CN104385414A - Production processing method of coating timber through pinus massoniana carbonized wood - Google Patents
Production processing method of coating timber through pinus massoniana carbonized wood Download PDFInfo
- Publication number
- CN104385414A CN104385414A CN201410587407.9A CN201410587407A CN104385414A CN 104385414 A CN104385414 A CN 104385414A CN 201410587407 A CN201410587407 A CN 201410587407A CN 104385414 A CN104385414 A CN 104385414A
- Authority
- CN
- China
- Prior art keywords
- wood
- masson pine
- coating
- charging
- carbonized wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production processing method of coating timber through pinus massoniana carbonized wood. The production processing method is completed through nine production processes of preparing materials, grinding for the first time, repairing, grinding for the second time, carrying out initial coating, grinding for the third time, recoating, grinding for the fourth time and spraying paint, and has the beneficial effects that superfine pinus massoniana carbonized wood flour is taken as a main raw material to repair the timer and a contact medium of the wood and the coating, meanwhile, a coating material is produced by utilizing calcium bicarbonate, white latex, epoxy acrylate, glutinous rice flour, a light trigger and a curing agent, so that the coating material is fine, moist, strong in adhesive force, wear resistant and stain resistant; the coating material is divided into the initial coating material and the recoating material, so that absorption of moisture in the coating material by the pinus massoniana carbonized wood can be reduced, and the coating timber keeps the smooth and fine outer surface; the test shows that the product coating has fine and compact texture, strong fire resistance, uniform coating, strong impact resistance, wear resistance, stain resistance and good waterproof effect, the performance of the pinus massoniana carbonized wood is improved, the pinus massoniana carbonized wood is well beautified, and the quality and the economic value are improved.
Description
Technical field
The invention belongs to wooden boards production and processing technical field, particularly a kind of production and processing method of masson pine carbonized wood application timber.
Background technology
Because wood surface hardness is relatively low, wear no resistance, external force is easier to cause damaged surfaces.The case hardness of timber can be improved after application to a certain extent, thus alleviate the damage of external force.Forming fine and close coating after application can stop woodwork that the movement of moisture content occurs because of the change of ambient temperature and humidity, thus avoids swelling of wood or contraction and be out of shape, ftracture.When after wood surface application, coating protective woodwork is not out of shape because of the change of ambient humidity, and damage is reduced to minimum level.Meanwhile, to the woodwork that low-grade wood makes, due to the protection of coating, the defect (small holes caused by worms, knot, crack etc.) of itself is also covered up, and improves the value of material inferior to a certain extent, improves the utilization rate of timber.
Woodwork outward appearance through application presents pleasant color, and its surface smoothing is bright and clean, has the gloss of appropriateness, and the decorative pattern that timber is intrinsic simultaneously more clearly manifests after application, is imbued with third dimension, allows the natural aesthetic feeling of timber obtain perfect wash with watercolours and let out.The timber flat for tone and particieboard, MDF can form the colored paint coating of various color and different-style through the application of different process, also can make as the various forms of places such as crackle see.
Timber kind is various, and has unique character as porous, anisotropy, moisture absorption and dehydration, dilation, the shortcoming such as apt to rot, and these change value and the service life of all easily reducing woodwork.Avoid the impact of so many undesirable element, again the natural aesthetic feelings such as their texture of wood, lines, color, texture are displayed, for application, there is many difficulties.
For carbonized wood particularly masson pine carbonized wood, due to the uniqueness of its material, its coating process also has uniqueness, and the research and development group of applicant company, through long term test, have developed a kind of processing method of masson pine carbonized wood application timber.
Summary of the invention
Technical problem to be solved by this invention is: for the deficiencies in the prior art, provides a kind of and better to play its economic worth, effectively utilizes timber resources with the method for masson pine carbonized wood for raw material production application timber, increases wood supply.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is a kind of production and processing method of masson pine carbonized wood application timber, by getting the raw materials ready, a mill, repairing, two mills, rendering, three mills, overcoating, four mills, totally nine large operations of spraying paint complete, and it is characterized in that concrete steps are as follows:
(1) get the raw materials ready: the coarse flour roughing of masson pine carbonized wood rim charge pulverizer being become below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 800-1000 object superfine masson pine charing wood powder; The another coarse flour roughing of glutinous rice pulverizer being become below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 800-1000 object superfine glutinous rice flour.
