CN104404523A - Oil-removing water-based antirust agent and preparation method thereof - Google Patents
Oil-removing water-based antirust agent and preparation method thereof Download PDFInfo
- Publication number
- CN104404523A CN104404523A CN201410622019.XA CN201410622019A CN104404523A CN 104404523 A CN104404523 A CN 104404523A CN 201410622019 A CN201410622019 A CN 201410622019A CN 104404523 A CN104404523 A CN 104404523A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- add
- 30min
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an oil-removing water-based antirust agent, which is characterized by being composed of the following raw materials in parts by weight: 3 to 5 parts of polyvinylidene fluoride emulsion, 1 to 2 parts of nonylphenol polyoxyethylene ether, 1 to 2 parts of dodecyl glucoside, 1 to 2 parts of sodium diethylhexyl sulfosuccinate, 1 to 2 parts of urea, 0.5 to 1 part of sodium pyrophosphate, 0.5 to 1 part of disodium ethylene diamine tetraacetate, 0.3 to 0.5 part of span 80, 2 to 4 parts of triethanolamine oleate, 0.5 to 1 part of konjak glucomannan, 6 to 8 parts of modification aid, and 30 to 40 parts of water. The metal surface processed by the provided antirust agent has the antirust and oil-removing functions at the same time, and moreover, the antirust membrane tightly combines with the substrate, can effectively protect the metal, and prevents corrosion.
Description
Technical field
The present invention relates to metal treatment field, be specifically related to a kind of oil water removal based anti-rusting agent and preparation method thereof.
Background technology
Metal works, in the process of process for processing and transport, is easy to get rusty, and once get rusty, and produces detrimentally affect by the outward appearance of finished product and performance, and the serious steel that even can cause of corrosion are scrapped.Iron and steel gets rusty and to bring about great losses to national economy, therefore needs to use rust-preventive agent to protect metal.The mode of action of rust-preventive agent prevents metal generation corrosion by forming thin film in metallic surface.Conventional rust-preventive agent major part is oiliness, and it uses a large amount of organic solvent in the process of production, use, and to environment, therefore the research of water-based antirust has great importance.
Traditional water-base metal antirusting agent great majority all contain nitrite, and it has the advantages such as inexpensive, respond well and easy to use, easy removal, but can change into carcinogens due to nitrite, and it uses and discharge and is subjected to strict restriction.At present, the research of novel environment friendly water-based antirust starts to be paid close attention to widely, becomes a kind of developing trend.
Summary of the invention
The object of this invention is to provide a kind of oil water removal based anti-rusting agent.
The present invention is achieved by the following technical solutions:
A kind of oil water removal based anti-rusting agent, it is characterized in that, it is obtained by the raw material of following weight parts:
Polyvinylidene fluoride emulsion 3-5, polyoxyethylene nonylphenol ether 1-2, Dodecyl Polyglucosides 1-2, dioctyl sodium sulfosuccinate 1-2, urea 1-2, trisodium phosphate 0.5-1, disodium ethylene diamine tetraacetate 0.5-1, sorbester p17 0.3-0.5, triethanolamine oleate 2-4, oxalic acid 0.5-1, Rhizoma amorphophalli glucomannan 0.5-1, modified additive 6-8, water 30-40;
Wherein modified additive is made up of the raw material of following weight part:
Nano imvite 10-20, organosilicon quaternary ammonium salt 3-5, polyoxyethylene glycol 2-4, oxysuccinic acid 0.5-1, Weibull 0.1-0.2, chlorogenic acid 0.05-0.1, tripoly phosphate sodium STPP 1-2;
The preparation method of modified additive is:
Nano imvite and oxysuccinic acid, tripoly phosphate sodium STPP are added ultrasonic disperse 15-30min in suitable quantity of water; dry after filtering; add polyoxyethylene glycol, Weibull, chlorogenic acid and ethanol in proper amount ultrasonic disperse 5-10min and add reaction vessel in the lump again; add organosilicon quaternary ammonium salt; heated and stirred back flow reaction 8-12h under nitrogen protection; filter and with washing with alcohol for several times, vacuum-drying is complete, to obtain final product.
A preparation method for oil water removal based anti-rusting agent, is characterized in that, comprises the following steps:
(1) sorbester p17 is added to the water, 60-80 DEG C, 800-1000r/min stirs 5-10min, then stir 15-30min under adding dioctyl sodium sulfosuccinate, triethanolamine oleate, Dodecyl Polyglucosides and oxalic acid similarity condition, obtains component A;
(2) add in the water of surplus by polyvinylidene fluoride emulsion and modified additive, first ultrasonic disperse 5-10min, then add disodium ethylene diamine tetraacetate and Rhizoma amorphophalli glucomannan, 8000-10000r/min high-speed homogenization 15-30min, obtains B component;
(3) 400-600r/min after the mixing of component A, B component and all the other raw materials is stirred 15-30min, after packing and get final product.
