A kind of orange disperse dye
Technical field
The present invention relates to orange disperse dye composition.
Background technology
Along with fast development and people's raising to textile demand of polyester Fresh fats in recent years, correspondingly, dyeability, environmental-protecting performance that dyestuff itself is had it is also proposed the requirement that history is high, it is desirable to dyestuff has high lifting force and every colorfastness. To this, compound synergic means how are utilized to develop new dye species, particularly application) general blue-black dye species, become the emphasis that industry experts is chased, but from existing composite dye species such as patent JP2005-036071, US2004339252, JP11-158402, the formula dyestuff that US6562082 etc. provide, still can not fully meet requirement in the application performance such as lifting force and dyefastness.
Summary of the invention
The technical problem to be solved is: provides a kind of dyeability good, is not easily disconnected from the orange disperse dye of polyster fibre after dyeing.
For solving above-mentioned technical problem, the technical solution used in the present invention: a kind of orange disperse dye, by mass fraction, it consists of: component A:38-40 part, component B:72-75 part, component C:30-35 part, component D:30-35 part, component E:15-20 part;
Described component A, its structural formula (I) is as follows:
Described component B, its structural formula (II) is as follows:
Described component C, its structural formula (III) is as follows:
Described component D, its structural formula (IV) is as follows:
Described component E is dispersant.
Described a kind of orange disperse dye, by mass fraction, it preferably constitutes as component A:38 part, component B:73 part, component C:33 part, component D:35 part, component E:18 part;
Or
Component A:40 part, component B:75 part, component C:30 part, component D:32 part, component E:15 part.
Described dispersant is: lignosulfonates or carbonate condensation substance.
Owing to have employed technique scheme, the invention have the advantages that and effect: the dye composite of the present invention, dye by ways customary in industry, the dyeing and weaving thing that the color fastness such as form and aspect full, light fastness, washing fastness, crock fastness are excellent can be obtained.
Detailed description of the invention
It is described in further detail in conjunction with specific embodiments, makes advantages of the present invention become apparent from. It should be understood that content therein is used merely as explanation, and absolutely not protection scope of the present invention is construed as limiting. The experimental technique of unreceipted actual conditions in the following example, generally conventionally condition, or according to manufacturer it is proposed that condition carry out.
Embodiment |
Component A |
Component B |
Component C |
Component D |
Component E |
Embodiment 1 |
38g |
72g |
35g |
32g |
15g |
Embodiment 2 |
40g |
75g |
30g |
30g |
16g |
Embodiment 3 |
39g |
73g |
31g |
32g |
17g |
Embodiment 4 |
38.5g |
74g |
33g |
31.5g |
18g |
Embodiment 5 |
39.5g |
73g |
32g |
30g |
19g |
Embodiment 6 |
40g |
72g |
34g |
32g |
20g |
Embodiment 7 |
39g |
73.5g |
33.5g |
34g |
17g |
Embodiment 8 |
38g |
73g |
33g |
35g |
18g |
Embodiment 9 |
40g |
75g |
30g |
32g |
15g |
Forming by above-mentioned quality, each component being fully ground stirs both obtains finished product; The orange disperse dye that above-mentioned enforcement prepares is carried out performance test, and method of testing is as follows:
Take this finished product 0.5 gram, it is scattered in 500 grams of cold water, mixs homogeneously with 32mL water after taking 8mL after being sufficiently stirred for, regulate PH=4.0 with acetic acid, put into 2 grams of polyster fibres to dye, rise to 130 DEG C with the heating rate of 3 DEG C/min, be cooled to 80 DEG C after insulation 30min, clean sampling, obtain black dyeing and weaving thing, without reduction cleaning, GB/T3921-1997, GB/T5718-1997, GB/T3920-1997 method of employing carries out fastness test, and test result is as shown in the table:
Embodiment title |
Washing fastness (60 DEG C) |
Sublimation reliability (180 DEG C) |
Fastness to wet rubbing |
Embodiment 1 |
4 grades |
5 grades |
5 grades |
Embodiment 2 |
5 grades |
4-5 level |
5 grades |
Embodiment 3 |
5 grades |
4-5 level |
5 grades |
Embodiment 4 |
4-5 level |
5 grades |
4-5 level |
Embodiment 5 |
4 grades |
4-5 level |
5 grades |
Embodiment 6 |
5 grades |
4-5 level |
5 grades |
Embodiment 7 |
4-5 level |
4 grades |
4-5 level |
Embodiment 8 |
5 grades |
5 grades |
5 grades |
Embodiment 9 |
5 grades |
4-5 level |
5 grades |
According to above-mentioned test result, and the dye shade performance of different ratio, selecting embodiment 8 is optimum proportioning: orange disperse dye provided by the present invention, without through reduction cleaning on polyster fibre, fastness can reach outstanding representation, shortens staining procedure, reduces dyeing time, reducing production cost, industrial application value is high.