Then superfine masson pine charing wood powder 18-22 part, glutinous rice flour 2-3 part, the rear mashing off of clear water 20-30 part mixing is got according to weight portion, then add 1-2 part epoxy acrylate to mix, stir 120-180 second by the speed of 1550-1650rpm, obtain repair paint.
Granularity is 800-1000 object heavy carbonic calcium powder 100-120 part, solids content is 30%-35% white glue with vinyl 30-40 part is got in addition and glutinous rice flour 8-12 part mixes according to weight portion, 120-180 second is stirred by the speed of 1550-1650rpm, add ethyl acetate 8-12 part and organosilicon-modified acrylate 6-8 part again, the speed of continuation 1550-1650rpm stirs 120-180 second, make fully to mix, obtain rendering charging.
Get granularity is 800-1000 object heavy carbonic calcium powder 100-120 part, solids content is 20%-25% white glue with vinyl 40-50 part, light trigger 5-6 part and glutinous rice flour 8-12 part in addition again to mix, 120-180 second is stirred by the speed of 1550-1650rpm, then nano-aluminium oxide 8-12 part is added, the speed of continuation 1550-1650rpm stirs 120-180 second, make fully to mix, obtain overcoating charging.
(2) a mill: masson pine charred wood sand mill is polished, makes smooth surface, and form knot eye, then maintenance 8-12 hour by dark for knot mill;
(3) repair: repair paint is put into coating machine, with coating machine, repair paint is brushed on the masson pine charred wood after polishing equably, filling chink, knot eye, small holes caused by worms, then masson pine charred wood is directly put into baking box to toast, baking temperature is 50-60 DEG C, baking time is 13-17 minute, then takes out natural curing 8-12 hour;
(4) two mills: polish with sand mill again, make smooth surface, then maintenance 8-12 hour;
(5) rendering: coating machine is put in rendering charging, is coated with on the masson pine charred wood after being contained in repairing polishing with coating machine by rendering charging equably; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 50-60 DEG C, and baking time is 13-17 minute, then takes out natural curing 8-12 hour;
(6) three mills: polish with sand mill again, make smooth surface, then maintenance 8-12 hour;
(7) overcoating: by overcoating charging put into coating machine, with coating machine by overcoating charging be equably coated be contained on masson pine charred wood; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 50-60 DEG C, and baking time is 13-17 minute, then takes out natural curing 8-12 hour;
(8) four mills: polish with sand mill again, make smooth surface, then maintenance 8-12 hour;
(9) spray paint: by the masson pine carbonized wood material appearance use environmental protection paint even application after polishing, then maintenance 8-12 hour, obtains masson pine carbonized wood application timber.
The invention has the beneficial effects as follows and repair timber with superfine masson pine charing wood powder for main raw material(s), and as the contact medium of timber and coating, more easily make painting feed and masson pine carbonized wood combines together fully; Be coated with charging with appropriate calcium bicarbonate, white glue with vinyl, epoxy acrylate, glutinous rice flour, light trigger and curing agent manufacture simultaneously, make to be coated with charging exquisiteness, to moisten, strong adhesion, wear-resisting, resistant; Painting charging point two kinds of proportionings are made rendering charging and overcoating charging, the low rendering of water content can be made to feed first to be attached on masson pine carbonized wood, thus reduce masson pine carbonized wood to the absorption being coated with moisture in charging, then second time application overcoating charging, can make application timber keep smooth in appearance fine and smooth; Through inspection, this product coating tissue is fine and smooth fine and close, and fire resistance is strong, and application is even, impact resistant capability is strong, wear-resisting, resistant, good water-proof effect, not only increase the performance of masson pine carbonized wood like this, also well beautified masson pine carbonized wood, improve quality and economic worth.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described, and following examples are intended to the present invention instead of limitation of the invention further are described, should not limit the scope of the invention with this.
