CN104479371A - 一种聚苯乙烯-聚丙烯共混物改性沥青的制备工艺 - Google Patents

一种聚苯乙烯-聚丙烯共混物改性沥青的制备工艺 Download PDF

Info

Publication number
CN104479371A
CN104479371A CN201410672762.6A CN201410672762A CN104479371A CN 104479371 A CN104479371 A CN 104479371A CN 201410672762 A CN201410672762 A CN 201410672762A CN 104479371 A CN104479371 A CN 104479371A
Authority
CN
China
Prior art keywords
polystyrene
pitch
polypropylene blend
polypropylene
modifying asphalt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410672762.6A
Other languages
English (en)
Inventor
黎裕发
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410672762.6A priority Critical patent/CN104479371A/zh
Publication of CN104479371A publication Critical patent/CN104479371A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种聚苯乙烯和聚丙烯共混物改性沥青的制备工艺，该工艺是先将沥青脱水，再加入一定比例的聚苯乙烯和聚丙烯共混物，在剪切机中剪切。该制备工艺流程简单、制备出的改性沥青稳定性较好。

Description

一种聚苯乙烯-聚丙烯共混物改性沥青的制备工艺
技术领域
本发明涉及一种沥青材料，特别涉及一种共混物改性沥青的制备工艺，属于新材料领域。
背景技术
自1988年我国建成第一条高速公路（沪嘉高速公路）以来，经过20多年的持续快速发展，到2013年底,我国高速公路总里程已达到8.0万公里，其中沥青混凝土路面约占80%
左右。道路沥青的需求逐年增加，“十二五”期间，道路沥青消费量平均每年在1500万吨左右。
沥青是原油加工过程的一种产品，在常温下是黑色或黑褐色的粘稠液体或者是固体，它是一种棕黑色有机胶凝状物质，主要成分是沥青质和树脂。沥青路面优点很多，一是车轮与路面两级减振，因此行车舒适性好、噪音小；二是柔性路面对路基、地基变形或不均匀沉降的适应性强；三是路面修复速度快，碾压后即可通车。但是我国地域辽阔，南方与北方气候差异大，,温度、雨量也不相同，导致沥青路面的使用状况差别很大，沥青路面破坏的原因差别大。如寒冷地区对沥青的低温性能要求高，炎热地区对沥青的高温稳定性要求高，潮湿多雨地区则对沥青的水稳定性要求高。而普通沥青并不能满足所有使用性能要求，必须采用质量好的沥青，以满足不同环境对路面使用性能的要求。
为了改善沥青路面使用品质，道路工作者从影响沥青路用性能的各个方面入手，逐
步改善沥青路面的使用性能，其中很重要的一方面就是对沥青尤其是重交道路沥青进行技术改进。公路建设一方面对道路沥青数量需求增大，另一方面对质量品质要求提高。而目前我国高等级道路沥青供应远远不足，根本不能满足不了市场需求，大量沥青主要依赖进口。因而，积极探索产量大、成本低、稳定性强、工艺简单的新型沥青，用以提高国产沥青的性能，实现降低工程成本、保证工程质量，己成为高性能沥青研究的重要内容。往沥青中加入聚合物是一种常用的改性方法，例如加入聚苯乙烯和聚丙烯，本发明以氯化聚乙烯为增溶剂使聚苯乙烯和聚丙烯共混，加入到沥青中，提高沥青的使用性能。由于具有较好的相容性，该沥青性能稳定。
发明内容
本发明的目的是提供一种聚苯乙烯和聚丙烯共混物改性沥青的制备方法，该制备方法按如下步骤进行：
⑴  先将沥青盛放器皿中，置于可控温的砂浴、油浴上加热脱水，并用玻璃棒轻轻搅拌，防止局部过热；
⑵ 观察沥青没泡沫冒出时，停止加热，迅速把沥青倒入高速剪切机中，启动高速剪切机，控制转速在500r/min以内；
⑶ 将聚苯乙烯和聚丙烯加入搅拌器中，再加入氯化聚乙烯，搅拌2min；
⑷ 将搅拌混合后的聚苯乙烯和聚丙烯共混物加入剪切机中；
⑸ 将剪切机速度提高至600r/min以上，剪切5-10min，即得一种聚苯乙烯和聚丙烯共混物改性沥青。
作为本发明的优先实施例，沥青脱水加热温度不超过100℃。
作为本发明的优先实施例，聚苯乙烯和聚丙烯的投入摩尔比为1:1。
作为本发明的优先实施例，聚苯乙烯和聚丙烯共混物添加量与沥青添加量的比例小于1：10。
本发明具有下列优点和特性：
⑴ 这种沥青稳定性好，不分层；
⑵ 产品资源丰富、价格低廉；
⑶ 制备工艺简单，易大规模生产。
具体实施方式
实施例一：
 ⑴ 称取200g沥青放入烧杯中，把烧杯置于80℃的水浴中加热，并用玻璃棒轻轻搅拌，防止局部过热；
⑵ 观察沥青冒泡情况，当停止冒出泡沫时，停止加热；
⑶ 迅速把脱水的沥青倒入高速剪切机中，启动高速剪切机，转速设置为300r/min；
⑷ 取聚苯乙烯和聚丙烯粉末各10g，加入搅拌器中，再加入氯化聚乙烯粉末5g，搅拌2min；
⑸ 将搅拌混合后的聚苯乙烯和聚丙烯共混物加入剪切机中；
⑹ 将剪切机速度提高至600r/min，剪切5min，即得一种聚苯乙烯和聚丙烯共混物改性沥青。
实施例二：
⑴  称取500g沥青放入烧杯中，把烧杯置于90℃的水浴中加热，并用玻璃棒轻轻搅拌，防止局部过热；
⑵  观察沥青冒泡情况，当停止冒出泡沫时，停止加热；
⑶ 迅速把脱水的沥青倒入高速剪切机中，启动高速剪切机，转速设置为400r/min；
⑷ 取聚苯乙烯和聚丙烯粉末各25g，加入搅拌器中，再加入氯化聚乙烯粉末10g，搅拌2min；
⑸  将搅拌混合后的聚苯乙烯和聚丙烯共混物加入剪切机中；
⑹ 将剪切机速度提高至700r/min，剪切8min，即制得一种聚苯乙烯和聚丙烯共混物改性沥青。
实施例三：
⑴ 称取5000g沥青放入烧杯中，把烧杯置于100℃的水浴中加热，并用木棒搅拌，防止局部过热；
⑵ 观察沥青冒泡情况，当停止冒出泡沫时，停止加热；
⑶ 迅速把脱水的沥青倒入高速剪切机中，启动高速剪切机，转速设置为500r/min；
⑷ 取聚苯乙烯和聚丙烯粉末各150g，加入搅拌器中，再加入氯化聚乙烯粉末50g，搅拌2min；
⑸ 将搅拌混合后聚苯乙烯和聚丙烯粉末共混物加入剪切机中；
⑹ 将剪切机速度提高至800r/min，剪切10min，即制得一种聚苯乙烯和聚丙烯共混物改性沥青。

