Molybdenum sulfide (0.5~3 μm), under the conditions of 80 DEG C, is added thereto to 1g stearic acid, and oil-soluble molybdenum bisuphide can be obtained after 2h.
Molybdenum bisuphide (0.5~3 μm) is substituted for into tourmaline powder (0.1~0.3 μm), oil-soluble tourmaline is obtained using identical method
Powder.Under the conditions of 5 DEG C, oil-soluble molybdenum bisuphide 50g, oil-soluble tourmaline powder 50g are added to into the 900g platforms modeling 500N of stirring
In base oil, 20min is stirred, being finally transferred to ultrasound 15min in ultrasonic container, that tourmaline of the present invention is obtained is auxiliary
Help molybdenum bisuphide class lubricating additive.The additive of preparation was not settled in 6 months, is shown that additive has and is divided well
Scattered property and stability.Additive is heated to into 150 DEG C, and air is passed through with the speed of 20ml/min, filtered after seven days, consolidate
Body powder, pressed powder is tested using X-ray photoelectron spectroscopic analysis, as a result shows that molybdenum element is deposited with molybdenum bisuphide state
;Simultaneously contrast test is carried out, (composition is the sulfur of 50g oil-solubles two to be not added with the molybdenum bisuphide additive of oil-soluble tourmaline powder
Change molybdenum and 900g platforms modeling 500N base oils) in molybdenum bisuphide state exist molybdenum only account for 30%, remaining be molybdenum trisulfide and three
Molybdenum oxide.The contrast test shows that tourmaline powder can suppress the oxidation of molybdenum bisuphide, prolongation to make under high temperature and oxidation atmosphere
Use the life-span.
Embodiment 2
Molybdenum bisuphide and the modified of tourmaline powder adopt the mixed machine of heat for modified device, and revolution is 900r/min.Take 150g bis-
Molybdenum sulfide (0.5~3 μm), under the conditions of 90 DEG C, is added thereto to 7.5g silane couplers, and the sulfur of oil-soluble two can be obtained after 2h
Change molybdenum.Molybdenum bisuphide (0.5~3 μm) is substituted for into tourmaline powder (0.1~0.3 μm), oil-soluble is obtained using identical method
Tourmaline powder.Under the conditions of 60 DEG C, oil-soluble molybdenum bisuphide 50g, oil-soluble tourmaline powder 100g are added to into the 850g of stirring
In double imperial 150N base oils, 5min is stirred, be finally transferred to ultrasound 30min in ultrasonic container and electricity of the present invention is obtained
Gas stone aids in molybdenum bisuphide class lubricating additive.The additive of preparation was not settled in 6 months, showed that additive has very
Dispersibility well and stability.Additive is heated to into 150 DEG C, and air is passed through with the speed of 20ml/min, filtered after seven days,
Pressed powder is obtained, pressed powder is tested using X-ray photoelectron spectroscopic analysis, as a result show molybdenum element with molybdenum bisuphide shape
State is present;Simultaneously contrast test is carried out, (composition is 50g oil-soluble molybdenum bisuphide to be not added with the additive of oil-soluble tourmaline powder
With the double dragon 150N base oils of 850g) in the molybdenum that exists with molybdenum bisuphide state only account for 33%, remaining is that molybdenum trisulfide and three aoxidize
Molybdenum.The contrast test shows that under high temperature and oxidation atmosphere tourmaline powder can suppress the oxidation of molybdenum bisuphide, prolongation to use the longevity
Life.
Embodiment 3
Molybdenum bisuphide and the modified of tourmaline powder adopt the mixed machine of heat for modified device, and revolution is 900r/min.Take 360g bis-
Molybdenum sulfide (0.5~3 μm), under the conditions of 90 DEG C, is added thereto to 10.8g silicone oil, and oil-soluble molybdenum bisuphide can be obtained after 2h.
Molybdenum bisuphide (0.5~3 μm) is substituted for into tourmaline powder (0.1~0.3 μm), oil-soluble tourmaline is obtained using identical method
Powder.Under the conditions of 40 DEG C, oil-soluble molybdenum bisuphide 250g, oil-soluble tourmaline powder 50g are added to into the 700g Korea SK of stirring
Poly alpha olefin in, stir 15min, be finally transferred to ultrasound 5min in ultrasonic container and tourmaline of the present invention be obtained
Auxiliary molybdenum bisuphide class lubricating additive.The additive of preparation was not settled in 6 months, showed that additive has good
Dispersibility and stability.Additive is heated to into 150 DEG C, and air is passed through with the speed of 20ml/min, filtered after seven days, obtained
Pressed powder, pressed powder is tested using X-ray photoelectron spectroscopic analysis, as a result shows that molybdenum element is deposited with molybdenum bisuphide state
;Simultaneously contrast test is carried out, (composition is 250g oil-solubles molybdenum bisuphide and 700g Korea SK to be not added with oil-soluble tourmaline powder
Poly alpha olefin) in the molybdenum that exists with molybdenum bisuphide state account for 29%, remaining is molybdenum trisulfide and molybdenum trioxide.The contrast test
Show that tourmaline powder can suppress the oxidation of molybdenum bisuphide, increase the service life under high temperature and oxidation atmosphere.
