CN104439949A - 一种加长焊接钢管的制备方法 - Google Patents
一种加长焊接钢管的制备方法 Download PDFInfo
- Publication number
- CN104439949A CN104439949A CN201410639033.0A CN201410639033A CN104439949A CN 104439949 A CN104439949 A CN 104439949A CN 201410639033 A CN201410639033 A CN 201410639033A CN 104439949 A CN104439949 A CN 104439949A
- Authority
- CN
- China
- Prior art keywords
- burr
- preparation
- welded still
- welding
- lengthening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种加长焊接钢管的制备方法,包括如下步骤:钢带放卷、纵剪、成型、清洗、焊接、清除内外毛刺及内毛刺屑、冷轧、矫直、热处理、酸洗、定尺切制、检验、标记、包装入库;所述成型方法为三维连续柔性排辊成型;所述钢管内毛刺屑的清除方法为先用人工通杆顶出,再用压缩空气清理;所述矫直方法采用6辊矫直。本发明一种加长钢管的制备方法,工艺合理,容易实现,通过合理的成型、焊接、矫直、冷轧等工序,制备了性能优异的小口径、加长型焊接钢管,所制备的奥氏体不锈钢管具有优异的力学强度,应用前景广阔。
Description
技术领域
本发明涉及钢管制备技术领域,特别是涉及一种加长焊接钢管的制备方法。
背景技术
焊接钢管是利用钢板或钢带经成型、焊接、内外焊道处理、退火热处理、整形等工艺制备而成的,其生产水平是焊接钢管技术进步和产品质量水平的标志。与无缝钢管相比,焊接钢管的优势在于:尺寸精度较高、表面质量较好、成材率较高、总体能源消耗较少,适合于大批量生产,成本也低于无缝钢管,具有较强的竞争力和良好的发展前景。但目前的焊接钢管大都是大口径的短管。近年来,随着科技的进步和发展,亟需一种小口径、加长型焊接钢管的生产方法,以满足市场的需求。
发明内容
本发明主要解决的技术问题是提供一种加长焊接钢管的制备方法。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种加长焊接钢管的制备方法,包括如下步骤:钢带放卷、纵剪、成型、清洗、焊接、清除内外毛刺及内毛刺屑、冷轧、矫直、热处理、酸洗、定尺切制、检验、标记、包装入库;所述钢带的成分包括如下质量百分数原料:C 0.05~0.12,Mn 0.33~0.42,P ≤0.02,S≤0.015,Cr 0.55~0.65、Ni 0.05~0.10,其余为Fe;所述成型方法为三维连续柔性排辊成型;所述清洗方法为用有机溶剂清洗成型钢板待焊接部位;所述焊接方法为激光焊接;所述钢管内毛刺屑的清除方法为先用人工通杆顶出,再用压缩空气清理;所述矫直方法采用6辊矫直;所述热处理方法为离线连续热处理,热处理后立即水冷至室温;所述酸洗方法为将热处理后的钢管置于酸洗液中浸泡20~30min,进行酸洗钝化处理。
在本发明一个较佳实施例中,所述有机溶剂为工业酒精。
在本发明一个较佳实施例中,所述激光焊接的工艺参数为:CO2激光器,焊接电压320U/V,焊接功率1500kW,焊接速度0.5m/min。
在本发明一个较佳实施例中,所述热处理条件为:温度1050℃,时间20min。
在本发明一个较佳实施例中,所述酸洗液为30wt%盐酸和15%氢氟酸的水溶液。
在本发明一个较佳实施例中,所述检验包括外观检验、尺寸检验、水压检验和无损探伤。
本发明的有益效果是:本发明一种加长钢管的制备方法,工艺合理,容易实现,通过合理的成型、焊接、矫直、冷轧工序,制备了性能优异的小口径、加长型焊接钢管,所制备的奥氏体不锈钢管具有优异的力学强度,应用前景广阔。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括:
实施例1
加工外径32mm,壁厚3mm,长度为12m的小口径、加长型焊接钢管
(1)钢带放卷:所用钢带的成分包括如下质量百分数原料:C 0.05,Mn 0.33,P≤0.02,S≤0.015,Cr 0.55、Ni 0.05,其余为Fe;将上述钢坯置于开卷机上开卷;
(2)纵剪:将开卷后的钢带纵剪分条成所需尺寸,纵剪时比预成型钢管尺寸多出2~3mm,在纵剪后再将多出的2~3mm部分剪除,以防止钢坯在纵剪吊运过程中造成损伤边缘,产生一些用肉眼看不清的微小裂纹和压痕,造成安全隐患;
(3)成型:采用三维连续柔性排辊成型;
(4)清洗:用工业酒精清洗成型钢板待焊接部位5~8次,以防止成型过程中产生的杂质进入焊缝,影响焊接质量;
(5)焊接:采用CO2激光器进行激光焊接,激光焊接的工艺参数为:焊接电压320U/V,焊接功率1500kW,焊接速度0.5m/min;焊接后,对焊缝进行打磨处理;
(6)清除内外毛刺及内毛刺屑:先采用压入法清楚内径毛刺,然后用人工通杆将内毛刺屑顶出,再用压缩空气清理;内外毛刺清除后的残余高度为-0.05~+0.05mm;
(7)冷轧:采用四辊轧机进行冷轧操作,轧制变量为0.05mm,轧制后用水冷却,用棕榈油润滑;
(8)矫直:采用6辊式矫直机进行矫直处理;
(9)热处理:采用离线连续热处理,热处理方法为固溶热处理,处理温度为1050℃,处理时间20min,热处理后立即水冷至室温;
(10)酸洗:将热处理后的钢管置于30wt%盐酸和15%氢氟酸的水溶液中浸泡20~30min,进行酸洗钝化处理;
(11)定尺切制:清除钢管内的焊筋,用飞锯加长定尺将焊接钢管切断、收集并打捆;
(12)检验:先对上述切制后的焊接钢管进行外观检验、尺寸精度检验,然后再进行无损探伤和水压检验;其中,无损探伤方法为射线探伤,所述水压试验的水压压力为22MPa;
(13)标记:对检验后无缺陷的钢管进行标记;
(14)包装入库。
实施例2
与实施例1的区别在于:
钢管尺寸为:外径38mm,壁厚3mm,长度为12.5m的小口径、加长型焊接钢管;
所用钢带的成分包括如下质量百分数原料:C 0.12,Mn 0.42,P≤0.02,S≤0.015,Cr 0.55、Ni 0.10,其余为Fe;
其他实施方法与实施例1相同。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (6)
1.一种加长焊接钢管的制备方法,其特征在于,包括如下步骤:钢带放卷、纵剪、成型、清洗、焊接、清除内外毛刺及内毛刺屑、冷轧、矫直、热处理、酸洗、定尺切制、检验、标记、包装入库;所述钢带的成分包括如下质量百分数原料:C 0.05~0.12,Mn 0.33~0.42,P ≤0.02,S≤0.015,Cr 0.55~0.65、Ni 0.05~0.10,其余为Fe;所述成型方法为三维连续柔性排辊成型;所述清洗方法为用有机溶剂清洗成型钢板待焊接部位;所述焊接方法为激光焊接;所述钢管内毛刺屑的清除方法为先用人工通杆顶出,再用压缩空气清理;所述矫直方法采用6辊矫直;所述热处理方法为离线连续热处理,热处理后立即水冷至室温;所述酸洗方法为将热处理后的钢管置于酸洗液中浸泡20~30min,进行酸洗钝化处理。
2.根据权利要求1所述的加长焊接钢管的制备方法,其特征在于,所述有机溶剂为工业酒精。
3.根据权利要求1所述的加长焊接钢管的制备方法,其特征在于,所述激光焊接的工艺参数为:CO2激光器,焊接电压320U/V,焊接功率1500kW,焊接速度0.5m/min。
4.根据权利要求1所述的加长焊接钢管的制备方法,其特征在于,所述热处理条件为:温度1050℃,时间20min。
5.根据权利要求1所述的加长焊接钢管的制备方法,其特征在于,所述酸洗液为30wt%盐酸和15%氢氟酸的水溶液。
6.根据权利要求1所述的加长焊接钢管的制备方法,其特征在于,所述检验包括外观检验、尺寸检验、水压检验和无损探伤。