CN104388800A - Lead-tin alloy die casting - Google Patents
Lead-tin alloy die casting Download PDFInfo
- Publication number
- CN104388800A CN104388800A CN201410607422.5A CN201410607422A CN104388800A CN 104388800 A CN104388800 A CN 104388800A CN 201410607422 A CN201410607422 A CN 201410607422A CN 104388800 A CN104388800 A CN 104388800A
- Authority
- CN
- China
- Prior art keywords
- parts
- die casting
- lead
- tin alloy
- alloy die
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a lead-tin alloy die casting. The lead-tin alloy die casting comprises the following materials in parts by weight: 20-35 parts of aluminum trioxide, 10-15 parts of manganese dioxide, 10-14 parts of copper sulfate, 5-8 parts of fine iron powder, 3-5 parts of chromium-molybdenum steel, 6-8 parts of silicon dioxide, 2-8 parts of yellow brass, 3-7 parts of tinplate, 6-8 parts of nickel hydroxide and 15-30 parts of lead-tin alloy. The lead-tin alloy die casting has the beneficial effects that the flow mark rate and bubble rate in the die casting can be effectively reduced by adjusting components and ratio of the die casting. Compared with the prior art, the quality can be improved by 3-4 times.
Description
Technical field
The present invention relates to terne metal die casting.
Background technology
Die casting is a kind of part of pressure die casting, use the pressure die casting machinery pressure die-casting machine installing casting die, the metal such as copper, zinc, aluminum or aluminum alloy being heated to be liquid state is poured into the feeding mouth of pressure die-casting machine, through pressure die-casting machine die casting, cast out the copper of the shape and size of mould restriction, zinc, aluminium part or aluminum alloy part, such part is just called die casting usually.Die casting has different calls in different places, as diecast parts, die-casting, die casting, die casting aluminium, die case zinc part, die casting copper piece, copper die casting, zine pressure casting, aluminium diecasting aluminium diecasting, aluminium pressure alloy-steel casting, aluminium alloy compression casting part etc.
Summary of the invention
Object of the present invention is exactly for above-mentioned defect of the prior art, provides a kind of through improvement, improves the terne metal die casting of quality of die casting.
To achieve these goals, technical scheme provided by the invention is: terne metal die casting, is made up of the following material according to parts by weight: aluminium sesquioxide 20-35 part, Manganse Dioxide 10-15 part, copper sulfate 10-14 part, Iron concentrate 5-8 part, chromemolybdenum steel 3-5 part, silicon-dioxide 6-8 part, brass 2-8 part, tinplate 3-7 part, nickel hydroxide 6-8 part, terne metal 15-30 part.
Further, above-mentioned terne metal die casting, is made up of the following material according to parts by weight: aluminium sesquioxide 25 parts, Manganse Dioxide 12 parts, 12 parts, copper sulfate, Iron concentrate 6 parts, chromemolybdenum steel 4 parts, silicon-dioxide 7 parts, brass 5 parts, tinplate 5 parts, nickel hydroxide 7 parts, terne metal 25 parts.
Beneficial effect of the present invention is: terne metal die casting provided by the invention, by adjusting the composition and ratio of die casting, effectively can reduce the current mark rate in die casting and bubble rate, and compared to prior art, quality can improve 3-4 doubly.
Embodiment
embodiment 1:
Terne metal die casting, be made up of the following material according to parts by weight: aluminium sesquioxide 20-35 part, Manganse Dioxide 10-15 part, copper sulfate 10-14 part, Iron concentrate 5-8 part, chromemolybdenum steel 3-5 part, silicon-dioxide 6-8 part, brass 2-8 part, tinplate 3-7 part, nickel hydroxide 6-8 part, terne metal 15-30 part.
embodiment 2:
Terne metal die casting, is made up of the following material according to parts by weight: aluminium sesquioxide 25 parts, Manganse Dioxide 12 parts, 12 parts, copper sulfate, Iron concentrate 6 parts, chromemolybdenum steel 4 parts, silicon-dioxide 7 parts, brass 5 parts, tinplate 5 parts, nickel hydroxide 7 parts, terne metal 25 parts.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. terne metal die casting, it is characterized in that, be made up of the following material according to parts by weight: aluminium sesquioxide 20-35 part, Manganse Dioxide 10-15 part, copper sulfate 10-14 part, Iron concentrate 5-8 part, chromemolybdenum steel 3-5 part, silicon-dioxide 6-8 part, brass 2-8 part, tinplate 3-7 part, nickel hydroxide 6-8 part, terne metal 15-30 part.
2. terne metal die casting according to claim 1, it is characterized in that, be made up of the following material according to parts by weight: aluminium sesquioxide 25 parts, Manganse Dioxide 12 parts, 12 parts, copper sulfate, Iron concentrate 6 parts, chromemolybdenum steel 4 parts, silicon-dioxide 7 parts, brass 5 parts, tinplate 5 parts, nickel hydroxide 7 parts, terne metal 25 parts.