Embodiment 1.
The roughing of masson pine carbonized wood rim charge pulverizer is become the coarse flour of below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 800 object superfine masson pine charing wood powders; The another coarse flour roughing of glutinous rice pulverizer being become below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 800 object superfine glutinous rice flours.
Get superfine masson pine charing wood powder 18kg, the rear mashing off of glutinous rice flour 2kg, clear water 20kg mixing, then add 1kg epoxy acrylate, stir 120 seconds by the speed of 1550rpm, mix, obtain repair paint.
Get that granularity is 800 object heavy carbonic calcium powder 100kg, solids content be 30% white glue with vinyl 30kg and glutinous rice flour 8kg mix, 120 seconds are stirred by the speed of 1550rpm, add ethyl acetate 8kg and organosilicon-modified acrylate 6kg again, the speed of continuation 1550rpm stirs 120 seconds, make fully to mix, obtain rendering charging.
Get that granularity is 800 object heavy carbonic calcium powder 100kg, solids content be 20% white glue with vinyl 40kg, light trigger 5kg and glutinous rice flour 8kg mix, 120 seconds are stirred by the speed of 1550rpm, then nano-aluminium oxide 8kg is added, the speed of continuation 1550rpm stirs 120 seconds, make fully to mix, obtain overcoating charging.
Masson pine charred wood sand mill is polished, makes smooth surface, form knot eye, then maintenance 8 hours by dark for knot mill; Repair paint is put into coating machine, with coating machine, repair paint is brushed on the masson pine charred wood after polishing equably, repair filling chink, knot eye, small holes caused by worms, then masson pine charred wood is directly put into baking box to toast, baking temperature is 50 DEG C, baking time is 13 minutes, then takes out natural curing 8 hours.
With sand mill, the masson pine charred wood after repairing is polished again, make smooth surface, then maintenance 8 hours; Coating machine is put in rendering charging, with coating machine, rendering charging is coated with on the masson pine charred wood after being contained in repairing polishing equably; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 50 DEG C, and baking time is 13 minutes, then takes out natural curing 8 hours.
With sand mill, the masson pine charred wood after rendering is polished again, make smooth surface, then maintenance 8 hours; Coating machine is put in overcoating charging, with coating machine, overcoating charging is coated with on the masson pine charred wood after being contained in rendering polishing equably; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 50 DEG C, and baking time is 13 minutes, then takes out natural curing 8 hours.
With sand mill, the masson pine charred wood after overcoating is polished again, make smooth surface, then maintenance 8 hours; By the masson pine carbonized wood material appearance use environmental protection paint even application after polishing, then maintenance 8 hours, obtains masson pine carbonized wood application timber.
Embodiment 2.
The roughing of masson pine carbonized wood rim charge pulverizer is become the coarse flour of below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 900 object superfine masson pine charing wood powders; The another coarse flour roughing of glutinous rice pulverizer being become below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 900 object superfine glutinous rice flours.
Get superfine masson pine charing wood powder 20kg, the rear mashing off of glutinous rice flour 2.5kg, clear water 25kg mixing, then add 1.5kg epoxy acrylate, stir 150 seconds by the speed of 1600rpm, mix, obtain repair paint.
Get that granularity is 900 object heavy carbonic calcium powder 110kg, solids content be 32.5% white glue with vinyl 35kg and glutinous rice flour 10kg mix, 150 seconds are stirred by the speed of 1600rpm, add ethyl acetate 10kg and organosilicon-modified acrylate 7kg again, the speed of continuation 1600rpm stirs 150 seconds, make fully to mix, obtain rendering charging.
Get that granularity is 900 object heavy carbonic calcium powder 110kg, solids content be 22.5% white glue with vinyl 45kg, light trigger 5.5kg and glutinous rice flour 10kg mix, 150 seconds are stirred by the speed of 1600rpm, then nano-aluminium oxide 10kg is added, the speed of continuation 1600rpm stirs 150 seconds, make fully to mix, obtain overcoating charging.
