CN104403572A - Liquid polishing wax and preparation method thereof - Google Patents
Liquid polishing wax and preparation method thereof Download PDFInfo
- Publication number
- CN104403572A CN104403572A CN201410682001.9A CN201410682001A CN104403572A CN 104403572 A CN104403572 A CN 104403572A CN 201410682001 A CN201410682001 A CN 201410682001A CN 104403572 A CN104403572 A CN 104403572A
- Authority
- CN
- China
- Prior art keywords
- liquid
- stir
- parts
- added
- liquor finish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a liquid polishing wax. The liquid polishing wax consists of the following components in parts by weight: 10-20 parts of a stearic acid, 20-30 parts of liquid paraffine, 6-10 parts of a brightener, 5-10 parts of an emulsifying agent, 10-15 parts of aluminium oxide, 15-20 parts of quartz powder and 15-20 parts of water. Compared with the prior art, the liquid polishing wax disclosed by the invention adopts different raw materials, different compounding ratios and different preparation technologies, compared with an ordinary liquid polishing wax, the polishing effect of the liquid polishing wax disclosed by the invention is enhanced by 1-2 times, and the use time is shortened by 1-2 times, so that the work efficiency is effectively improved, and the production cost is obviously saved.
Description
Technical field
The present invention relates to polished exterior surface buffing wax field, especially a kind of environment-friendly high-efficiency liquor finish wax coordinating Full-automatic polishing machine to use and preparation method thereof.
Background technology
Polishing refers to that carrying out leveling with polishing material to subject surface processes, and reduces roughness, improves the process of surface luster and visual appearance.The solid form that buffing wax (, rubbing paste, polishing rod cured also known as polishing) is polishing material, applies very wide at home.It is primarily of abrasive material and grease composition.
Polished finish is one of important procedure in the middle of surface treatment, and due to the rising of human cost, and quality product requires more and more higher, so full automatic polishing is by manual for replacement slowly polishing, and liquor finish wax substitutes solid polishing wax thereupon.This liquor finish wax feature is that it can be adapted to different base materials and different workpiece carries out polishing, and compare solid polishing wax use pollute less, more environmental protection, more efficiently.
Summary of the invention
The object of the invention is to provide a kind of liquor finish wax and preparation method thereof.
A kind of liquor finish wax, composed of the following components by weight:
Wherein said aluminum oxide is Calcined polishing aluminum oxide powder.
Preferably, described brightening agent is animal grease and/or Vegetable oil lipoprotein.
Preferably, described emulsifying agent is one or more in alkylphenol polyoxyethylene, polyoxyethylene nonylphenol ether, fatty alcohol-polyoxyethylene ether.
Preferably, described Calcined polishing aluminum oxide powder, particle diameter is 800-1200 order.
Preferably, the particle diameter of described silica powder is 500-700 order.
Another object of the present invention is to the preparation method of the preparation method providing a kind of aforesaid liquid buffing wax, the method comprises the following steps:
(1) by stearic acid and water mixing, stir to obtain A liquid;
(2) whiteruss is added A liquid, stir to obtain B liquid;
(3) brightening agent is added B liquid, stir to obtain C liquid;
(4) aluminum oxide is added C liquid, stir to obtain D liquid;
(5) silica powder is added D liquid, stir to obtain E liquid;
(6) emulsifying agent is added E liquid, stir liquor finish wax.
Described liquor finish wax coordinates Full-automatic polishing machine to use.Compared with prior art, present invention employs different raw materials, proportioning and manufacture craft, enhance more than 1-2 times than common liquor finish wax polishing effect, shorten more than 1-2 times duration of service, thus effectively increase work efficiency, provide significant conservation production cost.
Embodiment
Embodiment 1:
A kind of liquor finish wax, composed of the following components by weight:
Wherein said aluminum oxide is Calcined polishing aluminum oxide powder.
Described brightening agent is animal grease;
Described emulsifying agent is alkylphenol polyoxyethylene;
Described Calcined polishing aluminum oxide powder, particle diameter is 800 orders;
The particle diameter of described silica powder is 500 orders.
The preparation method of liquor finish wax comprises the following steps:
(1) by stearic acid and water mixing, stir to obtain A liquid;
(2) whiteruss is added A liquid, stir to obtain B liquid;
(3) brightening agent is added B liquid, stir to obtain C liquid;
(4) aluminum oxide is added C liquid, stir to obtain D liquid;
(5) silica powder is added D liquid, stir to obtain E liquid;
(6) emulsifying agent is added E liquid, stir liquor finish wax.
