CN104496259B - 一种缓凝型助磨剂 - Google Patents
一种缓凝型助磨剂 Download PDFInfo
- Publication number
- CN104496259B CN104496259B CN201410660556.3A CN201410660556A CN104496259B CN 104496259 B CN104496259 B CN 104496259B CN 201410660556 A CN201410660556 A CN 201410660556A CN 104496259 B CN104496259 B CN 104496259B
- Authority
- CN
- China
- Prior art keywords
- cement
- grinding aid
- waste liquid
- slow
- concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及水泥外加剂技术领域,特别涉及一种缓凝型助磨剂,由以下重量百分比的原料制成:醇胺类化合物10~25%,丙二醇12~17%,造纸废液10~18%,糖厂废液8~14%,纤维素保水材料0.02~0.05%,葡萄糖酸钙0.1~0.5%,十二烷基苯磺酸钠0.02~0.06%,水余量。本发明的助磨剂具有良好的缓凝效果,且能提高水泥的早后期强度,保证水泥的质量,还具有良好的保塑效果,成本低。本发明助磨剂可在炎热气候下施工的混凝土、大体积混凝土及需长时间停放或长距离运输的水泥混凝土中使用。
Description
技术领域
本发明涉及水泥外加剂技术领域,特别涉及一种缓凝型助磨剂。
背景技术
缓凝水泥助磨剂主要用于炎热气候下施工的混凝土、大体积混凝土及需长时间停放或长距离运输的水泥混凝土。缓凝水泥助磨剂的化学成分主要有:羟基羧酸类物质-酒石酸及其盐等、多羟基碳水化合物-糖类及其衍生物,糖蜜及其改性物等、木质素磺酸盐类、无机化合物、腐殖酸类减水剂等。缓凝水泥助磨剂能延长混凝土的凝结时间,使新拌水泥混凝土在较长时间内保持塑性,有利于浇筑成型和提高施工质量,抑制水化放热速度,减慢放热速率和降低水泥初期水化热,从而防止了早期温度裂缝的出现。掺缓凝剂及缓凝减水剂混凝土由于早期水化物生长变慢,而得到了更均匀分布和充分的生长,使水化产物搭接的更加完整和密实,有利于硬化混凝土抗掺和抗冻融性能的提高。
目前市场上普遍使用糖蜜、蔗糖做缓凝水泥助磨剂,现有的缓凝剂效果不佳,功能单一,而且成本较高。
发明内容
本发明所要解决的技术问题是提供一种缓凝型助磨剂,该助磨剂具有良好的缓凝效果,且能提高水泥的早后期强度,保证水泥的质量,还有良好的保塑效果,成本低。
为实现上述目的,本发明采用如下技术方案:
一种缓凝型助磨剂,由以下重量百分比的原料制成:
上述所述的醇胺类化合物为三乙醇胺、三异丙醇胺、二乙醇单异丙醇胺、二异丙基乙醇胺一种或多种任意比例混合。
上述所述纤维素保水材料为甲基纤维素、羟丙基甲基纤维素、羟乙基甲基纤维素中的一种。
优选地,本发明的缓凝型助磨剂,由以下重量百分比的原料制成:
优选地,所述的造纸废液的波美度为30~35°Bé。
本发明的上述配方中,醇胺类化合物分子中既含有氨基又含有羟基,具有胺和醇的综合性能,作为表面活性剂具有良好的分散性,还作为早强剂,提高水泥的早、后期强度;丙二醇端基是一个脂肪烃基且有独立的疏水基团在其外,具有较好的分散性,有利于粉体的流动,提高粉磨效率;造纸废液富含木质素磺酸盐,其对水泥颗粒以及水化产物新相表面具有较强的活性作用,吸附于固体颗粒表面,延缓了水泥的水化和浆体结构的形成,从而延缓水泥缓凝的时间,同时,造纸废液还富含甲酸钙,在水泥粉磨过程中能够提高磨内物料的流动速度,提高水泥的早期强度;糖厂废液具有较强极性,吸附作用好,可调节水泥凝结的时间和中后期强度;纤维素保水材料可在水泥中有效保水,且随着水化进行缓慢释放部分水分,为水泥的水化提供水源,与缓凝剂协同作用,增强缓凝效果且能提高水泥强度,同时纤维素保水材料还具有保塑效果,保持水泥的体积稳定性;葡萄糖酸钙进一步提高水泥的缓凝效果,同时保证水泥的强度;十二烷基苯磺酸钠能够提高助磨剂与水泥的适应性,扩大助磨剂的适用范围。
