CN104401009A - Method for molding of character on silica gel product surface - Google Patents
Method for molding of character on silica gel product surface Download PDFInfo
- Publication number
- CN104401009A CN104401009A CN201410577843.8A CN201410577843A CN104401009A CN 104401009 A CN104401009 A CN 104401009A CN 201410577843 A CN201410577843 A CN 201410577843A CN 104401009 A CN104401009 A CN 104401009A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- gel product
- character
- product surface
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of silica gel product processing, specifically to a method for molding of a character on a silica gel product surface. The method for molding of a character on a silica gel product surface comprises the steps of: 1) filling a die groove with a making raw material for the character, and buckling the silica gel product surface with the die filled with the making raw material so as to obtain a die equipped silica gel product; and 2) conducting vulcanizing treatment on the die equipped silica gel product, and then dismantling the die to obtain the silica gel product with the three-dimensional character molded on the surface. Compared with the prior art, the method for molding of the character on the silica gel product surface provided by the invention realizes the effect of character setting on the silica gel product surface by combining the die and vulcanization, is simple, easy to operate, and is low in labor cost. In addition, the mode can reflect the effect of three-dimensional characters, and can make the character on the silica gel product surface show a three-dimensional sense, thereby meeting the demands of three-dimensional silica gel products.
Description
Technical field
The present invention relates to silica gel product processing technique field, in particular to a kind of method of silica gel product surface forming character.
Background technology
High temperature resistant (Applicable temperature scope-40 DEG C is to 230 DEG C because it has for silica gel product, some product even can use in micro-wave oven or baking box), easy cleaning, life-span is long, soft comfortable, color is various, environment-protecting asepsis, electrical insulation capability, lower temperature resistance (as, the minimum serviceability temperature critical point of General Purpose Rubber is-20 DEG C to-30 DEG C, but silicon rubber then still has good elasticity-60 DEG C to-70 DEG C time) etc. multinomial excellent properties, therefore, be applied in a lot of field at present, as, can be used as the forming gasket of durable shape, the encapsulating material of electronic components, the maintenance materials of automotive electronics accessory, medical silica-gel, foam silica gel, molding blangel, the building in house and reparation, highway joint seal, the Seals such as the sealing of bridge, the parts such as fitting of medical apparatus use.
Meanwhile, when use silica gel product, often need to arrange various character on its surface, in correlation technique, the normal surface adopting the mode of silk-screen or spraying specific character to be arranged on silica gel product; But silk-screen and spraying operation require strict, cost of labor is large.And only embody plane effect by the character that these two kinds of modes are arranged on silica gel product surface, there is no third dimension, the demand of three-dimensional silica gel product can not be met.
Summary of the invention
The object of the invention is to a kind of method of silica gel product surface forming character, to solve above-mentioned technical problem.
Provide a kind of method of silica gel product surface forming character in an embodiment of the present invention, comprise the following steps:
1), by the making raw material of character be filled in the groove of mould, and the mould being filled with described making raw material is buckled on the surface of silica gel product, obtain the silica gel product with mould;
2), by described with after the silica gel product vulcanizing treatment of mould, described mould is removed, obtain the silica gel product that surface forming has three-dimensional character.
The method of this silica gel product surface forming character provided by the invention, the making raw material first passing through to fill character in the groove of mould is to realize the preparation of the character of given shape; And then the mould being filled with described making raw material is buckled on the surface of silica gel product, carry out vulcanizing treatment in the lump, and then the character making to have both shaped is shaping and be arranged on the surface of silica gel product.Compared with prior art, the mode that should be combined by mould and sulfuration realizes the method that silica gel product surface arranges the effect of character, and easy, easy to operate, cost of labor is low.In addition, which can embody the effect of three-dimensional character, makes the character being arranged on silica gel product surface embody third dimension, and then can meet the demand of three-dimensional silica gel product.
Optionally, in step 1) before, also comprise: use the shaping silica gel product of silica gel production mould.
Optionally, in step 1) in: the making raw material of described character is silica gel.
Optionally, in step 1) in: described mould is provided with multiple groove, and the character being filled with different colours in each groove makes raw material.
Optionally, in step 1) in: described mould is provided with multiple groove, and the character being filled with same color in each groove makes raw material.
Optionally, described step 2) in: use vulcanizer to carry out described vulcanizing treatment.
Optionally, in step 2) in: the temperature in described sulfidation processes is 10-300 DEG C; Pressure is 1-200 ton.
Optionally, in step 2) in: the time of described vulcanizing treatment is 1-500 second.