Embodiment 2:
A kind of liquor finish wax, composed of the following components by weight:
Wherein said aluminum oxide is Calcined polishing aluminum oxide powder.
Described brightening agent is Vegetable oil lipoprotein;
Described emulsifying agent is alkylphenol polyoxyethylene and polyoxyethylene nonylphenol ether;
Described Calcined polishing aluminum oxide powder, particle diameter is 1000 orders;
The particle diameter of described silica powder is 600 orders.
The preparation method of liquor finish wax comprises the following steps:
(1) by stearic acid and water mixing, stir to obtain A liquid;
(2) whiteruss is added A liquid, stir to obtain B liquid;
(3) brightening agent is added B liquid, stir to obtain C liquid;
(4) aluminum oxide is added C liquid, stir to obtain D liquid;
(5) silica powder is added D liquid, stir to obtain E liquid;
(6) emulsifying agent is added E liquid, stir liquor finish wax.
Embodiment 3:
A kind of liquor finish wax, composed of the following components by weight:
Wherein said aluminum oxide is Calcined polishing aluminum oxide powder.
Described brightening agent is Vegetable oil lipoprotein and animal grease;
Described emulsifying agent is alkylphenol polyoxyethylene, polyoxyethylene nonylphenol ether and fatty alcohol-polyoxyethylene ether;
Described Calcined polishing aluminum oxide powder, particle diameter is 1200 orders;
Preferably, the particle diameter of described silica powder is 700 orders.
The preparation method of liquor finish wax comprises the following steps:
(1) by stearic acid and water mixing, stir to obtain A liquid;
(2) whiteruss is added A liquid, stir to obtain B liquid;
(3) brightening agent is added B liquid, stir to obtain C liquid;
(4) aluminum oxide is added C liquid, stir to obtain D liquid;
(5) silica powder is added D liquid, stir to obtain E liquid;
(6) emulsifying agent is added E liquid, stir liquor finish wax.
Embodiment 4:
The effect experimental of the present composition
In order to prove product effect, the liquor finish wax getting the embodiment of the present invention 2 carries out effect mensuration, has carried out polishing effect experiment, concrete measuring method and measurement result specific as follows:
Choose the workpiece that two pieces of surface roughness value are the same, experimental group utilizes the liquor finish wax of inventive embodiments 2 to carry out polishing, and comparative group utilizes common liq buffing wax to carry out polishing, at 5 minutes, 10 minutes, within 30 minutes, 3 time points measured the surfaceness of workpiece respectively, and its numerical value is as follows:
Table one surfaceness is tested
| Time | Experimental group surfaceness | Comparative group surfaceness |
| 5 minutes | 0.03μm | 0.08μm |
| 10 minutes | 0.009μm | 0.05μm |
| 30 minutes | 0.005μm | 0.02μm |
Above-mentioned test shows: the liquor finish wax of the application is thrown and enhanced more than 1-2 times than common liquor finish wax polishing effect, shortens more than 1-2 times duration of service, thus effectively increases work efficiency.
Claims (7)
1. a liquor finish wax, is characterized in that: composed of the following components by weight:
Wherein said aluminum oxide is Calcined polishing aluminum oxide powder.
2. liquor finish wax according to claim 1, is characterized in that: described brightening agent is animal grease and/or Vegetable oil lipoprotein.
3. liquor finish wax according to claim 1, is characterized in that: described emulsifying agent is one or more in alkylphenol polyoxyethylene, polyoxyethylene nonylphenol ether and fatty alcohol-polyoxyethylene ether.
4. liquor finish wax according to claim 1, is characterized in that: described Calcined polishing aluminum oxide powder, and particle diameter is 800-1200 order.
5. liquor finish wax according to claim 1, is characterized in that: the particle diameter of described silica powder is 500-700 order.
6. the preparation method of a kind of liquor finish wax according to any one of claim 1-5, is characterized in that, comprise the following steps:
(1) by stearic acid and water mixing, stir to obtain A liquid;
(2) whiteruss is added A liquid, stir to obtain B liquid;
(3) brightening agent is added B liquid, stir to obtain C liquid;
(4) aluminum oxide is added C liquid, stir to obtain D liquid;
(5) silica powder is added D liquid, stir to obtain E liquid;
(6) emulsifying agent is added E liquid, stir to obtain liquor finish wax.
7. utilize the liquor finish wax according to any one of claim 1-5, it is characterized in that, coordinate Full-automatic polishing machine to use.