Claims (4)

1.一种聚苯乙烯和聚丙烯共混物改性沥青的制备工艺，其特征在于该工艺按如下步骤进行：
⑴  先将沥青盛放器皿中，置于可控温的砂浴、油浴上加热脱水，并用玻璃棒轻轻搅拌，防止局部过热；
⑵ 观察沥青没泡沫冒出时，停止加热，迅速把沥青倒入高速剪切机中，启动高速剪切机，控制转速在500r/min以内；
⑶ 将聚苯乙烯和聚丙烯粉末加入搅拌器中，再加入氯化聚乙烯粉末，搅拌2min；
⑷ 将搅拌混合后的聚苯乙烯和聚丙烯共混物加入剪切机中；
⑸ 将剪切机速度提高至600r/min以上，剪切5-10min，即制取一种聚苯乙烯和聚丙烯共混物改性沥青。
2.根据权利要求1所述的一种聚苯乙烯和聚丙烯共混物改性沥青的制备方法，其特征在于沥青脱水加热温度不超过100℃。
3.根据权利要求1所述的一种聚苯乙烯和聚丙烯共混物改性沥青的制备方法，其特征在于聚苯乙烯和聚丙烯的投入摩尔比为1:1。
4.根据权利要求1所述的一种聚苯乙烯和聚丙烯共混物改性沥青的制备方法，其特征在于聚苯乙烯和聚丙烯共混物添加量与沥青添加量的比例小于1：10。
CN201410672762.6A 2014-11-23 2014-11-23 一种聚苯乙烯-聚丙烯共混物改性沥青的制备工艺 Pending CN104479371A (zh)