Optionally, in step 2) in: the temperature in described sulfidation processes is 10-250 DEG C; Pressure is 1-200 ton.
Optionally, in step 2) in: the time of described vulcanizing treatment is 1-250 second.
Optionally, in step 1) in: silica gel product comprises: leg of spectacles, spectacle-frame, glasses gum cover, glasses fastener, spectacles nose holder or glasses paster.
Accompanying drawing explanation
In order to be illustrated more clearly in the specific embodiment of the invention or technical scheme of the prior art, be briefly described to the accompanying drawing used required in detailed description of the invention or description of the prior art below, apparently, accompanying drawing in the following describes is some embodiments of the present invention, for those of ordinary skill in the art, under the prerequisite not paying creative work, other accompanying drawing can also be obtained according to these accompanying drawings.
The preparation flow schematic diagram of the method for the silica gel product surface forming character that Fig. 1 provides for the embodiment of the present invention one.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearly; clear, complete description is carried out below by technical scheme of the present invention; based on the detailed description of the invention in the present invention; other embodiments all that those of ordinary skill in the art obtain under the prerequisite not making creative work, all belong to the scope that the present invention protects.
Embodiment one
Please refer to Fig. 1, the method for this silica gel product surface forming character provided by the invention, comprises the following steps:
Step 101: the making raw material of character is filled in the groove of mould, and the mould being filled with described making raw material is buckled on the surface of silica gel product, obtain the silica gel product with mould;
Step 101 is for being filled into the operation that it makes mould by character raw material, in this operation, the shape that the groove shapes of mould need have more required character specifically sets, and such as, can be English character, also can be product brand etc.After completing filling, whole mould is buckled on the surface of silica gel product and (needs to arrange the one side of character), to carry out the operation of follow-up sulfidization molding.
Step 102: with after the silica gel product vulcanizing treatment of mould, described mould is removed described, obtain the silica gel product that surface forming has three-dimensional character.
In a step 102, in sulfidation, under set pressure and temperature, on the one hand, character can be shaping; On the other hand, shaping character can became one with silica gel product, and then realizes the effect arranging three-dimensional character on silica gel product.
The method of this silica gel product surface forming character provided by the invention, the making raw material first passing through to fill character in the groove of mould is to realize the preparation of the character of given shape; And then the mould being filled with described making raw material is buckled on the surface of silica gel product, carry out vulcanizing treatment in the lump, and then the character making to have both shaped is shaping and be arranged on the surface of silica gel product.Compared with prior art, the mode that should be combined by mould and sulfuration realizes the method that silica gel product surface arranges the effect of character, and easy, easy to operate, cost of labor is low.In addition, which can embody the effect of three-dimensional character, makes the character being arranged on silica gel product surface embody third dimension, and then can meet the demand of three-dimensional silica gel product.
In order to the method for the silica gel product surface forming character making the above embodiment of the present invention is better applied, more effectively realize the effect of the surface forming character of silica gel product, the present invention also provides embodiment two-four on the basis of above-described embodiment, embodiment two-four is further restriction and the increase of the method for the silica gel product surface forming character of above-described embodiment, is now described in detail and explains:
Embodiment two
In the present embodiment, the preparation method of the method for silica gel product surface forming character comprises the following steps:
S1: use the shaping silica gel product of silica gel production mould.
Wherein, silica gel product uses its particular manufacturing craft compressing in advance, and is fixed in die cavity, for future use.
S2: the making raw material of character is filled in the groove of mould, and the mould being filled with described making raw material is buckled on the surface of silica gel product, obtain the silica gel product with mould;
Concrete, in S2, the making raw material of described character is silica gel; Silica gel character itself and silica gel product more easily realize in conjunction with effect, and the character after combining not easily is dropped.
In addition, in further technical scheme, preferably, in order to realize the effect of character polychrome, described mould is provided with multiple groove, and the character being filled with different colours in each groove makes raw material; Like this, the setting of multiple character can be realized, and the color of character is not identical, enhances its performance attractive in appearance.
S3: with after the silica gel product vulcanizing treatment of mould, described mould is removed described, obtain the silica gel product that surface forming has three-dimensional character;
Preferably, sulfuration is used to carry out described vulcanizing treatment; Vulcanizer is applicable to the sulfuration of various rubber, is the compressing advanced hot-press equipment of various thermosetting plastics.The function such as automatic-discharging gas, pressurize sulfuration, timing and alarming, automatic die sinking, goods depanning after preheating needed for rubber vulcanization process, material loading is in one.Adopt PLC or manual operation (customized by user's actual need), the technological process needed for record, handled easily management.Therefore, in the present embodiment, vulcanizer is used to carry out sulfuration to this silica gel product and character.