本发明的有益效果在于:
1、本发明的造纸废液和糖厂废液作为高度污染物,被综合利用,变废为宝,降低成本,保护环境。
2、本发明的缓凝型助磨剂,不但缓凝效果显著,且其能够提高水泥早后期的强度,还具有良好的保塑效果,提高水泥的实用性。
3、本发明的缓凝型助磨剂适应性强,适合不同等级强度的水泥使用。
具体实施方式
以下结合实施例对本发明作进一步说明,但本发明并不局限于这些实施例。
实施例1
按重量百分比称取以下原料:三异丙醇胺5%、二乙醇单异丙醇胺5%、丙二醇17%、波美度为30°Bé的造纸废液10%、糖厂废液14%、甲基纤维素0.02%、葡萄糖酸钙0.1%、十二烷基苯磺酸钠0.06%、水48.82%;
将水加热至55℃,依次放入三异丙醇胺、二乙醇单异丙醇胺、丙二醇、造纸废液、糖厂废液、甲基纤维素、葡萄糖酸钙、十二烷基苯磺酸钠,搅拌均匀,降至室温,即得产品。
实施例2
按重量百分比称取以下原料:三异丙醇胺8%、二异丙基乙醇胺6%、丙二醇16%、波美度为31°Bé的造纸废液12%、糖厂废液13%、羟丙基甲基纤维素0.02%、葡萄糖酸钙0.2%、十二烷基苯磺酸钠0.05%、水44.73%;
将水加热至55℃,依次放入三异丙醇胺、二异丙基乙醇胺、丙二醇、造纸废液、糖厂废液、羟丙基甲基纤维素、葡萄糖酸钙、十二烷基苯磺酸钠,搅拌均匀,降至室温,即得产品。
实施例3
按重量百分比称取以下原料:三乙醇胺10%、三异丙醇胺8%、丙二醇15%、波美度为32°Bé的造纸废液14%、糖厂废液11%、羟乙基甲基纤维素0.03%、葡萄糖酸钙0.3%、十二烷基苯磺酸钠0.04%、水41.63%;
将水加热至55℃,依次放入三乙醇胺、三异丙醇胺、丙二醇、造纸废液、糖厂废液、羟乙基甲基纤维素、葡萄糖酸钙、十二烷基苯磺酸钠,搅拌均匀,降至室温,即得产品。
实施例4
按重量百分比称取以下原料:二乙醇单异丙醇胺11%、二异丙基乙醇胺10%、丙二醇13%、波美度为33°Bé的造纸废液16%、糖厂废液10%、甲基纤维素0.04%、葡萄糖酸钙0.4%、十二烷基苯磺酸钠0.03%、水39.53%;
将水加热至55℃,依次放入二乙醇单异丙醇胺、二异丙基乙醇胺、丙二醇、造纸废液、糖厂废液、甲基纤维素、葡萄糖酸钙、十二烷基苯磺酸钠,搅拌均匀,降至室温,即得产品。
实施例5
按重量百分比称取以下原料:三乙醇胺25%、丙二醇12%、波美度为35°Bé的造纸废液18%、糖厂废液8%、羟丙基甲基纤维素0.05%、葡萄糖酸钙0.5%、十二烷基苯磺酸钠0.02%、水36.43%;
将水加热至55℃,依次放入三乙醇胺、丙二醇、造纸废液、糖厂废液、羟丙基甲基纤维素、葡萄糖酸钙、十二烷基苯磺酸钠,搅拌均匀,降至室温,即得产品。
将实施例1~5中制得的缓凝型助磨剂产品,用在普通水泥中来进行对比试验,试验结果如表1所示:
表1 实施例1~5产品的试验结果数据
Claims (3)
1.一种缓凝型助磨剂,其特征在于,由以下重量百分比的原料制成:
所述的醇胺类化合物为三乙醇胺、三异丙醇胺、二乙醇单异丙醇胺、二异丙基乙醇胺一种或多种任意比例混合,所述纤维素保水材料为甲基纤维素、羟丙基甲基纤维素、羟乙基甲基纤维素中的一种。
2.根据权利要求1所述的缓凝型助磨剂,其特征在于,由以下重量百分比的原料制成:
3.根据权利要求1或2所述的缓凝型助磨剂,其特征在于:所述的造纸废液的波美度为30~35°Bé。