CN104480705A - Finishing process for elastic fabric - Google Patents

Abstract

The invention discloses a finishing process for an elastic fabric. The finishing process comprises the following steps: (1) adding 2.5 parts by mass of butyl acrylate, 1.7 parts by mass of hydroxy propyl cellulose and 0.6 part by mass of ethanol into 9.3 parts of de-ionized water, and uniformly stirring; (2) slowly adding 1.7 parts by mass of hydroxypropyl methyl cellulose and 4.3 parts by mass of glycerin at the same time, and continuously stirring until the mixing is full and uniform to obtain a finishing agent; (3) performing padding treatment on the fabric in impregnation liquid containing the finishing agent, and drying at the constant temperature. According to the finishing process, the fabric processed by the finishing process is excellent in antibacterial property and antifouling property and good in washability.

Description

The finishing technique of elastic fabric

Technical field

The present invention relates to the finishing technique of elastic fabric.

Background technology

The anti-microbial property of existing fabric, antifouling property and washing fastness all have much room for improvement.

Summary of the invention

The object of the present invention is to provide a kind of finishing technique of elastic fabric, the fabric after its arrangement has excellent anti-microbial property, antifouling property, and washability is strong.

For achieving the above object, technical scheme of the present invention designs a kind of finishing technique of elastic fabric, comprises the steps:

1) in 9.3 parts by mass deionized waters, drop into 2.5 parts by mass butyl acrylates, 1.7 parts by mass hydroxypropyl celluloses, 0.6 parts by mass ethanol mixing, stir;

2) slowly add 1.7 parts by mass hydroxypropyl methylcelluloses, 4.3 parts by mass glycerine more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

Advantage of the present invention and beneficial effect are: a kind of finishing technique of elastic fabric, and the fabric after its arrangement has excellent anti-microbial property, antifouling property, and washability is strong.

Detailed description of the invention

Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.

The technical scheme that the present invention specifically implements is:

A finishing technique for elastic fabric, comprises the steps:

1) in 9.3 parts by mass deionized waters, drop into 2.5 parts by mass butyl acrylates, 1.7 parts by mass hydroxypropyl celluloses, 0.6 parts by mass ethanol mixing, stir;

2) slowly add 1.7 parts by mass hydroxypropyl methylcelluloses, 4.3 parts by mass glycerine more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.

The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (1)

1. the finishing technique of elastic fabric, is characterized in that, comprises the steps:

1) in 9.3 parts by mass deionized waters, drop into 2.5 parts by mass butyl acrylates, 1.7 parts by mass hydroxypropyl celluloses, 0.6 parts by mass ethanol mixing, stir;

2) slowly add 1.7 parts by mass hydroxypropyl methylcelluloses, 4.3 parts by mass glycerine more simultaneously, continue to stir, to fully mixing, obtained finishing agent;

3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.