Masson pine charred wood sand mill is polished, makes smooth surface, form knot eye, then maintenance 10 hours by dark for knot mill; Repair paint is put into coating machine, with coating machine, repair paint is brushed on the masson pine charred wood after polishing equably, repair filling chink, knot eye, small holes caused by worms, then masson pine charred wood is directly put into baking box to toast, baking temperature is 55 DEG C, baking time is 15 minutes, then takes out natural curing 10 hours.
With sand mill, the masson pine charred wood after repairing is polished again, make smooth surface, then maintenance 10 hours; Coating machine is put in rendering charging, with coating machine, rendering charging is coated with on the masson pine charred wood after being contained in repairing polishing equably; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 55 DEG C, and baking time is 15 minutes, then takes out natural curing 10 hours.
With sand mill, the masson pine charred wood after rendering is polished again, make smooth surface, then maintenance 10 hours; Coating machine is put in overcoating charging, with coating machine, overcoating charging is coated with on the masson pine charred wood after being contained in rendering polishing equably; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 55 DEG C, and baking time is 15 minutes, then takes out natural curing 10 hours.
With sand mill, the masson pine charred wood after overcoating is polished again, make smooth surface, then maintenance 10 hours; By the masson pine carbonized wood material appearance use environmental protection paint even application after polishing, then maintenance 10 hours, obtains masson pine carbonized wood application timber.
Embodiment 3.
The roughing of masson pine carbonized wood rim charge pulverizer is become the coarse flour of below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 1000 object superfine masson pine charing wood powders; The another coarse flour roughing of glutinous rice pulverizer being become below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 1000 object superfine glutinous rice flours.
Get superfine masson pine charing wood powder 22kg, the rear mashing off of glutinous rice flour 3kg, clear water 30kg mixing, then add 2kg epoxy acrylate, stir 180 seconds by the speed of 1650rpm, mix, obtain repair paint.
Get that granularity is 1000 object heavy carbonic calcium powder 120kg, solids content be 35% white glue with vinyl 40kg and glutinous rice flour 12kg mix, 180 seconds are stirred by the speed of 1550-1650rpm, add ethyl acetate 12kg and organosilicon-modified acrylate 8kg again, the speed of continuation 1650rpm stirs 180 seconds, make fully to mix, obtain rendering charging.
Get that granularity is 1000 object heavy carbonic calcium powder 120kg, solids content be 25% white glue with vinyl 50kg, light trigger 6kg and glutinous rice flour 12kg mix, 180 seconds are stirred by the speed of 1650rpm, then nano-aluminium oxide 12kg is added, the speed of continuation 1650rpm stirs 180 seconds, make fully to mix, obtain overcoating charging.
Masson pine charred wood sand mill is polished, makes smooth surface, form knot eye, then maintenance 12 hours by dark for knot mill; Repair paint is put into coating machine, with coating machine, repair paint is brushed on the masson pine charred wood after polishing equably, repair filling chink, knot eye, small holes caused by worms, then masson pine charred wood is directly put into baking box to toast, baking temperature is 60 DEG C, baking time is 17 minutes, then takes out natural curing 12 hours.
With sand mill, the masson pine charred wood after repairing is polished again, make smooth surface, then maintenance 12 hours; Coating machine is put in rendering charging, with coating machine, rendering charging is coated with on the masson pine charred wood after being contained in repairing polishing equably; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 60 DEG C, and baking time is 17 minutes, then takes out natural curing 12 hours.
With sand mill, the masson pine charred wood after rendering is polished again, make smooth surface, then maintenance 12 hours; Coating machine is put in overcoating charging, with coating machine, overcoating charging is coated with on the masson pine charred wood after being contained in rendering polishing equably; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 60 DEG C, and baking time is 17 minutes, then takes out natural curing 12 hours.
With sand mill, the masson pine charred wood after overcoating is polished again, make smooth surface, then maintenance 12 hours; By the masson pine carbonized wood material appearance use environmental protection paint even application after polishing, then maintenance 12 hours, obtains masson pine carbonized wood application timber.