Embodiment three
In the present embodiment, the preparation method of the method for silica gel product surface forming character comprises the following steps:
S1: use the shaping silica gel product of silica gel production mould.
S2: the making raw material of character is filled in the groove of mould, and the mould being filled with described making raw material is buckled on the surface of silica gel product, obtain the silica gel product with mould;
Above-mentioned steps S1 is consistent with embodiment two with S2, and therefore not to repeat here.
S3: with after the silica gel product vulcanizing treatment of mould, described mould is removed described, obtain the silica gel product that surface forming has three-dimensional character.
In the present embodiment, the temperature in described sulfidation processes is 10-300 DEG C; Pressure is 1-200 ton; Preferred, the temperature in described sulfidation processes is 150 DEG C; Pressure is 100 tons; The time of described vulcanizing treatment is 1-500 second; Preferably, the time of described vulcanizing treatment is 1-350 second.
The whole sulfidation of vulcanizer is a very complicated process, and wherein, the problem in pressure and temperature is exactly a very part and parcel.Sulfide stress is subject to very many-sided restriction, but the setting of sulfide stress and temperature is also to ensure that vulcanizer can better vulcanizate, is the important composition link of the quality ensureing product, so need in this respect to pay much attention to.
In the present invention, by repeatedly exploring, the cure efficiency of combination product and the loss reduced as much as possible machinery, just obtain above-mentioned technological parameter; Preferably, in the present embodiment, the temperature in described sulfidation processes is 200 DEG C; Pressure is 100 tons; The time of sulfuration is 250 seconds.
Embodiment four
In the present embodiment, the preparation method of the method for silica gel product surface forming character comprises the following steps:
S1: use the shaping silica gel product of silica gel production mould.
Concrete, in the present embodiment, silica gel product is specially any one in leg of spectacles, spectacle-frame, glasses gum cover, glasses fastener, spectacles nose holder or glasses paster.
S2: the making raw material of character is filled in the groove of mould, and the mould being filled with described making raw material is buckled on the surface of silica gel product, obtain the silica gel product with mould;
S3: with after the silica gel product vulcanizing treatment of mould, described mould is removed described, obtain the silica gel product that surface forming has three-dimensional character.
Step S2 is consistent with embodiment three with S3, and therefore not to repeat here.
To sum up, compared with the mode of the method for this silica gel product surface forming character provided by the invention and existing silk-screen or spraying, it is easy, easy to operate, and cost of labor is low.In addition, which can embody the effect of three-dimensional character, makes the character being arranged on silica gel product surface embody third dimension, and then can meet the demand of three-dimensional silica gel product.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (10)
1. a method for silica gel product surface forming character, is characterized in that, comprises the following steps:
1), by the making raw material of character be filled in the groove of mould, and the mould being filled with described making raw material is buckled on the surface of silica gel product, obtain the silica gel product with mould;
2), by described with after the silica gel product vulcanizing treatment of mould, described mould is removed, obtain the silica gel product that surface forming has three-dimensional character.
2. the method for silica gel product surface forming character according to claim 1, is characterized in that, in step 1) before, also comprise:
Use the shaping silica gel product of silica gel production mould.
3. the method for silica gel product surface forming character according to claim 1, is characterized in that, in step 1) in:
The making raw material of described character is silica gel.
4. the method for silica gel product surface forming character according to claim 1, is characterized in that, in step 1) in:
Described mould is provided with multiple groove, and the character being filled with different colours in each groove makes raw material.
5. the method for silica gel product surface forming character according to claim 1, is characterized in that, described step 2) in:
Vulcanizer is used to carry out described vulcanizing treatment.
6. the method for silica gel product surface forming character according to claim 5, is characterized in that, in step 2) in:
Temperature in described sulfidation processes is 10-300 DEG C; Pressure is 1-200 ton.
7. the method for silica gel product surface forming character according to claim 6, is characterized in that, in step 2) in:
The time of described vulcanizing treatment is 1-500 second.
8. the method for silica gel product surface forming character according to claim 5, is characterized in that, in step 2) in:
Temperature in described sulfidation processes is 10-250 DEG C; Pressure is 1-200 ton.
9. the method for silica gel product surface forming character according to claim 8, is characterized in that, in step 2) in:
The time of described vulcanizing treatment is 1-250 second.
10. the method for the silica gel product surface forming character according to any one of claim 1-9, is characterized in that, in step 1) in:
Silica gel product comprises: leg of spectacles, spectacle-frame, glasses gum cover, glasses fastener, spectacles nose holder or glasses paster.