Embodiment 4
Molybdenum bisuphide and the modified of tourmaline powder adopt the mixed machine of heat for modified device, and revolution is 900r/min.Take 120g bis-
Molybdenum sulfide (0.5~3 μm), under the conditions of 90 DEG C, is added thereto to 3.6g silicone oil, the titanate coupling agent of 1.4g, after 2h
Obtain oil-soluble molybdenum bisuphide.Molybdenum bisuphide (0.5~3 μm) is substituted for into tourmaline powder (0.1~0.3 μm), using identical
Method obtains oil-soluble tourmaline powder.Under the conditions of 30 DEG C, oil-soluble molybdenum bisuphide 100g, oil-soluble tourmaline powder 80g are added
Enter in the 820g Kelamayis 150BS of stirring, stir 20min, be finally transferred to ultrasound 15min in ultrasonic container and be obtained
Tourmaline of the present invention aids in molybdenum bisuphide class lubricating additive.The additive of preparation was not settled in 6 months, table
Bright additive has good dispersibility and stability.Additive is heated to into 150 DEG C, and sky is passed through with the speed of 20ml/min
Gas, filters after seven days, obtains pressed powder, and pressed powder is tested using X-ray photoelectron spectroscopic analysis, as a result shows molybdenum unit
Element is with the presence of molybdenum bisuphide state;Simultaneously contrast test is carried out, (composition is 100g oil-solubles two to be not added with oil-soluble tourmaline powder
Molybdenum sulfide and 820g Kelamayis 150BS) in the molybdenum that exists with molybdenum bisuphide state account for 31%, remaining is molybdenum trisulfide and three oxygen
Change molybdenum.The contrast test shows that tourmaline powder can suppress the oxidation of molybdenum bisuphide, prolongation to use under high temperature and oxidation atmosphere
Life-span.
The present invention includes but is not limited to above example, every any equivalent carried out under the principle of spirit of the present invention
Replace or local improvement, all will be regarded as within protection scope of the present invention.
Claims (4)
1. a kind of tourmaline aids in molybdenum bisuphide class lubricating additive, it is characterised in that the gross mass with the additive is
100% meter, wherein each component and its weight/mass percentage composition are as follows:
Oil-based solvent 70%~90%,
Oil-soluble molybdenum bisuphide 5%~25%,
Oil-soluble tourmaline powder 5%~10%,
Wherein, the oil-based solvent is the one kind in mineral oil and artificial oil;
The oil-soluble molybdenum bisuphide is obtained for molybdenum bisuphide through surface organic modification, and oil-soluble tourmaline powder is tourmaline powder
Obtain through surface organic modification
The surface organic modification is specially:
Under the conditions of 60 DEG C~90 DEG C, molybdenum bisuphide or tourmaline powder are mixed homogeneously with modified organisms, then place 2h with
On;
The modified organisms are one or more in stearic acid, silane coupler, titanate coupling agent and silicone oil
Mixture;
The addition of the modified organisms is the 0.5wt%~5wt% of molybdenum bisuphide or tourmaline powder.
2. a kind of tourmaline according to claim 1 aids in molybdenum bisuphide class lubricating additive, it is characterised in that described
Oil-soluble molybdenum bisuphide particle diameter is 0.5~3 μm;Oil-soluble tourmaline powder particle diameter is 0.1~0.3 μm.
3. a kind of tourmaline as claimed in claim 1 aids in the preparation method of molybdenum bisuphide class lubricating additive, its feature to exist
In methods described step is as follows:Under the conditions of 5~60 DEG C, under agitation, in proportion by oil-soluble molybdenum bisuphide and oil-soluble electricity
Gas stone powder is added in oil-based solvent, mix homogeneously, is finally transferred to 5~20min of ultrasound in ultrasonic container.
4. tourmaline according to claim 3 aids in the preparation method of molybdenum bisuphide class lubricating additive, it is characterised in that
The mix homogeneously specially stirs 5~30min.