CN104386735A - 氧化锌的制备方法 - Google Patents
氧化锌的制备方法 Download PDFInfo
- Publication number
- CN104386735A CN104386735A CN201410604214.XA CN201410604214A CN104386735A CN 104386735 A CN104386735 A CN 104386735A CN 201410604214 A CN201410604214 A CN 201410604214A CN 104386735 A CN104386735 A CN 104386735A
- Authority
- CN
- China
- Prior art keywords
- zinc oxide
- zinc
- preparation
- sulfate
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种氧化锌的制备方法,包括如下步骤:1)将硫酸锌溶液加热至60℃,加入0.16g/l的六偏磷酸钠、0.53g/l的氧化镁、0.13g/l的活性硅微粉、0.11g/l的乙二醇,搅拌30分钟,加1.5g/l的碳酸钠,调节PH值为9.3,搅拌生成包覆碱式碳酸锌和硫酸钠的混合物,再进行压滤;2)对压滤得到的碱式碳酸锌进行洗涤,洗涤至物料中无硫酸根,然后干燥至水分小于2.2%;3)对干燥后的物料于580℃焙烧,即得氧化锌产品。本发明氧化锌的制备方法,其制备的氢氧化镁纯度比较高,分散性好,还提高了氧化锌的活性。
Description
技术领域
本发明涉及氧化锌的制备方法。
背景技术
现有氧化锌的制备方法,其制备的氢氧化镁纯度不够高,分散性不够好,活性不高。
发明内容
本发明的目的在于提供一种氧化锌的制备方法,其制备的氢氧化镁纯度比较高,分散性好,还提高了氧化锌的活性。
为实现上述目的,本发明的技术方案是设计一种氧化锌的制备方法,包括如下步骤:
1)将硫酸锌溶液加热至60℃,加入0.16g/l的六偏磷酸钠、0.53g/l的氧化镁、0.13g/l的活性硅微粉、0.11g/l的乙二醇,搅拌30分钟,加1.5g/l的碳酸钠,调节PH值为9.3,搅拌生成包覆碱式碳酸锌和硫酸钠的混合物,再进行压滤;
2)对压滤得到的碱式碳酸锌进行洗涤,洗涤至物料中无硫酸根,然后干燥至水分小于2.2%;
3)对干燥后的物料于580℃焙烧,即得氧化锌产品。
本发明的优点和有益效果在于:提供一种氧化锌的制备方法,其制备的氢氧化镁纯度比较高,分散性好,还提高了氧化锌的活性。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
一种氧化锌的制备方法,包括如下步骤:
1)将硫酸锌溶液加热至60℃,加入0.16g/l的六偏磷酸钠、0.53g/l的氧化镁、0.13g/l的活性硅微粉、0.11g/l的乙二醇,搅拌30分钟,加1.5g/l的碳酸钠,调节PH值为9.3,搅拌生成包覆碱式碳酸锌和硫酸钠的混合物,再进行压滤;
2)对压滤得到的碱式碳酸锌进行洗涤,洗涤至物料中无硫酸根,然后干燥至水分小于2.2%;
3)对干燥后的物料于580℃焙烧,即得氧化锌产品。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.氧化锌的制备方法,其特征在于,包括如下步骤:
1)将硫酸锌溶液加热至60℃,加入0.16g/l的六偏磷酸钠、0.53g/l的氧化镁、0.13g/l的活性硅微粉、0.11g/l的乙二醇,搅拌30分钟,加1.5g/l的碳酸钠,调节PH值为9.3,搅拌生成包覆碱式碳酸锌和硫酸钠的混合物,再进行压滤;
2)对压滤得到的碱式碳酸锌进行洗涤,洗涤至物料中无硫酸根,然后干燥至水分小于2.2%;
3)对干燥后的物料于580℃焙烧,即得氧化锌产品。