The masson pine carbonized wood application timber that the application timber being adopted by common Masson pine timber the common painting charging that market is bought to adopt prior art to produce and above-mentioned three embodiments are produced carries out contrast and detects, and result is as following table:
As can be known from the above table, the masson pine carbonized wood application timber that the present invention produces and existing employing common wood and the common painting application timber produced of feeding are compared, the finer and smoother densification of its surface evenness, fire resistance is better, and impact resistance power is strong, and scratch-resistant, resistance to soiling are better, although all the same in waterproof effect, but, rear not easily broken owing to being subject to clashing into, so the waterproof effect of product of the present invention is also relatively better.
Claims (1)
1. the production and processing method of masson pine carbonized wood application timber, by getting the raw materials ready, a mill, repairing, two mills, rendering, three mills, overcoating, four mills, totally nine large operations of spraying paint complete, and it is characterized in that concrete steps are as follows:
(1) get the raw materials ready: the coarse flour roughing of masson pine carbonized wood rim charge pulverizer being become below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 800-1000 object superfine masson pine charing wood powder; The another coarse flour roughing of glutinous rice pulverizer being become below 8 orders, more repeatedly pulverize and selection by winnowing with ultra-fine grinding machine, obtaining granularity is 800-1000 object superfine glutinous rice flour;
Then superfine masson pine charing wood powder 18-22 part, glutinous rice flour 2-3 part, the rear mashing off of clear water 20-30 part mixing is got according to weight portion, then 1-2 part epoxy acrylate is added, stir 120-180 second by the speed of 1550-1650rpm, mix, obtain repair paint;
Granularity is 800-1000 object heavy carbonic calcium powder 100-120 part, solids content is 30%-35% white glue with vinyl 30-40 part is got in addition and glutinous rice flour 8-12 part mixes according to weight portion, 120-180 second is stirred by the speed of 1550-1650rpm, add ethyl acetate 8-12 part and organosilicon-modified acrylate 6-8 part again, the speed of continuation 1550-1650rpm stirs 120-180 second, make fully to mix, obtain rendering charging;
Get granularity is 800-1000 object heavy carbonic calcium powder 100-120 part, solids content is 20%-25% white glue with vinyl 40-50 part, light trigger 5-6 part and glutinous rice flour 8-12 part in addition again to mix, 120-180 second is stirred by the speed of 1550-1650rpm, then nano-aluminium oxide 8-12 part is added, the speed of continuation 1550-1650rpm stirs 120-180 second, make fully to mix, obtain overcoating charging;
(2) a mill: masson pine charred wood sand mill is polished, makes smooth surface, and form knot eye, then maintenance 8-12 hour by dark for knot mill;
(3) repair: repair paint is put into coating machine, with coating machine, repair paint is brushed on the masson pine charred wood after polishing equably, filling chink, knot eye, small holes caused by worms, then masson pine charred wood is directly put into baking box to toast, baking temperature is 50-60 DEG C, baking time is 13-17 minute, then takes out natural curing 8-12 hour;
(4) two mills: polish with sand mill again, make smooth surface, then maintenance 8-12 hour;
(5) rendering: coating machine is put in rendering charging, is coated with on the masson pine charred wood after being contained in repairing polishing with coating machine by rendering charging equably; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 50-60 DEG C, and baking time is 13-17 minute, then takes out natural curing 8-12 hour;
(6) three mills: polish with sand mill again, make smooth surface, then maintenance 8-12 hour;
(7) overcoating: by overcoating charging put into coating machine, with coating machine by overcoating charging be equably coated be contained on masson pine charred wood; Then masson pine charred wood is directly put into baking box to toast, baking temperature is 50-60 DEG C, and baking time is 13-17 minute, then takes out natural curing 8-12 hour;
(8) four mills: polish with sand mill again, make smooth surface, then maintenance 8-12 hour;
(9) spray paint: by the masson pine carbonized wood material appearance use environmental protection paint even application after polishing, then maintenance 8-12 hour, obtains masson pine carbonized wood application timber.