CN104448100A - 一种钻井液用聚合物抑制剂的制备方法 - Google Patents
一种钻井液用聚合物抑制剂的制备方法 Download PDFInfo
- Publication number
- CN104448100A CN104448100A CN201410678200.2A CN201410678200A CN104448100A CN 104448100 A CN104448100 A CN 104448100A CN 201410678200 A CN201410678200 A CN 201410678200A CN 104448100 A CN104448100 A CN 104448100A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- reaction
- concentration
- reactor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种钻井液用聚合物抑制剂的制备方法，首先将浓度为33%的三甲胺187份置于反应釜中，控制温度在20℃±2，再向反应釜中滴加环氧氯丙烷95.3份，期间控制反应釜内温度在35℃以下，直至滴加完毕；恒温40℃±2反应120分钟；将过硫酸铵15.3-18.7份放入32份的去离子水中，配制成引发剂溶液备用；待物料恒温反应120分钟后再依次加入331-566份去离子水和马来酸酐3份、丙烯酸24份、异丙醇25.5份搅拌混合均匀，升温至80～85℃之间；然后将引发剂溶液滴加进反应釜内，保持温度在90～100℃之间，从滴加引发剂溶液开始计时，持续反应120分钟；反应后用浓度40%的氢氧化钠溶液调节物料pH值为6-7，降物料温度至室温即可。它具有高效、长久的抑制性，且对页岩及泥页岩有良好的抑制性能。
Description
技术领域：
本发明是一种钻井液用聚合物抑制剂的制备方法，用它加入到钻井液中，能有效地抑制泥页岩水化膨胀，保障钻井液的滤失性能。
背景技术：
在油气钻采过程中，为了提高钻采效率，防止井壁坍塌，需要在钻井液中加入抑制剂。目前的钻井液抑制剂有两种，一种是无机盐抑制剂，另一种是聚合物抑制剂。无机盐抑制剂因其使用量大，易破坏钻井液的滤失性能，其用量逐渐下降，聚合物抑制剂多采用聚胺类原料制成，它虽优于无机盐抑制剂，但当钻遇泥页岩时，其抑制性能有限，不能广泛使用。
发明内容：
本发明的目的是提供一种抑制性能长久，适用范围广的一种钻井液用聚合物抑制剂的制备方法。
本发明包括有以下重量组分：浓度33%的三甲胺187份，环氧氯丙烷95.3份，马来酸酐3.0份，丙烯酸24份，异丙醇25.5份，过硫酸铵15.3~18.7份，去离子水363~600份，浓度为40%的氢氧化钠溶液约32份；其制备方法是：①首先将浓度为33%的三甲胺全部置于反应釜中，开启搅拌，控制温度在20℃±2，再向反应釜中滴加环氧氯丙烷，期间控制反应釜内温度在35℃以下，直至滴加完毕；将反应釜内物料升温至40℃±2，恒温反应120分钟；②将过硫酸铵放入32份的去离子水中，配制成引发剂溶液备用；③待反应釜内物料恒温反应120分钟后再依次加入剩下的去离子水和全部的马来酸酐、丙烯酸、异丙醇搅拌溶解混合均匀，将其溶液升温至80~85℃之间；④然后在搅拌状态下将引发剂溶液滴加进反应釜内，使温度升至90℃时加速搅拌，控制温度不超过100℃，保持温度在90~100℃之间，从滴加引发剂溶液开始计时，持续反应120分钟；⑤反应结束后用浓度40%的氢氧化钠溶液调节物料PH值为6-7,降物料温度至室温，停止搅拌即可。用该方法合成的钻井液用聚合物抑制剂，在不影响滤失性能的前提下具有高效、长久的抑制性，且对页岩及泥页岩有良好的抑制性能。
具体实施方式：
本发明有以下实施例：实施例1：①首先将浓度为33%的三甲胺187kg置于反应釜中，开启搅拌，控制温度在20℃±2，再向反应釜中滴加环氧氯丙烷95.2kg，期间控制反应釜内温度在35℃以下，直至滴加完毕；②将反应釜内物料升温至40℃±2，恒温反应120分钟；③将15.3kg过硫酸铵放入32kg的去离子水中，配制成引发剂溶液备用；④待反应釜内物料恒温反应120分钟后再依次加入去离子水331kg和马来酸酐3.0kg、丙烯酸24kg、异丙醇25.5kg搅拌溶解混合均匀，将其溶液升温至80~85℃之间；⑤然后在搅拌状态下将引发剂溶液滴加进反应釜内，使温度升至90℃时加速搅拌，控制温度不超过100℃，保持温度在90~100℃之间，从滴加引发剂溶液开始计时，持续反应120分钟；⑥反应结束后用浓度40%的氢氧化钠溶液约32kg调节物料PH值为6-7,降物料温度至室温，停止搅拌即可。
实施例2：①首先将浓度为33%的三甲胺187kg置于反应釜中，开启搅拌，控制温度在20℃±2，再向反应釜中滴加环氧氯丙烷95.2kg，期间控制反应釜内温度在35℃以下，直至滴加完毕；②将反应釜内物料升温至40℃±2，恒温反应120分钟；③将18.7kg过硫酸铵放入32kg的去离子水中，配制成引发剂溶液备用；④待反应釜内物料恒温反应120分钟后再依次加入去离子水568kg和马来酸酐3.0kg、丙烯酸24kg、异丙醇25.5kg搅拌溶解混合均匀，将其溶液升温至80~85℃之间；⑤然后在搅拌状态下将引发剂溶液滴加进反应釜内，使温度升至90℃时加速搅拌，控制温度不超过100℃，保持温度在90~100℃之间，从滴加引发剂溶液开始计时，持续反应120分钟；⑥反应结束后用浓度40%的氢氧化钠溶液约32kg调节物料PH值为6-7,降物料温度至室温，停止搅拌即可。
该发明提供了在不同聚合浓度下的实施例。反应过程中高浓度聚合反应不易控制，但高浓度聚合物实施例较低浓度聚合实施例所制得产品具有加量小，抑制性强的特点。
Claims (1)
1.一种钻井液用聚合物抑制剂的制备方法，其特征在于：包括有以下重量组分：浓度33%的三甲胺187份，环氧氯丙烷95.3份，马来酸酐3.0份，丙烯酸24份，异丙醇25.5份，过硫酸铵15.3~18.7份，去离子水363~600份，浓度为40%的氢氧化钠溶液约32份；其制备方法是：①首先将浓度为33%的三甲胺全部置于反应釜中，开启搅拌，控制温度在20℃±2，再向反应釜中滴加环氧氯丙烷，期间控制反应釜内温度在35℃以下，直至滴加完毕；将反应釜内物料升温至40℃±2，恒温反应120分钟；②将过硫酸铵放入32份的去离子水中，配制成引发剂溶液备用；③待反应釜内物料恒温反应120分钟后再依次加入剩下的去离子水和全部的马来酸酐、丙烯酸、异丙醇搅拌溶解混合均匀，将其溶液升温至80~85℃之间；④然后在搅拌状态下将引发剂溶液滴加进反应釜内，使温度升至90℃时加速搅拌，控制温度不超过100℃，保持温度在90~100℃之间，从滴加引发剂溶液开始计时，持续反应120分钟；⑤反应结束后用浓度40%的氢氧化钠溶液调节物料PH值为6-7,降物料温度至室温，停止搅拌即可。