Advantage of the present invention is:
1. rust-preventive agent of the present invention has antirust and function that is oil removing simultaneously when process metal surfaces, and by force, energy available protecting metal, prevents corrosion for antirust rete and basal body binding force;
2. by adding modified additive, rust-preventive agent being formed in metallic surface firmly, fine and close, corrosion resistant rete, also having the effect such as anti-electrostatic, antibacterial and mouldproof, easy decontamination simultaneously.
Embodiment
Non-limiting examples of the present invention is as follows:
A kind of oil water removal based anti-rusting agent, is prepared from by the component raw material of following weight (kg):
Polyvinylidene fluoride emulsion 4, polyoxyethylene nonylphenol ether 1.5, Dodecyl Polyglucosides 1.5, dioctyl sodium sulfosuccinate 1.5, urea 1.5, trisodium phosphate 0.8, disodium ethylene diamine tetraacetate 0.8, sorbester p17 0.4, triethanolamine oleate 3, oxalic acid 0.8, Rhizoma amorphophalli glucomannan 0.8, modified additive 7, water 35;
Wherein, modified additive is made up of the raw material of following weight (kg):
Nano imvite 15, organosilicon quaternary ammonium salt 4, polyoxyethylene glycol 3, oxysuccinic acid 0.8, Weibull 0.15, chlorogenic acid 0.08, tripoly phosphate sodium STPP 1.5;
The preparation method of modified additive:
Nano imvite and oxysuccinic acid, tripoly phosphate sodium STPP are added ultrasonic disperse 30min in suitable quantity of water; dry after filtering; add polyoxyethylene glycol, Weibull, chlorogenic acid and ethanol in proper amount ultrasonic disperse 10min and add reaction vessel in the lump again; add organosilicon quaternary ammonium salt; heated and stirred back flow reaction 10h under nitrogen protection; filter and with washing with alcohol for several times, vacuum-drying is complete, to obtain final product.
The preparation method of oil water removal based anti-rusting agent comprises the following steps:
(1) sorbester p17 is added to the water, 80 DEG C, 1000r/min stirs 5min, then stir 15min under adding dioctyl sodium sulfosuccinate, triethanolamine oleate, Dodecyl Polyglucosides and oxalic acid similarity condition, obtains component A;
(2) add in the water of surplus by polyvinylidene fluoride emulsion and modified additive, first ultrasonic disperse 5min, then add disodium ethylene diamine tetraacetate and Rhizoma amorphophalli glucomannan, 10000r/min high-speed homogenization 15min, obtains B component;
(3) 600r/min after the mixing of component A, B component and all the other raw materials is stirred 15min, after packing and get final product.
Through inspection, humid heat test 45# steel disc 15 days is qualified, and salt-fog test 45# steel disc 5 days is qualified.
Claims (2)
1. an oil water removal based anti-rusting agent, is characterized in that, it is obtained by the raw material of following weight parts:
Polyvinylidene fluoride emulsion 3-5, polyoxyethylene nonylphenol ether 1-2, Dodecyl Polyglucosides 1-2, dioctyl sodium sulfosuccinate 1-2, urea 1-2, trisodium phosphate 0.5-1, disodium ethylene diamine tetraacetate 0.5-1, sorbester p17 0.3-0.5, triethanolamine oleate 2-4, oxalic acid 0.5-1, Rhizoma amorphophalli glucomannan 0.5-1, modified additive 6-8, water 30-40;
Described modified additive is made up of the raw material of following weight part:
Nano imvite 10-20, organosilicon quaternary ammonium salt 3-5, polyoxyethylene glycol 2-4, oxysuccinic acid 0.5-1, Weibull 0.1-0.2, chlorogenic acid 0.05-0.1, tripoly phosphate sodium STPP 1-2;
The preparation method of described modified additive is:
Nano imvite and oxysuccinic acid, tripoly phosphate sodium STPP are added ultrasonic disperse 15-30min in suitable quantity of water; dry after filtering; add polyoxyethylene glycol, Weibull, chlorogenic acid and ethanol in proper amount ultrasonic disperse 5-10min and add reaction vessel in the lump again; add organosilicon quaternary ammonium salt; heated and stirred back flow reaction 8-12h under nitrogen protection; filter and with washing with alcohol for several times, vacuum-drying is complete, to obtain final product.
2. the preparation method of a kind of oil water removal based anti-rusting agent according to claim 1, is characterized in that, comprise the following steps:
(1) sorbester p17 is added to the water, 60-80 DEG C, 800-1000r/min stirs 5-10min, then stir 15-30min under adding dioctyl sodium sulfosuccinate, triethanolamine oleate, Dodecyl Polyglucosides and oxalic acid similarity condition, obtains component A;
(2) add in the water of surplus by polyvinylidene fluoride emulsion and modified additive, first ultrasonic disperse 5-10min, then add disodium ethylene diamine tetraacetate and Rhizoma amorphophalli glucomannan, 8000-10000r/min high-speed homogenization 15-30min, obtains B component;
(3) 400-600r/min after the mixing of component A, B component and all the other raw materials is stirred 15-30min, after packing and get final product.